CN107434400A - 一种提升酒液口感的陶瓷制品及其制备方法 - Google Patents

一种提升酒液口感的陶瓷制品及其制备方法 Download PDF

Info

Publication number
CN107434400A
CN107434400A CN201710711739.7A CN201710711739A CN107434400A CN 107434400 A CN107434400 A CN 107434400A CN 201710711739 A CN201710711739 A CN 201710711739A CN 107434400 A CN107434400 A CN 107434400A
Authority
CN
China
Prior art keywords
parts
ceramic
sand
stone
wine liquid
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201710711739.7A
Other languages
English (en)
Inventor
程燕文
周永富
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Guangdong Kangshitai New Material Technology Co Ltd
Original Assignee
Guangdong Kangshitai New Material Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Guangdong Kangshitai New Material Technology Co Ltd filed Critical Guangdong Kangshitai New Material Technology Co Ltd
Priority to CN201710711739.7A priority Critical patent/CN107434400A/zh
Publication of CN107434400A publication Critical patent/CN107434400A/zh
Withdrawn legal-status Critical Current

Abstract

本发明涉及一种提升酒液口感的陶瓷制品及其制备方法,按重量份数计算,陶瓷制品组分包括:东兴砂30‑38份、纯白砂33‑45份、福明砂10‑15份、超白球土5‑10份、惠东原坭7‑10份、石英粉7‑10份、烧滑石5‑10份、膨润土4‑8份、浮石8‑12份、花蕊石15‑25份、磁石8‑10份、寒水石8‑12份、玄武石8‑12份、代赭石8‑12份、沸石25‑32份、芒硝3‑8份、麦饭石12‑16份;本发明的陶瓷制品具有提升酒液口感的功能,市场前景广阔。

Description

一种提升酒液口感的陶瓷制品及其制备方法
技术领域
[0001]本发明涉及陶瓷制品的技术领域,具体涉及一种提升酒液口感的陶瓷制品及其制 备方法。
背景技术
[0002]目前陶瓷制品无法实现向人们长时间传递生物能量、提升自身整体健康、提升酒 液口感的效果需求,提升酒液口感的陶瓷制品在陶瓷行业处于空缺。
发明内容
[0003] 本发明的目的在于针对现有技术中的不足之处,提出一种提升酒液口感的陶瓷制 品及其制备方法,该陶瓷制品具有提升酒液口感的功能。
[0004] 为达此目的,本发明采用以下技术方案: 一种提升酒液口感的陶瓷制品,按重量份数计算,陶瓷制品组分包括:东兴砂30-38份、 纯白砂33-45份、福明砂10-15份、超白球土 5-10份、惠东原坭7-10份、石英粉7-10份、烧滑石 5-10份、膨润土 4-8份、浮石8-12份、花蕊石15-25份、磁石8-10份、寒水石8-12份、玄武石8-12份、代赫石8-12份、沸石25_32份、芒硝3_8份、麦饭石12_16份。
[0005] 更进一步地,按重量份数计算,陶瓷制品组分包括:东兴砂35份、纯白砂35份、福明 砂12份、超白球土 8份、惠东原坭9份、石英粉8份、烧滑石8份、膨润土 5份、浮石10份、花蕊石 20份、磁石9份、寒水石10份、玄武石10份、代赭石1 〇份、沸石30份、芒硝6份、麦饭石10份。 [0006] 一种制备上述的提升酒液口感的陶瓷制品的方法,包括步骤如下: A、原料配备;把东兴砂30-38份、纯白砂33-45份、福明砂10-15份、超白球土 5-10份、惠 东原坭7-10份、石英粉7-10份、烧滑石5-10份、膨润土 4-8份、浮石8-12份、花蕊石15-25份、 磁石8-10份、寒水石8-12份、玄武石8-12份、代赭石8-12份、沸石25-32份、芒硝3-8份、麦饭 石12-16份进行混合配备,得到成混合物A1 ;B、球磨;把所述混合物A1和水(按重量比2:1)加 入球磨机内进行混合研磨,形成浆料B1;C、喷雾造粒;把所述浆料B1喷射在喷雾干燥塔中对 其进行干燥,造粒,形成粉料C1;D、冲压成型;把所述粉料C1加入冲压机进行布料、冲压成 型,得到瓷砖坯体Dl; E、煅烧;把所述瓷砖坯体D1放入窑炉内进行煅烧,得到陶瓷砖E1。
[0007] 本发明的有益效果:1.本发明实现的陶瓷制品其具有弱碱性,产生负离子,能将 水、酒精、等食物进行分解和转化,把酒放在陶瓷制品上进行储存,可以分解酒中的涩味的 乙醛等物质,可以迅速使得酒变成陈年老酒,使之口感像陈年老酒一样,酒精度不变,满足 市场需求。
具体实施方式
[0008] 下面通过具体实施方式来进一步说明本发明的技术方案。
[0009] 实施例1: 一种制备所述的提升酒液口感的陶瓷制品的方法,包括步骤如下: A、原料配备;把按重量份数计算,陶瓷制品组分包括:东兴砂30份、纯白砂33份、福明砂 10份、超白球土 5份、惠东原坭7份、石英粉7份、烧滑石5份、膨润土 4份、浮石8份、花蕊石15 份、磁石8份、寒水石8份、玄武石8份、代赭石8份、沸石25份、芒硝3份、麦饭石12份进行混合 配备,得到成混合物A1;B、球磨;把所述混合物A1和水(按重量比2:1)加入球磨机内进行混 合研磨,形成浆料B1;C、喷雾造粒;把所述浆料B1喷射在喷雾干燥塔中对其进行干燥,造粒, 形成粉料Cl ;D、冲压成型;把所述粉料C1加入冲压机进行布料、冲压成型,得到瓷砖坯体D1; E、煅烧;把所述瓷砖坯体D1放入窑炉内进行煅烧,得到陶瓷砖E1。
[0010]实施例2: —种制备所述的提升酒液口感的陶瓷制品的方法,包括步骤如下: A、原料配备;把东兴砂38份、纯白砂45份、福明砂15份、超白球土 10份、惠东原坭10份、 石英粉10份、烧滑石10份、膨润土8份、浮石12份、花蕊石25份、磁石10份、寒水石12份、玄武 石12份、代赭石12份、沸石32份、芒硝8份、麦饭石16份进行混合配备,得到成混合物Al; B、球 磨;把所述混合物A1和水(按重量比2:1)加入球磨机内进行混合研磨,形成浆料Bl;C、喷雾 造粒;把所述浆料B1喷射在喷雾干燥塔中对其进行干燥,造粒,形成粉料C1;D、冲压成型;把 所述粉料C1加入冲压机进行布料、冲压成型,得到瓷砖坯体D1;E、煅烧;把所述瓷砖坯体D1 放入窑炉内进行煅烧,得到陶瓷砖E1。
[0011]实施例3:—种制备所述的提升酒液口感的陶瓷制品的方法,包括步骤如下: A、原料配备;把东兴砂35份、纯白砂35份、福明砂12份、超白球土 8份、惠东原坭9份、石 英粉8份、烧滑石8份、膨润土5份、浮石1 〇份、花蕊石20份、磁石9份、寒水石10份、玄武石丄〇 份、代赭石10份、沸石3〇份、芒硝6份、麦饭石10份进行混合配备,得到成混合物a 1; B、球磨; 把所述混合物A1和水(按重量比2:1)加入球磨机内进行混合研磨,形成浆料B1 ;c、喷雾造 粒;把所述浆料B1喷射在喷雾干燥塔中对其进行干燥,造粒,形成粉料C1;D、冲压成型j把所 述粉料C1加入冲压机进行布料、冲压成型,得到瓷砖坯体D1;E、锻烧;把所述瓷砖坯体01放 入窑炉内进行锻烧,得到陶瓷砖E1。
[0012]以上结合具体实施例描述了本发明的技术原理。这些描述只是为了解释本发明的 原理,而不能以任何方式解释为对本发明保护范围的限制。基于此处的解释,本领域的技术 人员不需要付出创造性的劳动即可联想到本发明的其它具体实施方式,这些方式都将落入 本发明的保护范围之内。

Claims (3)

1.一种提升酒液口感的陶瓷制品,其特征在于:按重量份数计算,陶瓷制品组分包括: 东兴砂30-38份、纯白砂33-45份、福明砂10-15份、超白球土 5-10份、惠东原坭7-10份、石英 粉7-10份、烧滑石5_10份、膨润土 4-S份、浮石S-12份、花蕊石15-25份、磁石8-10份、寒水石 8-12份、玄武石8-12份、代赭石8-12份、沸石25-32份、芒硝3-8份、麦饭石12-16份。
2.根据权利要求1所述的提升酒液口感的陶瓷制品,其特征在于:按重量份数计算,陶 瓷制品组分包括:东兴砂35份、纯白砂35份、福明砂12份、超白球土8份、惠东原坭9份、石英 粉8份、烧滑石8份、膨润土 5份、浮石10份、花蕊石20份、磁石9份、寒水石10份、玄武石10份、 代赭石10份、沸石30份、芒硝6份、麦饭石10份。
3.—种制备权利要求1-2所述的提升酒液口感的陶瓷制品的方法,其特征在于:包括步 骤如下:A、原料配备;把东兴砂30-38份、纯白砂33-45份、福明砂10-15份、超白球土 5-10份、 惠东原坭7-10份、石英粉7-10份、烧滑石5-10份、膨润土 4-8份、浮石8-12份、花蕊石15-25 份、磁石8-10份、寒水石8-12份、玄武石8-12份、代赭石8-12份、沸石25-32份、芒硝3-8份、麦 饭石12_16份进行混合配备,得到成混合物Al; B、球磨;把所述混合物A1和水(按重量比2:1) 加入球磨机内进行混合研磨,形成浆料Bl; C、喷雾造粒;把所述浆料B1喷射在喷雾干燥塔中 对其进行干燥,造粒,形成粉料Cl; D、冲压成型;把所述粉料C1加入冲压机进行布料、冲压成 型,得到瓷砖坯体Dl; E、煅烧;把所述瓷砖坯体D1放入窑炉内进行煅烧,得到陶瓷砖E1。
CN201710711739.7A 2017-08-18 2017-08-18 一种提升酒液口感的陶瓷制品及其制备方法 Withdrawn CN107434400A (zh)