CN107351499A - Medical three-layer co-extruded polypropylene film and preparation method thereof - Google Patents
Medical three-layer co-extruded polypropylene film and preparation method thereof Download PDFInfo
- Publication number
- CN107351499A CN107351499A CN201710583630.XA CN201710583630A CN107351499A CN 107351499 A CN107351499 A CN 107351499A CN 201710583630 A CN201710583630 A CN 201710583630A CN 107351499 A CN107351499 A CN 107351499A
- Authority
- CN
- China
- Prior art keywords
- parts
- polypropylene
- temperature
- layer
- medical
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of medical three-layer co-extruded polypropylene film, including internal layer, middle level and outer layer, outer layer to include 40 55 parts of polypropylene T3OS;Middle level includes 20 30 parts of polypropylene T3OS;Internal layer includes:15 20 parts of polypropylene, 13 parts of heat-sealing type anti-adhesion master batch, 0,723 10 15 parts of polypropylene, 6 10 parts of metallocene PEF, 7,042 25 parts of low density polyethylene (LDPE), 48 52 parts of polypropylene 800e.The invention also discloses the preparation method of above-mentioned medical three-layer co-extruded polypropylene film.The film, when doing pressuresteam sterilization experiment, does not occur adhesion phenomenon in 60 minutes, 135 degree by the rational design of formula;Production heat-sealing bag, valve bag, volume bag and during three-dimensional winding bag, when peeling off not occurring layering tears phenomenon;Meanwhile other each side physical properties of the film are all substantially improved.
Description
Technical field
The present invention relates to processing film field, and in particular to medical three-layer co-extruded poly- the third of a kind of medical sterilization packaging product
Alkene film and preparation method thereof.
Background technology
With the development of China's medical industry, medical film requires more and more higher.At present, the medical treatment of domestic market production is gone out
Bacterium bag fills CPP and is carrying out pressuresteam sterilization(135 degree), after 30 minutes, there is adhesion in medical sterilization packaging CPP.Therefore, exist
Heat-sealing bag is made, valve bag, when rolling up bag, is easily layered when peeling off, tears phenomenon.
The content of the invention
It is an object of the invention to provide a kind of medical three-layer co-extruded polypropylene film, the film is doing pressuresteam sterilization
During experiment, do not occur adhesion phenomenon within 60 minutes, 135 degree;When production heat-sealing bag, valve bag, volume bag and three-dimensional winding bag, peeling off
When do not occur layering and tear phenomenon;Meanwhile other each side physical properties of the film are all substantially improved.
A kind of medical three-layer co-extruded polypropylene film of the present invention, including internal layer, middle level and outer layer, wherein:
Outer layer is made up according to parts by weight of following raw materials according:Polypropylene T3OS 40-55 parts;
Middle level is made up according to parts by weight of following raw materials according:Polypropylene T3OS 20-30 parts;
Internal layer is made up according to parts by weight of following raw materials according:Polypropylene 15-20 parts, heat-sealing type anti-adhesion master batch 1-3 parts, polypropylene
0723 10-15 parts, metallocene PEF 6-10 parts, the 2-5 parts of low density polyethylene (LDPE) 7042, polypropylene 800e 48-52 parts.
It is another object of the present invention to provide the preparation method of above-mentioned medical three-layer co-extruded polypropylene film, including such as
Lower step:The raw material of said ratio is taken, carries out batch mixing, melting extrusion, slab, longitudinal stretching, cross directional stretch, traction trimming, receipts
Volume, cutting, finished product, extrusion temperature is 190-260 DEG C in described melting extrusion, and die head temperature is 230-55 DEG C;Described casting
Chilling roller and tank temperature are 25-50 DEG C during piece;Longitudinal preheating temperature is 116-145 in described longitudinal stretching process
DEG C, longitudinal drawing temperature is 120-135 DEG C, and longitudinal setting temperature is 128-145 DEG C, and longitudinal stretching ratio is 4-6 times;Described horizontal stroke
Into drawing process, horizontal preheating temperature is 160-175 DEG C, and transverse drawing temperature is 150-168 DEG C, and horizontal setting temperature is
160-170 DEG C, cross directional stretch ratio is 7-10 times.
The beneficial effects of the invention are as follows:
1st, by adding heat-sealing type anti-adhesion master batch, the starting heat-sealing temperature of heat-sealing material is reduced;
2nd, Low Temperature Thermal sealer of the invention is heat sealable in 85 degree of -95 degree;
Heating-up temperature reduces when the 2nd, sealing, and is advantageous to save;
3rd, because being sealed under low-temperature condition, Low Temperature Thermal sealer will not improve Low Temperature Thermal sealer product quality because of heat distortion.
Embodiment
Medical three-layer co-extruded polypropylene film of the present invention and preparation method thereof is done into one with reference to specific embodiment
Walk explanation.
Embodiment 1:
Outer layer:40 parts of polypropylene T3OS;
Middle level:20 parts of polypropylene T3OS;
Internal layer:15 parts of polypropylene, 1 part of heat-sealing type anti-adhesion master batch, 0,723 1 parts of polypropylene, 6 parts of metallocene PEF, low-density
The 2- parts of polyethylene 7042,48 parts of polypropylene 800e.
Take above-mentioned raw materials by batch mixing, melting extrusion, slab, longitudinal stretching, cross directional stretch, traction trimming, winding, then
Finished product is cut, extrusion temperature is 190 DEG C in extrusion, and die head temperature is 248 DEG C, and chilling roller and tank temperature are during slab
32℃;Longitudinal preheating temperature is 116 DEG C, and longitudinal drawing temperature is 126 DEG C, and longitudinal setting temperature is 140 DEG C, and longitudinal stretching ratio is
4.9 again;Horizontal preheating temperature is 166 DEG C during the cross directional stretch, and transverse drawing temperature is 152 DEG C, horizontal setting temperature
For 165 DEG C, cross directional stretch ratio is 9 times.
Embodiment 2:
Outer layer:50 parts of polypropylene T3OS;
Middle level:25 parts of polypropylene T3OS;
Internal layer:18 parts of polypropylene, 2 parts of heat-sealing type anti-adhesion master batch, 0,723 12 parts of polypropylene, 8 parts of metallocene PEF, low-density
7,042 3 parts of polyethylene, 50 parts of polypropylene 800e.
Take above-mentioned raw materials by batch mixing, melting extrusion, slab, longitudinal stretching, cross directional stretch, traction trimming, winding, then
Finished product is cut, extrusion temperature is 220 DEG C in extrusion, and die head temperature is 248 DEG C, and chilling roller and tank temperature are during slab
32℃;Longitudinal preheating temperature is 120 DEG C, and longitudinal drawing temperature is 130 DEG C, and longitudinal setting temperature is 140 DEG C, and longitudinal stretching ratio is
4.9 again;Horizontal preheating temperature is 170 DEG C during the cross directional stretch, and transverse drawing temperature is 154 DEG C, horizontal setting temperature
For 165 DEG C, cross directional stretch ratio is 9 times.
Embodiment 3:
Outer layer:55 parts of polypropylene T3OS;
Middle level into:30 parts of polypropylene T3OS;
Internal layer:20 parts of polypropylene, 3 parts of heat-sealing type anti-adhesion master batch, 0,723 15 parts of polypropylene, 10 parts of metallocene PEF, low-density
7,042 5 parts of polyethylene, 52 parts of polypropylene 800e.
Take above-mentioned raw materials by batch mixing, melting extrusion, slab, longitudinal stretching, cross directional stretch, traction trimming, winding, then
Finished product is cut, extrusion temperature is 260 DEG C in extrusion, and die head temperature is 248 DEG C, and chilling roller and tank temperature are during slab
32℃;Longitudinal preheating temperature is 142 DEG C, and longitudinal drawing temperature is 135 DEG C, and longitudinal setting temperature is 140 DEG C, and longitudinal stretching ratio is
4.9 again;Horizontal preheating temperature is 174 DEG C during the cross directional stretch, and transverse drawing temperature is 155 DEG C, horizontal setting temperature
For 165 DEG C, cross directional stretch ratio is 9 times.
Medical three-layer co-extruded polypropylene film in the various embodiments described above has following physical property by experiment:
a:Peeling force:≥3.5N
b:Pull-off force:≥50N
c:Fracture rises long rate:≥45%
d:Right-angle tearing rate:≥4.5N
e:Anti- Charpy impact energy:≥1.2j
The above described is only a preferred embodiment of the present invention, any formal limitation not is made to the present invention;It is any ripe
Know those skilled in the art, without departing from the scope of the technical proposal of the invention, all using above-mentioned prompting method and
Technology contents make many possible changes and modifications to technical solution of the present invention, or are revised as the equivalence enforcement of equivalent variations
Example.Therefore, every content without departing from technical solution of the present invention, the technical spirit according to the present invention is to made for any of the above embodiments
Any simple modification, equivalent substitution, equivalence changes and modification, still fall within the range of technical solution of the present invention protects.
Claims (2)
1. a kind of medical three-layer co-extruded polypropylene film, including internal layer, middle level and outer layer, wherein:
Outer layer is made up according to parts by weight of following raw materials according:Polypropylene T3OS 40-55 parts;
Middle level is made up according to parts by weight of following raw materials according:Polypropylene T3OS 20-30 parts;
Internal layer is made up according to parts by weight of following raw materials according:Polypropylene 15-20 parts, heat-sealing type anti-adhesion master batch 1-3 parts, polypropylene
0723 10-15 parts, metallocene PEF 6-10 parts, the 2-5 parts of low density polyethylene (LDPE) 7042, polypropylene 800e 48-52 parts.
2. a kind of preparation method of medical three-layer co-extruded polypropylene film as claimed in claim 1, comprises the following steps:Take
Proportioning raw material is stated, carries out batch mixing, melting extrusion, slab, longitudinal stretching, cross directional stretch, traction trimming, winding, cutting, finished product,
It is characterized in that:Extrusion temperature is 190-260 DEG C in described melting extrusion, and die head temperature is 230-255 DEG C;Described slab
During chilling roller and tank temperature be 25-50 DEG C;Longitudinal preheating temperature is 116-145 in described longitudinal stretching process
DEG C, longitudinal drawing temperature is 120-135 DEG C, and longitudinal setting temperature is 128-145 DEG C, and longitudinal stretching ratio is 4-6 times;Described horizontal stroke
Into drawing process, horizontal preheating temperature is 160-175 DEG C, and transverse drawing temperature is 150-168 DEG C, and horizontal setting temperature is
160-170 DEG C, cross directional stretch ratio is 7-10 times.