CN107721364A - A kind of preparation method of fire resistant doorsets packing material - Google Patents

A kind of preparation method of fire resistant doorsets packing material Download PDF

Info

Publication number
CN107721364A
CN107721364A CN201710970913.XA CN201710970913A CN107721364A CN 107721364 A CN107721364 A CN 107721364A CN 201710970913 A CN201710970913 A CN 201710970913A CN 107721364 A CN107721364 A CN 107721364A
Authority
CN
China
Prior art keywords
parts
fire resistant
resistant doorsets
packing
perlite
Prior art date
Application number
CN201710970913.XA
Other languages
Chinese (zh)
Inventor
余小豪
Original Assignee
安徽美林凯迪木业有限公司
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 安徽美林凯迪木业有限公司 filed Critical 安徽美林凯迪木业有限公司
Priority to CN201710970913.XA priority Critical patent/CN107721364A/en
Publication of CN107721364A publication Critical patent/CN107721364A/en

Abstract

The invention discloses a kind of preparation method of fire resistant doorsets packing material, it is prepared from the following raw materials in parts by weight:13 parts of expansion type flame retardant, 8 15 parts of wood powder, 23 parts of additive, 10 15 parts of magnesia, 10 14 parts of magnesium sulfate, 30 40 parts of perlite, 15 25 parts of Firebrake ZB, 8 12 parts of calcium hydroxide and suitable quantity of water, not only will not do harm to huamn body in fire, and rigidity is very strong, the service life of fire resistant doorsets is added, while has good flameproof effect.

Description

A kind of preparation method of fire resistant doorsets packing material

Technical field

The present invention relates to fire proofing material field, and in particular to a kind of preparation method of fire resistant doorsets packing material.

Background technology

Fire resistant doorsets are the doors for having made of applied fireproofing fire stability, integrality and thermal insulation, main to use In the fire wall opening of Building Fire Protection subregion, staircase gateway, evacu-ation walk, pipeline well head etc., the personnel of being ordinarily used for are led to OK, can be played when fire occurs and prevent propagation of flame and to prevent combustion product gases from flowing, and when positive supply air system works from it is close The effect of envelope.In fire prevention increasingly mature today, the building for having fire protection requirement has the figure of fire resistant doorsets, domestic at present Most code for fire protection design are distinctly claimed using fire resistant doorsets.Development, exploitation and the production of fire resistant doorsets product are to ensureing people The safety of people's lives and properties serves positive effect.

The inner core packing material of existing fire resistant doorsets fire-proof wooden door, frequently with mineral fiber material.Such as mineral wool, rock Cotton, glass fibre, aluminosilicate fiber cotton etc..The advantages of these materials is that resistance to elevated temperatures is good, but fibre dust is to operative employee The artificial harm into health, simultaneously because fiber substance is rigidly very poor, door leaf is being opened and closed in use, because vibrations can cause The situation that fiber substance is wriggled downwards gradually, the top of door leaf is set to form space in the course of time, so as to cause fire resistant doorsets to be lost Fire-proof function.

The content of the invention

The present invention provides a kind of preparation method of fire-resistant door core plate material, to solve above-mentioned background technology proposition, by The harm of health is caused to operator in fibre dust, simultaneously because fiber substance is rigidly very poor, door leaf is opening and closing In use, because shaking the situation that fiber substance can be caused to wriggle downwards gradually, the top of door leaf is set to form space in the course of time, So as to cause fire resistant doorsets to lose the technical problem of fire-proof function.

To solve the above problems, the technical solution adopted by the present invention is:A kind of preparation method of fire resistant doorsets packing material, by The raw material of following weight proportion is made:Expansion type flame retardant 1-3 parts, wood powder 8-15 parts, additive 2-3 parts, magnesia 10-15 Part, magnesium sulfate 10-14 parts, perlite 30-40 parts, Firebrake ZB 15-25 parts, calcium hydroxide 8-12 parts and suitable quantity of water.

Preferably, it is prepared from the following raw materials in parts by weight:Expansion type flame retardant 1-2 parts, wood powder 8-11 parts, additive 2- 2.5 parts, magnesia 10-13 parts, magnesium sulfate 10-12 parts, perlite 30-35 parts, Firebrake ZB 15-20 parts, calcium hydroxide 8-10 parts And suitable quantity of water.

Preferably, the raw material is when preparing fire resistant doorsets packing material, after magnesium sulfate first is poured into water into thawing, then by oxygen Change magnesium, which is poured into Adlerika, to stir, and obtains mixed solution;Mixed solution is added thereto under perlite stirring;Treat pearl After rock and mixed solution stir, then pour into calcium hydroxide, Firebrake ZB, wood powder, expansion type flame retardant and additive mixing Even, fire resistant doorsets packing material can be carried out by producing.

Preferably, it, which is made, comprises the following steps:

A, the weight proportion that raw material in core material is filled out by above-mentioned fire resistant doorsets prepares raw material;

B, after epsom salt being poured into water into thawing, then magnesia is poured into Adlerika and stirred, must mixed molten Liquid;

C, step B mixed solution is added thereto under perlite stirring;

D, mixed solution is added thereto under perlite stirring;After perlite and mixed solution stir, then pour into hydrogen-oxygen Change calcium, Firebrake ZB, wood powder, expansion type flame retardant and additive to be well mixed, fire resistant doorsets packing material can be carried out by producing;

E, in the fire resistant doorsets packing material injection fire resistant doorsets obtained step D, 15-20 points are incubated after 70-80 degrees Celsius of heating again Clock.

Preferably, after the material of the anti-fire door core board is mixed, fire resistant doorsets are injected into using compress mode is poured In tempering layer.

Compared with prior art, beneficial effects of the present invention are:The present invention is used and is prepared from the following raw materials in parts by weight: Expansion type flame retardant 1-3 parts, wood powder 8-15 parts, additive 2-3 parts, magnesia 10-15 parts, magnesium sulfate 10-14 parts, perlite 30-40 parts, Firebrake ZB 15-25 parts, the packing material of calcium hydroxide 8-12 parts and fire resistant doorsets made of suitable quantity of water, not only in fire Shi Buhui do harm to huamn bodys, and rigidity is very strong, adds the service life of fire resistant doorsets, while have fire prevention effect well Fruit.

Embodiment

To be readily apparent from technological means, creation feature, reached purpose and effect that the present invention realizes and understanding, tie below Embodiment is closed, the present invention is expanded on further.

A kind of embodiment 1, preparation method of fire resistant doorsets packing material, is prepared from the following raw materials in parts by weight:Intumescent Fire retardant 1-3 parts, wood powder 8-15 parts, additive 2-3 parts, magnesia 10-15 parts, magnesium sulfate 10-14 parts, perlite 30-40 parts, Firebrake ZB 15-25 parts, calcium hydroxide 8-12 parts and suitable quantity of water.

Specifically, it is prepared from the following raw materials in parts by weight:Expansion type flame retardant 1-2 parts, wood powder 8-11 parts, additive 2- 2.5 parts, magnesia 10-13 parts, magnesium sulfate 10-12 parts, perlite 30-35 parts, Firebrake ZB 15-20 parts, calcium hydroxide 8-10 parts And suitable quantity of water.

Specifically, the raw material is when preparing fire resistant doorsets packing material, after magnesium sulfate first is poured into water into thawing, then by oxygen Change magnesium, which is poured into Adlerika, to stir, and obtains mixed solution;Mixed solution is added thereto under perlite stirring;Treat pearl After rock and mixed solution stir, then pour into calcium hydroxide, Firebrake ZB, wood powder, expansion type flame retardant and additive mixing Even, fire resistant doorsets packing material can be carried out by producing.

Comprise the following steps specifically, it is made:

A, the weight proportion that raw material in core material is filled out by above-mentioned fire resistant doorsets prepares raw material;

B, after epsom salt being poured into water into thawing, then magnesia is poured into Adlerika and stirred, must mixed molten Liquid;

C, step B mixed solution is added thereto under perlite stirring;

D, mixed solution is added thereto under perlite stirring;After perlite and mixed solution stir, then pour into hydrogen-oxygen Change calcium, Firebrake ZB, wood powder, expansion type flame retardant and additive to be well mixed, fire resistant doorsets packing material can be carried out by producing;

E, in the fire resistant doorsets packing material injection fire resistant doorsets obtained step D, 15-20 points are incubated after 70-80 degrees Celsius of heating again Clock.

Specifically, after the material of the anti-fire door core board is mixed, fire resistant doorsets are injected into using compress mode is poured In tempering layer.

A kind of embodiment 2, preparation method of fire resistant doorsets packing material, is prepared from the following raw materials in parts by weight:Intumescent Fire retardant 1-3 parts, wood powder 8-15 parts, additive 2-3 parts, magnesia 10-15 parts, magnesium sulfate 10-14 parts, perlite 30-40 parts, Firebrake ZB 15-25 parts, calcium hydroxide 8-12 parts and suitable quantity of water.

Specifically, it is prepared from the following raw materials in parts by weight:Expansion type flame retardant 2-3 parts, wood powder 12-15 parts, additive 2.5-3 parts, magnesia 13-15 parts, magnesium sulfate 12-14 parts, perlite 35-40 parts, Firebrake ZB 20-25 parts, calcium hydroxide 10-12 Part and suitable quantity of water.

Specifically, the raw material is when preparing fire resistant doorsets packing material, after magnesium sulfate first is poured into water into thawing, then by oxygen Change magnesium, which is poured into Adlerika, to stir, and obtains mixed solution;Mixed solution is added thereto under perlite stirring;Treat pearl After rock and mixed solution stir, then pour into calcium hydroxide, Firebrake ZB, wood powder, expansion type flame retardant and additive mixing Even, fire resistant doorsets packing material can be carried out by producing.

Comprise the following steps specifically, it is made:

A, the weight proportion that raw material in core material is filled out by above-mentioned fire resistant doorsets prepares raw material;

B, after epsom salt being poured into water into thawing, then magnesia is poured into Adlerika and stirred, must mixed molten Liquid;

C, step B mixed solution is added thereto under perlite stirring;

D, mixed solution is added thereto under perlite stirring;After perlite and mixed solution stir, then pour into hydrogen-oxygen Change calcium, Firebrake ZB, wood powder, expansion type flame retardant and additive to be well mixed, fire resistant doorsets packing material can be carried out by producing;

E, in the fire resistant doorsets packing material injection fire resistant doorsets obtained step D, 20-25 points are incubated after 75-85 degrees Celsius of heating again Clock.

Specifically, after the material of the anti-fire door core board is mixed, fire resistant doorsets are injected into using compress mode is poured In tempering layer.

Above example only expresses certain embodiment of the present invention, and its description is more specific and detailed, but can not Therefore it is interpreted as the limitation to the scope of the claims of the present invention.It should be pointed out that for the person of ordinary skill of the art, Without departing from the inventive concept of the premise, various modifications and improvements can be made, these belong to the protection model of the present invention Enclose.Therefore, the protection domain of patent of the present invention should be determined by the appended claims.

Claims (5)

1. a kind of preparation method of fire resistant doorsets packing material, it is characterised in that be prepared from the following raw materials in parts by weight:Intumescent Fire retardant 1-3 parts, wood powder 8-15 parts, additive 2-3 parts, magnesia 10-15 parts, magnesium sulfate 10-14 parts, perlite 30-40 parts, Firebrake ZB 15-25 parts, calcium hydroxide 8-12 parts and suitable quantity of water.
2. the preparation method of a kind of fire resistant doorsets packing material according to claim 1, it is characterised in that matched somebody with somebody by following weight The raw material of ratio is made:Expansion type flame retardant 1-2 parts, wood powder 8-11 parts, additive 2-2.5 parts, magnesia 10-13 parts, magnesium sulfate 10-12 parts, perlite 30-35 parts, Firebrake ZB 15-20 parts, calcium hydroxide 8-10 parts and suitable quantity of water.
A kind of 3. preparation method of fire resistant doorsets packing material according to claim 1, it is characterised in that:The raw material is being made During standby fire resistant doorsets packing material, after magnesium sulfate first is poured into water into thawing, then magnesia is poured into Adlerika and stirred It is even, obtain mixed solution;Mixed solution is added thereto under perlite stirring;After perlite and mixed solution stir, then Pour into calcium hydroxide, Firebrake ZB, wood powder, expansion type flame retardant and additive to be well mixed, fire resistant doorsets filling material can be carried out by producing Material.
A kind of 4. preparation method of fire resistant doorsets packing material according to claim 1-3, it is characterised in that its be made including Following steps:
A, the weight proportion that raw material in core material is filled out by above-mentioned fire resistant doorsets prepares raw material;
B, after epsom salt being poured into water into thawing, then magnesia is poured into Adlerika and stirred, must mixed molten Liquid;
C, step B mixed solution is added thereto under perlite stirring;
D, mixed solution is added thereto under perlite stirring;After perlite and mixed solution stir, then pour into hydrogen-oxygen Change calcium, Firebrake ZB, wood powder, expansion type flame retardant and additive to be well mixed, fire resistant doorsets packing material can be carried out by producing;
E, in the fire resistant doorsets packing material injection fire resistant doorsets obtained step D, 15-20 points are incubated after 70-80 degrees Celsius of heating again Clock.
A kind of 5. preparation method of fire resistant doorsets packing material according to claim 1, it is characterised in that:The fire-resistant door core After the material of plate is mixed, it is injected into using compress mode is poured in the tempering layer of fire resistant doorsets.
CN201710970913.XA 2017-10-18 2017-10-18 A kind of preparation method of fire resistant doorsets packing material CN107721364A (en)