CN107500666A - Unburned quincunx colored zeolite light ceramic - Google Patents
Unburned quincunx colored zeolite light ceramic Download PDFInfo
- Publication number
- CN107500666A CN107500666A CN201710873618.2A CN201710873618A CN107500666A CN 107500666 A CN107500666 A CN 107500666A CN 201710873618 A CN201710873618 A CN 201710873618A CN 107500666 A CN107500666 A CN 107500666A
- Authority
- CN
- China
- Prior art keywords
- zeolite
- light ceramic
- unburned quincunx
- quincunx colored
- unburned
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of unburned quincunx colored zeolite light ceramic,The main points of its technical scheme are,The dispensing of unburned quincunx colored zeolite light ceramic is by the zeolite after being acidified,Colored portland cement,Powdery attapulgite foaming agent,Precipitated calcium carbonate,Light magnesium oxide,Hollow glass micropearl and titanium dioxide composition,The dispensing of unburned quincunx colored zeolite light ceramic is stirred mixing,Extruder grain,Steam curing,Steam drying,Unburned quincunx colored zeolite light ceramic is packaged as after screening,With bright in luster,Appearance and modeling is attractive in appearance,Lightweight intensity is good,Specific surface area is big,Bulk density is low,Permeability is superior,The characteristics of porosity and high water absorption rate,Unburned quincunx colored zeolite light ceramic can ensure that growth and development of plants is good,Survival rate is high and the life-span is longer,And the number of moisturizing can be greatly reduced,Unburned quincunx colored zeolite light ceramic is applied to garden landscape engineering,Home gardening and preparation soilless culture substrate.
Description
Technical field
The present invention relates to haydite, and in particular to a kind of unburned quincunx colored zeolite light ceramic.
Background technology
Colored haydite on the market, it is to be granulated to be made after mixing using cement, fine sand and dyestuff, proportion and heap
Product density is all very big, and water absorption rate is smaller, it is impossible to the normal growth and development of plant is ensured, also without the work(for adsorbing and purifying air
Energy.
Tested through multiple sampling:Colored haydite average bulk density >=1200kg/m3 on the market, mean water absorption rate
≤ 20%.
The content of the invention
The purpose of the present invention is to overcome weak point in the prior art, there is provided a kind of unburned quincunx colored zeolite Lightweight ceramic
Grain.
The dispensing of unburned quincunx colored zeolite light ceramic is recessed by the zeolite after being acidified, colored portland cement, powdery
Convex rod foaming agent, precipitated calcium carbonate, light magnesium oxide, hollow glass micropearl and titanium dioxide composition.
The production method of unburned quincunx colored zeolite light ceramic:By matching somebody with somebody for unburned quincunx colored zeolite light ceramic
Material is packed as unburned quincunx colored zeolite after being stirred mixing, extruder grain, steam curing, steam drying, screening
Light ceramic.
Natural zeolite has unique internal structure and Crystallochemical Properties, makes it have water suction, absorption, selectivity suction
The excellent physicochemical properties such as attached, ion exchange, catalytic reaction, acidproof and radiation hardness, it is a kind of new nonmetallic ore raw material, this
Granularity≤0.42 millimeter of the invention from zeolite.
After the acidified processing of zeolite, loose porous cavernous body is formed, enables the characteristics such as absorption and cation exchange
Play, and after the water in zeolite crystal structure is heated effusion, passage and hole are more spacious, and respective inner surfaces product is huger
Greatly, zeolite is made to show strong adsorptivity.
Colored portland cement be by portland cement hot material and proper amount of gypsum (or white portland cement), mixing material and
Band the colorful one hydraulic cementing materials that colouring agent is levigate or is mixed is referred to as colored portland cement, colored portland water
Mud Essential colour has white, red, green, yellow, blueness, brown and black etc., and quality needs to meet " JC/T 870-2012
The standard of colored portland cement ".
Attapulgite also known as palygorskite or Palygorskite, it is the clay pit of zeopan containing Shuifu County of a kind of layer of chain structure
Thing, Concave-convex clay rod have unique layer chain structure feature, and crystal is in needle-like, threadiness or fiber collection shape.Concave convex rod
Stone clay has good colloidal nature and the higher adsorption capacities such as unique scattered, high temperature resistant, salt resistance alkali.
Powdery attapulgite foaming agent has that foaming capacity is strong, coefficient of foaming is high, unit volume bubble production volume is big, foam outer membrane is tough
Property it is good non-breakable, foam stability is good, can not defoam for a long time, foam is fine and smooth, the hole size that is generated in medium uniformly,
The advantages that bleeding quantity is low and good using the compatibility of medium.
Precipitated calcium carbonate is a kind of white powder, and odorlessness is tasteless, and precipitated calcium carbonate fine particles, surface are rougher, than
Surface area is big, and the present invention selects granularity≤0.074 millimeter of precipitated calcium carbonate.
Light magnesium oxide is the loose unformed powder of white lightweight, and odorless, tasteless is nontoxic, and volume shared by light magnesium oxide is about
Three times for heavy-burned magnesia or so, there is extremely fireproof heat-insulating property, reinforcing agent, adhesive, and the present invention selects light magnesium oxide
Granularity≤0.074 millimeter.
Hollow glass micropearl(Hollow glass microbead)It is a kind of small, hollow ball sprills, particle diameter can be as needed
Arbitrarily selected between 30-100 microns, have lightweight is big, thermal conductivity factor is low, compression strength is high, dispersiveness, flowing
Property, the advantages of stability is good, the present invention selects particle diameter≤0.1 millimeter of hollow glass micropearl.
Anatase thpe white powder is a kind of excellent white powder pigment, has good light scattering ability, thus whiteness is good,
Tinting strength, tinting power is high, strong covering power, while has higher chemical stability and preferable weatherability, nonpoisonous and tasteless, stingless to human body
Swash effect.
The technical scheme is that:
1st, the dispensing of unburned quincunx colored zeolite light ceramic is made up of following component by weight percentage:Zeolite after acidifying
10~50%, powdery attapulgite foaming agent 2~10%, precipitated calcium carbonate 2~10%, light magnesium oxide 1~10%, hollow glass
Microballon 1~8%, white portland cement 0~30%, red portland cement 0~30%, green silicate cement 0~30%,
Yellow portland cement 0~30%, blue silicate cement 0~30%, brown portland cement 0~30%, black silicate
Cement 0~30%, titanium dioxide 0~5% and water 5~40%.
2nd, the zeolite dispensing after being acidified is made up of following component by weight percentage:Zeolite semi-finished product 90 after acidifying~
98%th, quick dissolved sodium silicate 0.1~5%, polyvinyl alcohol 0.1~5%, hydroxypropyl methyl cellulose 0.01~3% and sodium carbonate 0~
3%;The production method of zeolite after acidifying:It will be milled in zeolite dispensing after acidifying input grinding machine, grain fineness≤0.074 is in the least
Meter, the powder after milling is the zeolite finished product after acidifying.
The production method of zeolite semi-finished product after acidifying:(1) the mixer dispensing input of zeolite mixture operated
Middle stirring, then watery hydrochloric acid is slowly added to carry out acidification in zeolite mixture;(2) by the zeolite mixture after acidification,
It is zeolite tablet to be extruded by twin rollers, thickness≤3 millimeter of zeolite tablet;(3) zeolite tablet is transported to swinging
It is calcined in drying oven, roasting time is 1~3 hour, and sintering temperature is controlled at 300~400 DEG C, and the zeolite tablet after roasting contains
Water≤2%, the zeolite tablet after roasting is the zeolite semi-finished product after acidifying, and percentage of water content is weight percentage.
The dispensing of zeolite tablet is made up of following component by weight percentage:Zeolite mixture 75~95% and watery hydrochloric acid
5~25%, the dispensing of zeolite mixture is made up of following component by weight percentage:Zeolite 68~92%, Concave-convex clay rod 5
~30% and magnesia 0.1~3%, the dispensing of watery hydrochloric acid be made up of by weight percentage following component:Concentration is 37% dense salt
Acid 1~25% and water 75~99%, the concentrated hydrochloric acid percentage that concentration is 37% are weight percentage.
Zeolite after acidifying was applied " zeolite after acidifying " using by the present inventor on 06 01st, 2014, Chinese
License notification number is:CN 103979573B, authorized announcement date:On 2 17th, 2016.
3rd, powdery attapulgite foaming agent dispensing is made up of following component by weight percentage:Activated attapulgite 45~
95%th, lauryl sodium sulfate 1~35%, SODIUM PERCARBONATE 1~25%, Sodium Polyacrylate 0.01~5%, sodium pyrophosphate 0.01~
5% and poly- naphthalene formaldehyde sulfonate salt 0.01~5%;The production method of powdery attapulgite foaming agent:By powdery attapulgite foaming agent
It is stirred in dispensing input mixer, inputs in grinding machine and be milled after stirring, grain fineness≤0.074 millimeter.
Powdery attapulgite foaming agent using applied by the present inventor on 05 26th, 2013 " powdery attapulgite foam
Agent ", Chinese patent Authorization Notice No. are:The B of CN 103265213, authorized announcement date:On 09 24th, 2014.
4th, the color of unburned quincunx colored zeolite light ceramic has white, red, green, yellow, blueness, orange, brown
Color and black.
5th, the dispensing of unburned quincunx colored zeolite light ceramic is applied to produce unburned spheroidal colour zeolite Lightweight ceramic
Grain, cylindrical sintering-free colour zeolite light ceramic, baking-free gravel colour zeolite light ceramic, unburned quincunx colored zeolite are light
Matter through hole haydite, unburned spheroidal colour zeolite lightweight through hole haydite and cylindrical sintering-free colour zeolite lightweight through hole haydite.
6th, the production method of unburned quincunx colored zeolite light ceramic:(1) by unburned quincunx colored zeolite light ceramic
The stirring mixer that has operated of dispensing input in, be stirred as the mixing of unburned quincunx colored zeolite light ceramic
Thing;(2) the mixture of unburned quincunx colored zeolite light ceramic is transported in Squeezinggranulator, extruder grain is unburned plum
Flower-shape colour zeolite light ceramic semi-finished product;(3) unburned quincunx colored zeolite light ceramic semi-finished product are transported to steam curing
Room carries out steam curing, and at 55~75 DEG C, curing time controlled at 7~15 days temperature control in steam curing room;(4) by steam
Unburned quincunx colored zeolite light ceramic semi-finished product after maintenance, are transported in steam rotary dryer and processing are dried,
At 60~100 DEG C, drying time was controlled at 1~5 hour for drying temperature control;(5) by dried unburned quincunx colored zeolite
Light ceramic semi-finished product, which are transported in vibratory sieve, to be sieved, be packaged as after screening unburned quincunx colored zeolite light ceramic into
Product.
Zeolite after acidifying has water suction, absorption, selective absorption, ion exchange, catalytic reaction, acidproof and radiation hardness etc.
Excellent physicochemical property, the absorption of unburned quincunx colored zeolite light ceramic can be improved and purify the function of air.
Colored portland cement can ensure that the color of unburned quincunx colored zeolite light ceramic is more gorgeous.
Powdery attapulgite foaming agent be stirred for unburned quincunx colored zeolite light ceramic mixture when, it will production
Raw a certain amount of bubble, be advantageous to increase unburned quincunx colored zeolite light ceramic surface and internal porosity.
It is micro- using light magnesium oxide, precipitated calcium carbonate, hollow glass in unburned quincunx colored zeolite light ceramic dispensing
Pearl and titanium dioxide, it is ensured that unburned quincunx colored zeolite light ceramic color is more bright-coloured, increases unburned quincunx colored zeolite
Light ceramic surface and internal porosity, improve the specific surface area and intensity of unburned quincunx colored zeolite light ceramic.
Unburned quincunx colored zeolite light ceramic be advantageous to increase unburned quincunx colored zeolite light ceramic mutually it
Between voidage and reduce the bulk density of unburned quincunx colored zeolite light ceramic.
There is largely interconnected micropore unburned quincunx colored zeolite light ceramic surface and inside, are advantageous to increase and exempt from
Burn effective ratio area, intensity and the reduction bulk density of quincunx colored zeolite light ceramic.
Unburned quincunx colored zeolite light ceramic is put into water, unburned quincunx colored zeolite light ceramic can be rapid
Sink under water, can be by the air in unburned quincunx colored zeolite light ceramic internal capillary while large quantity of moisture is sucked
Cement out.
When unburned quincunx colored zeolite light ceramic water absorption rate >=25%, unburned quincunx colored zeolite light ceramic
Appearance be a kind of state of moistening, not obvious water leaks out, by unburned quincunx colored zeolite light ceramic
It is packed together, forms numerous spaces between each other, will not be bonded together, permeability is good, unburned quincunx colored boiling
Stone light ceramic does not have dust in the dry state, and disintegration will not also be produced by being immersed in all the year round in water.
Unburned quincunx colored zeolite light ceramic has that bright in luster, appearance and modeling is attractive in appearance, lightweight intensity is good, compares surface
The characteristics of product is big, bulk density is low, permeability is superior, porosity and water absorption rate are high.
In order to ensure the normal growth and development of plant, water, the organic fertilizer of liquid or inorganic fertilizer are sprayed at unburned quincunx
In colored zeolite light ceramic, or unburned quincunx colored zeolite light ceramic is immersed in the molten of water, organic fertilizer or inorganic fertilizer
In liquid, unburned quincunx colored zeolite light ceramic takes out after absorbing a certain amount of water of storage or liquid fertilizer, for cultivating or planting
When planting various nursery stocks, flowers and plants and vegetables, the root of plant will be absorbed in unburned quincunx colored zeolite light ceramic water or
The nutritional ingredient of liquid fertilizer, it is ensured that growth and development of plants is good, and survival rate is high and the life-span is longer, and can greatly reduce time of moisturizing
Number.
Unburned quincunx colored zeolite light ceramic is applied to garden landscape engineering, home gardening and prepares soilless culture base
Matter.
Brief description of the drawings
Fig. 1 is unburned quincunx colored zeolite light ceramic schematic diagram, and Fig. 2 is unburned quincunx colored zeolite light ceramic
A-A sections.
As shown in the figure:1 is unburned quincunx colored zeolite light ceramic.
Embodiment
With reference to embodiment, the invention will be further described:
1st, the dispensing of unburned quincunx white zeolite light ceramic is made up of following component by weight percentage:Zeolite after acidifying
35%th, powdery attapulgite foaming agent 8%, precipitated calcium carbonate 6%, light magnesium oxide 4%, hollow glass micropearl 3%, white silicic acid
Salt cement 24%, red portland cement 0%, green silicate cement 0%, yellow portland cement 0%, blue silicate cement
Mud 0%, brown portland cement 0%, black portland cement 0%, titanium dioxide 2% and water 18%.
2nd, the dispensing of unburned quincunx red zeolite light ceramic is made up of following component by weight percentage:After acidifying
Zeolite 36%, powdery attapulgite foaming agent 8%, precipitated calcium carbonate 6%, light magnesium oxide 4%, hollow glass micropearl 3%, white
Portland cement 0%, red portland cement 25%, green silicate cement 0%, yellow portland cement 0%, blue silicic acid
Salt cement 0%, brown portland cement 0%, black portland cement 0%, titanium dioxide 0% and water 18%.
3rd, the dispensing of unburned quincunx green zeolite light ceramic is made up of following component by weight percentage:After acidifying
Zeolite 35%, powdery attapulgite foaming agent 8%, precipitated calcium carbonate 6%, light magnesium oxide 4%, hollow glass micropearl 4%, white
Portland cement 0%, red portland cement 0%, green silicate cement 25%, yellow portland cement 0%, blue silicic acid
Salt cement 0%, brown portland cement 0%, black portland cement 0%, titanium dioxide 0% and water 18%.
4th, the dispensing of unburned quincunx yellow zeolite light ceramic is made up of following component by weight percentage:After acidifying
Zeolite 35%, powdery attapulgite foaming agent 8%, precipitated calcium carbonate 6%, light magnesium oxide 4%, hollow glass micropearl 3%, white
Portland cement 0%, red portland cement 0%, green silicate cement 0%, yellow portland cement 26%, blue silicic acid
Salt cement 0%, brown portland cement 0%, black portland cement 0%, titanium dioxide 0% and water 18%.
5th, the dispensing of unburned quincunx blue zeolite light ceramic is made up of following component by weight percentage:After acidifying
Zeolite 35%, powdery attapulgite foaming agent 8%, precipitated calcium carbonate 6%, light magnesium oxide 4%, hollow glass micropearl 4%, white
Portland cement 0%, red portland cement 0%, green silicate cement 0%, yellow portland cement 0%, blue silicic acid
Salt cement 25%, brown portland cement 0%, black portland cement 0%, titanium dioxide 0% and water 18%.
6th, the dispensing of unburned quincunx brown zeolite light ceramic is made up of following component by weight percentage:After acidifying
Zeolite 35%, powdery attapulgite foaming agent 8%, precipitated calcium carbonate 6%, light magnesium oxide 5%, hollow glass micropearl 3%, white
Portland cement 0%, red portland cement 0%, green silicate cement 0%, yellow portland cement 0%, blue silicic acid
Salt cement 0%, brown portland cement 25%, black portland cement 0%, titanium dioxide 0% and water 18%.
7th, the dispensing of unburned quincunx black zeolite light ceramic is made up of following component by weight percentage:After acidifying
Zeolite 38%, powdery attapulgite foaming agent 8%, precipitated calcium carbonate 4%, light magnesium oxide 4%, hollow glass micropearl 3%, white
Portland cement 0%, red portland cement 0%, green silicate cement 0%, yellow portland cement 0%, blue silicic acid
Salt cement 0%, brown portland cement 0%, black portland cement 25%, titanium dioxide 0% and water 18%.
8th, the production method of unburned quincunx colored zeolite light ceramic:(1) by unburned quincunx colored zeolite light ceramic
The stirring mixer that has operated of dispensing input in, be stirred as the mixing of unburned quincunx colored zeolite light ceramic
Thing;(2) the mixture of unburned quincunx colored zeolite light ceramic is transported in Squeezinggranulator, extruder grain is unburned plum
Flower-shape colour zeolite light ceramic semi-finished product;(3) the unburned quincunx colored semi-finished product of zeolite light ceramic 1 are transported into steam to support
Protect room and carry out steam curing, at 55~75 DEG C, curing time controlled at 12 days temperature control in steam curing room;(4) steam is supported
The unburned quincunx colored semi-finished product of zeolite light ceramic 1 after shield, are transported in steam rotary dryer and processing are dried, and do
At 60~100 DEG C, drying time controlled at 2 hours dry temperature control;(5) by dried unburned quincunx colored zeolite lightweight
The semi-finished product of haydite 1, which are transported in vibratory sieve, to be sieved, be packaged as after screening unburned quincunx colored zeolite light ceramic 1 into
Product.
9th, it is 820kg/m3 to survey unburned quincunx colored zeolite light ceramic average bulk density, water absorption rate 56%.
Claims (4)
1. a kind of unburned quincunx colored zeolite light ceramic, it is characterised in that unburned quincunx colored zeolite light ceramic
Dispensing is made up of following component by weight percentage:Zeolite 10~50%, powdery attapulgite foaming agent 2~10% after acidifying,
Precipitated calcium carbonate 2~10%, light magnesium oxide 1~10%, hollow glass micropearl 1~8%, white portland cement 0~30%,
Red portland cement 0~30%, green silicate cement 0~30%, yellow portland cement 0~30%, blue silicate
Cement 0~30%, brown portland cement 0~30%, black portland cement 0~30%, titanium dioxide 0~5% and water 5~
40%.
2. unburned quincunx colored zeolite light ceramic according to claim 1, it is characterised in that unburned quincunx colour
The color of zeolite light ceramic has white, red, green, yellow, blueness, orange, brown and black.
3. unburned quincunx colored zeolite light ceramic according to claim 1, it is characterised in that unburned quincunx colour
The dispensing of zeolite light ceramic is applied to produce unburned spheroidal colour zeolite light ceramic, cylindrical sintering-free colour zeolite lightweight
Haydite, baking-free gravel colour zeolite light ceramic, unburned quincunx colored zeolite lightweight through hole haydite, unburned spheroidal are colored
Zeolite lightweight through hole haydite and cylindrical sintering-free colour zeolite lightweight through hole haydite.
4. unburned quincunx colored zeolite light ceramic according to claim 1, it is characterised in that unburned quincunx colour
The production method of zeolite light ceramic:(1) the stirring dispensing input of unburned quincunx colored zeolite light ceramic operated
In mixer, it is stirred as the mixture of unburned quincunx colored zeolite light ceramic;(2) by unburned quincunx colored zeolite
The mixture of light ceramic is transported in Squeezinggranulator, extruder grain be unburned quincunx colored zeolite light ceramic half into
Product;(3) unburned quincunx colored zeolite light ceramic semi-finished product are transported to steam-curing chamber and carry out steam curing, steam curing
At 55~75 DEG C, curing time was controlled at 7~15 days for indoor temperature control;(4) by the unburned quincunx colored boiling after steam curing
Stone light ceramic semi-finished product, it is transported in steam rotary dryer and processing is dried, drying temperature is controlled at 60~100 DEG C,
Drying time was controlled at 1~5 hour;(5) dried unburned quincunx colored zeolite light ceramic semi-finished product are transported to vibration
Sieved in sieve, unburned quincunx colored zeolite light ceramic finished product is packaged as after screening.