CN107502687B - 一种复合树脂鞣剂 - Google Patents
一种复合树脂鞣剂 Download PDFInfo
- Publication number
- CN107502687B CN107502687B CN201710735936.2A CN201710735936A CN107502687B CN 107502687 B CN107502687 B CN 107502687B CN 201710735936 A CN201710735936 A CN 201710735936A CN 107502687 B CN107502687 B CN 107502687B
- Authority
- CN
- China
- Prior art keywords
- tanning agent
- parts
- resin tanning
- composite resin
- leather
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明涉及一种复合树脂鞣剂,所述复合树脂鞣剂是由以下重量份的组分制备而成的:树脂鞣剂R6 25~35份;高岭土2~4份;元明粉5~6份;滑石粉4~5份;木质素磺酸钠3~3.6份;面粉1~1.4份。本发明的优点在于:本发明制备出的复合树脂鞣剂可用于各种类型铬鞣皮革的复鞣,并可保持铬鞣皮革原有的各种性能,且本品具有较好的选择填充作用,可以很好地填充于皮革结构松弛的部位,改善皮革的致密性和丰满性,手感好;此外,本品收敛性较小,匀染性好,可产生良好的粒面,有利于压花抛光。
Description
技术领域
本发明属于皮革化学品合成技术领域,特别涉及一种复合树脂鞣剂。
背景技术
对于制革工艺来说,皮革复鞣技术十分重要,被称为“点金术”。 在制革工艺中,复鞣剂有许多种,其中常用的树脂复鞣剂有丙烯酸 类,马来酸类聚合物水溶液。但这类树脂复鞣剂多属阴离子型,对制革后工序染色工序中染料的上染影响较大,成革染深色时常出现 “败色”现象。解决“败色”问题的途径之一是采用含金属离子的 树脂复鞣剂。如德国专利DE 3724807报导了一种含铬硫代丙烯酸树 脂复鞣剂;苏联专利SU1447853报导了一种含铬铝丙烯酸树脂鞣剂; SU1675333则报导了一种含铝聚合物鞣剂的生产。然而,铬是国际上公认的战略物质,价格昂贵,也是制革工业的重要污染源。为此,人们正在努力开发新的复鞣剂,在制革工艺中尽量不用或少用含铬复鞣剂。
发明内容
本发明要解决的技术问题是提供一种复合树脂鞣剂,以解决现有
技术问题。
为解决上述技术问题,本发明的技术方案为:一种复合树脂鞣剂,其创新点在于:所述复合树脂鞣剂是由以下重量份的组分制备而成的:
树脂鞣剂R6 25~35份;
高岭土 2~4份;
元明粉 5~6份;
滑石粉 4~5份;
木质素磺酸钠 3~3.6份;
面粉 1~1.4份。
进一步地,所述树脂鞣剂R6选用含固量为95%、PH值为8.5~9.5的树脂鞣剂R6。
进一步地,所述高岭土的粒径为0.2~5µm。
进一步地,所述元明粉的粒度为1800~2000目。
进一步地,所述滑石粉的粒度为1200~1500目。
进一步地,所述木质素磺酸钠的粒度为100~150目。
本发明的优点在于:
(1)本发明复合树脂鞣剂,采用高岭土、元明粉、滑石粉、木质素磺酸钠和面粉为填料,均为常见的原料,价格便宜,且混用这些填料与单用填料相比,使得复合树脂鞣剂具有更好的填充作用;此外,再将填料与树脂鞣剂R6进行复合,进而使得制备出的复合树脂鞣剂可用于各种类型铬鞣皮革的复鞣,并可保持铬鞣皮革原有的各种性能,且本品具有较好的选择填充作用,可以很好地填充于皮革结构松弛的部位,改善皮革的致密性和丰满性,手感好;此外,本品收敛性较小,匀染性好,可产生良好的粒面,有利于压花抛光;
(2)本发明复合树脂鞣剂,其中,树脂鞣剂R6选用含固量为95%、PH值为8.5~9.5的树脂鞣剂R6,该树脂鞣剂R6,能有效解决坯革的松面为题,能改善成革粒面,使成革的革身更平整,粒面更细致,成革丰满,柔软并且有弹性,经其处理后皮革摔软,可得到均匀的摔纹。
具体实施方式
下面的实施例可以使本专业的技术人员更全面地理解本发明,但并不因此将本发明限制在所述的实施例范围之中。
实施例1
依次按顺序将树脂鞣剂R6 25kg、高岭土 2kg、元明粉 5kg、滑石粉 4kg、木质素磺酸钠 3kg和面粉1kg投入混合器中,搅拌30min,再放料进行包装,即得复合树脂鞣剂;其中,树脂鞣剂R6选用含固量为95%、PH值为8.5~9.5的树脂鞣剂R6,高岭土的粒径为0.2~5µm,元明粉的粒度为1800~2000目,滑石粉的粒度为1200~1500目和木质素磺酸钠的粒度为100~150目。
实施例2
依次按顺序将树脂鞣剂R6 35kg、高岭土 4kg、元明粉 6kg、滑石粉 5kg、木质素磺酸钠 3.6kg和面粉1.4kg投入混合器中,搅拌30min,再放料进行包装,即得复合树脂鞣剂;其中,树脂鞣剂R6选用含固量为95%、PH值为8.5~9.5的树脂鞣剂R6,高岭土的粒径为0.2~5µm,元明粉的粒度为1800~2000目,滑石粉的粒度为1200~1500目和木质素磺酸钠的粒度为100~150目。
实施例3
依次按顺序将树脂鞣剂R6 30kg、高岭土 3kg、元明粉 5.5kg、滑石粉 4.5kg、木质素磺酸钠 3.3kg和面粉1.2kg投入混合器中,搅拌30min,再放料进行包装,即得复合树脂鞣剂;其中,树脂鞣剂R6选用含固量为95%、PH值为8.5~9.5的树脂鞣剂R6,高岭土的粒径为0.2~5µm,元明粉的粒度为1800~2000目,滑石粉的粒度为1200~1500目和木质素磺酸钠的粒度为100~150目。
由实施例1-3制备的复合树脂鞣剂的理化指标如表1所示。
由实施例1-3制备的复合树脂鞣剂对皮革复鞣的应用指标如表2所示。
表1实施例1-3制备的复合树脂鞣剂的理化指标
注:外观以目力测试;固含量按GB/T2793-1995标准;10%的复合树脂鞣剂水溶液pH值按GB/T6368-2008标准;游离甲醛含量按HJ601-2011标准。
表2实施例1-3制备的复合树脂鞣剂对皮革复鞣的应用指标
注:增厚率按QB/T2709-2005标准,根据公式计算(其中d1为生皮的厚度,d2为鞣制成革晾干后的厚度);收缩温度按QB/T2713-2005标准;丰满度、柔软性、粒面细粒程度根据感官评价,其中满分为10分。
由表1和表2可知,实施例1-3制得的复合树脂鞣剂能够和铬鞣剂相容,且通过鞣制之后成革具有较好的丰满度和良好的柔性,对皮革松软部位有极强的填充效果;此外,可产生良好的粒面,有利于压花抛光。
以上显示和描述了本发明的基本原理和主要特征以及本发明的优点。本行业的技术人员应该了解,本发明不受上述实施例的限制,上述实施例和说明书中描述的只是说明本发明的原理,在不脱离本发明精神和范围的前提下,本发明还会有各种变化和改进,这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。
Claims (6)
1.一种复合树脂鞣剂,其特征在于:所述复合树脂鞣剂是由以下重量份的组分制备而成的:
树脂鞣剂R6 25~35份;
高岭土 2~4份;
元明粉 5~6份;
滑石粉 4~5份;
木质素磺酸钠 3~3.6份;
面粉 1~1.4份。
2.根据权利要求1所述的复合树脂鞣剂,其特征在于:所述树脂鞣剂R6选用含固量为95%、pH 值为8.5~9.5的树脂鞣剂R6。
3.根据权利要求1所述的复合树脂鞣剂,其特征在于:所述高岭土的粒径为0.2~5µm。
4.根据权利要求1所述的复合树脂鞣剂,其特征在于:所述元明粉的粒度为1800~2000目。
5.根据权利要求1所述的复合树脂鞣剂,其特征在于:所述滑石粉的粒度为1200~1500目。
6.根据权利要求1所述的复合树脂鞣剂,其特征在于:所述木质素磺酸钠的粒度为100~150目。