CN107309746A - A kind of method for lifting the mould proof anti-aging characteristic of bamboo plaited article - Google Patents
A kind of method for lifting the mould proof anti-aging characteristic of bamboo plaited article Download PDFInfo
- Publication number
- CN107309746A CN107309746A CN201710754116.8A CN201710754116A CN107309746A CN 107309746 A CN107309746 A CN 107309746A CN 201710754116 A CN201710754116 A CN 201710754116A CN 107309746 A CN107309746 A CN 107309746A
- Authority
- CN
- China
- Prior art keywords
- processing
- plaited article
- bamboo
- bamboo plaited
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of method for lifting the mould proof anti-aging characteristic of bamboo plaited article, comprise the following steps:(1)Polishing,(2)Boiling processing,(3)Drying process,(4)Spray painting processing,(5)Cooling treatment.The present invention has carried out special improvement to the handling process of wicker products and handled, and effectively improves its resistance to mould ageing resistance, its service life and quality is extended, with good economic benefit.
Description
Technical field
The invention belongs to bamboo weaving processing and manufacturing technical field, and in particular to one kind lifting mould proof anti-aging characteristic of bamboo plaited article
Method.
Background technology
Bamboo, You Mingzhu.Scientific name Bambusoideae(Bambusaceae or Bamboo), it is a branch gramineous,
Subtropical zone is distributed in, there is short like grass, there is high such as big tree again.The rhizome generally crawled by underground grows in flakes.Also may be used
So that by procreation of blossoming and having seeds, its seed is referred to as bamboo rice.For perennial plant.There are some species of bamboo shoots edible.For
Tall and big, the rapid grass kind plant of growth, stem is wooden.It is distributed in the torrid zone, subtropical zone to warm temperate zone area, East Asia, Southeast Asia
Most concentrated with being distributed on the Indian Ocean and Pacific Islands, species is also most.Our people always likes bamboo, and China is also the world
It is upper to study, cultivate and utilize the earliest country of bamboo.Produced from bamboo in Chinese historical culture development and spirit culture are formed
Raw great function, bamboo and Chinese poems painting and calligraphy and the relation of long standing and well established of gardens construction, and bamboo and people's lives
It is closely bound up in be not difficult to find out, China deserve to be called and is described as " country of bamboo civilization ".
The product woven with bamboo material can be collectively referred to as bamboo plaited article, and it is widely used in people live, such as bamboo basket, bamboo
Comb, bamboo mat, bamboo cage, special formed handicraft etc., and bamboo is because of the characteristic of itself, easily by mould, insect in natural environment
Deng corroding, mouldy, phenomenon of damaging by worms is produced, spray painting processing, but existing spray painting processing side are generally carried out to it in order to improve this problem
The problems such as bamboo plaited article after method processing is easily cracking in use, the effect for causing spray painting to handle is had a greatly reduced quality, shadow
Service life and quality are rung.
The content of the invention
The purpose of the present invention is that there is provided a kind of side for lifting the mould proof anti-aging characteristic of bamboo plaited article the problem of being directed to existing
Method.
The present invention is achieved by the following technical solutions:
A kind of method for lifting the mould proof anti-aging characteristic of bamboo plaited article, comprises the following steps:
(1)Polishing:
Sanding and polishing processing is carried out to woven bamboo plaited article, after the completion of it is standby;
(2)Boiling is handled:
By step(1)Bamboo plaited article after processing is put into the pot for filling cooking liquor, heating keep the temperature of cooking liquor for 60 ~
65 DEG C, boiling is handled and taken out after 20 ~ 25min, is naturally cooled to standby after room temperature;Each composition and its correspondingly in described cooking liquor
Parts by weight are:6 ~ 10 parts of Chinese medicine extracts, 0.2 ~ 0.5 part of sodium hydroxide, 90 ~ 100 parts of water;
(3)Drying process:
By step(2)Bamboo plaited article after processing, which is put into microwave drier, is dried processing, treats that the water of bamboo plaited article contains
Amount takes out standby after being not more than 10%;
(4)Spray painting is handled:
By step(3)Bamboo plaited article after processing is put into change incubator and carries out spray painting processing, first keeps the temperature become in incubator
For 22 ~ 24 DEG C, once spray painting is carried out to bamboo plaited article and handled, after the enamelled coating on bamboo plaited article surface is half-dried, with 2 ~ 3 DEG C/min's
The temperature become in incubator is risen to 35 ~ 37 DEG C by programming rate, is then carried out secondary spray painting processing to bamboo plaited article, is treated bamboo plaited article
After the enamelled coating on surface is half-dried, the temperature become in incubator is risen to 46 ~ 48 DEG C with 1 ~ 2 DEG C/min programming rate, then to bamboo weaving
Product carries out three spray paintings processing, takes out standby after the enamelled coating on bamboo plaited article surface is absolutely dry;After previous spray painting enamelled coating is half-dried
Next spray painting is carried out again, can effectively be lifted compatible bond strength between the two, be easily caused if being coated after enamelled coating is absolutely dry
The problem of enamelled coating is peeled off, the problem of speed of during which control heating prevents enamelled coating and wicker products deformation and excessive stress, is easy to
The holding of the original mechanical characteristic of wicker products;
(5)Cooling treatment:
By step(4)Bamboo plaited article after processing, which is put into air, to be naturally cooled to after room temperature.
Further, step(1)Described in bamboo plaited article carry out sanding and polishing processing be is carried out with sand paper craft beat
Grinding and polishing light.
Further, step(2)Described in the preparation method of Chinese medicine extract be:By correspondence parts by weight by 7 ~ 10 parts of plates
Lan Gen, 5 ~ 8 parts of myrobalans, 6 ~ 9 parts of Radixs Astragali, 3 ~ 5 parts of folium isatidis, 2 ~ 4 parts of reed rhizome mixing are put into marmite, then add its total matter
The clear water of 4 ~ 6 times of amount, big fire boiling is boiled and filtered after 1 ~ 2h of processing, and gained filtrate is Chinese medicine extract.
Further, step(3)Described in drying process when control microwave drier power be 4 ~ 6kW.
Further, step(4)Described in spray painting processing used in paint vehicle be water paint.
Further, step(4)Described in change incubator in relative humidity control all the time as 35 ~ 40%.
It is once or many to wicker products progress at normal temperatures for the mode that wicker products surface is coated in existing method
Secondary spray painting processing, after the completion of dry, and in actual use when variation of ambient temperature is larger, wicker products is cold in heat expansion
It can produce deformation in the case of contracting, it is corresponding the problems such as can cause the cracking of enamelled coating or even peel off, and then mould, worm's ovum can be caused
Deng invasion, have impact on overall service life and quality, this present invention improved processing method of bamboo plaited article
Processing, carries out boiling processing to bamboo plaited article, bamboo plaited article is immersed in cooking liquor, bamboo weaving is improved using Chinese medicine extract
The characteristic of the resistance to mould insect prevention of product, the nutriment in bamboo plaited article is eliminated using sodium hydroxide composition, mould worm is reduced
The growth substance basis of ovum etc., further improves the characteristic of the resistance to mould insect prevention of bamboo plaited article, it has been carried out at spray painting afterwards
Reason, is specifically divided into three steps by spray painting, is first once painted at normal temperatures, temperature lifting then is carried out into secondary spray painting, most
Temperature lifting is carried out into three times again afterwards to paint, constantly environment temperature slowly lifted in this three painting process, to willow
Establishment product generate the effect of heat expansion deformation, and the temperature simulated in normal use becomes service condition, per wicker products of alternating temperature
Enamelled coating and textura epidermoidea occur certain deformation, produce small crack, then handled and fill by follow-up spray painting, pass through
The enamelled coating on wicker products surface is finer and close after multiple spray painting processing, enamelled coating for wicker products surface fiber depth of penetration more
Greatly, so as to improve the effect of spray painting.
The present invention has advantages below compared with prior art:
The present invention has carried out special improvement to the handling process of wicker products and handled, and effectively improves its resistance to mould anti-aging energy
Power, extends its service life and quality, with good economic benefit.
Embodiment
Embodiment 1
A kind of method for lifting the mould proof anti-aging characteristic of bamboo plaited article, comprises the following steps:
(1)Polishing:
Sanding and polishing processing is carried out to woven bamboo plaited article, after the completion of it is standby;
(2)Boiling is handled:
By step(1)Bamboo plaited article after processing is put into the pot for filling cooking liquor, and heating keeps the temperature of cooking liquor to be 60
DEG C, take out, naturally cool to standby after room temperature after boiling processing 20min;Each composition and its correspondence weight in described cooking liquor
Part it is:6 parts of Chinese medicine extracts, 0.2 part of sodium hydroxide, 90 parts of water;
(3)Drying process:
By step(2)Bamboo plaited article after processing, which is put into microwave drier, is dried processing, treats that the water of bamboo plaited article contains
Amount takes out standby after being not more than 10%;
(4)Spray painting is handled:
By step(3)Bamboo plaited article after processing is put into change incubator and carries out spray painting processing, first keeps the temperature become in incubator
For 22 DEG C, once spray painting is carried out to bamboo plaited article and handled, after the enamelled coating on bamboo plaited article surface is half-dried, with 2 DEG C/min heating
The temperature become in incubator is risen to 35 DEG C by speed, is then carried out secondary spray painting processing to bamboo plaited article, is treated bamboo plaited article surface
After enamelled coating is half-dried, the temperature become in incubator is risen to 46 DEG C with 1 DEG C/min programming rate, then bamboo plaited article carried out three times
Spray painting is handled, and takes out standby after the enamelled coating on bamboo plaited article surface is absolutely dry;
(5)Cooling treatment:
By step(4)Bamboo plaited article after processing, which is put into air, to be naturally cooled to after room temperature.
Further, step(1)Described in bamboo plaited article carry out sanding and polishing processing be is carried out with sand paper craft beat
Grinding and polishing light.
Further, step(2)Described in the preparation method of Chinese medicine extract be:By correspondence parts by weight by 7 parts of plate indigo plants
Root, 5 parts of myrobalans, 6 parts of Radixs Astragali, 3 parts of folium isatidis, 2 parts of reed rhizome mixing are put into marmite, then add the clear of 4 times of its gross mass
Water, big fire boiling is filtered after boiling processing 1h, and gained filtrate is Chinese medicine extract.
Further, step(3)Described in drying process when control microwave drier power be 4kW.
Further, step(4)Described in spray painting processing used in paint vehicle be water paint.
Further, step(4)Described in change incubator in relative humidity control all the time as 35 ~ 40%.
Embodiment 2
A kind of method for lifting the mould proof anti-aging characteristic of bamboo plaited article, comprises the following steps:
(1)Polishing:
Sanding and polishing processing is carried out to woven bamboo plaited article, after the completion of it is standby;
(2)Boiling is handled:
By step(1)Bamboo plaited article after processing is put into the pot for filling cooking liquor, and heating keeps the temperature of cooking liquor to be 63
DEG C, take out, naturally cool to standby after room temperature after boiling processing 22min;Each composition and its correspondence weight in described cooking liquor
Part it is:8 parts of Chinese medicine extracts, 0.4 part of sodium hydroxide, 95 parts of water;
(3)Drying process:
By step(2)Bamboo plaited article after processing, which is put into microwave drier, is dried processing, treats that the water of bamboo plaited article contains
Amount takes out standby after being not more than 9%;
(4)Spray painting is handled:
By step(3)Bamboo plaited article after processing is put into change incubator and carries out spray painting processing, first keeps the temperature become in incubator
For 23 DEG C, once spray painting is carried out to bamboo plaited article and handled, after the enamelled coating on bamboo plaited article surface is half-dried, with 2.5 DEG C/min liter
The temperature become in incubator is risen to 36 DEG C by warm speed, is then carried out secondary spray painting processing to bamboo plaited article, is treated bamboo plaited article surface
Enamelled coating it is half-dried after, with 1.5 DEG C/min programming rate by become incubator in temperature rise to 47 DEG C, then to bamboo plaited article carry out
Three spray paintings are handled, and take out standby after the enamelled coating on bamboo plaited article surface is absolutely dry;
(5)Cooling treatment:
By step(4)Bamboo plaited article after processing, which is put into air, to be naturally cooled to after room temperature.
Further, step(1)Described in bamboo plaited article carry out sanding and polishing processing be is carried out with sand paper craft beat
Grinding and polishing light.
Further, step(2)Described in the preparation method of Chinese medicine extract be:By correspondence parts by weight by 9 parts of plate indigo plants
Root, 7 parts of myrobalans, 8 parts of Radixs Astragali, 4 parts of folium isatidis, 3 parts of reed rhizome mixing are put into marmite, then add the clear of 5 times of its gross mass
Water, big fire boiling is filtered after boiling processing 1.5h, and gained filtrate is Chinese medicine extract.
Further, step(3)Described in drying process when control microwave drier power be 5kW.
Further, step(4)Described in spray painting processing used in paint vehicle be water paint.
Further, step(4)Described in change incubator in relative humidity control all the time as 35 ~ 40%.
Embodiment 3
A kind of method for lifting the mould proof anti-aging characteristic of bamboo plaited article, comprises the following steps:
(1)Polishing:
Sanding and polishing processing is carried out to woven bamboo plaited article, after the completion of it is standby;
(2)Boiling is handled:
By step(1)Bamboo plaited article after processing is put into the pot for filling cooking liquor, and heating keeps the temperature of cooking liquor to be 65
DEG C, take out, naturally cool to standby after room temperature after boiling processing 25min;Each composition and its correspondence weight in described cooking liquor
Part it is:10 parts of Chinese medicine extracts, 0.5 part of sodium hydroxide, 100 parts of water;
(3)Drying process:
By step(2)Bamboo plaited article after processing, which is put into microwave drier, is dried processing, treats that the water of bamboo plaited article contains
Amount takes out standby after being not more than 8%;
(4)Spray painting is handled:
By step(3)Bamboo plaited article after processing is put into change incubator and carries out spray painting processing, first keeps the temperature become in incubator
For 24 DEG C, once spray painting is carried out to bamboo plaited article and handled, after the enamelled coating on bamboo plaited article surface is half-dried, with 3 DEG C/min heating
The temperature become in incubator is risen to 37 DEG C by speed, is then carried out secondary spray painting processing to bamboo plaited article, is treated bamboo plaited article surface
After enamelled coating is half-dried, the temperature become in incubator is risen to 48 DEG C with 2 DEG C/min programming rate, then bamboo plaited article carried out three times
Spray painting is handled, and takes out standby after the enamelled coating on bamboo plaited article surface is absolutely dry;
(5)Cooling treatment:
By step(4)Bamboo plaited article after processing, which is put into air, to be naturally cooled to after room temperature.
Further, step(1)Described in bamboo plaited article carry out sanding and polishing processing be is carried out with sand paper craft beat
Grinding and polishing light.
Further, step(2)Described in the preparation method of Chinese medicine extract be:By correspondence parts by weight by 10 parts of plate indigo plants
Root, 8 parts of myrobalans, 9 parts of Radixs Astragali, 5 parts of folium isatidis, 4 parts of reed rhizome mixing are put into marmite, then add the clear of 6 times of its gross mass
Water, big fire boiling is filtered after boiling processing 2h, and gained filtrate is Chinese medicine extract.
Further, step(3)Described in drying process when control microwave drier power be 6kW.
Further, step(4)Described in spray painting processing used in paint vehicle be water paint.
Further, step(4)Described in change incubator in relative humidity control all the time as 35 ~ 40%.
Comparative example 1
This comparative example 1 compared with Example 2, saves step(4)Intermittent warming operation in spray painting processing, remains change
Temperature in incubator is normal temperature, carries out the spray painting processing of next time, method and step in addition after every inferior previous enamelled coating is absolutely dry again
All same.
Comparative example 2
This comparative example 2 compared with Example 2, saves step(4)Secondary spray painting and three spray paintings processing in spray painting processing,
Method and step all same in addition.
In order to contrast effect of the present invention, implemented respectively with above-described embodiment 2, contrast from the bamboo plaited article with a collection of braiding
Method described in example 1, comparative example 2 is handled, after the completion of to after processing finished product bamboo plaited article carry out performance test, tool
Body correction data is as shown in table 1 below:
Table 1
Note:After average killed value described in upper table 1 is the bamboo plaited article placement 1 year/5 years after each group is handled, then by its
It is put into the culture dish for filling stain fungus spore and mycelia liquid(Strain therein is aspergillus fumigatus and Trichoderma harzianum), two glass of underlay
Glass rod, is cultivated 28 days in 28 DEG C of temperature, the incubator of humidity 80%, and the killed value of evaluation, the evaluation criteria of the killed value is shown in
Shown in table 2 below.
Table 2
Processing method of the present invention can effectively lift the resistance to mould characteristic of wicker products it can be seen from upper table 1, hence it is evident that improve spray
The treatment effect of paint etc., improves it and uses quality, with good promotional value.
Claims (6)
1. a kind of method for lifting the mould proof anti-aging characteristic of bamboo plaited article, it is characterised in that comprise the following steps:
(1)Polishing:
Sanding and polishing processing is carried out to woven bamboo plaited article, after the completion of it is standby;
(2)Boiling is handled:
By step(1)Bamboo plaited article after processing is put into the pot for filling cooking liquor, heating keep the temperature of cooking liquor for 60 ~
65 DEG C, boiling is handled and taken out after 20 ~ 25min, is naturally cooled to standby after room temperature;Each composition and its correspondingly in described cooking liquor
Parts by weight are:6 ~ 10 parts of Chinese medicine extracts, 0.2 ~ 0.5 part of sodium hydroxide, 90 ~ 100 parts of water;
(3)Drying process:
By step(2)Bamboo plaited article after processing, which is put into microwave drier, is dried processing, treats that the water of bamboo plaited article contains
Amount takes out standby after being not more than 10%;
(4)Spray painting is handled:
By step(3)Bamboo plaited article after processing is put into change incubator and carries out spray painting processing, first keeps the temperature become in incubator
For 22 ~ 24 DEG C, once spray painting is carried out to bamboo plaited article and handled, after the enamelled coating on bamboo plaited article surface is half-dried, with 2 ~ 3 DEG C/min's
The temperature become in incubator is risen to 35 ~ 37 DEG C by programming rate, is then carried out secondary spray painting processing to bamboo plaited article, is treated bamboo plaited article
After the enamelled coating on surface is half-dried, the temperature become in incubator is risen to 46 ~ 48 DEG C with 1 ~ 2 DEG C/min programming rate, then to bamboo weaving
Product carries out three spray paintings processing, takes out standby after the enamelled coating on bamboo plaited article surface is absolutely dry;
(5)Cooling treatment:
By step(4)Bamboo plaited article after processing, which is put into air, to be naturally cooled to after room temperature.
2. a kind of method for lifting the mould proof anti-aging characteristic of bamboo plaited article according to claim 1, it is characterised in that step
(1)Described in bamboo plaited article carry out sanding and polishing processing be to carry out manual grinding polishing with sand paper.
3. a kind of method for lifting the mould proof anti-aging characteristic of bamboo plaited article according to claim 1, it is characterised in that step
(2)Described in the preparation method of Chinese medicine extract be:By correspondence parts by weight by 7 ~ 10 parts of Radix Isatidis, 5 ~ 8 parts of myrobalans, 6 ~ 9 parts
The Radix Astragali, 3 ~ 5 parts of folium isatidis, 2 ~ 4 parts of reed rhizome mixing are put into marmite, then add the clear water of 4 ~ 6 times of its gross mass, big fire boiling
Boil and filtered after 1 ~ 2h of processing, gained filtrate is Chinese medicine extract.
4. a kind of method for lifting the mould proof anti-aging characteristic of bamboo plaited article according to claim 1, it is characterised in that step
(3)Described in drying process when control microwave drier power be 4 ~ 6kW.
5. a kind of method for lifting the mould proof anti-aging characteristic of bamboo plaited article according to claim 1, it is characterised in that step
(4)Described in spray painting processing used in paint vehicle be water paint.
6. a kind of method for lifting the mould proof anti-aging characteristic of bamboo plaited article according to claim 1, it is characterised in that step
(4)Described in change incubator in relative humidity control all the time as 35 ~ 40%.