CN107686327A - A kind of non-slip artificial stone - Google Patents
A kind of non-slip artificial stone Download PDFInfo
- Publication number
- CN107686327A CN107686327A CN201710902822.2A CN201710902822A CN107686327A CN 107686327 A CN107686327 A CN 107686327A CN 201710902822 A CN201710902822 A CN 201710902822A CN 107686327 A CN107686327 A CN 107686327A
- Authority
- CN
- China
- Prior art keywords
- parts
- mesh
- accounted
- artificial stone
- granularity
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of non-slip artificial stone, fraction proportioning by weight is made up of following components：18 21 parts of low-melting-point glass powder, 40 parts of resin, 44 57 parts of quartz sand, 30 parts of inanimate matter pellet, 16 21 parts of silica flour, 20 parts of middling flour, 26 parts of accelerator, 5 parts of low-melting-point glass powder, 41 53 parts of water, 34 parts of emulsion adhesive, 69 parts of water reducer, 23 43 parts of hollow glass microbead, 35 parts of pigment, 23 parts of dyestuff.The advantage of the invention is that：In the present invention, the outfit of various materials, the artificial quartz in lump of lines excellent can be formed.
Description
Technical field
The present invention relates to building material field, more particularly to a kind of non-slip artificial stone.
Background technology
The technique of existing resin type artificial slabstone is resin be first stirred with quartz sand powder carry out afterwards mould into
Type, it will be chemically reacted after being opened because of resin with air, solvent begins to volatilize, therefore can be by the time in mould cloth
Limitation, and because resin adhesive viscosity is rendered, material dispersion is difficult in mould, skewness, causes plate surface to spend
Each position Density inhomogeneity of line, sheet material, density cause stress to differ and yielding for a moment.
Artificial slabstone traditional at present is entirely adhesive with unsaturated-resin, therefore needs accelerator, coupling agent, consolidates
Agent is chemically auxiliary material, it is specific the shortcomings that：1st, there are harmful exhaust, waste water in process.2nd, sheet material is harmful in use
Material separates out unsuitable and direct food contact.3rd, case hardness is low typically in 6 Mohs or so, and finish is poor.
The content of the invention
The technical problem to be solved in the present invention is to provide a kind of stress uniformly, be unlikely to deform, without any chemical addition agent, ring
Protect nontoxic non-slip artificial stone.
In order to solve the above technical problems, the technical scheme is that：A kind of non-slip artificial stone, its innovative point are：Press
Weight fraction proportioning is made up of following components：
Low-melting-point glass powder 18-21 parts, 40 parts of resin, quartz sand 44-57 parts, 30 parts of inanimate matter pellet, silica flour 16-21 parts, slightly
20 parts of stone flour, accelerator 2-6 parts, 5 parts of low-melting-point glass powder, water 41-53 parts, emulsion adhesive 3-4 parts, water reducer 6-9 parts, double glazing
Microballon 23-43 parts, pigment 3-5 parts, dyestuff 2-3 parts.
Further, the granularity of the quartz sand is that 10 ~ 20 mesh account for 30%, accounts for 25% for 30 ~ 60 mesh, is accounted for for 60 ~ 80 mesh
30%, 10% is accounted for for 80 ~ 100 mesh, 5% is accounted for for 100 ~ 120 mesh.
Further, the granularity of the glass dust is that 400 ~ 500 mesh account for 26%, and the granularity of silica flour accounts for for 150 ~ 250 mesh
28%, 30% is accounted for for 250 ~ 300 mesh, accounts for 16% for 300 ~ 400 mesh, the glass dust and silica flour are blended into melten gel matrix.
Further, the compressive strength of the hollow glass microbead is in 25MPa-120MPa, the particle diameter of hollow glass microbead
For 10-100um.
The advantage of the invention is that：The non-slip artificial stone of the present invention is solid durable, good antiskid effect, and using effect is good.
It is emery dust state in mould cloth, cloth is very easy to and uniformly, the time is unrestricted, is melted soft in the present invention
Bonding is just started in pressure forming after the completion of cloth, and the plate surface decorative pattern of formation is controllable and uniform, each position of sheet material is close
Degree is uniform, and stress is uniform, is unlikely to deform, and hardness and thickness requirement is greatly improved.
The outfit of various materials, the artificial quartz in lump of lines excellent can be formed.
Using a variety of different grain sizes（Mesh number）The purpose that quartz sand carries out different proportion mixing is to reach quartz sand same
Loading in one volume reaches maximization, while improving intensity, improves lines visual effect.
Embodiment
The following examples can make professional and technical personnel that the present invention be more fully understood, but therefore not send out this
It is bright to be limited among described scope of embodiments.
Embodiment 1
The non-slip artificial stone of present invention fraction proportioning by weight is made up of following components：
Fraction proportioning by weight is made up of following components：
18 parts of low-melting-point glass powder, 40 parts of resin, 44 parts of quartz sand, 30 parts of inanimate matter pellet, 16 parts of silica flour, 20 parts of middling flour,
2 parts of accelerator, 5 parts of low-melting-point glass powder, 41 parts of water, 3 parts of emulsion adhesive, 6 parts of water reducer, 23 parts of hollow glass microbead, 3 parts of pigment,
2 parts of dyestuff.
In above-mentioned formula, the granularity of quartz sand accounts for 30% for 10 ~ 20 mesh, accounts for 25% for 30 ~ 60 mesh, is accounted for for 60 ~ 80 mesh
30%, 10% is accounted for for 80 ~ 100 mesh, accounts for 5% for 100 ~ 120 mesh, the granularity of glass dust accounts for 26% for 400 ~ 500 mesh, the granularity of silica flour
28% is accounted for for 150 ~ 250 mesh, 30% is accounted for for 250 ~ 300 mesh, accounts for 16% for 300 ~ 400 mesh, the glass dust and silica flour are blended into molten
Matrix body, in 25MPa-120MPa, the particle diameter of hollow glass microbead is 10-100um for the compressive strength of hollow glass microbead.
Embodiment 2
The non-slip artificial stone of present invention fraction proportioning by weight is made up of following components：
Fraction proportioning by weight is made up of following components：
21 parts of low-melting-point glass powder, 40 parts of resin, 57 parts of quartz sand, 30 parts of inanimate matter pellet, 21 parts of silica flour, 20 parts of middling flour,
6 parts of accelerator, 5 parts of low-melting-point glass powder, 53 parts of water, 4 parts of emulsion adhesive, 9 parts of water reducer, 43 parts of hollow glass microbead, 5 parts of pigment,
3 parts of dyestuff.
In above-mentioned formula, the granularity of quartz sand accounts for 30% for 10 ~ 20 mesh, accounts for 25% for 30 ~ 60 mesh, is accounted for for 60 ~ 80 mesh
30%, 10% is accounted for for 80 ~ 100 mesh, accounts for 5% for 100 ~ 120 mesh, the granularity of glass dust accounts for 26% for 400 ~ 500 mesh, the granularity of silica flour
28% is accounted for for 150 ~ 250 mesh, 30% is accounted for for 250 ~ 300 mesh, accounts for 16% for 300 ~ 400 mesh, the glass dust and silica flour are blended into molten
Matrix body, in 25MPa-120MPa, the particle diameter of hollow glass microbead is 10-100um for the compressive strength of hollow glass microbead.
Embodiment 3
The non-slip artificial stone of present invention fraction proportioning by weight is made up of following components：
Fraction proportioning by weight is made up of following components：
20 parts of low-melting-point glass powder, 40 parts of resin, 50 parts of quartz sand, 30 parts of inanimate matter pellet, 18 parts of silica flour, 20 parts of middling flour,
4 parts of accelerator, 5 parts of low-melting-point glass powder, 47 parts of water, 3 parts of emulsion adhesive, 7 parts of water reducer, 33 parts of hollow glass microbead, 4 parts of pigment,
2 parts of dyestuff.
In above-mentioned formula, the granularity of quartz sand accounts for 30% for 10 ~ 20 mesh, accounts for 25% for 30 ~ 60 mesh, is accounted for for 60 ~ 80 mesh
30%, 10% is accounted for for 80 ~ 100 mesh, accounts for 5% for 100 ~ 120 mesh, the granularity of glass dust accounts for 26% for 400 ~ 500 mesh, the granularity of silica flour
28% is accounted for for 150 ~ 250 mesh, 30% is accounted for for 250 ~ 300 mesh, accounts for 16% for 300 ~ 400 mesh, the glass dust and silica flour are blended into molten
Matrix body, in 25MPa-120MPa, the particle diameter of hollow glass microbead is 10-100um for the compressive strength of hollow glass microbead.
The non-slip artificial stone of the present invention is solid durable, good antiskid effect, and using effect is good.
It is emery dust state in mould cloth, cloth is very easy to and uniformly, the time is unrestricted, is melted soft in the present invention
Bonding is just started in pressure forming after the completion of cloth, and the plate surface decorative pattern of formation is controllable and uniform, each position of sheet material is close
Degree is uniform, and stress is uniform, is unlikely to deform, and hardness and thickness requirement is greatly improved.
The outfit of various materials, the artificial quartz in lump of lines excellent can be formed.
Using a variety of different grain sizes（Mesh number）The purpose that quartz sand carries out different proportion mixing is to reach quartz sand same
Loading in one volume reaches maximization, while improving intensity, improves lines visual effect.
It should be understood by those skilled in the art that the present invention is not limited to the above embodiments, above-described embodiment and explanation
Merely illustrating the principles of the invention described in book, without departing from the spirit and scope of the present invention, the present invention also have
Various changes and modifications, these changes and improvements all fall within the protetion scope of the claimed invention.The claimed scope of the invention
By appended claims and its equivalent thereof.
Claims (4)
- A kind of 1. non-slip artificial stone, it is characterised in that：Fraction proportioning by weight is made up of following components：Low-melting-point glass powder 18-21 parts, 40 parts of resin, quartz sand 44-57 parts, 30 parts of inanimate matter pellet, silica flour 16-21 parts, slightly 20 parts of stone flour, accelerator 2-6 parts, 5 parts of low-melting-point glass powder, water 41-53 parts, emulsion adhesive 3-4 parts, water reducer 6-9 parts, double glazing Microballon 23-43 parts, pigment 3-5 parts, dyestuff 2-3 parts.
- 2. non-slip artificial stone according to claim 1, it is characterised in that：The granularity of the quartz sand is that 10 ~ 20 mesh account for 30%, 25% is accounted for for 30 ~ 60 mesh, 30% is accounted for for 60 ~ 80 mesh, 10% is accounted for for 80 ~ 100 mesh, 5% is accounted for for 100 ~ 120 mesh.
- 3. non-slip artificial stone according to claim 1, it is characterised in that：The granularity of the glass dust is that 400 ~ 500 mesh account for 26%, the granularity of silica flour accounts for 28% for 150 ~ 250 mesh, and 30% is accounted for for 250 ~ 300 mesh, accounts for 16% for 300 ~ 400 mesh, the glass dust Melten gel matrix is blended into silica flour.
- 4. non-slip artificial stone according to claim 1, it is characterised in that：The compressive strength of the hollow glass microbead exists 25MPa-120MPa, the particle diameter of hollow glass microbead is 10-100um.