CN107604406A - 一种高硬度螺栓的电镀工艺 - Google Patents

一种高硬度螺栓的电镀工艺 Download PDF

Info

Publication number
CN107604406A
CN107604406A CN201711013100.8A CN201711013100A CN107604406A CN 107604406 A CN107604406 A CN 107604406A CN 201711013100 A CN201711013100 A CN 201711013100A CN 107604406 A CN107604406 A CN 107604406A
Authority
CN
China
Prior art keywords
bolt
electroplating
pickling
time
rigidity
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201711013100.8A
Other languages
English (en)
Inventor
徐建华
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Suzhou Huafeng Stainless Steel Fastener Co Ltd
Original Assignee
Suzhou Huafeng Stainless Steel Fastener Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Suzhou Huafeng Stainless Steel Fastener Co Ltd filed Critical Suzhou Huafeng Stainless Steel Fastener Co Ltd
Priority to CN201711013100.8A priority Critical patent/CN107604406A/zh
Publication of CN107604406A publication Critical patent/CN107604406A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种高硬度螺栓的电镀工艺,具体包括如下步骤:将螺栓放入酸洗池内进行酸洗处理,去除表面氧化层,酸洗温度为30‑50℃,酸洗时间为10‑20min,完成后将螺栓放入清洗池内清洗干净;将螺栓接入电流为30‑50mA的电路中进行电击处理,电击时间为5‑10min;将螺栓放于电镀池的阴极,并将高硬度合金放于电镀池的阳极,所述电镀池内电流密度为2‑10mA/cm2,电镀温度为20‑60℃,电镀时间为6‑14min,通过上述方式,本发明不仅能够提高螺栓表面的硬度性能,使用寿命长,而且能够使得螺栓表面的电镀层均匀分布,电镀质量高。

Description

一种高硬度螺栓的电镀工艺
技术领域
[0001]本发明涉及一种加工方法,特别涉及一种高硬度螺栓的电镀工艺。
背景技术
[0002]众所周知,螺栓,配用螺母的圆柱形带螺纹的紧固件,是由头部和螺杆(带有外螺 纹的圆柱体)两部分组成的一类紧固件,需与螺母配合,用于紧固连接两个带有通孔的零 件,随着科学技术的不断提高,螺栓的应用市场也越来广阔,几乎所有生产制造业均需采用 螺栓,因此对于螺栓的性能要求也越来越高,而为了提高产品性能,往往需要在螺栓表面电 镀功能层,但是目前的电镀工艺过于复杂,且电镀质量较差,常常出现电镀层分布不均匀的 现象。
发明内容
[0003]本发明主要解决的技术问题是提供一种高硬度螺栓的电镀工艺,不仅能够提高螺 栓表面的硬度性能,使用寿命长,而且能够使得螺栓表面的电镀层均匀分布,电镀质量高。 [0004]为解决上述技术问题,本发明采用的一个技术方案是:提供一种高硬度螺栓的电 镀工艺,具体包括如下步骤: (1) 将螺栓放入酸洗池内进行酸洗处理,去除表面氧化层,酸洗温度为30-50°C,酸洗时 间为10-20min,完成后将螺栓放入清洗池内清洗干净; (2) 将螺栓接入电流为30-50mA的电路中进行电击处理,电击时间为5-10min; (3) 将螺栓放于电镀池的阴极,并将高硬度合金放于电镀池的阳极,所述电镀池内电流 密度为2-1011^/〇112,电镀温度为20-60°(:,电镀时间为6-141^11。
[0005]在本发明一个较佳实施例中,所述步骤(1)中的清洗池采用超声波清洗。
[0006]在本发明一个较佳实施例中,所述步骤(2)中的高硬度合金为铜锌合金。
[0007]在本发明一个较佳实施例中,所述步骤(2)的电击处理后采用绝缘夹进行搬运,且 搬运时间不超过10s。
[0008]本发明的有益效果是:本发明一种高硬度螺栓的电镀工艺,通过采用在电镀前先 进行电击处理,使得螺栓自身带弱电进入电镀池,从而使得电镀过程中,各离子能够均匀分 布至螺栓各处,防止出现螺栓表面电镀分布不均的现象,不仅提高了螺栓表面的硬度性能, 使用寿命长,使得螺栓表面的电镀层均匀分布,电镀质量更高。
具体实施方式
[0009]下面对本发明的较佳实施例进行详细阐述,以使本发明的优点和特征能更易于被 本领域技术人员理解,从而对本发明的保护范围做出更为清楚明确的界定。
[0010] 实施例1: 一种高硬度螺栓的电镀工艺,具体包括如下步骤: (1)将螺栓放入酸洗池内进行酸洗处理,去除表面氧化层,酸洗温度为30 °C,酸洗时间 为20min,芫成后将螺栓放入清洗池内清洗干净; (2) 将螺栓接入电流为3〇mA的电路中进行电击处理,电击时间为10min; (3) 将螺栓放于电镀池的阴极,并将高硬度合金放于电镀池的阳极,所述电镀池内电流 密度为2mA/cm2,电镀温度为60°C,电镀时间为6min。
[0011] 实施例2: 一种高硬度螺栓的电镀工艺,具体包括如下步骤: (1) 将螺栓放入酸洗池内进行酸洗处理,去除表面氧化层,酸洗温度为50»C,酸洗时间 为lOmin,完成后将螺栓放入清洗池内清洗干净; (2) 将螺栓接入电流为5〇mA的电路中进行电击处理,电击时间为5min; (3) 将螺栓放于电镀池的阴极,并将高硬度合金放于电镀池的阳极,所述电镀池内电流 密度为10mA/cm2,电镀温度为20°C,电镀时间为14min。
[0012] 实施例3: 一种高硬度螺栓的电镀工艺,具体包括如下步骤: (1) 将螺栓放入酸洗池内进行酸洗处理,去除表面氧化层,酸洗温度为4〇 r,酸洗时间 为15min,完成后将螺检放入清洗池内清洗干净; (2) 将螺栓接入电流为40mA的电路中进行电击处理,电击时间为7.5min; (3) 将螺栓放于电镀池的阴极,并将高硬度合金放于电镀池的阳极,所述电镀池内电流 密度为6mA/cm2,电镀温度为40°C,电镀时间为lOmin。
[0013]其中,所述步骤(1)中的清洗池采用超声波清洗。
[0014]所述步骤(2)中的高硬度合金为铜锌合金。
[0015]所述步骤(2)的电击处理后采用绝缘夹进行搬运,且搬运时间不超过i〇s。
[0016]区别于现有技术,本发明一种高硬度螺栓的电镀工艺,通过采用在电镀前先进行 电击处理,使得螺栓自身带弱电进入电镀池,从而使得电镀过程中,各离子能够均匀分布至 螺栓各处,防止出现螺栓表面电镀分布不均的现象,不仅提高了螺栓表面的硬度性能,使用 寿命长,使得螺栓表面的电镀层均匀分布,电镀质量更高。
[0017]以上所述仅为本发明的优选实施例而已,并不用于限制本发明,对于本领域的技 术人员来说,本发明可以有各种更改和变化。凡在本发明的精神和原则之内,所作的任何修 改、等同替换、改进等,均应包含在本发明的保护范围之内。

Claims (4)

1. 一种高硬度螺栓的电镀工艺,其特征在于,具体包括如下步骤: (1) 将螺栓放入酸洗池内进行酸洗处理,去除表面氧化层,酸洗温度为30_50 r,酸、冼时 间为10-20min,完成后将螺栓放入清洗池内清洗干净; 又 ’ (2) 将螺栓接入电流为30-50mA的电路中进行电击处理,电击时间为5—1〇min; (3) 将螺栓放于电键池的阴极,并将高硬度合金放于电锻池的阳极,所述电镀池内电流 密度为2-lOmA/cm2,电镀温度为20-60°C,电镀时间为6-14min。
2.根据权利要求1所述的高硬度螺栓的电镀工艺,其特征在于,所述步骤a)中的清洗 池采用超声波清洗。
3.根据权利要求1所述的高硬度螺栓的电镀工艺,其特征在于,所述步骤(2)中的高硬 度合金为铜锌合金。
4.根据权利要求1所述的高硬度螺栓的电镀工艺,其特征在于,所述步骤(2)的电击处 理后采用绝缘夹进行搬运,且搬运时间不超过l〇s。
CN201711013100.8A 2017-10-25 2017-10-25 一种高硬度螺栓的电镀工艺 Pending CN107604406A (zh)