CN107225692A - A kind of mobile lens protect slice processing method - Google Patents
A kind of mobile lens protect slice processing method Download PDFInfo
- Publication number
- CN107225692A CN107225692A CN201710472857.7A CN201710472857A CN107225692A CN 107225692 A CN107225692 A CN 107225692A CN 201710472857 A CN201710472857 A CN 201710472857A CN 107225692 A CN107225692 A CN 107225692A
- Authority
- CN
- China
- Prior art keywords
- glass
- ink
- processing method
- mobile lens
- slice processing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Slice processing method is protected the invention discloses a kind of mobile lens, it is characterised in that comprised the following steps：(1) glass substrate is etched；(2) ink is protected to the glass substrate silk-screen after etching process, and protects the glass substrate after ink to dry silk-screen, base glass is obtained；(3) forming processes are processed to base glass, obtain formed glass；(4) the protection ink on formed glass is removed；(5) chemical intensification treatment is carried out to removing the formed glass after protection ink using potassium nitrate solution, strengthened glass；(6) strengthened glass is cleaned；(7) to the strengthened glass ink for screen printing after cleaning, and the strengthened glass after ink for screen printing is dried, obtains mobile lens screening glass.The mobile lens protection slice processing method of the present invention is high in machining efficiency, with low cost.
Description
Technical field
The present invention relates to glass processing field, a kind of mobile lens protection slice processing method is specifically referred to.
Background technology
With continuing to develop for science and technology, mobile phone be not only the means of communication of people, and has become people's life
It is used for keeping here the photography instrument of fine moment in work.This allows for our the requirement more and more highers of the photographic quality to mobile phone, in order to
The photographic quality of mobile phone can be improved, we are just provided with mobile lens can not only protect mobile lens, and can also reduce
The screening glass of exposure rate of the mobile lens in photography.With a large amount of productions of mobile phone, the demand of mobile lens screening glass is also anxious
Increase severely and add, and the production efficiency of mobile lens screening glass is relatively low at present, it is impossible to meet the demand of people.
The content of the invention
It is an object of the invention to overcome the relatively low defect of the production efficiency of current mobile lens screening glass, there is provided a kind of hand
Machine lens protection slice processing method.
The purpose of the present invention passes through following technical proposals reality：A kind of mobile lens protect slice processing method, including following
Step：
(1) glass substrate is etched；
(2) ink is protected to the glass substrate silk-screen after etching process, and protects the glass substrate after ink to enter silk-screen
Row drying, obtains base glass；
(3) forming processes are processed to base glass, obtain formed glass；
(4) the protection ink on formed glass is removed；
(5) chemical intensification treatment is carried out to removing the formed glass after protection ink using potassium nitrate solution, strengthened
Glass；
(6) strengthened glass is cleaned；
(7) to the strengthened glass ink for screen printing after cleaning, and the strengthened glass after ink for screen printing is dried, obtains in one's hands
Machine lens protection piece.
Further, the etch temperature in the step (1) is 20 DEG C~80 DEG C.
The concentration of potassium nitrate solution is 99.5% in the step (5), and the chemical intensification treatment time is 4h~8h, and chemistry is strong
It is 400 DEG C~450 DEG C to change treatment temperature.
Drying temperature in the step (2) and step (7) is 120 DEG C~180 DEG C, drying time be 20min~
40min。
Ink in the step (2) and step (7) is UV ink.
The present invention has advantages below and beneficial effect compared with prior art：The mobile lens screening glass processing of the present invention
Method is high in machining efficiency, with low cost.
Embodiment
The present invention is described in further detail with reference to embodiment, but embodiments of the present invention are not limited to
This.
Embodiment
The mobile lens protection slice processing method of the present invention, comprises the following steps：
(1) glass substrate is etched；Large stretch of pearl glass substrate is etched, made in glass base stage
Pattern required for being formed.The etching solution used during etching is made up of the composition of following weight/mass percentage composition meter：Water 18.4%,
Hydrofluoric acid ammonium 23.5%, oxalic acid 12.4%, ammonium sulfate 15.7%, glycerine 6.5%, barium sulfate 23.5%, etch temperature are 20 DEG C
~80 DEG C, etch temperature can be 20 DEG C or 80 DEG C or optimal 60 DEG C in the present embodiment.
(2) ink is protected to the glass substrate silk-screen after etching process, and protects the glass substrate after ink to enter silk-screen
Row drying, obtains base glass.Silk-screen protection ink can avoid glass substrate during following process on the glass substrate
It is damaged.To silk-screen protect ink after glass substrate dry when, drying temperature for 120 DEG C~180 DEG C, the present embodiment
The drying temperature of middle setting is 120 DEG C, 180 DEG C or 160 DEG C；Drying time is the drying in 20min~40min, the present embodiment
Set of time is 20min, 40min or 30min.The protection ink is UV ink.
(3) forming processes are processed to base glass, obtain formed glass；Large stretch of base glass is opened
Material, size, shape needed for forming it into, and shape type processing is carried out to the base glass after sawing sheet using forming machine, to remove
Burr, so as to obtain formed glass.Because glass substrate has been etched before forming processes, therefore on formed glass
The etched pattern needed, compared with monolithic formed glass is etched, greatly improves processing efficiency.
(4) the protection ink on formed glass is removed using the black agent of optical glass de-oiling.
(5) chemical intensification treatment is carried out to removing the formed glass after protection ink using potassium nitrate solution, strengthened
Glass.The concentration of the potassium nitrate solution is 99.5%, and the chemical intensification treatment time is 4h~8h, in the present embodiment, chemistry
The time of intensive treatment is 4h, 6h or 8h；Chemical intensification treatment temperature is 400 DEG C~450 DEG C, chemical enhanced place in the present embodiment
It is 400 DEG C, 420 DEG C or 450 DEG C to manage temperature setting.
(6) strengthened glass is cleaned using WIN-18 cleaning agents.
(7) to the strengthened glass ink for screen printing after cleaning, and the strengthened glass after ink for screen printing is dried, obtains in one's hands
Machine lens protection piece.Specifically, the drying temperature dried to the strengthened glass after ink for screen printing is 120 DEG C~180 DEG C, this
The drying temperature set in embodiment is 120 DEG C, 180 DEG C or 160 DEG C；Drying time is 20min~40min, in the present embodiment
Drying time be set to 20min, 40min or 30min.The protection ink is UV ink.
As described above, the present invention just can be realized well.
Claims (5)
1. a kind of mobile lens protect slice processing method, it is characterised in that comprise the following steps：
(1) glass substrate is etched；
(2) ink is protected to the glass substrate silk-screen after etching process, and protects the glass substrate after ink to dry silk-screen
It is dry, obtain base glass；
(3) forming processes are processed to base glass, obtain formed glass；
(4) the protection ink on formed glass is removed；
(5) chemical intensification treatment is carried out to removing the formed glass after protection ink using potassium nitrate solution, strengthened glass；
(6) strengthened glass is cleaned；
(7) to the strengthened glass ink for screen printing after cleaning, and the strengthened glass after ink for screen printing is dried, obtains Mobile phone mirror
Head protection piece.
2. a kind of mobile lens protection slice processing method according to claim 1, it is characterised in that in the step (1)
Etch temperature be 20 DEG C~80 DEG C.
3. a kind of mobile lens protection slice processing method according to claim 1, it is characterised in that in the step (5)
The concentration of potassium nitrate solution be 99.5%, the chemical intensification treatment time be 4h~8h, chemical intensification treatment temperature be 400 DEG C~
450℃。
4. a kind of mobile lens protection slice processing method according to claim 1, it is characterised in that the step (2) and
Drying temperature in step (7) is 120 DEG C~180 DEG C, and drying time is 20min~40min.
5. a kind of mobile lens protection slice processing method according to claim 1, it is characterised in that the step (2) and
Ink in step (7) is UV ink.