CN107663405A - A kind of anti-flaming dope - Google Patents
A kind of anti-flaming dope Download PDFInfo
- Publication number
- CN107663405A CN107663405A CN201710869409.0A CN201710869409A CN107663405A CN 107663405 A CN107663405 A CN 107663405A CN 201710869409 A CN201710869409 A CN 201710869409A CN 107663405 A CN107663405 A CN 107663405A
- Authority
- CN
- China
- Prior art keywords
- parts
- flaming dope
- raw material
- fire retardant
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
A kind of anti-flaming dope of the present invention, is made up of the raw material of following parts by weight:36-68 parts of phenolic resin, 16-28 parts of polyvinyl alcohol, 14-18 parts of cellulose acetate, 12-28 parts of polyvinylpyrrolidone, 4-18 parts of trihydroxy methyl propane, 2-8 parts of diethyl toluene diamine, 12 parts of fire retardant.The fire resistance of the coating of gained of the invention is splendid.
Description
Technical field
The present invention relates to a kind of coating, more particularly to a kind of anti-flaming dope.
Background technology
Traditional anti-flaming dope is usually halogenated flame retardant, but halogenated flame retardant can produce poisonous stimulation in burning
Property gas and its be also easy to produce secondary pollution as discarded object.To meet increasingly strict environmental requirement, it is badly in need of searching one kind and has concurrently
The anti-flaming dope of fire resistance and environmental-protecting performance.
The content of the invention
The present invention proposes a kind of anti-flaming dope regarding to the issue above.
Specific technical scheme is as follows:
A kind of anti-flaming dope, it is characterised in that be made up of the raw material of following parts by weight:
36-68 parts of phenolic resin, 16-28 parts of polyvinyl alcohol, 14-18 parts of cellulose acetate, polyvinylpyrrolidone 12-28
Part, 4-18 parts of trihydroxy methyl propane, 2-8 parts of diethyl toluene diamine, fire retardant 1-2 parts.
Above-mentioned a kind of anti-flaming dope, it is characterised in that the fire retardant is made up of the raw material of following parts by weight:
2-23 parts of APP, 6-18 parts of pentaerythrite, 2-6 parts of melamine, 2-7 parts of magnesium hydroxide, aluminium hydroxide 3-
7 parts, 11-28 parts of titanium dioxide, 1-9 parts of carbon black pellet, 11-19 parts of diethyl ethylphosphate.
Above-mentioned a kind of anti-flaming dope, it is characterised in that the particle diameter of carbon black pellet is 60-120nm.
The fire resistance of the coating of gained of the invention is splendid, and to environment environmental protection.
Embodiment
To make technical scheme become apparent from clearly, below the present invention is described further, it is any to this
The scheme that the technical characteristic progress equivalencing of inventive technique scheme and conventional reasoning are drawn each falls within the scope of the present invention.
Embodiment 1
A kind of anti-flaming dope, it is characterised in that be made up of the raw material of following parts by weight:
36 parts of phenolic resin, 16 parts of polyvinyl alcohol, 14 parts of cellulose acetate, 12 parts of polyvinylpyrrolidone, trihydroxy methyl third
4 parts of alkane, 2 parts of diethyl toluene diamine, 1 part of fire retardant.
Above-mentioned a kind of anti-flaming dope, it is characterised in that the fire retardant is made up of the raw material of following parts by weight:
2 parts of APP, 6 parts of pentaerythrite, 2 parts of melamine, 2 parts of magnesium hydroxide, 3 parts of aluminium hydroxide, 11 parts of titanium dioxide, charcoal
Black 1 part of particle, 11 parts of diethyl ethylphosphate.
The particle diameter of carbon black pellet is 60nm.
Embodiment 2
A kind of anti-flaming dope, it is characterised in that be made up of the raw material of following parts by weight:
68 parts of phenolic resin, 28 parts of polyvinyl alcohol, 18 parts of cellulose acetate, 28 parts of polyvinylpyrrolidone, trihydroxy methyl third
18 parts of alkane, 8 parts of diethyl toluene diamine, 2 parts of fire retardant.
Above-mentioned a kind of anti-flaming dope, it is characterised in that the fire retardant is made up of the raw material of following parts by weight:
23 parts of APP, 18 parts of pentaerythrite, 6 parts of melamine, 7 parts of magnesium hydroxide, 7 parts of aluminium hydroxide, 28 parts of titanium dioxide,
9 parts of carbon black pellet, 19 parts of diethyl ethylphosphate.
The particle diameter of carbon black pellet is 120nm.
Claims (3)
1. a kind of anti-flaming dope, it is characterised in that be made up of the raw material of following parts by weight:
36-68 parts of phenolic resin, 16-28 parts of polyvinyl alcohol, 14-18 parts of cellulose acetate, polyvinylpyrrolidone 12-28
Part, 4-18 parts of trihydroxy methyl propane, 2-8 parts of diethyl toluene diamine, fire retardant 1-2 parts.
A kind of 2. anti-flaming dope as claimed in claim 1, it is characterised in that the fire retardant by following parts by weight raw material system
Into:
2-23 parts of APP, 6-18 parts of pentaerythrite, 2-6 parts of melamine, 2-7 parts of magnesium hydroxide, aluminium hydroxide 3-
7 parts, 11-28 parts of titanium dioxide, 1-9 parts of carbon black pellet, 11-19 parts of diethyl ethylphosphate.
3. a kind of anti-flaming dope as claimed in claim 1, it is characterised in that the particle diameter of the carbon black pellet is 60-120nm.