CN107434403A - It is a kind of to activate ceramic of Tea Polyphenols and preparation method thereof - Google Patents

It is a kind of to activate ceramic of Tea Polyphenols and preparation method thereof Download PDF

Info

Publication number
CN107434403A
CN107434403A CN201710712118.0A CN201710712118A CN107434403A CN 107434403 A CN107434403 A CN 107434403A CN 201710712118 A CN201710712118 A CN 201710712118A CN 107434403 A CN107434403 A CN 107434403A
Authority
CN
China
Prior art keywords
parts
ceramic
sand
stone
tea polyphenols
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201710712118.0A
Other languages
Chinese (zh)
Inventor
程燕文
周永富
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Guangdong Kangshitai New Material Technology Co Ltd
Original Assignee
Guangdong Kangshitai New Material Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Guangdong Kangshitai New Material Technology Co Ltd filed Critical Guangdong Kangshitai New Material Technology Co Ltd
Priority to CN201710712118.0A priority Critical patent/CN107434403A/en
Publication of CN107434403A publication Critical patent/CN107434403A/en
Withdrawn legal-status Critical Current

Abstract

The present invention relates to a kind of ceramic that can activate Tea Polyphenols and preparation method thereof, and in parts by weight, ceramic component includes:30 38 parts of Dongxing sand, 33 45 parts of pure white sand, 10 15 parts of the bright sand of good fortune, 7 10 parts of Huidong original mud, 7 10 parts of silica flour, 5 10 parts of talcum of burning, 8 12 parts of float stone, 15 25 parts of marmor serpentinatum, 8 10 parts of magnetite, 8 12 parts of gypsum rubrum, 8 12 parts of Black Warrior stone, 8 12 parts of raddle;The ceramic of the present invention has the function that can activate Tea Polyphenols, wide market.

Description

It is a kind of to activate ceramic of Tea Polyphenols and preparation method thereof
Technical field
The present invention relates to the technical field of ceramic, and in particular to a kind of ceramic and its system that can activate Tea Polyphenols Preparation Method.
Background technology
Ceramic can not be realized at present transmits bio-energy to people, lifts itself holistic health, can activate for a long time The effect demand of Tea Polyphenols, the ceramic that can activate Tea Polyphenols are in vacancy in ceramic industry.
The content of the invention
It is an object of the invention to for weak point of the prior art, propose a kind of ceramics system that can activate Tea Polyphenols Product and preparation method thereof, the ceramic have the function that can activate Tea Polyphenols.
To use following technical scheme up to this purpose, the present invention:
A kind of ceramic that can activate Tea Polyphenols, in parts by weight, ceramic component includes:Dongxing sand 30-38 parts, Pure white sand 33-45 parts, the bright sand 10-15 parts of good fortune, Huidong original mud 7-10 parts, silica flour 7-10 parts, burning talcum 5-10 parts, float stone 8-12 Part, marmor serpentinatum 15-25 parts, magnetite 8-10 parts, gypsum rubrum 8-12 parts, Black Warrior stone 8-12 parts, raddle 8-12 parts.
Further, in parts by weight, ceramic component includes:35 parts of Dongxing sand, 35 parts of pure white sand, good fortune are bright 12 parts of sand, 8 parts of ultrawhite ball clay, 9 parts of Huidong original mud, 8 parts of silica flour, 8 parts of talcum of burning, 5 parts of bentonite, 10 parts of float stone, marmor serpentinatum 20 parts, 9 parts of magnetite, 10 parts of gypsum rubrum, 10 parts of Black Warrior stone, 10 parts of raddle.
A kind of method for preparing the above-mentioned ceramic that can activate Tea Polyphenols, including step are as follows:
A, raw material preparation;Dongxing sand 30-38 parts, pure white sand 33-45 parts, the bright sand 10-15 parts of good fortune, Huidong original mud 7-10 parts, stone English powder 7-10 parts, burn talcum 5-10 parts, float stone 8-12 parts, marmor serpentinatum 15-25 parts, magnetite 8-10 parts, gypsum rubrum 8-12 parts, the Black Warrior Stone 8-12 parts, raddle 8-12 parts carry out mixing outfit, obtain resulting mixture A1;B, ball milling;The mixture A1 and water(Press Weight is than 2:1)Add and mixed grinding is carried out in ball mill, form slurry B1;C, mist projection granulating;The slurry B1 is injected in It is dried in mist drying tower, is granulated, forms powder C1;D, punch forming;The powder C1 is added stamping machine to carry out Cloth, punch forming, obtain ceramic tile blank D1;E, calcine;The ceramic tile blank D1 is put into kiln and calcined, is made pottery Ceramic tile E1.
Beneficial effects of the present invention:1. it has alkalescent to the ceramic that the present invention realizes, anion is produced, can be incited somebody to action Water, alcohol, etc. food decomposed and converted, promote nutrient absorption, enhancing metabolism, effectively mitigate alcohol to the wound of human body Evil, absorption of the human body to water, strengthen immunity are improved, and internal toxin and heavy metal can be excluded, stimulated circulation, help Preferable health product that is metabolic, being dispelling fatigue, meets the market demand.
Embodiment
Technical scheme is further illustrated below by embodiment.
Embodiment 1:
A kind of method for preparing the described ceramic that can activate Tea Polyphenols, including step are as follows:
A, raw material preparation;In parts by weight, ceramic component includes:30 parts of Dongxing sand, 33 parts of pure white sand, the bright sand of good fortune 10 parts, 5 parts of ultrawhite ball clay, 7 parts of Huidong original mud, 7 parts of silica flour, burn 5 parts of talcum, 4 parts of bentonite, 8 parts of float stone, marmor serpentinatum 15 Part, 8 parts of magnetite, 8 parts of gypsum rubrum, 8 parts of Black Warrior stone, 8 parts of raddle carry out mixing outfit, obtain resulting mixture A1;B, ball milling; The mixture A1 and water(By weight 2:1)Add and mixed grinding is carried out in ball mill, form slurry B1;C, mist projection granulating; Slurry B1 injections are dried to it in the spray drying tower, are granulated, form powder C1;D, punch forming;Described in Powder C1 adds stamping machine and carries out cloth, punch forming, obtains ceramic tile blank D1;E, calcine;The ceramic tile blank D1 is put into Calcined in kiln, obtain Ceramic Tiles E1.
Embodiment 2:
A kind of method for preparing the described ceramic that can activate Tea Polyphenols, including step are as follows:
A, raw material preparation;38 parts of Dongxing sand, 45 parts of pure white sand, 15 parts of the bright sand of good fortune, 10 parts of ultrawhite ball clay, 10 parts of Huidong original mud, 10 parts of silica flour, burn 10 parts of talcum, 8 parts of bentonite, 12 parts of float stone, 25 parts of marmor serpentinatum, 10 parts of magnetite, 12 parts of gypsum rubrum, the Black Warrior 12 parts of stone, 12 parts of raddle carry out mixing outfit, obtain resulting mixture A1;B, ball milling;The mixture A1 and water(By weight Than 2:1)Add and mixed grinding is carried out in ball mill, form slurry B1;C, mist projection granulating;It is dry that the slurry B1 is injected in spraying It is dried in dry tower, is granulated, forms powder C1;D, punch forming;The powder C1 add stamping machine carry out cloth, Punch forming, obtain ceramic tile blank D1;E, calcine;The ceramic tile blank D1 is put into kiln and calcined, obtains Ceramic Tiles E1。
Embodiment 3:
A kind of method for preparing the described ceramic that can activate Tea Polyphenols, including step are as follows:
A, raw material preparation;35 parts of Dongxing sand, 35 parts of pure white sand, 12 parts of the bright sand of good fortune, 8 parts of ultrawhite ball clay, 9 parts of Huidong original mud, stone 8 parts of English powder, burn 8 parts of talcum, 5 parts of bentonite, 10 parts of float stone, 20 parts of marmor serpentinatum, 9 parts of magnetite, 10 parts of gypsum rubrum, Black Warrior stone 10 Part, 10 parts of raddle carry out mixing outfit, obtain resulting mixture A1;B, ball milling;The mixture A1 and water(By weight 2: 1)Add and mixed grinding is carried out in ball mill, form slurry B1;C, mist projection granulating;The slurry B1 is injected in spray drying tower In it is dried, be granulated, form powder C1;D, punch forming;The powder C1 is added stamping machine and carries out cloth, punching press Shaping, obtains ceramic tile blank D1;E, calcine;The ceramic tile blank D1 is put into kiln and calcined, obtains Ceramic Tiles E1.
The technical principle of the present invention is described above in association with specific embodiment.These descriptions are intended merely to explain the present invention's Principle, and limiting the scope of the invention can not be construed in any way.Based on explanation herein, the technology of this area Personnel would not require any inventive effort the other embodiments that can associate the present invention, and these modes are fallen within Within protection scope of the present invention.

Claims (3)

  1. A kind of 1. ceramic that can activate Tea Polyphenols, it is characterised in that:In parts by weight, ceramic component includes: Dongxing sand 30-38 parts, pure white sand 33-45 parts, the bright sand 10-15 parts of good fortune, Huidong original mud 7-10 parts, silica flour 7-10 parts, burning talcum 5-10 parts, float stone 8-12 parts, marmor serpentinatum 15-25 parts, magnetite 8-10 parts, gypsum rubrum 8-12 parts, Black Warrior stone 8-12 parts, raddle 8- 12 parts.
  2. 2. the ceramic according to claim 1 that Tea Polyphenols can be activated, it is characterised in that:In parts by weight, make pottery Ceramic products component includes:35 parts of Dongxing sand, 35 parts of pure white sand, 12 parts of the bright sand of good fortune, 8 parts of ultrawhite ball clay, 9 parts of Huidong original mud, quartz 8 parts of powder, burn 8 parts of talcum, 5 parts of bentonite, 10 parts of float stone, 20 parts of marmor serpentinatum, 9 parts of magnetite, 10 parts of gypsum rubrum, 10 parts of Black Warrior stone, 10 parts of raddle.
  3. A kind of 3. method for preparing the ceramic that can activate Tea Polyphenols described in claim 1-2, it is characterised in that:Including step It is rapid as follows:A, raw material preparation;Dongxing sand 30-38 parts, pure white sand 33-45 parts, the bright sand 10-15 parts of good fortune, Huidong original mud 7-10 parts, Silica flour 7-10 parts, burn talcum 5-10 parts, be float stone 8-12 parts, marmor serpentinatum 15-25 parts, magnetite 8-10 parts, gypsum rubrum 8-12 parts, profound Military stone 8-12 parts, raddle 8-12 parts carry out mixing outfit, obtain resulting mixture A1;B, ball milling;The mixture A1 and water (By weight 2:1)Add and mixed grinding is carried out in ball mill, form slurry B1;C, mist projection granulating;The slurry B1 is sprayed It is dried in the spray drying tower, is granulated, forms powder C1;D, punch forming;The powder C1 is added stamping machine Cloth, punch forming are carried out, obtains ceramic tile blank D1;E, calcine;The ceramic tile blank D1 is put into kiln and calcined, is obtained To Ceramic Tiles E1.
CN201710712118.0A 2017-08-18 2017-08-18 It is a kind of to activate ceramic of Tea Polyphenols and preparation method thereof Withdrawn CN107434403A (en)