CN107556660A - A kind of shuttlecock floor and preparation method thereof - Google Patents
A kind of shuttlecock floor and preparation method thereof Download PDFInfo
- Publication number
- CN107556660A CN107556660A CN201710939133.9A CN201710939133A CN107556660A CN 107556660 A CN107556660 A CN 107556660A CN 201710939133 A CN201710939133 A CN 201710939133A CN 107556660 A CN107556660 A CN 107556660A
- Authority
- CN
- China
- Prior art keywords
- wear
- resistant surface
- surface layer
- bottom layer
- layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to technical field of construction and decoration materials, specifically discloses a kind of shuttlecock floor and preparation method thereof.The floor includes wear-resistant coat and foamed bottom layer successively from top to bottom；Wherein, the wear-resistant coat by weight percentage, including following components：PVC paste resin：40 50%, nitrile rubber：5 15%, plasticiser：35 45%, calcium zinc stabilizer：1 5%, pigment：1 5%；The foamed bottom layer by weight percentage, including following components：PVC paste resin：40 50%, foaming agent：5 15%, plasticiser：35 45%, calcium zinc stabilizer：1 5%, pigment：1 5%.Shuttlecock floor provided by the invention improves superficial density and toughness, has excellent non-skid property, elasticity, and the low convenience of weight is carried and mated formation.
Description
Technical Field
The invention relates to the technical field of building decoration materials, in particular to a badminton court floor and a preparation method thereof.
Background
With the improvement of living standard, more and more people are put into exercise, and with the development of sports ground technology, people who do sports put forward a higher place to. At present, the floor surface of the indoor badminton professional competition field is hard, the antiskid performance is poor, the badminton professional competition field is easy to fall down and scratch, the sport scratch is easy to appear in the using process, the badminton professional competition field is difficult to clean, the elasticity is poor, the weight is heavy, and the badminton professional competition field is difficult to carry and pave.
Disclosure of Invention
The invention provides a badminton court floor, aiming at the problems of poor skid resistance, difficulty in cleaning, poor elasticity, heavy weight and the like of the conventional indoor badminton professional competition court.
Further, the invention also provides a preparation method of the badminton court floor.
In order to achieve the purpose of the invention, the embodiment of the invention adopts the following technical scheme:
a badminton court floor comprises a wear-resistant surface layer and a foaming bottom layer from top to bottom in sequence; wherein,
the wear-resistant surface layer comprises the following components in percentage by weight: PVC paste resin: 40-50%, nitrile rubber: 5-15%, plasticizer: 35-45%, calcium zinc stabilizer: 1-5%, pigment: 1 to 5 percent;
the foaming bottom layer comprises the following components in percentage by weight: PVC paste resin: 40-50%, foaming agent: 5-15%, plasticizer: 35-45%, calcium zinc stabilizer: 1-5%, pigment: 1 to 5 percent.
Compared with the prior art, the badminton court floor provided by the invention adopts the PVC paste resin and the nitrile rubber to be fused together, combines the advantages of the two materials, has high airtightness and high toughness strength, effectively solves the sports scratch, does not contain calcium carbonate and filler in the formula, greatly reduces the weight of the floor, and is light and convenient to carry and install.
Further, the invention also provides a preparation method of the badminton court floor. The preparation method at least comprises the following steps:
weighing the components according to the raw material ratio;
respectively preparing a wear-resistant surface layer and a foaming bottom layer;
and gluing the wear-resistant surface layer on the bottom foam layer, and performing Glaze + treatment on the surface.
Compared with the prior art, the badminton court floor provided by the invention has the advantages that the surface of the floor is subjected to Glaze + treatment, so that the effects of resisting dirt and sports scratches are achieved.
Detailed Description
In order to make the objects, technical solutions and advantages of the present invention more apparent, the present invention is further described in detail with reference to the following embodiments. It should be understood that the specific embodiments described herein are merely illustrative of the invention and are not intended to limit the invention.
The embodiment of the invention provides a badminton court floor, which sequentially comprises a wear-resistant surface layer and a foaming bottom layer from top to bottom; wherein,
the wear-resistant surface layer comprises the following components in percentage by weight: PVC paste resin: 40-50%, nitrile rubber: 5-15%, plasticizer: 35-45%, calcium zinc stabilizer: 1-5%, pigment: 1 to 5 percent;
the foaming bottom layer comprises the following components in percentage by weight: PVC paste resin: 40-50%, foaming agent: 5-15%, plasticizer: 35-45%, calcium zinc stabilizer: 1-5%, pigment: 1 to 5 percent.
The badminton court floor provided by the invention adopts PVC paste resin and nitrile rubber to be fused together, and combines the advantages of two materials, so that the floor has high airtightness and high toughness strength, sports scratches are effectively solved, and the formula does not contain calcium carbonate and filler, so that the weight of the floor is greatly reduced, and the floor is light and convenient to carry and install.
Preferably, the wear-resistant surface layer and the foaming bottom layer are bonded and fixed through an adhesive.
Preferably, the adhesive is a water-based polyurethane adhesive.
Preferably, the plasticizer is dioctyl terephthalate.
The invention further provides a preparation method of the badminton court floor on the premise of providing the badminton court floor.
In any embodiment, the preparation method comprises at least the following steps:
weighing the components according to the raw material ratio;
respectively preparing a wear-resistant surface layer and a foaming bottom layer;
and gluing the wear-resistant surface layer on the bottom foam layer, and performing Glaze + treatment on the surface.
The floor surface is preferably subjected to Glaze + treatment, so that the effects of resisting dirt and sports scratches are achieved.
The above preparation process is further explained below:
preferably, the wear-resistant surface layer is glued on the foaming bottom layer by adopting an adhesive, and the gluing amount of the adhesive is 45-50g/m2。
Preferably, the wear-resistant surface layer is glued on the foaming bottom layer under the condition of heating and pressurizing, wherein the temperature is 150-160 ℃, and the pressure is 140-160 Pa.
Preferably, the preparation process flow of the wear-resistant surface layer is as follows:
mixing the components of the wear-resistant surface layer, and stirring to form pasty slurry;
coating the slurry on the first surface of the PET polyester cloth, baking and curing at 210-220 ℃, cooling and shaping, then coating the slurry on the second surface of the PET polyester cloth, and cooling and shaping;
and heating the first surface of the PET polyester cloth, designing anti-skid lines on the surface, and cooling and shaping to obtain the wear-resistant surface layer.
Preferably, the preparation process flow of the foaming bottom layer is as follows: mixing the components of the foaming bottom layer, stirring into paste slurry, coating the slurry on a plane release paper base fabric, baking and curing at 210-220 ℃, and cooling and shaping to obtain the foaming bottom layer.
The invention adopts the foaming process to ensure that the bottom layer foam is fine and uniform, and the prepared badminton court floor has enough elasticity, thereby effectively protecting athletes and reducing sports injury.
The following examples are provided to better illustrate the embodiments of the present invention.
Example 1
The invention provides a badminton court floor, which sequentially comprises a wear-resistant surface layer and a foaming bottom layer from top to bottom; wherein,
the wear-resistant surface layer comprises the following components in percentage by weight: PVC paste resin: 45%, nitrile rubber: 10%, dioctyl terephthalate: 40%, calcium zinc stabilizer: 3%, pigment: 2 percent;
the foaming bottom layer comprises the following components in percentage by weight: PVC paste resin: 45%, foaming agent: 10%, dioctyl terephthalate: 40%, calcium zinc stabilizer: 3%, pigment: 2 percent.
The preparation process flow of the badminton court floor is as follows:
weighing the components according to the raw material ratio.
Preparing a wear-resistant surface layer: mixing the components of the wear-resistant surface layer, and stirring to form pasty slurry;
coating the slurry on the first surface of the PET polyester cloth, baking and curing at 220 ℃, cooling and shaping, then coating the slurry on the second surface of the PET polyester cloth, and cooling and shaping;
and heating the first surface of the PET polyester cloth, designing anti-skid lines on the surface, and cooling and shaping to obtain the wear-resistant surface layer.
Preparing a foaming bottom layer: mixing the components of the foaming bottom layer, stirring into pasty slurry, coating the slurry on a plane release paper base fabric, baking and curing at 220 ℃, cooling and shaping to obtain the foaming bottom layer.
Gluing the wear-resistant surface layer on the foaming bottom layer, and carrying out Glaze + treatment on the surface, wherein the glue is compounded by adopting a water-based polyurethane adhesive, and the gluing amount of the glue is 50g/m2And the glue is coated under the conditions of heating and pressurizing, the temperature is 160 ℃, and the pressure is 160 Pa.
Example 2
The invention provides a badminton court floor, which sequentially comprises a wear-resistant surface layer and a foaming bottom layer from top to bottom; wherein,
the wear-resistant surface layer comprises the following components in percentage by weight: PVC paste resin: 40%, nitrile rubber: 15%, dioctyl terephthalate: 35%, calcium zinc stabilizer: 5%, pigment: 5 percent;
the foaming bottom layer comprises the following components in percentage by weight: PVC paste resin: 50%, foaming agent: 5%, dioctyl terephthalate: 42%, calcium zinc stabilizer: 2%, pigment: 1 percent.
The preparation method of the badminton court floor provided by the invention is as described in embodiment 1, and is not described again.
The above description is only for the purpose of illustrating the preferred embodiments of the present invention and is not to be construed as limiting the invention, and any modifications, equivalents or improvements made within the spirit and principle of the present invention should be included in the scope of the present invention.
Claims (9)
1. The utility model provides a badminton court floor which characterized in that: the wear-resistant surface layer and the foaming bottom layer are sequentially arranged from top to bottom; wherein,
the wear-resistant surface layer comprises the following components in percentage by weight: PVC paste resin: 40-50%, nitrile rubber: 5-15%, plasticizer: 35-45%, calcium zinc stabilizer: 1-5%, pigment: 1 to 5 percent;
the foaming bottom layer comprises the following components in percentage by weight: PVC paste resin: 40-50%, foaming agent: 5-15%, plasticizer: 35-45%, calcium zinc stabilizer: 1-5%, pigment: 1 to 5 percent.
2. The badminton court floor of claim 1, wherein: the wear-resistant surface layer and the foaming bottom layer are bonded and fixed through an adhesive.
3. The badminton court floor of claim 2, wherein: the adhesive is a water-based polyurethane adhesive.
4. A badminton court floor as claimed in any one of claims 1 to 3, wherein: the plasticizer is dioctyl terephthalate.
5. A preparation method of a badminton court floor is characterized by comprising the following steps: at least comprises the following steps:
weighing the components according to the raw material proportion of any one of claims 1 to 4;
respectively preparing a wear-resistant surface layer and a foaming bottom layer;
and gluing the wear-resistant surface layer on the bottom foam layer, and performing Glaze + treatment on the surface.
6. The method for preparing a badminton court floor as claimed in claim 5, wherein the method comprises the following steps: the wear-resistant surface layer is glued on the foaming bottom layer by adopting an adhesive, and the gluing amount of the adhesive is 45-50g/m2。
7. The method for preparing a badminton court floor as claimed in claim 6, wherein the method comprises the following steps: and gluing the wear-resistant surface layer on the foaming bottom layer under the conditions of heating and pressurizing, wherein the temperature is 150-160 ℃, and the pressure is 140-160 Pa.
8. The method for preparing a badminton court floor as claimed in claim 6, wherein the method comprises the following steps: the preparation process flow of the wear-resistant surface layer is as follows:
mixing the components of the wear-resistant surface layer, and stirring to form pasty slurry;
coating the slurry on the first surface of the PET polyester cloth, baking and curing at 210-220 ℃, cooling and shaping, then coating the slurry on the second surface of the PET polyester cloth, and cooling and shaping;
and heating the first surface of the PET polyester cloth, designing anti-skid lines on the surface, and cooling and shaping to obtain the wear-resistant surface layer.
9. The method for preparing a badminton court floor as claimed in claim 6, wherein the method comprises the following steps: the preparation process flow of the foaming bottom layer is as follows: mixing the components of the foaming bottom layer, stirring into paste slurry, coating the slurry on a plane release paper base fabric, baking and curing at 210-220 ℃, and cooling and shaping to obtain the foaming bottom layer.