CN107446439B - Multifunctional engine line protective agent - Google Patents
Multifunctional engine line protective agent Download PDFInfo
- Publication number
- CN107446439B CN107446439B CN201710658801.0A CN201710658801A CN107446439B CN 107446439 B CN107446439 B CN 107446439B CN 201710658801 A CN201710658801 A CN 201710658801A CN 107446439 B CN107446439 B CN 107446439B
- Authority
- CN
- China
- Prior art keywords
- parts
- protective agent
- line protective
- engine line
- graphene oxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention relates to the field of engines, in particular to a multifunctional engine line protective agent. The protective agent is prepared by uniformly mixing the following materials in parts by weight: 30-60 parts of ethylene glycol ethyl ether, 20-30 parts of insulating resin, 0.3-0.5 part of OP emulsifier, 0.1-0.2 part of ethyl orthosilicate, 0.5-1 part of graphene oxide, 10-20 parts of propane and 10-20 parts of butane. Uniformly mixing ethylene glycol monoethyl ether, insulating resin, OP emulsifier, ethyl orthosilicate and graphene oxide at normal temperature, pouring the mixture into a metal aerosol can, and then filling propane and butane to obtain the composite material. The engine line protective agent has the functions of isolating moisture, avoiding oxidation, resisting high voltage, insulating, delaying line aging, repairing fine cracks, keeping cleanness and the like.
Description
Technical Field
The invention relates to the field of engines, in particular to a multifunctional engine line protective agent.
Background
The engine cabin is subjected to high temperature, severe cold, rain, moisture and sand storm, and the phenomena of aging and even cracking of the wire harness, the sensor joint, the rubber hose and the like in the engine cabin occur over time, which is more obvious for old vehicles. These aged circuits are highly susceptible to spontaneous ignition once they are short-circuited by oxidation.
The conventional engine wiring harness is generally composed of a plurality of strands of copper flexible wires, and the outer surface of the copper flexible wires is wrapped by plastic. In daily running, the cabin temperature is very high, and the plastic on the surface of the wire harness releases chemical substances such as plasticizers and the like after being heated, and the substances react with copper wires in the wire harness to reduce the strength of the plastic, increase the resistance of the copper wires and finally cause the wire harness to age to generate short circuit. The rubber hose in the engine room belongs to unsaturated macromolecular hydrocarbon, and the rubber is easy to oxidize after aging to cause vehicle spontaneous combustion.
Graphene oxide is a novel carbon material with excellent performance, and composite materials of the graphene oxide comprise polymer composite materials and inorganic composite materials, and further have wide application fields. The graphene oxide has a small-size effect, and the stacking of the sheets can form compact physical isolation, so that the graphene oxide has strong barrier capability on small molecules and repairs fine cracks. After the product is used, a layer of protective film can be formed on the surfaces of the engine wire, the battery joint and the wire harness, so that moisture is isolated and oxidation is avoided. The product has the characteristics of high pressure resistance and insulativity, so that the aging and cracking of rubber and plastic pipes in the engine room can be delayed, and the electric leakage of the wire harness caused by aging can be prevented. In addition, the sprayed protective film is not easy to be dusty, and the cabin can be kept clean for a long time by being easy to wipe.
The current patents for protecting engine circuits are few, and the Chinese patent of invention (publication No. CN101177588A) discloses a method for manufacturing an engine circuit protective agent, wherein phenolic resin or alkyd resin is used as a film-forming substance, and the phenolic resin is a resin with poor weather resistance and is easy to crack and fall off in the cold north in winter. The alkyd resin is not resistant to acid and alkali and hydrolysis, and the protection time is short, so that the effect is influenced. The resin with more excellent weather resistance, acid and alkali resistance and hydrolysis resistance is adopted, and the resin can not be re-adhered in hot summer and can not crack in cold winter after being used, so that the lines around the engine can be protected for a long time all the year round, and the aging of the lines can be delayed.
Disclosure of Invention
In order to overcome the problems of the existing products, the invention aims to provide a multifunctional engine circuit protective agent with self-repairing and flame-retardant functions.
In order to achieve the effect, the technical scheme of the invention is as follows:
a multifunctional engine line protective agent is prepared by uniformly mixing the following materials in parts by weight:
the multifunctional engine line protective agent is preferably 58.3 parts of ethylene glycol ethyl ether, 20 parts of insulating resin, 0.5 part of OP emulsifier, 0.2 part of ethyl orthosilicate, 1 part of graphene oxide, 10 parts of propane and 10 parts of butane.
The multifunctional engine line protective agent is characterized in that the insulating resin is one or more than two of acrylic resin, polyurethane resin and epoxy resin.
The multifunctional engine line protective agent is characterized in that the graphene oxide has a sheet diameter of 3-5000 nm.
The multifunctional engine line protective agent is preferably used, and the sheet diameter of the graphene oxide is 1-5 mu m.
The preparation method of the multifunctional engine line protective agent comprises the following steps: uniformly mixing ethylene glycol monoethyl ether, insulating resin, OP emulsifier, ethyl orthosilicate and graphene oxide at normal temperature, pouring the mixture into a metal aerosol can, and then filling propane and butane to obtain the composite material.
The design idea of the coating composition of the invention is as follows:
the protective agent comprises 30-60 parts of ethylene glycol ethyl ether, 20-30 parts of insulating resin, 0.3-0.5 part of OP emulsifier, 0.1-0.2 part of ethyl orthosilicate, 0.5-1 part of graphene oxide, 10-20 parts of propane, 10-20 parts of butane and the like. The functions of the components are as follows: ethylene glycol ethyl ether is used as a dispersing agent, an OP emulsifier can be used as a metal detergent, and tetraethoxysilane can improve the heat resistance of the product.
The invention has the following advantages and beneficial effects:
1. the invention can form a layer of protective film on the surfaces of the engine wire, the battery joint and the wire harness, isolate moisture, avoid oxidation, delay the aging and cracking of rubber and plastic pipes in the engine room and prevent the wire harness from electric leakage caused by aging.
2. The invention has the characteristics of high pressure resistance and insulativity.
3. The invention is not easy to be stained with dust, is easy to be wiped, and can keep the cabin clean for a long time.
Detailed Description
The following examples are presented to facilitate a more clear understanding of the invention and are to be considered as further illustrative and not restrictive.
Example 1:
in the embodiment, the multifunctional engine line protective agent is prepared by uniformly mixing the following materials in parts by weight:
example 2:
in the embodiment, the multifunctional engine line protective agent is prepared by uniformly mixing the following materials in parts by weight:
example 3:
in the embodiment, the multifunctional engine line protective agent is prepared by uniformly mixing the following materials in parts by weight:
in examples 1 to 3, the specific preparation method of the multifunctional engine line protective agent comprises the following steps: the finished product of the invention can be prepared by uniformly mixing ethylene glycol monoethyl ether, insulating resin, OP emulsifier, ethyl orthosilicate and graphene oxide at normal temperature, pouring the mixture into a metal aerosol can and then filling propane and butane.
The results of the tests on breakdown voltage and resistivity by the analysis test center of northeast university are shown in table 1.
TABLE 1
Detecting items | The result of the detection | Detection standard |
Breakdown voltage | 20KV/mm | GB/T 507-2002 |
Resistivity of | 3×1012Ω | DL 421-91 |
The results of the examples show that the engine line protective agent has the functions of isolating moisture, avoiding oxidation, resisting high voltage, insulating, delaying line aging, repairing fine cracks, keeping cleanness and the like.
The above description is only a preferred example of the present invention and is not intended to limit the present invention, and modifications and equivalents thereof may be made by those skilled in the art. Any modification, equivalent replacement, or improvement made within the spirit and principle of the present invention should be included in the protection scope of the present invention.
Claims (3)
1. The multifunctional engine line protective agent is characterized by being prepared by uniformly mixing the following materials in parts by weight:
the insulating resin is one or more of acrylic resin, polyurethane resin and epoxy resin;
the sheet diameter of the graphene oxide is 3-5000 nm;
the preparation method of the multifunctional engine line protective agent comprises the following steps: uniformly mixing ethylene glycol monoethyl ether, insulating resin, OP emulsifier, ethyl orthosilicate and graphene oxide at normal temperature, pouring the mixture into a metal aerosol can, and then filling propane and butane to obtain the composite material.
2. The multifunctional engine line protective agent according to claim 1, wherein the multifunctional engine line protective agent is preferably 58.3 parts of ethylene glycol ethyl ether, 20 parts of insulating resin, 0.5 part of OP emulsifier, 0.2 part of ethyl orthosilicate, 1 part of graphene oxide, 10 parts of propane and 10 parts of butane.
3. The multifunctional engine line protective agent according to claim 1, wherein the graphene oxide has a sheet diameter of 1-5 μm.