CN107236342A - Glue without cull and discoloration and preparation method thereof - Google Patents
Glue without cull and discoloration and preparation method thereof Download PDFInfo
- Publication number
- CN107236342A CN107236342A CN201710447531.9A CN201710447531A CN107236342A CN 107236342 A CN107236342 A CN 107236342A CN 201710447531 A CN201710447531 A CN 201710447531A CN 107236342 A CN107236342 A CN 107236342A
- Authority
- CN
- China
- Prior art keywords
- mass parts
- nitrous
- acrylic acid
- glue
- cull
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of glue without cull and discoloration, it is made up of the following raw material：The mass parts of nitrous acrylic acid 95 105；The mass parts of levelling agent 67；The mass parts of UV curing agent 24.The present invention uses nitrous acrylic acid, and the glue cohesive force being made is high, after label is peeled off from clothing cloth, it is not easy to leave cull, and temperature tolerance is strong, and cloth is not allowed to be also easy to produce discoloration.
Description
Technical field
The invention belongs to label glue technical field, more particularly to it is a kind of without cull and the glue of discoloration and its preparation side
Method.
Background technology
Label for clothing is generally adhered on clothes (such as size patch) by glue.
At present, the conventional acrylic pressure sensitive glue cohesive force of label for clothing is not enough, after label stripping easily on clothes
Cull is left, and temperature tolerance is not strong, and discoloration is easily produced on clothes at high temperature.
The content of the invention
Based on this, for above-mentioned technical problem, there is provided a kind of glue without cull and discoloration and preparation method thereof.
In order to solve the above technical problems, the present invention is adopted the following technical scheme that：
A kind of glue without cull and discoloration, is made up of the following raw material：
Nitrous acrylic acid 95-105 mass parts；
Levelling agent 6-7 mass parts；
UV curing agent 2-4 mass parts.
The nitrous acrylic acid is 100 mass parts, and the levelling agent is 6.5 mass parts, and the UV curing agent is 3 mass
Part.
This programme further relates to a kind of preparation method of the glue without cull and discoloration, including：
Levelling agent and UV curing agent are added in nitrous acrylic acid, three's proportioning is：
Nitrous acrylic acid 95-105 mass parts；
Levelling agent 6-7 mass parts；
UV curing agent 2-4 mass parts；
The nitrous acrylic acid for adding levelling agent and UV curing agent is stirred by mixer, mixing speed was at 30 seconds
It is interior that 3000 revolutions per seconds, mixing time 10-20 minutes are promoted to from 300 revolutions per seconds.
The nitrous acrylic acid is 100 mass parts, and the levelling agent is 6.5 mass parts, and the UV curing agent is 3 mass
Part.
The present invention uses nitrous acrylic acid, and the glue cohesive force being made is high, after label is peeled off from clothing cloth, it is not easy to
Cull is left, and temperature tolerance is strong, and cloth is not allowed to be also easy to produce discoloration.
Embodiment
A kind of glue without cull and discoloration, is made up of the following raw material：
Nitrous acrylic acid 95-105 mass parts；
Levelling agent 6-7 mass parts；
UV curing agent 2-4 mass parts.
Its preparation process is as follows：
Levelling agent and UV curing agent are added in nitrous acrylic acid by said ratio.
The nitrous acrylic acid for adding levelling agent and UV curing agent is stirred by mixer, mixing speed was at 30 seconds
It is interior that 3000 revolutions per seconds, mixing time 10-20 minutes are promoted to from 300 revolutions per seconds.
The present invention uses nitrous acrylic acid, and the glue cohesive force being made is high, after label is peeled off from clothing cloth, it is not easy to
Cull is left, and temperature tolerance is strong, and cloth is not allowed to be also easy to produce discoloration.
Preferably, nitrous acrylic acid is 100 mass parts, the levelling agent is 6.5 mass parts, and the UV curing agent is 3 matter
Part is measured, the glue cohesive force being made, temperature tolerance are more preferably.
Above-mentioned performance is verified by testing as follows：
In the environment of 60-80 DEG C of temperature, humidity 60-80%, pass through the present invention's on the cloth of a variety of conventional clothes
Glue is labelled (such as size patch), and is pressed on label and shells label from clothing cloth with 5kg weight after 7 days, 7 days
From experimental result is shown in Table 1：
Embodiment 1
The present embodiment is a kind of glue without cull and discoloration, is made up of the following raw material：
The mass parts of nitrous acrylic acid 105；
The mass parts of levelling agent 6；
The mass parts of UV curing agent 2.
Its preparation process is as follows：
Levelling agent and UV curing agent are added in nitrous acrylic acid by said ratio.
The nitrous acrylic acid for adding levelling agent and UV curing agent is stirred by mixer, mixing speed was at 30 seconds
It is interior that 3000 revolutions per seconds, mixing time 10 minutes are promoted to from 300 revolutions per seconds.
Embodiment 2
The present embodiment is a kind of glue without cull and discoloration, is made up of the following raw material：
The mass parts of nitrous acrylic acid 95；
The mass parts of levelling agent 7；
The mass parts of UV curing agent 4.
Its preparation process is as follows：
Levelling agent and UV curing agent are added in nitrous acrylic acid by said ratio.It is logical
Cross mixer to be stirred the nitrous acrylic acid for adding levelling agent and UV curing agent, mixing speed is in 30 seconds
3000 revolutions per seconds, mixing time 20 minutes are promoted to from 300 revolutions per seconds.
Embodiment 3
The present embodiment is a kind of glue without cull and discoloration, is made up of the following raw material：
The mass parts of nitrous acrylic acid 100；
The mass parts of levelling agent 6.5；
The mass parts of UV curing agent 3.
Its preparation process is as follows：
Levelling agent and UV curing agent are added in nitrous acrylic acid by said ratio.
The nitrous acrylic acid for adding levelling agent and UV curing agent is stirred by mixer, mixing speed was at 30 seconds
It is interior that 3000 revolutions per seconds, mixing time 15 minutes are promoted to from 300 revolutions per seconds.
But, those of ordinary skill in the art is it should be appreciated that the embodiment of the above is intended merely to explanation originally
Invention, and be not used as limitation of the invention, as long as in the spirit of the present invention, to embodiment described above
Change, modification will all fall in the range of claims of the present invention.
Claims (4)
1. a kind of glue without cull and discoloration, it is characterised in that be made up of the following raw material：
Nitrous acrylic acid 95-105 mass parts；
Levelling agent 6-7 mass parts；
UV curing agent 2-4 mass parts.
2. a kind of glue without cull and discoloration according to claim 1, it is characterised in that the nitrous acrylic acid is
100 mass parts, the levelling agent is 6.5 mass parts, and the UV curing agent is 3 mass parts.
3. a kind of preparation method of the glue without cull and discoloration, it is characterised in that including：
Levelling agent and UV curing agent are added in nitrous acrylic acid, three's proportioning is：
Nitrous acrylic acid 95-105 mass parts；
Levelling agent 6-7 mass parts；
UV curing agent 2-4 mass parts；
The nitrous acrylic acid for adding levelling agent and UV curing agent is stirred by mixer, mixing speed in 30 seconds from
300 revolutions per seconds are promoted to 3000 revolutions per seconds, mixing time 10-20 minutes.
4. a kind of preparation method of glue without cull and discoloration according to claim 3, it is characterised in that the nitrous
Acrylic acid is 100 mass parts, and the levelling agent is 6.5 mass parts, and the UV curing agent is 3 mass parts.