CN107415334A - A kind of antistatic fabric and processing method - Google Patents
A kind of antistatic fabric and processing method Download PDFInfo
- Publication number
- CN107415334A CN107415334A CN201710672486.7A CN201710672486A CN107415334A CN 107415334 A CN107415334 A CN 107415334A CN 201710672486 A CN201710672486 A CN 201710672486A CN 107415334 A CN107415334 A CN 107415334A
- Authority
- CN
- China
- Prior art keywords
- layer
- antistatic backing
- antistatic
- retardant
- flame
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of antistatic fabric and processing method,Including the first antistatic backing,Second antistatic backing,3rd antistatic backing,Waterproof layer,Antibiotic layer,Flame-retardant layer,Thermal insulation layer and internal layer,The top surface of internal layer is provided with the first antistatic backing,The top surface of 3rd antistatic backing is provided with thermal insulation layer,First antistatic backing,The specification of second antistatic backing and the 3rd antistatic backing is identical,First antistatic backing,Second antistatic backing and the 3rd antistatic backing include the elastomer at center,It is set around the conductive wire group on elastomer surface and is coated on the protective layer of outer layer,Multigroup conductive wire group is wound with elastomer,Conductive wire group includes 4~15 conductive wires,Between multigroup conductive wire group around 5~15 times away from adjacent two conductive wire distances for same group of conductive wire group,Thermal insulation layer is formed using cotton material braiding,Unique structure of the present invention,Anti-static effect is obvious,Good flame retardation effect,It is adapted to promote.
Description
Technical field
The present invention relates to antistatic fabric technical field, more particularly to a kind of antistatic fabric and processing method.
Background technology
Fabric is exactly the material for making clothes.As one of clothes three elements, fabric can not only annotate clothes
Style and characteristic, and directly left and right the color of clothes, the expression effect of moulding.In clothes big world, the fabric of clothes
It is multifarious, make rapid progress.But generally, high-quality, high-grade fabric, mostly with wear is comfortable, sweat-absorbing breathable,
The characteristics of several aspects such as well-pressed, vision is noble, tactile is soft and graceful of dangling.The clothes of formal social life institute wear are produced on,
Preferably select pure cotton, pure wool, pure silk, pure gunny products.The clothes made with these four pure natural quality fabrics, mostly class are higher.Have
When, the clothes of the pure leatherwork of wear, also it is allowed.Shuttle-woven fabric:It is that warp thread and weft yarn are mutually perpendicular to weave in
The fabric of formation.There are plain weave (plain), twill (twill), three kinds of satin weave (satinweave) in its elementary organization.Different shuttles
Knitted fabric is also to be formed by these three elementary organizations and by its protean tissue.It is knitted fabric:With knitting needle by yarn or
Long filament forms coil, then coil is mutually gone here and there set and formed, due to the loop construction feature of knitted fabric, in unit length yarn storage amount compared with
It is more, therefore have good elasticity mostly.Knitting fabric has one side and two-sided point.
The requirement of antistatic clothing is very high, it is necessary to which worker wears antistatic clothing in some factories, No Open Flames in factory and
Electrostatic, electrostatic have an impact to equipment, and existing antistatic clothing is simple in construction, and function is single, antistatic fabric function more than one, respectively
Electrostatic is easily produced between interlayer, how to avoid the generation of electrostatic, therefore, the present invention proposes a kind of antistatic fabric and added
Work method.
The content of the invention
The invention aims to solve shortcoming present in prior art, and a kind of antistatic fabric for proposing and
Processing method.
To achieve these goals, present invention employs following technical scheme:
A kind of antistatic fabric, including the first antistatic backing, the second antistatic backing, the 3rd antistatic backing, waterproof layer, antibacterial
Layer, flame-retardant layer, thermal insulation layer and internal layer, the top surface of internal layer are provided with the first antistatic backing, and the top surface of the first antistatic backing is provided with fire-retardant
Layer, the top of the flame-retardant layer are provided with the second antistatic backing, and the top surface of the second antistatic backing is provided with antibiotic layer, the top surface of antibiotic layer
Provided with the 3rd antistatic backing, the top surface of the 3rd antistatic backing is provided with thermal insulation layer, and the top surface of thermal insulation layer is provided with waterproof layer, and first is anti-quiet
The specification of electric layer, the second antistatic backing and the 3rd antistatic backing is identical, and the first antistatic backing, the second antistatic backing and three proofings are quiet
Electric layer includes the elastomer at center, is set around the conductive wire group on elastomer surface and is coated on the protection of outer layer
Layer, multigroup conductive wire group is wound with elastomer, conductive wire group includes 4~15 conductive wires, multigroup to lead
Between electric metal silk group around 5~15 times away from adjacent two conductive wire distances for same group of conductive wire group, every
Thermosphere is formed using cotton material braiding.
Preferably, the waterproof layer surface scribbles one layer of water-repellent paint, and the water-repellent paint uses Teflon high-performance special
Coating, Teflon high-performance special coating are the fluoro coatings using polytetrafluoroethylene (PTFE) as matrix resin.
Preferably, the warp thread of the internal layer and weft yarn are respectively cotton thread and knitting wool, and cotton thread and knitting wool are mutually to rise and fall, hand over
Wrong mode, which weaves, to be formed.
Preferably, using silver fiber polyester thread, alternately sink-float braiding forms the antibiotic layer, and silver fiber polyester thread includes washing
Synthetic fibre line main body and silver ion shell, wherein polyester thread main body are coated with silver ion shell, and silver ion shell is by argent
Composition.
A kind of processing method of antistatic fabric, comprises the following steps,
S1, flame-retardant layer have each raw material of following parts by weight:It is 55~80 parts of flame-retardant acrylic fibre, 15~40 parts of combed cotton, fire-retardant
3~7 parts of nylon, 3~7 parts of aramid fiber, 1~3 part of anti-flaming viscose, 5~10 parts of polyphenylene sulfide fibre, 10~15 parts of fire retardant ATP;
S2, the melting of flame-retardant acrylic fibre, combed cotton, fire-retardant nylon, aramid fiber, anti-flaming viscose and polyphenylene sulfide fibre is put into stirring
It is sufficiently stirred in device, rotating speed is 5000~6000 turns/min, and mixing time is 2~3h, then fire retardant ATP is added, and regulation turns
6000~7000 turns/min of speed, mixing time are 1~1.5h, add surfactant and mix, are extruded from spinneret, are formed fine
Dimension, by fibrage into yarn A;
S3, the yarn A in S2 is woven into flame-retardant layer;
S4, the first antistatic backing, the second antistatic backing, the 3rd antistatic backing, antibiotic layer, flame-retardant layer, thermal insulation layer and internal layer
It is stitched together by needlework, the surface spraying of thermal insulation layer has one layer of waterproof layer, obtains this product.
Preferably, the orifice diameter of spinneret is 0.10-0.20mm.
Preferably, the fabric warp density of flame-retardant layer is 70-90 roots/cm, and weft density is 60-100 roots/cm.
In the present invention, the specification by the first antistatic backing, the second antistatic backing and the 3rd antistatic backing is identical, and first is anti-
Electrostatic layer, the second antistatic backing and the 3rd antistatic backing include the elastomer at center, are set around leading for elastomer surface
Electric metal silk group and the protective layer for being coated on outer layer, antistatic backing is provided between each layer function precoat, is so effectively kept away
Exempt from the triboelectrification between each layer, the warp thread and weft yarn of internal layer are respectively cotton thread and knitting wool, and cotton thread and knitting wool mutually to rise and fall,
Mode staggeredly, which weaves, to be formed, and is worn on a human body very comfortably, knitting wool and cotton thread are very soft, very personal, and antibiotic layer uses silver fiber
Alternately sink-float braiding forms polyester thread, has the function that sterilization, unique structure of the present invention, anti-static effect is obvious, flame retardant effect
It is good, it is adapted to promote.
Embodiment
The technical scheme in the embodiment of the present invention will be clearly and completely described below, it is clear that described implementation
Example only part of the embodiment of the present invention, rather than whole embodiments.
Embodiment one
A kind of antistatic fabric proposed by the present invention, including the first antistatic backing, the second antistatic backing, the 3rd antistatic
Layer, waterproof layer, antibiotic layer, flame-retardant layer, thermal insulation layer and internal layer, it is characterised in that the top surface of internal layer is provided with the first antistatic backing, the
The top surface of one antistatic backing is provided with flame-retardant layer, and the top of the flame-retardant layer is provided with the second antistatic backing, the top of the second antistatic backing
Face is provided with antibiotic layer, and the top surface of antibiotic layer is provided with the 3rd antistatic backing, and the top surface of the 3rd antistatic backing is provided with thermal insulation layer, thermal insulation layer
Top surface be provided with waterproof layer, the specification of the first antistatic backing, the second antistatic backing and the 3rd antistatic backing is identical, the first antistatic
Layer, the second antistatic backing and the 3rd antistatic backing include the elastomer at center, are set around the conductive gold on elastomer surface
Belong to silk group and be coated on the protective layer of outer layer, multigroup conductive wire group, conductive wire group bag are wound with elastomer
Include 5 conductive wires, between multigroup conductive wire group around away from adjacent two conductions for same group of conductive wire group
6 times of wire distance, thermal insulation layer are formed using cotton material braiding.
A kind of processing method of antistatic fabric proposed by the present invention, comprises the following steps,
S1, flame-retardant layer have each raw material of following parts by weight:60 parts of flame-retardant acrylic fibre, 20 parts of combed cotton, 4 parts of fire-retardant nylon,
4 parts of aramid fiber, 1 part of anti-flaming viscose, 6 parts of polyphenylene sulfide fibre, 11 parts of fire retardant ATP;
S2, the melting of flame-retardant acrylic fibre, combed cotton, fire-retardant nylon, aramid fiber, anti-flaming viscose and polyphenylene sulfide fibre is put into stirring
It is sufficiently stirred in device, rotating speed is 5100 turns/min, mixing time 2.2h, then fire retardant ATP is added, and adjusts rotating speed 6100
Turn/min, mixing time 1h, add surfactant and mix, extruded from spinneret, fiber is formed, by fibrage resultant yarn
Line A;
S3, the yarn A in S2 is woven into flame-retardant layer;
S4, the first antistatic backing, the second antistatic backing, the 3rd antistatic backing, antibiotic layer, flame-retardant layer, thermal insulation layer and internal layer
It is stitched together by needlework, the surface spraying of thermal insulation layer has one layer of waterproof layer, obtains this product.
Embodiment two
A kind of antistatic fabric proposed by the present invention, including the first antistatic backing, the second antistatic backing, the 3rd antistatic
Layer, waterproof layer, antibiotic layer, flame-retardant layer, thermal insulation layer and internal layer, it is characterised in that the top surface of internal layer is provided with the first antistatic backing, the
The top surface of one antistatic backing is provided with flame-retardant layer, and the top of the flame-retardant layer is provided with the second antistatic backing, the top of the second antistatic backing
Face is provided with antibiotic layer, and the top surface of antibiotic layer is provided with the 3rd antistatic backing, and the top surface of the 3rd antistatic backing is provided with thermal insulation layer, thermal insulation layer
Top surface be provided with waterproof layer, the specification of the first antistatic backing, the second antistatic backing and the 3rd antistatic backing is identical, the first antistatic
Layer, the second antistatic backing and the 3rd antistatic backing include the elastomer at center, are set around the conductive gold on elastomer surface
Belong to silk group and be coated on the protective layer of outer layer, multigroup conductive wire group, conductive wire group bag are wound with elastomer
Include 7 conductive wires, between multigroup conductive wire group around away from adjacent two conductions for same group of conductive wire group
8 times of wire distance, thermal insulation layer are formed using cotton material braiding.
A kind of processing method of antistatic fabric proposed by the present invention, comprises the following steps,
S1, flame-retardant layer have each raw material of following parts by weight:65 parts of flame-retardant acrylic fibre, 25 parts of combed cotton, 4 parts of fire-retardant nylon,
4 parts of aramid fiber, 2 parts of anti-flaming viscose, 7 parts of polyphenylene sulfide fibre, 12 parts of fire retardant ATP;
S2, the melting of flame-retardant acrylic fibre, combed cotton, fire-retardant nylon, aramid fiber, anti-flaming viscose and polyphenylene sulfide fibre is put into stirring
It is sufficiently stirred in device, rotating speed is 5400 turns/min, mixing time 2.5h, then fire retardant ATP is added, and adjusts rotating speed 6400
Turn/min, mixing time 1.2h, add surfactant mix, extruded from spinneret, formed fiber, by fibrage into
Yarn A;
S3, the yarn A in S2 is woven into flame-retardant layer;
S4, the first antistatic backing, the second antistatic backing, the 3rd antistatic backing, antibiotic layer, flame-retardant layer, thermal insulation layer and internal layer
It is stitched together by needlework, the surface spraying of thermal insulation layer has one layer of waterproof layer, obtains this product.
Embodiment three
A kind of antistatic fabric proposed by the present invention, including the first antistatic backing, the second antistatic backing, the 3rd antistatic
Layer, waterproof layer, antibiotic layer, flame-retardant layer, thermal insulation layer and internal layer, it is characterised in that the top surface of internal layer is provided with the first antistatic backing, the
The top surface of one antistatic backing is provided with flame-retardant layer, and the top of the flame-retardant layer is provided with the second antistatic backing, the top of the second antistatic backing
Face is provided with antibiotic layer, and the top surface of antibiotic layer is provided with the 3rd antistatic backing, and the top surface of the 3rd antistatic backing is provided with thermal insulation layer, thermal insulation layer
Top surface be provided with waterproof layer, the specification of the first antistatic backing, the second antistatic backing and the 3rd antistatic backing is identical, the first antistatic
Layer, the second antistatic backing and the 3rd antistatic backing include the elastomer at center, are set around the conductive gold on elastomer surface
Belong to silk group and be coated on the protective layer of outer layer, multigroup conductive wire group, conductive wire group bag are wound with elastomer
Include 9 conductive wires, between multigroup conductive wire group around away from adjacent two conductions for same group of conductive wire group
10 times of wire distance, thermal insulation layer are formed using cotton material braiding.
A kind of processing method of antistatic fabric proposed by the present invention, comprises the following steps,
S1, flame-retardant layer have each raw material of following parts by weight:66 parts of flame-retardant acrylic fibre, 30 parts of combed cotton, 5 parts of fire-retardant nylon,
5 parts of aramid fiber, 2 parts of anti-flaming viscose, 8 parts of polyphenylene sulfide fibre, 13 parts of fire retardant ATP;
S2, the melting of flame-retardant acrylic fibre, combed cotton, fire-retardant nylon, aramid fiber, anti-flaming viscose and polyphenylene sulfide fibre is put into stirring
It is sufficiently stirred in device, rotating speed is 5600 turns/min, mixing time 2.6h, then fire retardant ATP is added, and adjusts rotating speed 6600
Turn/min, mixing time 1.25h, add surfactant and mix, extruded from spinneret, fiber is formed, by fibrage
Into yarn A;
S3, the yarn A in S2 is woven into flame-retardant layer;
S4, the first antistatic backing, the second antistatic backing, the 3rd antistatic backing, antibiotic layer, flame-retardant layer, thermal insulation layer and internal layer
It is stitched together by needlework, the surface spraying of thermal insulation layer has one layer of waterproof layer, obtains this product.
Example IV
A kind of antistatic fabric proposed by the present invention, including the first antistatic backing, the second antistatic backing, the 3rd antistatic
Layer, waterproof layer, antibiotic layer, flame-retardant layer, thermal insulation layer and internal layer, it is characterised in that the top surface of internal layer is provided with the first antistatic backing, the
The top surface of one antistatic backing is provided with flame-retardant layer, and the top of the flame-retardant layer is provided with the second antistatic backing, the top of the second antistatic backing
Face is provided with antibiotic layer, and the top surface of antibiotic layer is provided with the 3rd antistatic backing, and the top surface of the 3rd antistatic backing is provided with thermal insulation layer, thermal insulation layer
Top surface be provided with waterproof layer, the specification of the first antistatic backing, the second antistatic backing and the 3rd antistatic backing is identical, the first antistatic
Layer, the second antistatic backing and the 3rd antistatic backing include the elastomer at center, are set around the conductive gold on elastomer surface
Belong to silk group and be coated on the protective layer of outer layer, multigroup conductive wire group, conductive wire group bag are wound with elastomer
Include 12 conductive wires, between multigroup conductive wire group around away from adjacent two conductions for same group of conductive wire group
12 times of wire distance, thermal insulation layer are formed using cotton material braiding.
A kind of processing method of antistatic fabric proposed by the present invention, comprises the following steps,
S1, flame-retardant layer have each raw material of following parts by weight:70 parts of flame-retardant acrylic fibre, 32 parts of combed cotton, 5 parts of fire-retardant nylon,
5 parts of aramid fiber, 3 parts of anti-flaming viscose, 8 parts of polyphenylene sulfide fibre, 14 parts of fire retardant ATP;
S2, the melting of flame-retardant acrylic fibre, combed cotton, fire-retardant nylon, aramid fiber, anti-flaming viscose and polyphenylene sulfide fibre is put into stirring
It is sufficiently stirred in device, rotating speed is 5800 turns/min, mixing time 2.7h, then fire retardant ATP is added, and adjusts rotating speed 6800
Turn/min, mixing time 1.5h, add surfactant mix, extruded from spinneret, formed fiber, by fibrage into
Yarn A;
S3, the yarn A in S2 is woven into flame-retardant layer;
S4, the first antistatic backing, the second antistatic backing, the 3rd antistatic backing, antibiotic layer, flame-retardant layer, thermal insulation layer and internal layer
It is stitched together by needlework, the surface spraying of thermal insulation layer has one layer of waterproof layer, obtains this product.
The tensile capacity of the antistatic fabric prepared is tested in the embodiment of the present invention one~tetra- respectively, and is tested market and sold
Fabric compare, draw following parameter:
The foregoing is only a preferred embodiment of the present invention, but protection scope of the present invention be not limited thereto,
Any one skilled in the art the invention discloses technical scope in, technique according to the invention scheme and its
Inventive concept is subject to equivalent substitution or change, should all be included within the scope of the present invention.
Claims (7)
1. a kind of antistatic fabric, including the first antistatic backing, the second antistatic backing, the 3rd antistatic backing, waterproof layer, antibacterial
Layer, flame-retardant layer, thermal insulation layer and internal layer, it is characterised in that the top surface of internal layer is provided with the first antistatic backing, the top of the first antistatic backing
Face is provided with flame-retardant layer, and the top of the flame-retardant layer is provided with the second antistatic backing, and the top surface of the second antistatic backing is provided with antibiotic layer, resists
The top surface of bacterium layer is provided with the 3rd antistatic backing, and the top surface of the 3rd antistatic backing is provided with thermal insulation layer, and the top surface of thermal insulation layer is provided with waterproof
Layer, the specification of the first antistatic backing, the second antistatic backing and the 3rd antistatic backing is identical, the first antistatic backing, the second antistatic
Layer and the 3rd antistatic backing include the elastomer at center, are set around the conductive wire group and cladding on elastomer surface
In being wound with multigroup conductive wire group on the protective layer of outer layer, elastomer, conductive wire group includes 4~15 conductive golds
Belong to silk, between multigroup conductive wire group around away from adjacent two conductive wire distances for same group of conductive wire group
5~15 times, thermal insulation layer is formed using cotton material braiding.
2. a kind of antistatic fabric according to claim 1, it is characterised in that the waterproof layer surface scribbles one layer of waterproof
Coating, the water-repellent paint use Teflon high-performance special coating, Teflon high-performance special coating be using polytetrafluoroethylene (PTFE) as
The fluoro coatings of matrix resin.
3. a kind of antistatic fabric according to claim 1, it is characterised in that the warp thread and weft yarn of the internal layer be respectively
Cotton thread and knitting wool, and cotton thread and knitting wool mutually to rise and fall, staggeredly in a manner of weave and form.
4. a kind of antistatic fabric according to claim 1, it is characterised in that the antibiotic layer uses silver fiber polyester thread
Alternately sink-float braiding forms, and silver fiber polyester thread includes the surface of polyester thread main body and silver ion shell, wherein polyester thread main body
Silver ion shell is enclosed with, silver ion shell is made up of argent.
A kind of 5. processing method of antistatic fabric, it is characterised in that comprise the following steps,
S1, flame-retardant layer have each raw material of following parts by weight:55~80 parts of flame-retardant acrylic fibre, 15~40 parts of combed cotton, fire-retardant nylon 3
~7 parts, 3~7 parts of aramid fiber, 1~3 part of anti-flaming viscose, 5~10 parts of polyphenylene sulfide fibre, 10~15 parts of fire retardant ATP;
S2, the melting of flame-retardant acrylic fibre, combed cotton, fire-retardant nylon, aramid fiber, anti-flaming viscose and polyphenylene sulfide fibre is put into agitator
It is sufficiently stirred, rotating speed is 5000~6000 turns/min, and mixing time is 2~3h, then fire retardant ATP is added, and adjusts rotating speed
6000~7000 turns/min, mixing time is 1~1.5h, adds surfactant and mixes, is extruded from spinneret, is formed fine
Dimension, by fibrage into yarn A;
S3, the yarn A in S2 is woven into flame-retardant layer;
S4, the first antistatic backing, the second antistatic backing, the 3rd antistatic backing, antibiotic layer, flame-retardant layer, thermal insulation layer and internal layer pass through
Needlework are stitched together, and the surface spraying of thermal insulation layer has one layer of waterproof layer, obtains this product.
6. the processing method of a kind of antistatic fabric according to claim 5, it is characterised in that the spinneret orifice of spinneret is straight
Footpath is 0.10-0.20mm.
A kind of 7. processing method of antistatic fabric according to claim 5, it is characterised in that the fabric warp of flame-retardant layer
Density is 70-90 roots/cm, and weft density is 60-100 roots/cm.