CN107383859A - 一种用于移液管架的抗菌防霉尼龙材料 - Google Patents

一种用于移液管架的抗菌防霉尼龙材料 Download PDF

Info

Publication number
CN107383859A
CN107383859A CN201710643964.1A CN201710643964A CN107383859A CN 107383859 A CN107383859 A CN 107383859A CN 201710643964 A CN201710643964 A CN 201710643964A CN 107383859 A CN107383859 A CN 107383859A
Authority
CN
China
Prior art keywords
parts
antibacterial
mouldproof
nylon material
pipet stand
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710643964.1A
Other languages
English (en)
Inventor
陆裕聪
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Suzhou Kun Yang Machinery Technology Co Ltd
Original Assignee
Suzhou Kun Yang Machinery Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Suzhou Kun Yang Machinery Technology Co Ltd filed Critical Suzhou Kun Yang Machinery Technology Co Ltd
Priority to CN201710643964.1A priority Critical patent/CN107383859A/zh
Publication of CN107383859A publication Critical patent/CN107383859A/zh
Pending legal-status Critical Current

Abstract

本发明提供一种用于移液管架的抗菌防霉尼龙材料，其特征在于，包括如下重量份数的组分：尼龙：30~45份；抗菌银离子母粒：10~22份；玻璃纤维：3~8份；钛酸四丁酯：5~10份；邻苯二甲酸二丁酯：2~5份；无机填料：2~7份；增韧剂：1~5份；热稳定剂：2~5份；抗氧化剂：0.5~3份。本发明所述的一种用于移液管架的抗菌防霉尼龙材料，强度高、韧性好、抗冲击性强、不易老化，能有效避免空气细菌的滋生和霉变，抗菌性能好，使用方便可靠，为实验的准确性提供保障。

Description

一种用于移液管架的抗菌防霉尼龙材料
技术领域
本发明涉及一种用于移液管架的抗菌防霉尼龙材料。
背景技术
在日常的实验室或工业生产中，经常需要在化学反应、生物反应等过程使用移液管。移液管架是用于放置移液管的一种实验器材。由于长期暴露于空气中，移液管架容易滋生细菌，尤其是在潮湿的环境中特别是黄梅季节，发生霉变，使得在取用移液管过程中对移液管造成污染，从而影响实验结果，导致实验数据可信度降低，反应难以重复。
因此，需要一种抗菌防霉的移液管架。
发明内容
为解决上述存在的问题，本发明的目的在于提供一种用于移液管架的抗菌防霉尼龙材料。所述用于移液管架的抗菌防霉尼龙材料，强度高、韧性好、抗冲击性强、不易老化，能有效避免空气细菌的滋生和霉变，抗菌性能好，使用方便可靠，为实验的准确性提供保障。
为达到上述目的，本发明的技术方案是：
一种用于移液管架的抗菌防霉尼龙材料，包括如下重量份数的组分：尼龙：30~45份；抗菌银离子母粒：10~22份；玻璃纤维：3~8份；钛酸四丁酯：5~10份；邻苯二甲酸二丁酯：2~5份；无机填料：2~7份；增韧剂：1~5份；热稳定剂：2~5份；抗氧化剂：0.5~3份。
进一步地，包括如下重量份数的组分：尼龙：30~40份；抗菌银离子母粒：16~22份；玻璃纤维：5~8份；钛酸四丁酯：7~10份；邻苯二甲酸二丁酯：2~4份；无机填料：2~5份；增韧剂：3~5份；热稳定剂：2~4份；抗氧化剂：0.5~2份。
进一步地，包括如下重量份数的组分：尼龙：33份；抗菌银离子母粒：19份；玻璃纤维：7份；钛酸四丁酯：9份；邻苯二甲酸二丁酯：3份；无机填料：4份；增韧剂：4.5份；热稳定剂：2.5份；抗氧化剂：1份。
进一步地，所述无机填料为膨胀珍珠岩、膨胀蛭石、漂珠、粉煤灰、硅藻土中的任一种。
进一步地，所述增韧剂为聚乙烯醇。
进一步地，所述热稳定剂为亚磷酸三苯酯或聚烯二醇二月桂酸酯。
进一步地，所述抗氧化剂为二苯胺类或对苯二胺类或亚磷酸脂类抗氧化剂。
本发明的有益效果在于：
本发明所述的一种用于移液管架的抗菌防霉尼龙材料，强度高、韧性好、抗冲击性强、不易老化，能有效避免空气细菌的滋生和霉变，抗菌性能好，使用方便可靠，为实验的准确性提供保障。
具体实施方式
实施例1
一种用于移液管架的抗菌防霉尼龙材料，包括如下重量份数的组分：尼龙：30份；抗菌银离子母粒：10份；玻璃纤维：3份；钛酸四丁酯：6份；邻苯二甲酸二丁酯：3份；无机填料：3份；增韧剂：1份；热稳定剂：2份；抗氧化剂：1.5份。
实施例2
一种用于移液管架的抗菌防霉尼龙材料，包括如下重量份数的组分：尼龙：36份；抗菌银离子母粒：14份；玻璃纤维：5份；钛酸四丁酯：5份；邻苯二甲酸二丁酯：2份；无机填料：2份；增韧剂：4份；热稳定剂：3份；抗氧化剂：0.5份。
实施例3
一种用于移液管架的抗菌防霉尼龙材料，包括如下重量份数的组分：尼龙：33份；抗菌银离子母粒：19份；玻璃纤维：7份；钛酸四丁酯：9份；邻苯二甲酸二丁酯：3份；无机填料：4份；增韧剂：4.5份；热稳定剂：2.5份；抗氧化剂：1份。
实施例4
一种用于移液管架的抗菌防霉尼龙材料，包括如下重量份数的组分：尼龙：45份；抗菌银离子母粒：19份；玻璃纤维：8份；钛酸四丁酯：8份；邻苯二甲酸二丁酯：5份；无机填料：5份；增韧剂：5份；热稳定剂：5份；抗氧化剂：3份。
实施例5
一种用于移液管架的抗菌防霉尼龙材料，包括如下重量份数的组分：尼龙：41份；抗菌银离子母粒：22份；玻璃纤维：6份；钛酸四丁酯：10份；邻苯二甲酸二丁酯：5份；无机填料：7份；增韧剂：2份；热稳定剂：3份；抗氧化剂：2份。
本发明所述的一种用于移液管架的抗菌防霉尼龙材料，强度高、韧性好、抗冲击性强、不易老化，能有效避免空气细菌的滋生和霉变，抗菌性能好，使用方便可靠，为实验的准确性提供保障。
需要说明的是，以上实施例仅用以说明本发明的技术方案而非限制。尽管参照较佳实施例对本发明进行了详细说明，本领域的普通技术人员应当理解，可以对发明的技术方案进行修改或者等同替换，而不脱离本发明技术方案的范围，其均应涵盖在本发明的权利要求范围中。

Claims (7)

1.一种用于移液管架的抗菌防霉尼龙材料，其特征在于，包括如下重量份数的组分：尼龙：30~45份；抗菌银离子母粒：10~22份；玻璃纤维：3~8份；钛酸四丁酯：5~10份；邻苯二甲酸二丁酯：2~5份；无机填料：2~7份；增韧剂：1~5份；热稳定剂：2~5份；抗氧化剂：0.5~3份。
2.根据权利要求1所述的用于移液管架的抗菌防霉尼龙材料，其特征在于，包括如下重量份数的组分：尼龙：30~40份；抗菌银离子母粒：16~22份；玻璃纤维：5~8份；钛酸四丁酯：7~10份；邻苯二甲酸二丁酯：2~4份；无机填料：2~5份；增韧剂：3~5份；热稳定剂：2~4份；抗氧化剂：0.5~2份。
3.根据权利要求1所述的用于移液管架的抗菌防霉尼龙材料，其特征在于，包括如下重量份数的组分：尼龙：33份；抗菌银离子母粒：19份；玻璃纤维：7份；钛酸四丁酯：9份；邻苯二甲酸二丁酯：3份；无机填料：4份；增韧剂：4.5份；热稳定剂：2.5份；抗氧化剂：1份。
4.根据权利要求1所述的用于移液管架的抗菌防霉尼龙材料，其特征在于，所述无机填料为膨胀珍珠岩、膨胀蛭石、漂珠、粉煤灰、硅藻土中的任一种。
5.根据权利要求1所述的用于移液管架的抗菌防霉尼龙材料，其特征在于，所述增韧剂为聚乙烯醇。
6.根据权利要求1所述的用于移液管架的抗菌防霉尼龙材料，其特征在于，所述热稳定剂为亚磷酸三苯酯或聚烯二醇二月桂酸酯。
7.根据权利要求1所述的用于移液管架的抗菌防霉尼龙材料，其特征在于，所述抗氧化剂为二苯胺类或对苯二胺类或亚磷酸脂类抗氧化剂。
CN201710643964.1A 2017-07-31 2017-07-31 一种用于移液管架的抗菌防霉尼龙材料 Pending CN107383859A (zh)