CN107812937B - 一种适用于激光增材制造用钛合金粉末及制备方法 - Google Patents

一种适用于激光增材制造用钛合金粉末及制备方法 Download PDF

Info

Publication number
CN107812937B
CN107812937B CN201711249301.8A CN201711249301A CN107812937B CN 107812937 B CN107812937 B CN 107812937B CN 201711249301 A CN201711249301 A CN 201711249301A CN 107812937 B CN107812937 B CN 107812937B
Authority
CN
China
Prior art keywords
titanium alloy
less
alloy powder
powder
equal
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201711249301.8A
Other languages
English (en)
Other versions
CN107812937A (zh
Inventor
赵琳
田志凌
韩伟
沈伟
马成勇
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Central Iron and Steel Research Institute
Original Assignee
Central Iron and Steel Research Institute
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Central Iron and Steel Research Institute filed Critical Central Iron and Steel Research Institute
Priority to CN201711249301.8A priority Critical patent/CN107812937B/zh
Publication of CN107812937A publication Critical patent/CN107812937A/zh
Application granted granted Critical
Publication of CN107812937B publication Critical patent/CN107812937B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种适用于激光增材制造用钛合金粉末及制备方法,属于金属粉末技术领域。其化学成分按质量百分比为:Al:5.80%~6.50%,V:3.70%~4.20%,O:≤650ppm,H:≤25ppm,C:≤100ppm,Fe:≤0.2%,N:≤100ppm,余量为Ti。钛合金粉末颗粒为球形形貌,粉末粒径为1~120μm,流动性为5.0~20.0s/50g,钛合金粉末的空心球率小于0.5%。采用等离子旋转电极法制备钛合金粉末,粒径为1~120μm的钛合金粉末,占粉末总质量的65%以上。优点在于,解决现有钛合金粉末存在的问题尤其是氧含量和粉末空心率问题。

Description

一种适用于激光增材制造用钛合金粉末及制备方法
技术领域
本发明属于金属粉末技术领域,尤其涉及一种适用于激光增材制造用钛合金粉末及制备方法。
背景技术
增材制造(3D打印)技术是前沿性、先导性的智能制造技术,引领着传统生产方式和生产工艺的深刻变革,被认为是推动新一轮工业革命的源动力。其中,金属增材制造是增材制造行业中技术难度最大、市场潜力和增长最快的领域之一。金属增材制造能够提升我国工业领域产品开发水平,提高工业设计能力,是建设制造强国、提升综合国力的重要支撑和保障。
金属增材制造技术主要包括激光选区熔化(SLM)、激光近净成形(LENS)、电子束选区熔化(EBSM)、电子束熔丝沉积(EBDM)等,能够直接加工成形不锈钢、Al基合金、Ti基合金,Ni基合金等金属材料。
金属粉末的质量是保证增材制造质量的前提基础,其已成为制约增材制造在我国快速发展的技术瓶颈之一。作为金属激光增材制造最重要材料之一,钛合金粉末传统制备方法为采用坩埚感应熔炼气雾化制备技术,其制备的钛合金粉末存在着氧含量高、粉末空心率高等严重问题。目前,国外知名增材制造用粉末供应商主要采用电极感应熔化气体雾化(EIGA)制粉技术制备钛合金粉末,尽管能有效降低钛合金粉末的氧含量,但由于气雾化制粉技术的局限性,EIGA技术制备的钛合金粉末氧含量仍较高(约1000ppm),并且依旧存在球形度差、空心粉末率高、成分均匀性差以及粒度分布不佳等问题。国内用于激光增材制造的高品质钛合金粉末主要依赖进口,大都由增材制造设备制造企业直接提供,尚未实现第三方供应通用金属粉末材料的模式,导致材料的成本非常高。这在一定程度上限制着我国高端增材制造产业的进一步发展。
因此,适用于激光增材制造技术的钛合金粉末材料的国产化势在必行,研发具有自主知识产权的国产金属粉末材料亟待得到突破解决。
发明内容
本发明的目的在于提供一种激光增材制造用钛合金粉末及制备方法,解决现有钛合金粉末存在的问题尤其是氧含量和粉末空心率问题。
本发明的适用于激光增材制造用钛合金粉末的化学成分按质量百分比为:Al:5.80%~6.50%,V:3.70%~4.20%,O:≤650ppm,H:≤25ppm,C:≤100ppm,Fe:≤0.2%,N:≤100ppm,余量为Ti。钛合金粉末颗粒为球形形貌,粉末粒径为1~120μm,流动性为5.0~20.0s/50g,钛合金粉末的空心球率小于0.5%。
本发明所述的适用于激光增材制造用钛合金粉末的制备方法包括以下步骤:
(1)对钛合金原料进行加工,制备成棒材,化学成分按质量百分比为:Al:5.80%~6.50%,V:3.70%~4.20%,O:≤550ppm,H:≤20ppm,C:≤100ppm,Fe:≤0.2%,N:≤100ppm,余量为Ti。将棒材锻造后,精加工成直径为50~85mm、长度为650~850mm的电极棒,粗糙度小于0.8μm。
(2)采用等离子旋转电极法制备钛合金粉末,电极转速为:10000~20000r/min,采用惰性气体作为保护气体。制成的钛合金粉末,粒径为1~120μm的钛合金粉末,占粉末总质量的65%以上。
所述的一种适用于激光增材制造用钛合金粉末的制备方法,其特征在于,对钛合金粉末分级筛分,采用振动筛机,筛分粒径小于53μm的高品质超细球形钛合金粉末和粒径为53~120μm的高品质球形钛合金粉末;粒径小于53μm的高品质超细球形钛合金粉末为基于铺粉的激光选区熔化(SLM)技术用粉末,粒径为53~120μm的高品质球形钛合金粉末为基于送粉的激光近净成形(LENS)技术用粉末。
附图说明
图1是粒径为小于53μm的高品质超细球形钛合金粉末形貌图
图2是粒径为53~120μm的高品质球形钛合金粉末形貌图。
具体实施方式
以下结合附图以及示例性实施例,对本发明提供的一种适用于激光增材制造用钛合金粉末及其制备方法进行详细说明。
实施例1
对钛合金原料进行加工,制备成棒材,化学成分按质量百分比为:Al 5.85%,V4.10%,O 400ppm,H 20ppm,C 100ppm,Fe 0.08%,N 75ppm,余量为Ti。将棒材锻造后,精加工成直径为75mm、长度为700mm的电极棒,表面粗糙度0.32μm。采用等离子旋转电极法制备钛合金粉末,电极转速为20000r/min,采用Ar作为保护气体。制得钛合金粉末化学成分按质量百分比为:Al 5.98%,V 3.95%,O 480ppm,H 15ppm,C 70ppm,Fe 0.11%,N 85ppm,余量为Ti。钛合金粉末颗粒为球形形貌,粉末粒径为1~120μm,流动性为8.5s/50g,钛合金粉末的空心球率约0.2%。制得的钛合金粉末,粒径为1~120μm的钛合金粉末,占粉末总质量的80%。粒径为1~53μm的高品质超细球形钛合金粉末如图1所示,粒径为53~120μm的高品质球形钛合金粉末如图2所示。
实施例2
对钛合金原料进行加工,制备成棒材,化学成分按质量百分比为:Al 6.28%,V4.22%,O 530ppm,H 20ppm,C 95ppm,Fe 0.13%,N 85ppm,余量为Ti。将棒材锻造后,精加工成直径为50mm、长度为750mm的电极棒,表面粗糙度0.8μm。采用等离子旋转电极法制备钛合金粉末,电极转速为15000r/min,采用Ar作为保护气体。制得钛合金粉末化学成分按质量百分比为:Al 6.41%,V 4.07%,O 630ppm,H 17ppm,C 73ppm,Fe 0.16%,N 96ppm,余量为Ti。钛合金粉末颗粒为球形形貌,粉末粒径为1~120μm,流动性为15s/50g,钛合金粉末的空心球率约0.4%。制得的钛合金粉末,粒径为1~120μm的钛合金粉末,占粉末总质量的67%。
实施例3
对钛合金原料进行加工,制备成棒材,化学成分按质量百分比为:Al 6.03%,V3.92%,O 495ppm,H 19ppm,C 99ppm,Fe 0.09%,N 73ppm,余量为Ti。将棒材锻造后,精加工成直径为80mm、长度为800mm的电极棒,表面粗糙度0.8μm。采用等离子旋转电极法制备钛合金粉末,电极转速为20000r/min,采用Ar作为保护气体。制得钛合金粉末化学成分按质量百分比为:Al 6.11%,V 3.73%,O 590ppm,H 16ppm,C 79ppm,Fe 0.11%,N 81ppm,余量为Ti。钛合金粉末颗粒为球形形貌,粉末粒径为1~120μm,流动性为7.5s/50g,钛合金粉末的空心球率约0.3%。制得的钛合金粉末,粒径为1~120μm的钛合金粉末,占粉末总质量的82%。

Claims (3)

1.一种适用于激光增材制造用钛合金粉末,其特征在于,化学成分按质量百分比为:Al:5.80%~6.50%,V:3.70%~4.20%,O:≤650ppm,H:≤25ppm,C:≤100ppm,Fe:≤0.2%,N:≤100ppm,余量为Ti;钛合金粉末颗粒为球形形貌,粉末粒径为1~120μm,流动性大于等于5.0s/50g且小于20.0s/50g,钛合金粉末的空心球率小于0.5%。
2.一种权利要求1所述的适用于激光增材制造用钛合金粉末的制备方法,其特征在于,包括以下步骤:
(1)对钛合金原料进行加工,制备成棒材,化学成分按质量百分比为:Al:5.80%~6.50%,V:3.70%~4.20%,O:≤550ppm,H:≤20ppm,C:≤100ppm,Fe:≤0.2%,N:≤100ppm,余量为Ti;将棒材锻造后,精加工成直径为50~85mm、长度为650~850mm的电极棒,粗糙度小于0.8μm;
(2)采用等离子旋转电极法制备钛合金粉末,电极转速为:10000~20000r/min,采用惰性气体作为保护气体;制成钛合金粉末,粒径为1~120μm的钛合金粉末,占粉末总质量的65%以上。
3.根据权利要求2所述的方法,其特征在于,采用振动筛机对钛合金粉末分级,筛分粒径为小于53μm的球形钛合金粉末为基于铺粉的激光选区熔化技术用粉末;粒径为53~120μm的球形钛合金粉末为基于送粉的激光近净成形技术用粉末。
CN201711249301.8A 2017-11-30 2017-11-30 一种适用于激光增材制造用钛合金粉末及制备方法 Active CN107812937B (zh)