CN107815901A - A kind of printed fabric preparation method - Google Patents
A kind of printed fabric preparation method Download PDFInfo
- Publication number
- CN107815901A CN107815901A CN201711038012.3A CN201711038012A CN107815901A CN 107815901 A CN107815901 A CN 107815901A CN 201711038012 A CN201711038012 A CN 201711038012A CN 107815901 A CN107815901 A CN 107815901A
- Authority
- CN
- China
- Prior art keywords
- fabric
- transfer paper
- stamp
- printed
- dyeing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of printed fabric preparation method, including connect cloth, it would be desirable to which the neat corrugationless of fabric of stamp is wrapped on A cabinet frames；Secondly stamp, by dyestuff air brushing in the stamp of transfer paper, described transfer paper is neatly put face-to-face with described fabric, it is 0 to make the dye strength in described fabric and air-gap, described transfer paper is peeled off after 200 DEG C of high-temperature process, treat that described fabric is cooled to 20 DEG C, then liquid color fixing agent is sprayed on fabric after dyeing, and be gradually heating to 60 DEG C；Last sofening treatment, the fabric after dyeing is placed in the liquid containing softening agent after soaking 1 hour to take out and dried, fabric sublimation reliability can be improved, reduce the hardness that printing and dyeing are expected below.
Description
Technical field
The present invention relates to dyeing fabric field, and in particular to a kind of printed fabric preparation method.
Background technology
Printing in textiles there is several methods that, wherein the printing method for having much commercial significance has two kinds：Screen printing and rolling
Cylinder stamp, the third method is thermal transfer printing, and importance is relatively low, other stamps being rarely employed in textile production
Method has：Plank sheathing stamp, wax figured silk fabrics (i.e. wax is prevented) stamp, ikat stamp and resisting printing, many printing in textiles factories
Using screen printing method and roller printing method printing fabric, most of thermal transfer printings that print works are carried out also print in this way
System.
Existing thermal transfer printing pattern has the characteristics of flower pattern is true to nature, decorative pattern is careful, clear layer, strong third dimension, turns
Moving printing equipment has the characteristics of simple in construction, occupation of land is small, small investment, high business efficiency, because equipment is no-station pole canopy processing, fits
Together in the stamp of various thickness, problem of environmental pollution is not present in transfer printing, has high production efficiency, saving labour and operation letter
Just the advantages of, but big there is also paper consumption, the shortcomings of cost is relatively high, disperse dyes liter used in thermal shift assay
The problems such as magnificent fastness is relatively low, and fabric hardens is left to be desired.
The content of the invention
To solve the deficiencies in the prior art, it is an object of the invention to improve fabric sublimation reliability, reduce printing and dyeing and expect below
Hardness.
In order to realize above-mentioned target, the present invention adopts the following technical scheme that：
A kind of printed fabric preparation method, comprises the following steps：
（1）Connect cloth, it would be desirable to which the neat corrugationless of fabric of stamp is wrapped on A cabinet frames；
（2）Stamp, by dyestuff air brushing in the stamp of transfer paper, by one side of the described transfer paper with dyestuff and described face
Charge level opposite is neatly put, and it is 0 to make the dye strength in described fabric and air-gap, is shelled after 200 DEG C of high-temperature process
From described transfer paper；
（3）Fixation, treat that described fabric is cooled to 10 ~ 20 DEG C, then liquid color fixing agent is sprayed on fabric after dyeing, and gradually
It is warming up to 50 ~ 60 DEG C；
（4）Sofening treatment, the fabric after dyeing is placed in the liquid containing softening agent after soaking 1 hour to take out and dried.
Preferably, described fabric uses fabrics of polyester, terylene is with p-phthalic acid（PTA）Or to benzene two
Formic acid dimethyl ester（DMT）And ethylene glycol（EG）For raw material through esterification or ester exchange with it is into fine high poly- prepared by polycondensation reaction
Thing --- polyethylene terephthalate（PET）, through fiber made of spinning and post processing, there is extremely excellent shape stability
Energy.
Preferably, described dyestuff is to include mass ratio to be（2~4）：（1~2）：1000 disperse dyes, ethyl cellulose
Element and the mill base that is mixed of water, disperse dyes have the characteristic of distillation, can be divided into disperse orange, disperse blue, disperse yellow, scattered
It is red, it can according to a certain percentage be arranged in pairs or groups with several different disperse dyes, obtain scattered black, scattered green, disperse violet decile
Dyestuff is dissipated, makes dyestuff color that there is diversity.
Preferably, described transfer paper is resistant substrates film, transferred the pattern onto by temperature and pressure described
On fabric, the stamp that it is printed and dyed out is bright in luster, and in sublimation process, the tar in dyestuff is left in transfer paper, will not
Pollute fabric, the percentage of A-class goods is high, can once print during transfer more sets it is color patterned and needn't be to flower, flexibility is strong.
Preferably, described high-temperature process need to be by described fabric and described transfer paper jointly by 25 ~ 30 seconds
Time-triggered protocol, enable the abundant activity of disperse dyes, improve the color fastness of fabric, faded during pre- prevention fabric use,
Phenomena such as color lump comes off.
Preferably, described liquid fixation agent is, described liquid fixation agent is to include mass ratio to be（10~20）：
1000 color fixing agent Y and water is blended, and is advantageous to the decorative pattern firmly printed and dyed, and is reduced fabric in use and is decolourized.
Preferably, described softening agent is to include mass ratio to be（10~20）：1000 ester quat softening agent and water mixes
System, this softening agent stable performance, dosage is small, prominent biological degradability, more with the multinomial work(such as yellowing-resistant, sterilizing
Energy.
The present invention is advantageous in that：Fabric sublimation reliability can be improved, reduces the hardness that printing and dyeing are expected below.
Embodiment
Make specific introduce to the present invention below in conjunction with specific embodiment.
Embodiment 1
In order to realize above-mentioned target, the present invention adopts the following technical scheme that：
A kind of printed fabric preparation method, comprises the following steps：
（1）Connect cloth, it would be desirable to which the neat corrugationless of fabric of stamp is wrapped on A cabinet frames；
（2）Stamp, by dyestuff air brushing in the stamp of transfer paper, by one side of the described transfer paper with dyestuff and described face
Charge level opposite is neatly put, and it is 0 to make the dye strength in described fabric and air-gap, is shelled after 200 DEG C of high-temperature process
From described transfer paper；
（3）Fixation, treat that described fabric is cooled to 10 DEG C, then liquid color fixing agent is sprayed on fabric after dyeing, and gradually rise
Temperature is to 50 DEG C；
（4）Sofening treatment, the fabric after dyeing is placed in the liquid containing softening agent after soaking 1 hour to take out and dried.
Fabric in the present embodiment uses fabrics of polyester, and terylene is with p-phthalic acid（PTA）Or terephthaldehyde
Dimethyl phthalate（DMT）And ethylene glycol（EG）It is raw material fiber-forming polymer through esterification or prepared by ester exchange and polycondensation reaction ---
Polyethylene terephthalate（PET）, through fiber made of spinning and post processing, there is extremely excellent setting performance.
Dyestuff in the present embodiment is to include mass ratio for 2：1：1000 disperse dyes, ethyl cellulose and water mixing system
Into mill base, disperse dyes have distillation characteristic, disperse orange, disperse blue, disperse yellow, disperse red can be divided into, can with it is several not
Arranged in pairs or groups according to a certain percentage with disperse dyes, obtain the disperse dyes such as scattered black, scattered green, disperse violet, make dyestuff
Color has diversity.
Transfer paper in the present embodiment is resistant substrates film, and described fabric is transferred the pattern onto by temperature and pressure
On, the stamp that it is printed and dyed out is bright in luster, and in sublimation process, the tar in dyestuff is left in transfer paper, will not be polluted
Fabric, the percentage of A-class goods are high, can once print during transfer more sets it is color patterned and needn't be to flower, flexibility is strong.
High-temperature process in the present embodiment need to pass through described fabric and described transfer paper at the time of 25 seconds jointly
Reason, enables the abundant activity of disperse dyes, improves the color fastness of fabric, faded during pre- prevention fabric use, color lump takes off
Phenomena such as falling.
Liquid fixation agent in the present embodiment is that described liquid fixation agent is to include mass ratio for 10：1000 fixation
Agent Y and water are blended, and are advantageous to the decorative pattern firmly printed and dyed, and are reduced fabric in use and are decolourized.
Softening agent in the present embodiment is to include mass ratio for 10：1000 ester quat softening agent and water is blended, this
Softening agent stable performance, dosage is small, prominent biological degradability, more with multiple functions such as yellowing-resistant, sterilizings.
Embodiment 2
In order to realize above-mentioned target, the present invention adopts the following technical scheme that：
A kind of printed fabric preparation method, comprises the following steps：
（1）Connect cloth, it would be desirable to which the neat corrugationless of fabric of stamp is wrapped on A cabinet frames；
（2）Stamp, by dyestuff air brushing in the stamp of transfer paper, by one side of the described transfer paper with dyestuff and described face
Charge level opposite is neatly put, and it is 0 to make the dye strength in described fabric and air-gap, is shelled after 200 DEG C of high-temperature process
From described transfer paper；
（3）Fixation, treat that described fabric is cooled to 15 DEG C, then liquid color fixing agent is sprayed on fabric after dyeing, and gradually rise
Temperature is to 55 DEG C；
（4）Sofening treatment, the fabric after dyeing is placed in the liquid containing softening agent after soaking 1 hour to take out and dried.
Fabric in the present embodiment uses fabrics of polyester, and terylene is with p-phthalic acid（PTA）Or terephthaldehyde
Dimethyl phthalate（DMT）And ethylene glycol（EG）It is raw material fiber-forming polymer through esterification or prepared by ester exchange and polycondensation reaction ---
Polyethylene terephthalate（PET）, through fiber made of spinning and post processing, there is extremely excellent setting performance.
Dyestuff in the present embodiment is to include mass ratio for 3：2：1000 disperse dyes, ethyl cellulose and water mixing system
Into mill base, disperse dyes have distillation characteristic, disperse orange, disperse blue, disperse yellow, disperse red can be divided into, can with it is several not
Arranged in pairs or groups according to a certain percentage with disperse dyes, obtain the disperse dyes such as scattered black, scattered green, disperse violet, make dyestuff
Color has diversity.
Transfer paper in the present embodiment is resistant substrates film, and described fabric is transferred the pattern onto by temperature and pressure
On, the stamp that it is printed and dyed out is bright in luster, and in sublimation process, the tar in dyestuff is left in transfer paper, will not be polluted
Fabric, the percentage of A-class goods are high, can once print during transfer more sets it is color patterned and needn't be to flower, flexibility is strong.
High-temperature process in the present embodiment need to pass through described fabric and described transfer paper at the time of 28 seconds jointly
Reason, enables the abundant activity of disperse dyes, improves the color fastness of fabric, faded during pre- prevention fabric use, color lump takes off
Phenomena such as falling.
Liquid fixation agent in the present embodiment is that described liquid fixation agent is to include mass ratio for 15：1000 fixation
Agent Y and water are blended, and are advantageous to the decorative pattern firmly printed and dyed, and are reduced fabric in use and are decolourized.
Softening agent in the present embodiment is to include mass ratio for 15：1000 ester quat softening agent and water is blended, this
Softening agent stable performance, dosage is small, prominent biological degradability, more with multiple functions such as yellowing-resistant, sterilizings.
Embodiment 3
In order to realize above-mentioned target, the present invention adopts the following technical scheme that：
A kind of printed fabric preparation method, comprises the following steps：
（1）Connect cloth, it would be desirable to which the neat corrugationless of fabric of stamp is wrapped on A cabinet frames；
（2）Stamp, by dyestuff air brushing in the stamp of transfer paper, by one side of the described transfer paper with dyestuff and described face
Charge level opposite is neatly put, and it is 0 to make the dye strength in described fabric and air-gap, is shelled after 200 DEG C of high-temperature process
From described transfer paper；
（3）Fixation, treat that described fabric is cooled to 20 DEG C, then liquid color fixing agent is sprayed on fabric after dyeing, and gradually rise
Temperature is to 60 DEG C；
（4）Sofening treatment, the fabric after dyeing is placed in the liquid containing softening agent after soaking 1 hour to take out and dried.
Fabric in the present embodiment uses fabrics of polyester, and terylene is with p-phthalic acid（PTA）Or terephthaldehyde
Dimethyl phthalate（DMT）And ethylene glycol（EG）It is raw material fiber-forming polymer through esterification or prepared by ester exchange and polycondensation reaction ---
Polyethylene terephthalate（PET）, through fiber made of spinning and post processing, there is extremely excellent setting performance.
Dyestuff in the present embodiment is to include mass ratio for 4：2：1000 disperse dyes, ethyl cellulose and water mixing system
Into mill base, disperse dyes have distillation characteristic, disperse orange, disperse blue, disperse yellow, disperse red can be divided into, can with it is several not
Arranged in pairs or groups according to a certain percentage with disperse dyes, obtain the disperse dyes such as scattered black, scattered green, disperse violet, make dyestuff
Color has diversity.
Transfer paper in the present embodiment is resistant substrates film, and described fabric is transferred the pattern onto by temperature and pressure
On, the stamp that it is printed and dyed out is bright in luster, and in sublimation process, the tar in dyestuff is left in transfer paper, will not be polluted
Fabric, the percentage of A-class goods are high, can once print during transfer more sets it is color patterned and needn't be to flower, flexibility is strong.
High-temperature process in the present embodiment need to pass through described fabric and described transfer paper at the time of 30 seconds jointly
Reason, enables the abundant activity of disperse dyes, improves the color fastness of fabric, faded during pre- prevention fabric use, color lump takes off
Phenomena such as falling.
Liquid fixation agent in the present embodiment is that described liquid fixation agent is to include mass ratio for 20：1000 fixation
Agent Y and water are blended, and are advantageous to the decorative pattern firmly printed and dyed, and are reduced fabric in use and are decolourized.
Softening agent in the present embodiment is to include mass ratio for 20：1000 ester quat softening agent and water is blended, this
Softening agent stable performance, dosage is small, prominent biological degradability, more with multiple functions such as yellowing-resistant, sterilizings.
The present invention's can improve fabric sublimation reliability, reduce the hardness that printing and dyeing are expected below, improve fabric printing quality.
The basic principles, principal features and advantages of the present invention have been shown and described above.The technical staff of the industry should
Understand, the invention is not limited in any way for above-described embodiment, all to be obtained by the way of equivalent substitution or equivalent transformation
Technical scheme, all fall within protection scope of the present invention.
Claims (7)
1. a kind of printed fabric preparation method, it is characterised in that comprise the following steps：
Connect cloth, it would be desirable to which the neat corrugationless of fabric of stamp is wrapped on A cabinet frames；
Stamp, by dyestuff air brushing in the stamp of transfer paper, by one side of the described transfer paper with dyestuff and described fabric
Neatly put face-to-face, it is 0 to make the dye strength in described fabric and air-gap, is peeled off after 200 DEG C of high-temperature process
Described transfer paper；
Fixation, treat that described fabric is cooled to 10 ~ 20 DEG C, then liquid color fixing agent is sprayed on fabric after dyeing, and gradually rise
Temperature is to 50 ~ 60 DEG C；
Sofening treatment, the fabric after dyeing is placed in the liquid containing softening agent after soaking 1 hour to take out and dried.
2. a kind of printed fabric preparation method according to claim 1, it is characterised in that described fabric is fine using terylene
Dimensional fabric.
3. a kind of printed fabric preparation method according to claim 1, it is characterised in that described dyestuff is to include quality
Than for（2~4）：（1~2）：The mill base that 1000 disperse dyes, ethyl cellulose and water is mixed.
4. a kind of printed fabric preparation method according to claim 1, it is characterised in that described transfer paper is resistance to hot radical
Material film, transferred the pattern onto by temperature and pressure on described fabric.
5. a kind of printed fabric preparation method according to claim 1, it is characterised in that described high-temperature process need to be by institute
The fabric stated passes through the time-triggered protocol of 25 ~ 30 seconds with described transfer paper jointly.
A kind of 6. printed fabric preparation method according to claim 1, it is characterised in that described liquid fixation agent is,
Described liquid fixation agent is to include mass ratio to be（10~20）：1000 color fixing agent Y and water is blended.
7. a kind of printed fabric preparation method according to claim 1, it is characterised in that described softening agent is to include matter
Measuring ratio is（10~20）：1000 ester quat softening agent and water is blended.