CN107572806A - A kind of moon white glaze pottery with health-preserving function - Google Patents
A kind of moon white glaze pottery with health-preserving function Download PDFInfo
- Publication number
- CN107572806A CN107572806A CN201710954164.1A CN201710954164A CN107572806A CN 107572806 A CN107572806 A CN 107572806A CN 201710954164 A CN201710954164 A CN 201710954164A CN 107572806 A CN107572806 A CN 107572806A
- Authority
- CN
- China
- Prior art keywords
- parts
- glaze
- pottery
- health
- frit
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
A kind of moon white glaze pottery with health-preserving function, including base substrate and glaze, the glaze are prepared by the raw material of following parts by weight：38 42 parts of melilite, 57 parts of stalactite, 7 10 parts of calcite, 20 24 parts of quartz, 57 parts of medical stone, 35 parts of talcum, 57 parts of frit, 57 parts of Copper Ores, 1.2 1.6 parts of bone ash, 68 parts of plant ash.The present invention is on the basis of from above-mentioned formula, and firing process is optimized through having gone, the moon white glaze pottery yield rate finally given reaches more than 80%, and for a long time with when it makees tableware or tea set uses, releasable certain trace element and absorption harmful substance, have certain help function to human body.
Description
Technical field
The invention belongs to pottery production technical field, and in particular to a kind of moon white glaze pottery and its system with health-preserving function
Preparation Method.
Background technology
Pottery is one of five big porcelain of China's Song Dynasty, and it is world-famous for " transmutation " glaze colours of uniqueness, is China Henan
The exclusive national treasure porcelain in province Yuzhou City god Hou towns." moon white glaze " is pure white clear just as moonlight in pottery, and enamel is bright and clean moist, is in
Milkiness shape, " surpassing jade like beautiful non-jade "；With the improvement of living standards, tableware, tea set with health-preserving function are research heat
Point, such as medical stone, tourmaline are applied on electric cooker, still, the pottery report of current few health-preserving functions, traced it to its cause
It is that pottery is fired originally and there is larger difficulty, it is fired after addition health material and requires higher.
The content of the invention
The purpose of the present invention, which is that, to be provided a kind of high yield rate for solution the deficiencies in the prior art and has health
The moon white glaze pottery and preparation method thereof of function.
The purpose of the present invention is realized with following technical proposals：
A kind of moon white glaze pottery with health-preserving function, including base substrate and glaze, the glaze by following parts by weight raw material system
It is standby to form：Melilite 38-42 parts, stalactite 5-7 parts, calcite 7-10 parts, quartzy 20-24 parts, medical stone 5-7 parts, talcum 3-5
Part, frit 5-7 parts, Copper Ores 5-7 parts, bone ash 1.2-1.6 parts, plant ash 6-8 parts.
Preferably, the glaze is prepared by the raw material of following parts by weight：40 parts of melilite, 6 parts of stalactite, calcite
8.5 parts, quartz 22 parts, 6 parts of medical stone, 4 parts of talcum, 6 parts of frit, 6 parts of Copper Ores, 1.4 parts of bone ash, 7 parts of plant ash.
The frit is zinc frit, and Zn content is more than 15%.
The preparation method of moon white glaze pottery as described above, comprises the following steps：
（1）Blank forming, biscuiting；
（2）Add water to mix above-mentioned glaze raw material, ball milling, obtain glaze slip；
（3）Glazing；
（4）Burn till, firing temperature is 1280-1300 DEG C.
Step（2）Middle glaze slip mass concentration is 56-58%.
Step（3）Specifically burning till step is：1. oxidation stage：Base substrate after glazing is put into kiln, under oxidizing atmosphere
Fire, temperature is ramped up 1020-1080 DEG C in 4-6h；2. reduction phase：Under reducing atmosphere, make temperature uniform in 5-6h
Rise to 1280-1300 DEG C；3. cooling stage：Room temperature is naturally cooled to, is made.
The present invention from traditional pottery materials melilite, calcite, quartz, talcum as primary solvent and cosolvent, so
Afterwards for obtain health-preserving function, other glaze used be free of chemical industry material, and add medical stone and stalactite, add medical stone with
After stalactite, the especially calcium content of essential element in glaze is had a great influence, therefore, inventor is right on the basis of many experiments
Formula is optimized.
In formula, bone ash makees opacifiers, and medical stone and plant ash contain more trace element, especially medical stone,
Containing the mineral matter and trace element needed for 18 kinds of human bodies and animal body nutrition, also there is strong absorption affinity to harmful substance；Clock
The main calcium carbonate of mammary calculus, alternative part calcite, also find that stalactite is in the present invention with QI invigorating help function, experiment
Also there is opacifiers in formula；Part raw glaze material is replaced from frit, what reduction raw material were formed in sintering procedure has
Toxicity solable matter；Copper Ores are colouring agent and cosolvent, on the basis of from above-mentioned formula, and to firing process through row
Optimization, the moon white glaze pottery yield rate that finally gives reach more than 80%, and make tableware with it for a long time or tea set uses
When, releasable certain micro- and absorption harmful substance, there is certain help function to human body.
Embodiment
Embodiment 1
A kind of moon white glaze pottery with health-preserving function, including base substrate and glaze, the glaze by following parts by weight raw material system
It is standby to form：Melilite 38-42 parts, stalactite 5-7 parts, calcite 7-10 parts, quartzy 20-24 parts, medical stone 5-7 parts, talcum 3-5
Part, frit 5-7 parts, Copper Ores 5-7 parts, bone ash 1.2-1.6 parts, plant ash 6-8 parts.Frit is preferably zinc frit, and Zn content is big
In 15%.The blank that pottery is conventional in the prior art can be selected in base substrate.
It is as described above with health-preserving function the moon white glaze pottery preparation method, comprise the following steps：
（1）Blank forming, biscuiting；
（2）Add water to mix above-mentioned glaze raw material, ball milling, obtain glaze slip；Glaze slip mass concentration is 56-58%；
（3）Glazing；
（4）Burn till, firing temperature is 1280-1300 DEG C；Specifically burning till step is：1. oxidation stage：Base substrate after glazing is put into
In kiln, fired under oxidizing atmosphere, temperature is ramped up 1020-1080 DEG C in 4-6h；2. reduction phase：In reducing atmosphere
Under, temperature is ramped up 1280-1300 DEG C in 5-6h；3. cooling stage：Room temperature is naturally cooled to, is made.Burn till and preferably adopt
With gas firing method, yield rate raising 5-10% is burnt with charcoal than being burnt using coal.
Melilite, stalactite, calcite, quartz, the Copper Ores used in the present invention are taken from Yuzhou, and bone ash is preferred
For ox bone ash.Found in experiment, after adding medical stone and stalactite on the basis of traditional glaze, the glaze colours that it is generated is easily inclined
Huang, comparing zinc oxide and cupric oxide with zinc frit from Copper Ores contributes to the generation of bluish white glaze colours, from bone ash and plant ash
Contribute to hydrotropy and play milkiness effect.
Embodiment 2
A kind of moon white glaze pottery with health-preserving function, including base substrate and glaze, the glaze by following parts by weight raw material system
It is standby to form：40 parts of melilite, 6 parts of stalactite, 8.5 parts of calcite, 22 parts of quartz, 6 parts of medical stone, 4 parts of talcum, 6 parts of frit, copper
6 parts of ore, 1.4 parts of bone ash, 7 parts of plant ash.Frit is preferably zinc frit, and Zn content is more than 15%.Prior art can be selected in base substrate
The conventional blank of middle pottery.
It is as described above with health-preserving function the moon white glaze pottery preparation method, comprise the following steps：
（1）Blank forming, biscuiting；
（2）Add water to mix above-mentioned glaze raw material, ball milling, obtain glaze slip；Glaze slip mass concentration is 57%；
（3）Glazing；
（4）Burn till, specifically burning till step is：1. oxidation stage：Base substrate after glazing is put into kiln, is burnt under oxidizing atmosphere
System, makes temperature be ramped up 1050 DEG C in 5h；2. reduction phase：Under reducing atmosphere, temperature is made to be ramped up 1290 in 5.5h
℃；3. cooling stage：Room temperature is naturally cooled to, is made.Burn till and use gas firing method, yield rate can be made to reach 90%.
3-23 of the embodiment of the present invention provide with health-preserving function the moon white glaze pottery formula be shown in Table 1-3, other with reality
Apply example 2.
Claims (6)
1. a kind of moon white glaze pottery with health-preserving function, including base substrate and glaze, it is characterised in that the glaze is by following heavy
The raw material of amount part is prepared：Melilite 38-42 parts, stalactite 5-7 parts, calcite 7-10 parts, quartzy 20-24 parts, medical stone
5-7 parts, talcum 3-5 parts, frit 5-7 parts, Copper Ores 5-7 parts, bone ash 1.2-1.6 parts, plant ash 6-8 parts.
2. there is the moon white glaze pottery of health-preserving function as claimed in claim 1, it is characterised in that the glaze is by following weight
The raw material of part is prepared：40 parts of melilite, 6 parts of stalactite, 8.5 parts of calcite, quartz 22 parts, 6 parts of medical stone, 4 parts of talcum,
6 parts of frit, 6 parts of Copper Ores, 1.4 parts of bone ash, 7 parts of plant ash.
3. the moon white glaze pottery with health-preserving function as described in claim any one of 1-2, it is characterised in that the frit is
Zinc frit, Zn content are more than 15%.
4. as described in claim any one of 1-3 the moon white glaze pottery preparation method, it is characterised in that comprise the following steps：
（1）Blank forming, biscuiting；
（2）Add water to mix above-mentioned glaze raw material, ball milling, obtain glaze slip；
（3）Glazing；
（4）Burn till, firing temperature is 1280-1300 DEG C.
5. the preparation method of as claimed in claim 4 month white glaze pottery, it is characterised in that step（2）Middle glaze slip mass concentration is
56-58%。
6. the preparation method of as claimed in claim 4 month white glaze pottery, it is characterised in that step（3）Specifically burning till step is：
1. oxidation stage：Base substrate after glazing is put into kiln, is fired under oxidizing atmosphere, temperature is ramped up 1020- in 4-6h
1080℃；2. reduction phase：Under reducing atmosphere, temperature is made to be ramped up 1280-1300 DEG C in 5-6h；3. cooling stage：From
Room temperature so is cooled to, is made.