CN107587228A - A kind of antistatic textile fabric and preparation method thereof - Google Patents
A kind of antistatic textile fabric and preparation method thereof Download PDFInfo
- Publication number
- CN107587228A CN107587228A CN201710713951.7A CN201710713951A CN107587228A CN 107587228 A CN107587228 A CN 107587228A CN 201710713951 A CN201710713951 A CN 201710713951A CN 107587228 A CN107587228 A CN 107587228A
- Authority
- CN
- China
- Prior art keywords
- textile fabric
- antistatic
- fibre
- fibrous layer
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention proposes a kind of antistatic textile fabric and preparation method thereof, and the raw material that the weaving face fabric includes following parts by weight forms：50 ~ 80 parts of string；50 ~ 80 parts of functional fiber；1 ~ 3 part of antistatic additive；Its preparation method is（1）Fibrous layer is formed as institutional framework, weaving using double layer plain weave as warp using bamboo fibre as parallel, functional fiber；（2）By step（1）After obtained fibrous layer tentering arranges, antistatic additive is coated on the surface of fibrous layer, is dried, washing, is dried to obtain required weaving face fabric.Fabric proposed by the present invention has excellent antistatic effect, can be effectively prevented from the influence to quality in production process, simultaneously, the defects of avoiding because of absorption of the electrostatic to dust, balling-up, and permeability penetrability is strong, and feature is lasting, resistance to cleaning, meet requirement of the people to functional textile fabric.
Description
Technical field
The present invention relates to technical field of textile fabric, and in particular to a kind of antistatic textile fabric and preparation method thereof.
Background technology
With the continuous offer that people live, more and more start to pursue the quality of life, and wear especially by people
Valued, common saying has the saying of title " people leans on saddle by clothes horse ", can embody importance of the people to dressing.Existing fabric one
As be made up of chemical fibre fabric, chemical fibre is because with good wearability, stiffness, elasticity, the spy such as resistant to chemical etching
Point, it is used widely in fields such as clothes, decoration, industries.Compared with the fibers such as natural cotton, chemical fibre intensity is high, cloth cover
Texture is good, bright in color, affordable, disposable processing, it is deep to be liked by consumers in general.But due to chemical fibre category
In hydrophobic fibre, easy balling-up, electrostatic is produced, build up of electrostatic charge is more easy in the environment of low humidity so that chemical fibre is being spun
There can be certain difficulty in each production process such as yarn, twisting, weaving and knitting, dyeing and arrangement, or even cause quality to ask
Topic, when wearing, make one to produce sticky feeling, fabric easily adsorbs dust.Particularly in some special dimensions, chemical fibre clothes
Caused electrostatic even can cause major accident.
Therefore, in view of the above-mentioned problems, the present invention proposes a kind of new technical scheme.
The content of the invention
There is excellent antistatic effect it is an object of the invention to provide a kind of, anti-pilling, washable work(is endurable anti-quiet
Electrospinning knitted fabric and preparation method thereof.
The present invention is achieved through the following technical solutions：
A kind of antistatic textile fabric, include the raw material composition of following parts by weight：
50 ~ 80 parts of string；
50 ~ 80 parts of functional fiber；
1 ~ 3 part of antistatic additive.
Further, the string is bamboo fibre, cotton fiber, abutilon fibre, monkey grass, one in coconut fibre
Kind is a variety of.
Further, the functional fiber is chemical fibre section and nanometer conductive material blended melting or screw extruding
Spinning solution is made, then spinning is carried out to spinning solution and obtains functional fiber.
Further, the chemical fibre is acrylic fibers, terylene, polyester fiber, polypropylene fibre, viscose rayon, polyethylene
Alcohol formal fiber, the one or more in CUP.
Further, the guiding principle material lead material be receive material ATO, ZnOw, CNT, one kind in graphene or
It is a variety of.
A kind of preparation method of antistatic textile fabric：Comprise the following steps：
（1）, using double layer plain weave as institutional framework, knitted string as parallel, functional fiber as warp
Appearance is into fibrous layer；
（2）By step（1）After obtained fibrous layer tentering arranges, antistatic additive is coated on the surface of fibrous layer, is dried, washing,
It is dried to obtain required weaving face fabric.
The beneficial effects of the invention are as follows：Fabric proposed by the present invention has excellent antistatic effect, can be effectively prevented from
To the influence of quality in production process, meanwhile, the defects of avoiding because of absorption of the electrostatic to dust, balling-up, and permeability moisture-inhibiting
Property is strong, and feature is lasting, resistance to cleaning, meets requirement of the people to functional textile fabric.
Embodiment
The present invention is described further with reference to embodiment.
Embodiment 1
A kind of antistatic textile fabric, include the raw material composition of following parts by weight：
50 parts of bamboo fibre；
50 parts of functional fiber；
1 part of antistatic additive.
In the present embodiment, functional fiber is that acrylic fibers section expects that spinning is made in ATO blended meltings or screw extruding with receiving
Liquid, then spinning is carried out to spinning solution and obtains functional fiber.
A kind of preparation method of antistatic textile fabric：Comprise the following steps：
（1）Using bamboo fibre as parallel, functional fiber is as warp, using double layer plain weave as institutional framework, weaving
Form fibrous layer；
（2）By step（1）After obtained fibrous layer tentering arranges, antistatic additive is coated on the surface of fibrous layer, is dried, washing,
It is dried to obtain required weaving face fabric.
Embodiment 2
A kind of antistatic textile fabric, include the raw material composition of following parts by weight：
60 parts of cotton fiber；
60 parts of functional fiber；
2 parts of antistatic additive.
In the present embodiment, the functional fiber is that polypropylene fibre section is squeezed with CNT blended melting or screw rod
Spinning solution is pressed into, then spinning is carried out to spinning solution and obtains functional fiber.
A kind of preparation method of antistatic textile fabric：Comprise the following steps：
（1）, using double layer plain weave as institutional framework, knitted string as parallel, functional fiber as warp
Appearance is into fibrous layer；
（2）By step（1）After obtained fibrous layer tentering arranges, antistatic additive is coated on the surface of fibrous layer, is dried, washing,
It is dried to obtain required weaving face fabric.
Embodiment 3
A kind of antistatic textile fabric, include the raw material composition of following parts by weight：
80 parts of abutilon fibre；
80 parts of functional fiber；
3 parts of antistatic additive.
In the present embodiment, functional fiber is made up of polypropylene fibre section with graphene blended melting or screw extruding
Spinning solution, then spinning is carried out to spinning solution and obtains functional fiber.
A kind of preparation method of antistatic textile fabric：Comprise the following steps：
（1）, using double layer plain weave as institutional framework, knitted string as parallel, functional fiber as warp
Appearance is into fibrous layer；
（2）By step（1）After obtained fibrous layer tentering arranges, antistatic additive is coated on the surface of fibrous layer, is dried, washing,
It is dried to obtain required weaving face fabric.
Fabric proposed by the present invention has excellent antistatic effect, can be effectively prevented from production process to the shadow of quality
Ring, meanwhile, the defects of avoiding because of absorption of the electrostatic to dust, balling-up, and permeability penetrability is strong, and feature is lasting, resistance to clear
Wash, meet requirement of the people to functional textile fabric.
The preferred embodiments of the present invention are the foregoing is only, are not intended to limit the invention, for the skill of this area
For art personnel, the present invention can have various modifications and variations.Within the spirit and principles of the invention, that is made any repaiies
Change, equivalent substitution, improvement etc., should be included in the scope of the protection.
Claims (6)
- A kind of 1. antistatic textile fabric, it is characterised in that：Raw material composition including following parts by weight：50 ~ 80 parts of string；50 ~ 80 parts of functional fiber；1 ~ 3 part of antistatic additive.
- A kind of 2. antistatic textile fabric according to claim 1, it is characterised in that：The string is bamboo fibre, cotton Fiber, abutilon fibre, monkey grass, the one or more in coconut fibre.
- A kind of 3. antistatic textile fabric according to claim 1, it is characterised in that：The functional fiber is chemical fibre Spinning solution is made with nanometer conductive material blended melting or screw extruding in section, then spinning is carried out to spinning solution and obtains feature fibre Dimension.
- A kind of 4. antistatic textile fabric according to claim 3, it is characterised in that：The chemical fibre is acrylic fibers, terylene, Polyester fiber, polypropylene fibre, viscose rayon, vinylon, the one or more in CUP.
- A kind of 5. antistatic textile fabric according to claim 3, it is characterised in that：The guiding principle material lead material for receive material ATO, One or more in ZnOw, CNT, graphene.
- A kind of 6. preparation method of antistatic textile fabric according to claim 1：It is characterized in that：Comprise the following steps：（1）, using double layer plain weave as institutional framework, knitted string as parallel, functional fiber as warp Appearance is into fibrous layer；（2）By step（1）After obtained fibrous layer tentering arranges, antistatic additive is coated on the surface of fibrous layer, is dried, washing, It is dried to obtain required weaving face fabric.