CN107776111A - 双层保暖面料的生产工艺 - Google Patents

双层保暖面料的生产工艺 Download PDF

Info

Publication number
CN107776111A
CN107776111A CN201610748835.4A CN201610748835A CN107776111A CN 107776111 A CN107776111 A CN 107776111A CN 201610748835 A CN201610748835 A CN 201610748835A CN 107776111 A CN107776111 A CN 107776111A
Authority
CN
China
Prior art keywords
fabric
fabric body
layer
fiber
articulamentum
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610748835.4A
Other languages
English (en)
Inventor
夏忠伟
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangyin Quanshun Textile Co Ltd
Original Assignee
Jiangyin Quanshun Textile Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jiangyin Quanshun Textile Co Ltd filed Critical Jiangyin Quanshun Textile Co Ltd
Priority to CN201610748835.4A priority Critical patent/CN107776111A/zh
Publication of CN107776111A publication Critical patent/CN107776111A/zh
Pending legal-status Critical Current

Abstract

本发明涉及双层保暖面料的生产工艺，其特征在于：包括双层面料本体和连接层，双层面料本体通过所述连接层连接为一个整体，所述面料本体包括双层，分别为面料本体里层和面料本体外层，所述面料本体里层通过连接层相互连接，面料外层朝外，所述面料本体外层上设置有立体条纹，所述立体条纹成折叠状。本发明双层保暖面料的生产工艺通过面料双层设计，大大增强了其面料的保暖性，面料本体外层的立体条纹也大大增强了新型面料的层次感。

Description

双层保暖面料的生产工艺
技术领域
本发明涉及双层保暖面料的生产工艺，属于面料技术领域。
背景技术
随着人类生活水平的提高，人们对制成衣物的面料的性能要求也越来越高。然而目前衣服的面料的层次感不强，保暖效果不好，不能满足人们日益增长的需求。
发明内容
本发明的目的在于克服上述不足，提供层次感强，保暖性好的双层保暖面料的生产工艺。
本发明的目的是这样实现的：
一种双层保暖面料的生产工艺，包括双层面料本体和连接层，双层面料本体通过所述连接层连接为一个整体，所述面料本体包括双层，分别为面料本体里层和面料本体外层，所述面料本体里层通过连接层相互连接，面料外层朝外，所述面料本体外层上设置有立体条纹，所述立体条纹成折叠状。
面料的生产工艺为：
将染色后70%的细支羊毛纤维，30%的聚酯纤维通过和毛→打毛→开松→梳毛（成条）→并条(一并、二并) →气流纺→自动络筒，其中纺纱工艺流程中控制相对湿度50%～55%，温度25℃～30℃；
在和毛工艺中，选用NimateCF-5和毛油，NimateC602阳离子型抗静电剂，以喷雾法，添加占毛量10%的和毛油及占毛量10%的抗静电剂，使纤维具有优异的润滑性，增加纤维的抱合性、抗静电性，提高了纤维的可梳理性，有助于不同性能纤维充分均匀混合；
在梳毛工艺中，喂毛周期掌握50s～60s，出条速度不超过100m/min，出条克重5g/m，不匀系数控制在2%以内；
在并条工艺中，纺制25/1公支的高支粗纺纱，一并的参数8.2，二并后毛条克重控制在4g/m。选用进口自调匀整并条机（D45型），下机毛条克重均匀差异系数不超过0.5%～1%。在这个过程中，必须要控制好牵伸倍数，总牵伸控制7.8倍，其中主牵伸4.58倍，后续牵伸1.7倍，整经→穿综、插筘、插片→剑杆织造，在剑杆织机上将25/1 公支的高支粗纺纱，以2/2的斜纹为基础组织，采用单经单纬的方式上机织造，上机幅宽为178cm，上机经密为225 根/10cm，纬密为216 根/10c，随后经过烧毛-单煮-洗呢-双煮-烘呢-光触媒加工液浸轧-烘呢-TEFLON三防整理-焙烘-熟修-刷毛-剪毛-刷毛-给湿-罐蒸，另外，光触媒加工液的用量30g/l—50g/l，轧液率75%—85%，在光触媒加工液的使用时保持车25m/min—30m/min，温度120℃—135℃，TEFLON三防整理加工的轧液75-85%，车速保持18-22m/min，温度160-180℃，最后制得的面料规格为：纱支96/2-100/2Nm，总紧度145-165，经密615-796根/10厘米，纬密400-358根/10厘米，克重340-390克/米。
与现有技术相比，本发明的有益效果是：
本发明双层保暖面料的生产工艺通过面料双层设计，大大增强了其面料的保暖性，面料本体外层的立体条纹也大大增强了新型面料的层次感。
具体实施方式
本发明涉及一种双层保暖面料的生产工艺，包括双层面料本体和连接层，双层面料本体通过所述连接层连接为一个整体，所述面料本体包括双层，分别为面料本体里层和面料本体外层，所述面料本体里层通过连接层相互连接，面料外层朝外，所述面料本体外层上设置有立体条纹，所述立体条纹成折叠状。
面料的生产工艺为：
将染色后70%的细支羊毛纤维，30%的聚酯纤维通过和毛→打毛→开松→梳毛（成条）→并条(一并、二并) →气流纺→自动络筒，其中纺纱工艺流程中控制相对湿度50%～55%，温度25℃～30℃；
在和毛工艺中，选用NimateCF-5和毛油，NimateC602阳离子型抗静电剂，以喷雾法，添加占毛量10%的和毛油及占毛量10%的抗静电剂，使纤维具有优异的润滑性，增加纤维的抱合性、抗静电性，提高了纤维的可梳理性，有助于不同性能纤维充分均匀混合；
在梳毛工艺中，喂毛周期掌握50s～60s，出条速度不超过100m/min，出条克重5g/m，不匀系数控制在2%以内；
在并条工艺中，纺制25/1公支的高支粗纺纱，一并的参数8.2，二并后毛条克重控制在4g/m。选用进口自调匀整并条机（D45型），下机毛条克重均匀差异系数不超过0.5%～1%。在这个过程中，必须要控制好牵伸倍数，总牵伸控制7.8倍，其中主牵伸4.58倍，后续牵伸1.7倍，整经→穿综、插筘、插片→剑杆织造，在剑杆织机上将25/1 公支的高支粗纺纱，以2/2的斜纹为基础组织，采用单经单纬的方式上机织造，上机幅宽为178cm，上机经密为225 根/10cm，纬密为216 根/10c，随后经过烧毛-单煮-洗呢-双煮-烘呢-光触媒加工液浸轧-烘呢-TEFLON三防整理-焙烘-熟修-刷毛-剪毛-刷毛-给湿-罐蒸，另外，光触媒加工液的用量30g/l—50g/l，轧液率75%—85%，在光触媒加工液的使用时保持车25m/min—30m/min，温度120℃—135℃，TEFLON三防整理加工的轧液75-85%，车速保持18-22m/min，温度160-180℃，最后制得的面料规格为：纱支96/2-100/2Nm，总紧度145-165，经密615-796根/10厘米，纬密400-358根/10厘米，克重340-390克/米。

Claims (1)

1.一种双层保暖面料的生产工艺，其特征在于：包括双层面料本体和连接层，双层面料本体通过所述连接层连接为一个整体，所述面料本体包括双层，分别为面料本体里层和面料本体外层，所述面料本体里层通过连接层相互连接，面料外层朝外，所述面料本体外层上设置有立体条纹，所述立体条纹成折叠状；
面料的生产工艺为：
将染色后70%的细支羊毛纤维，30%的聚酯纤维通过和毛→打毛→开松→梳毛（成条）→并条(一并、二并) →气流纺→自动络筒，其中纺纱工艺流程中控制相对湿度50%～55%，温度25℃～30℃；
在和毛工艺中，选用NimateCF-5和毛油，NimateC602阳离子型抗静电剂，以喷雾法，添加占毛量10%的和毛油及占毛量10%的抗静电剂，使纤维具有优异的润滑性，增加纤维的抱合性、抗静电性，提高了纤维的可梳理性，有助于不同性能纤维充分均匀混合；
在梳毛工艺中，喂毛周期掌握50s～60s，出条速度不超过100m/min，出条克重5g/m，不匀系数控制在2%以内；
在并条工艺中，纺制25/1公支的高支粗纺纱，一并的参数8.2，二并后毛条克重控制在4g/m。选用进口自调匀整并条机（D45型），下机毛条克重均匀差异系数不超过0.5%～1%。在这个过程中，必须要控制好牵伸倍数，总牵伸控制7.8倍，其中主牵伸4.58倍，后续牵伸1.7倍，整经→穿综、插筘、插片→剑杆织造，在剑杆织机上将25/1 公支的高支粗纺纱，以2/2的斜纹为基础组织，采用单经单纬的方式上机织造，上机幅宽为178cm，上机经密为225 根/10cm，纬密为216 根/10c，随后经过烧毛-单煮-洗呢-双煮-烘呢-光触媒加工液浸轧-烘呢-TEFLON三防整理-焙烘-熟修-刷毛-剪毛-刷毛-给湿-罐蒸，另外，光触媒加工液的用量30g/l—50g/l，轧液率75%—85%，在光触媒加工液的使用时保持车25m/min—30m/min，温度120℃—135℃，TEFLON三防整理加工的轧液75-85%，车速保持18-22m/min，温度160-180℃，最后制得的面料规格为：纱支96/2-100/2Nm，总紧度145-165，经密615-796根/10厘米，纬密400-358根/10厘米，克重340-390克/米。
CN201610748835.4A 2016-08-30 2016-08-30 双层保暖面料的生产工艺 Pending CN107776111A (zh)