CN107675332A - The production method of the light and warm fabric of gas is deposited in a kind of tatting - Google Patents

The production method of the light and warm fabric of gas is deposited in a kind of tatting Download PDF

Info

Publication number
CN107675332A
CN107675332A CN201711232972.3A CN201711232972A CN107675332A CN 107675332 A CN107675332 A CN 107675332A CN 201711232972 A CN201711232972 A CN 201711232972A CN 107675332 A CN107675332 A CN 107675332A
Authority
CN
China
Prior art keywords
fabric
yarn
gas
light
warm
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201711232972.3A
Other languages
Chinese (zh)
Inventor
俞金林
符爱芬
徐导
姜红飞
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
JIANGSU DANMAO TEXTILE CO Ltd
Original Assignee
JIANGSU DANMAO TEXTILE CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by JIANGSU DANMAO TEXTILE CO Ltd filed Critical JIANGSU DANMAO TEXTILE CO Ltd
Priority to CN201711232972.3A priority Critical patent/CN107675332A/en
Publication of CN107675332A publication Critical patent/CN107675332A/en
Pending legal-status Critical Current

Abstract

The invention discloses the production method that the light and warm fabric of gas is deposited in a kind of tatting, such Fabric Design uses plain weave basic structure, and by the use of additional warp or weft yarn as flotation line in cloth bottom, crepe weaves using plain weave, pass through the design of fabric construction, difference is shunk to increase air storage space using different yarns, improves the warm degree of fabric;Using the multiple yarn of color, be a kind of no twist spun yarn and superfine long filament color again, make fabric filling and warmth retention property increased by bristle;Wrinkle fabrics are produced using elastomeric yarn, its effect that wrinkles depends on dressing or the dyeing close to boiling point, contraction and fabric face is deformed and is reached ideal, and retain required deform using stentering forming;Fulling milling, fluffing technique are produced along volt lint in final finishing, are made fabric bulk and are not emerging on cloth cover.Produce that structure is bulk, has and deposits the fabric of gas effect by these methods so that the fabric is with excellent warming effect and with frivolous style.

Description

The production method of the light and warm fabric of gas is deposited in a kind of tatting
Technical field
The present invention, which develops series, has the light and warm woven fabric for depositing gas effect, is particularly suitable for the warming of wool fabric The performance of characteristic, belong to textile designs field.
Background technology
Wool makes as a kind of natural fiber with excellent thermal property, its unique natural crimp and surface scale layer It has a wide range of applications possibility.At present, the exploitation to wool fabric is generally divided into thick and heavy type and light and thin type, and traditional product is in order to send out The warmth retention property for waving wool fabric then develops product specification to thick and heavy type, and Gram Mass is very high.On the one hand causing raw material makes Dosage is big, and entreprise cost increase is huge;On the other hand, the wearability of heavily fabric and easy care performance can be produced not as light and thin type Product.But light and thin type product does not possess excellent thermal property again.
The content of the invention
In order to overcome light and thin type product not have the characteristics of warmth retention property, meet that the increasingly harsh clothes of consumer use and want Ask, the present invention develops serial light and warm woven fabric.Not only weight significantly mitigates the serial fabric, and raw material is also had more using upper Extensive adaptability, meet frivolous and warm requirement.
To achieve the above object, the technical solution adopted by the present invention is as follows:
1st, ramuscule and thick branch wool are mixed, produces the yarn of bulk fabric, bulk Lambswool Yarns, sheep son's hair are produced in this programme Fineness is 22.1u, spins 18s rove and makees weft yarn, warp thread spins 96s yarns using fineness 18.5u wool tops.
2nd, such Fabric Design uses plain weave basic structure, and makes by the use of additional warp or weft yarn as flotation line in cloth bottom Warm degree improves;Crepe weaves using plain weave, difference is shunk to increase air storage space using different yarns, spins 52s sheep 3% elastic spandex silk is added during wool worsted yarn, and 48s/2 and sth. made by twisting, spins wool elastomeric yarn.
3rd, using the multiple yarn of color, it is a kind of spun yarn of no twist, is got up again by superfine long filament color, makees fabric filling simultaneously Warmth retention property is increased by bristle, is spun into 12.5s warp thread and the multiple weft yarn of 12s colors and wool slubbing.
4th, wrinkle fabrics are produced using elastomeric yarn, its effect that wrinkles depends on dressing or the dyeing close to boiling point, makes Shrink and fabric face deformation reaches ideal, and deformed using needed for stentering forming reservation.
5th, produced by fulling milling, fluffing technique in final finishing along volt lint, make fabric bulk and be not emerging on cloth cover, The auxiliary cropping for pressing close to cloth cover, make face, bottom difference bigger, design three kinds of finishing techniques altogether:Squezzing drying-braying-fulling milling- Dye-drying-cloth bottom fluffing-cloth cover cropping-light decatizing;Squezzing is shaped(Base steams)- braying-fulling milling-cloth cover cropping-cloth bottom fluffing- It is dry whole;Pre-setting-crabbing-open washing boils-piece dyeing(Wash)- drying-sizing-is dry whole.
Beneficial effects of the present invention:By increasing the loftiness of fabric, flexing increases between making yarn, and it is more that structure is bulk Bullet, and further intensification and this system of sealing are processed by final finishing, fabric is produced air chamber, utilize the low heat conduction system of air Number improves the overall warmth retention property of fabric and fabric is had lightening feature.
Brief description of the drawings
The present invention is further described with example below in conjunction with the accompanying drawings.
Fig. 1 does weft yarn using delaine yarn as warp thread and bulk Lambswool Yarns, makes plain cloth, and cloth bottom is to fluff Processing, to provide kind extra warming sense, while did not increased weight.
Fig. 2 soft coarse woolen fabrics are the multiple yarns of the bulk non-twist color added using cloth bottom to increase warming sense.
Fig. 3 is combined using spun yarn and pure wool spandex core-spun yarn, makes the air chamber structure for depositing gas.
Embodiment
Example 1:
In Fig. 1, design organization structure:Plain cloth, through 95 close 355/10cm, filling density/10cm.
Design yams:Spin warp thread 96s/2 wool plugs Lip river(18.5u), weft yarn 18s/2 sheep son's woolen spinning yarns(22.1u Sheep son's hair).
Design arranges flow:Squezzing drying-braying-fulling milling-piece dyeing-drying-cloth bottom fluffing-cloth cover cropping-light decatizing.
Example 2:
In Fig. 2, institutional framework is as schemed, through 215 close 120/10cm, filling density/10cm.
Yarn texture:Through -12.5/1,21.5u~23u wool slubbing yarns, latitude -12.5/1,21.5u~23u wools Slubbing yarn, latitude -12/1, the multiple yarn of 23u~25u colors.
Arrange flow:Squezzing is shaped(Base steams)- braying-fulling milling-cloth cover cropping-fluffing at cloth bottom-is done whole.
Example 3:
In Fig. 3, institutional framework is as schemed, through 198 close 205/10cm, filling density/10cm.
Yarn texture:The wool worsted yarn of 52s/2,19.5u, 48s/2(97%), 19.5u, 3% Lycra.
Arrange flow:Pre-setting-crabbing-open washing boils-piece dyeing(Wash)- drying-sizing-is dry whole.

Claims (5)

1. the production method of the light and warm fabric of gas is deposited in a kind of tatting, it is used in conjunction with each other using spun yarn and slubbing yarn, makes fabric Leavening structure, which generates, deposits gas effect, and fabric has warming effect and frivolous style, it is characterised in that:By ramuscule and thick branch wool The yarn of mixture manufacturing is bulk fabric, bulk Lambswool Yarns is produced in this programme, its sheep son's capillary degree is 22.1u, spins 18s rove Make weft yarn, warp thread spins 96s yarns using fineness 18.5u wool tops.
2. the production method of the light and warm fabric of gas is deposited in a kind of tatting according to right 1, it is characterised in that:Such Fabric Design is adopted With plain weave basic structure, and by the use of additional warp or weft yarn as flotation line in cloth bottom, make warm degree raising;Wrinkle using plain weave Tissue, difference is shunk using different yarns to increase air storage space, spin the wool worsted yarns of 52s, and 48s/2 and during twisting with the fingers 3% elastic spandex silk is added, spins wool elastomeric yarn.
3. the production method of the light and warm fabric of gas is deposited in a kind of tatting according to right 1, it is characterised in that:Yarn is answered using color, it It is a kind of spun yarn of no twist, is got up again by superfine long filament color, makees fabric filling and warmth retention property, spinning are increased by bristle Into 12.5s warp thread and the multiple weft yarn of 12s colors and wool slubbing.
4. the production method of the light and warm fabric of gas is deposited in a kind of tatting according to right 1, it is characterised in that:Produced using elastomeric yarn Go out wrinkle fabrics, its effect that wrinkles depends on dressing or the dyeing close to boiling point, contraction and fabric face is deformed and is reached reason Think, and retain required deform using stentering forming.
5. the production method of the light and warm fabric of gas is deposited in a kind of tatting according to right 1, it is characterised in that:By being contracted in final finishing Suede, fluffing technique produce along volt lint, make fabric bulk and be not emerging on cloth cover, the auxiliary cropping for pressing close to cloth cover, make face, Bottom difference is bigger, designs three kinds of finishing techniques altogether:Squezzing drying-braying-fulling milling-piece dyeing-drying-cloth bottom fluffing-cloth cover cropping- Light decatizing;Squezzing is shaped(Base steams)- braying-fulling milling-cloth cover cropping-fluffing at cloth bottom-is done whole;Pre-setting-crabbing-open washing boils- Dye(Wash)- drying-sizing-is dry whole.
CN201711232972.3A 2017-11-30 2017-11-30 The production method of the light and warm fabric of gas is deposited in a kind of tatting Pending CN107675332A (en)