CN107345031A - A kind of antistatic enhancing PP/ABS alloy materials and preparation method thereof - Google Patents
A kind of antistatic enhancing PP/ABS alloy materials and preparation method thereof Download PDFInfo
- Publication number
- CN107345031A CN107345031A CN201710662768.9A CN201710662768A CN107345031A CN 107345031 A CN107345031 A CN 107345031A CN 201710662768 A CN201710662768 A CN 201710662768A CN 107345031 A CN107345031 A CN 107345031A
- Authority
- CN
- China
- Prior art keywords
- parts
- abs
- alloy materials
- abs alloy
- antistatic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of antistatic enhancing PP/ABS alloy materials and preparation method thereof, including following raw material by weight：35 ~ 55 parts of PP, 15 ~ 30 parts of ABS, 2 ~ 5 parts of compatilizer, 0.3 ~ 0.5 part of coupling agent, 0.3 ~ 0.5 part of compound antioxidant, 3 ~ 5 parts of antistatic additive of compounding, 0.3 ~ 0.5 part of lubricant, 15 ~ 30 parts of alkali-free glass fiber, the antistatic enhancing PP/ABS alloy materials of the application have the advantages that heat resisting temperature is high, shrinkage factor is low, surface impedance is low, mechanical property is good, widely applicable.
Description
Technical field
The present invention relates to the technical field of plastic alloy material, refers in particular to a kind of antistatic enhancing PP/ABS alloy materials
Material.
Background technology
PP（Polypropylene）It is a kind of general-purpose plastics of excellent performance, there is good toughness, moderate strength, light specific gravity,
It is widely used in the fields such as packaging, electronic apparatus, machine-building, but PP materials there are big shrinkage factor, rigidity and heat resistance
The defects of being difficult to be applied to harsh use environment.Secondly, ABS（Acrylonitrile-butadiene-styrene copolymer）To be a kind of excellent
High polymer alloy, there is the advantages of high intensity, toughness is adjustable, lower shrinkage.The PP/ABS formed using being modified the advantages of PP and ABS
The advantages of alloy can have the two concurrently, product has preferably rigidity and pliability and compared with low-shrinkage, and effectively reduces product
Surface resistivity, but the PP and ABS Vicat softening points of itself are not high, it is difficult to apply in the occasion high to heat resistant requirements, and
Because the surface resistivity of material in itself causes greatly to be difficult to meet most of requirements.
The content of the invention
It is an object of the invention to overcome the deficiencies of the prior art and provide one kind is antistatic, heat resistance is high, Material shrinkage rate
Low enhancing PP/ABS alloy materials and preparation method thereof.
In order to realize above-mentioned purpose, the antistatic enhancing PP/ABS alloy materials of one kind provided by the present invention, including with
Under raw material by weight：35 ~ 55 parts of PP, 15 ~ 30 parts of ABS, 2 ~ 5 parts of compatilizer, 0.3 ~ 0.5 part of coupling agent, compounding
0.3 ~ 0.5 part of antioxidant, 3 ~ 5 parts of antistatic additive of compounding, 0.3 ~ 0.5 part of lubricant, 15 ~ 30 parts of alkali-free glass fiber.
Further, the PP includes HOPP and COPP, wherein, the HOPP is poly- with copolymerization
The proportioning of propylene is 5:1.
Further, the compatilizer includes POE-g-MAH.
Further, the coupling agent is silane coupler.
Further, the compound antioxidant included for four [β-(3,5- di-tert-butyl-hydroxy phenyl) propionic acid] seasons penta
Four alcohol esters and three [2.4- di-tert-butyl-phenyls] phosphite esters, wherein, four [β-(3,5- di-tert-butyl-hydroxy phenyl) propionic acid]
The compound proportion of pentaerythritol ester and three [2.4- di-tert-butyl-phenyls] phosphite esters is 1:1.
Further, the compounding antistatic additive includes N- (3- dodecyloxy -2- hydroxypropyls) monoethanolamines and N, N-
It is double（2- ethoxys）Alkylamine, wherein, N- (3- dodecyloxy -2- hydroxypropyls) monoethanolamines and N, N- are double（2- ethoxys）Alkane
The compound proportion of base amine is 2：1..
Further, the lubricant is dimethicone.
A kind of preparation method of antistatic enhancing PP/ABS alloy materials, includes following steps：
S1. processing is dried respectively to PP and ABS in advance, wherein, PP drying temperature is 80 ~ 100 DEG C and dries 3 ~ 5H；
ABS drying temperature is 85 ~ 105 DEG C and dries 3 ~ 5H；
S2. after the completion of processing to be dried, 35 ~ 55 parts of PP is weighed by weight and 15 ~ 30 parts of ABS is added to high-speed mixer
In, also, 2 ~ 5 parts of compatilizer, 0.3 ~ 0.5 part of coupling agent, 0.3 ~ 0.5 part of compound antioxidant, compounding are weighed by weight
0.3 ~ 0.5 part of 3 ~ 5 parts of antistatic additive and lubricant are added in high-speed mixer, through high-speed mixer progress mixed processing 10 ~
20min is to obtain compound；
S3. it is to be mixed uniformly after, add mixture into double screw extruder, meanwhile, weigh by weight glass fibre 15 ~
30 parts are added in double screw extruder, are extruded through double screw extruder melt blending, wherein, the screw rod of double screw extruder turns
Speed is 300 ~ 400r/min, and extrusion temperature is 190 ~ 210 DEG C；
S4. after double screw extruder extrusion, PP/ABS alloy materials are obtained after water cooled, air-dried, pelletizing.
The above-mentioned antistatic enhancing PP/ABS alloy materials of the present invention, solves PP and ABS using compatilizers such as POE-g-MAH
Compatible and toughness reinforcing, pass through PP-H and PP-R 5:1 proportioning system reaches toughening effect, and addition silane coupler is further lifted
PP/ABS and glass it is compatible, be aided with antioxidant and high-temperature silicon oil etc., one-step method blending extrusion is granulated in double screw extruder,
Then water cooling pelletizing, packed products are passed through.Therefore, antistatic enhancing PP/ABS alloy materials of the invention have heat resisting temperature
High, the advantages that shrinkage factor is low, surface impedance is low, mechanical property is good, widely applicable.
Embodiment
With reference to specific embodiment, the present invention is further illustrated.
A kind of antistatic enhancing PP/ABS alloy materials, including following raw material by weight：35 ~ 55 parts of PP, ABS
15 ~ 30 parts, 2 ~ 5 parts of compatilizer, 0.3 ~ 0.5 part of coupling agent, 0.3 ~ 0.5 part of compound antioxidant, compounding antistatic additive 3 ~ 5
Part, 0.3 ~ 0.5 part of lubricant, 15 ~ 30 parts of alkali-free glass fiber.
Specifically, PP includes HOPP（PP-H）And COPP（PP-R）, wherein, HOPP（PP-
H）With COPP（PP-R）Proportioning be 5:1, pass through HOPP（PP-H）With COPP（PP-R）With 5:1 enters
Row is matched to realize toughening effect.
Specifically, compatilizer includes POE-g-MAH, by compatilizer to solve compatible between PP and ABS and reach
To toughening effect.
Specifically, coupling agent is silane coupler, further deducted a percentage using coupling agent PP/ABS and alkali-free glass fiber it is compatible.
Specifically, compound antioxidant includes four [β-(3,5- di-tert-butyl-hydroxy phenyl) propionic acid] pentaerythrites
Ester and three [2.4- di-tert-butyl-phenyls] phosphite esters, wherein, four [β-(3,5- di-tert-butyl-hydroxy phenyl) propionic acid] seasons penta
The compound proportion of four alcohol esters and three [2.4- di-tert-butyl-phenyls] phosphite esters is 1:1.
Specifically, compounding antistatic additive includes N- (3- dodecyloxy -2- hydroxypropyls) monoethanolamines and N, N- are double（2-
Ethoxy）Alkylamine, wherein, N- (3- dodecyloxy -2- hydroxypropyls) monoethanolamines and N, N- are double（2- ethoxys）Alkylamine
Compound proportion be 2：1.
Specifically, compounding antistatic additive includes N- (3- dodecyloxy -2- hydroxypropyls) monoethanolamines and N, N- are double（2-
Ethoxy）Alkylamine, wherein, N- (3- dodecyloxy -2- hydroxypropyls) monoethanolamines and N, N- are double（2- ethoxys）Alkylamine
Compound proportion be 2：1；Secondly, the compounding antistatic additive being made up of mentioned component has good heat endurance, at 250 DEG C
It is stable, so that will not be decomposed discoloration in modeling process in extrusion molding and touching, and has and significantly reduce material
Surface resistivity.
Specifically, lubricant is dimethicone.
A kind of preparation method of antistatic enhancing PP/ABS alloy materials is described further in conjunction with specific embodiment.
A kind of preparation method of antistatic enhancing PP/ABS alloy materials, includes following steps：
S1. processing is dried respectively to PP and ABS in advance, wherein, PP drying temperature is 80 ~ 100 DEG C and dries 3 ~ 5H；
ABS drying temperature is 85 ~ 105 DEG C and dries 3 ~ 5H；
S2. after the completion of processing to be dried, weigh by weight and 15 ~ 30 parts of 35 ~ 55 parts of PP and ABS are added to high-speed mixer
In, also, 2 ~ 5 parts of compatilizer, 0.3 ~ 0.5 part of coupling agent, 0.3 ~ 0.5 part of compound antioxidant, compounding are weighed by weight
0.3 ~ 0.5 part of 3 ~ 5 parts of antistatic additive and lubricant are added in high-speed mixer, through high-speed mixer progress mixed processing 10 ~
20min is to obtain compound；
S3. it is to be mixed uniformly after, add mixture into double screw extruder, meanwhile, weigh by weight glass fibre 15 ~
30 parts are added in double screw extruder, are extruded through double screw extruder melt blending, wherein, the screw rod of double screw extruder turns
Speed is 300 ~ 400r/min, and extrusion temperature is 190 ~ 210 DEG C；
S4. after double screw extruder extrusion, PP/ABS alloy finished products are obtained after water cooled, air-dried, pelletizing processing.
In conjunction with specific embodiment to the present invention antistatic enhancing PP ABS alloy material illustrate.
Embodiment one：
A kind of antistatic enhancing PP/ABS alloy materials, including following raw material by weight：HOPP（PP-H）40
Part, COPP（PP-R）8 parts, 17.4 parts of ABS, 3.8 parts of POE-g-MAH, 0.3 part of silane coupler, compound antioxidant
0.3 part, compounding 5 parts of antistatic additive, 0.2 part of lubricant, 25 parts of glass fibre.
The properties of product of the present embodiment are tested, specific data are as follows：
| Test Method | Density/ g.cm-2 | Stretching is strong Degree/MPa | Extension at break Rate/% | Bending is strong Degree/MPa | Notch shock is strong Degree/Kj.m-2 | Dimension card softening Point/DEG C | Surface electricity Resistance rate | Shrink Rate/% |
| Implement Example one | 1.08 | 40.4 | 9.0 | 55.7 | 5.7 | 106 | 107 | 0.2 |
Embodiment two：
A kind of antistatic enhancing PP/ABS alloy materials, including following raw material by weight：HOPP（PP-H）
40.5 parts, COPP（PP-R）8.1 parts, 18.6 parts of ABS, 2 parts of POE-g-MAH, 0.3 part of silane coupler, compounding it is anti-
0.3 part of oxygen agent, 5 parts of antistatic additive of compounding, 0.2 part of lubricant, 25 parts of glass fibre.
The properties of product of the present embodiment are tested, specific data are as follows：
| Test Method | Density/ g.cm-2 | Stretching is strong Degree/MPa | Extension at break Rate/% | Bending is strong Degree/MPa | Notch shock is strong Degree/Kj.m-2 | Dimension card softening Point/DEG C | Surface electricity Resistance rate | Shrink Rate/% |
| Implement Example one | 1.10 | 42.1 | 9.7 | 57.0 | 5.3 | 109 | 107 | 0.2 |
Embodiment three：
A kind of antistatic enhancing PP/ABS alloy materials, including following raw material by weight：HOPP（PP-H）
45.6 parts, COPP（PP-R）9.6 parts, 20.7 parts of ABS, 4.3 parts of POE-g-MAH, 0.3 part of silane coupler, compounding
0.3 part of antioxidant, 4 parts of antistatic additive of compounding, 0.2 part of lubricant, 15 parts of glass fibre.
The properties of product of the present embodiment are tested, specific data are as follows：
| Test Method | Density/ g.cm-2 | Stretching is strong Degree/MPa | Extension at break Rate/% | Bending is strong Degree/MPa | Notch shock is strong Degree/Kj.m-2 | Dimension card softening Point/DEG C | Surface electricity Resistance rate | Shrink Rate/% |
| Implement Example one | 1.04 | 31.5 | 8.5 | 46.8 | 5.0 | 103 | 108 | 0.4 |
Example IV：
A kind of antistatic enhancing PP/ABS alloy materials, including following raw material by weight：HOPP（PP-H）
35.5 parts, COPP（PP-R）6.7 parts, 18.5 parts of ABS, 3.5 parts of POE-g-MAH, 0.3 part of silane coupler, compounding
0.3 part of antioxidant, 5 parts of antistatic additive of compounding, 0.2 part of lubricant, 30 parts of glass fibre.
The properties of product of the present embodiment are tested, specific data are as follows：
| Test Method | Density/ g.cm-2 | Stretching is strong Degree/MPa | Extension at break Rate/% | Bending is strong Degree/MPa | Notch shock is strong Degree/Kj.m-2 | Dimension card softening Point/DEG C | Surface electricity Resistance rate | Shrink Rate/% |
| Implement Example one | 1.14 | 46.3 | 11 | 70 | 6.6 | 116 | 106 | 0.1 |
Aforementioned four embodiment solves the compatible of PP and ABS by adding the good POE-g-MAH of compatibility, passes through PP-H and PP-R
5:1 proportioning system reaches toughening effect, and addition silane coupler further lifts the compatible of PP/ABS and glass, is squeezed in twin-screw
Go out one-step method blending extrusion in machine to be granulated, then pass through water cooling pelletizing, packed products.The PP/ABS alloys of the present invention have mechanics
Performance is good, and heat resisting temperature is high and surface resistivity is low, and the PP/ABS alloys of the present invention is applied widely.
Embodiment described above is only presently preferred embodiments of the present invention, not does any formal limit to the present invention
System.Any those skilled in the art, without departing from the scope of the technical proposal of the invention, utilize the skill of the disclosure above
Art content makes more possible variations and retouching to technical solution of the present invention, or modification is the equivalent embodiment of the present invention.
Therefore all contents without departing from technical solution of the present invention, the equivalent equivalence changes that the thinking according to the present invention is made, it all should be covered by
In protection scope of the present invention.
Claims (8)
- A kind of 1. antistatic enhancing PP/ABS alloy materials, it is characterised in that：Including following raw material by weight：PP 35~ 55 parts, 15 ~ 30 parts of ABS, 2 ~ 5 parts of compatilizer, 0.3 ~ 0.5 part of coupling agent, 0.3 ~ 0.5 part of compound antioxidant, compounding it is anti- 3 ~ 5 parts of electrostatic agent, 0.3 ~ 0.5 part of lubricant, 15 ~ 30 parts of alkali-free glass fiber.
- 2. the antistatic enhancing PP/ABS alloy materials of one kind according to claim 1, it is characterised in that：The PP includes HOPP and COPP, wherein, the HOPP is 5 with being copolymerized polyacrylic proportioning:1.
- 3. the antistatic enhancing PP/ABS alloy materials of one kind according to claim 1, it is characterised in that：The compatilizer bag POE-g-MAH is included.
- 4. the antistatic enhancing PP/ABS alloy materials of one kind according to claim 1, it is characterised in that：The coupling agent is Silane coupler.
- 5. the antistatic enhancing PP/ABS alloy materials of one kind according to claim 1, it is characterised in that：The compounding antioxygen Agent includes four [β-(3,5- di-tert-butyl-hydroxy phenyl) propionic acid] pentaerythritol esters and three [2.4- di-tert-butyl-phenyls] Phosphite ester, wherein, four [β-(3,5- di-tert-butyl-hydroxy phenyl) propionic acid] pentaerythritol esters and three [2.4- di-t-butyls Phenyl] phosphite ester compound proportion be 1:1.
- 6. the antistatic enhancing PP/ABS alloy materials of one kind according to claim 1, it is characterised in that：The compounding is anti-quiet Electric agent includes N- (3- dodecyloxy -2- hydroxypropyls) monoethanolamines and N, N- are double（2- ethoxys）Alkylamine, wherein, N- (3- dodecyloxy -2- hydroxypropyls) monoethanolamine and N, N- are double（2- ethoxys）The compound proportion of alkylamine is 2：1..
- 7. the antistatic enhancing PP/ABS alloy materials of one kind according to claim 1, it is characterised in that：The lubricant is Dimethicone.
- 8. a kind of a kind of preparation method of such as antistatic enhancing PP/ABS alloy materials of any one of claim 1-7, it is special Sign is：Include following steps：S1. processing is dried respectively to PP and ABS in advance, wherein, PP drying temperature is 80 ~ 100 DEG C and dries 3 ~ 5H； ABS drying temperature is 85 ~ 105 DEG C and dries 3 ~ 5H；S2. after the completion of processing to be dried, 35 ~ 55 parts of PP is weighed by weight and 15 ~ 30 parts of ABS is added to high-speed mixer In, also, 2 ~ 5 parts of compatilizer, 0.3 ~ 0.5 part of coupling agent, 0.3 ~ 0.5 part of compound antioxidant, compounding are weighed by weight 0.3 ~ 0.5 part of 3 ~ 5 parts of antistatic additive and lubricant are added in high-speed mixer, through high-speed mixer progress mixed processing 10 ~ 20min is to obtain compound；S3. it is to be mixed uniformly after, add mixture into double screw extruder, meanwhile, weigh by weight glass fibre 15 ~ 30 parts are added in double screw extruder, are extruded through double screw extruder melt blending, wherein, the screw rod of double screw extruder turns Speed is 300 ~ 400r/min, and extrusion temperature is 190 ~ 210 DEG C；S4. after double screw extruder extrusion, PP/ABS alloy materials are obtained after water cooled, air-dried, pelletizing.