CN107162570A - It is a kind of to strengthen ceramic of total balance of the body and preparation method thereof - Google Patents

It is a kind of to strengthen ceramic of total balance of the body and preparation method thereof Download PDF

Info

Publication number
CN107162570A
CN107162570A CN201710549485.3A CN201710549485A CN107162570A CN 107162570 A CN107162570 A CN 107162570A CN 201710549485 A CN201710549485 A CN 201710549485A CN 107162570 A CN107162570 A CN 107162570A
Authority
CN
China
Prior art keywords
parts
sand
ceramic
powder
strengthen
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201710549485.3A
Other languages
Chinese (zh)
Inventor
程燕文
周永富
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Guangdong Kangshitai New Material Technology Co Ltd
Original Assignee
Guangdong Kangshitai New Material Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Guangdong Kangshitai New Material Technology Co Ltd filed Critical Guangdong Kangshitai New Material Technology Co Ltd
Priority to CN201710549485.3A priority Critical patent/CN107162570A/en
Publication of CN107162570A publication Critical patent/CN107162570A/en
Withdrawn legal-status Critical Current

Abstract

The present invention relates to a kind of ceramic that can strengthen total balance of the body and preparation method thereof, calculate by weight, ceramic component includes:30 38 parts of Dongxing sand, 33 45 parts of pure white sand, 10 15 parts of the bright sand of good fortune, 70 90 parts of quartz sand, 35 50 parts of nine eyestone shale, 25 40 parts of magnetic iron ore, 15 25 parts of white clay, 10 15 parts of kerosene shale ash, 24 38 parts of serpentine, 16 25 parts of olivine, 10 15 parts of waste mortar, 14 22 parts of tufa stone, 15 20 parts of sludge dry powder, 12 18 parts of bauxite, 10 14 parts of magnesium borate crystal whisker, 10 15 parts of red mud, 17 23 parts of slag micro powder;The ceramic of the present invention has intensity high, and water absorption rate is low, and the advantages of wearability is good, shock resistance is good can strengthen the function of total balance of the body, meet the market demand.

Description

It is a kind of to strengthen ceramic of total balance of the body and preparation method thereof
Technical field
The present invention relates to the technical field of ceramic, and in particular to a kind of ceramic that can strengthen total balance of the body and its Preparation method.
Background technology
Ceramic Tiles are tabular or bulk through technique productions such as shaping, sintering by clay and other inorganic non-metallic raw materials Ceramic, it is as important architectural decorative and fitting materialses, in the energy, medical treatment, national defence, space flight and aviation, electronics, petrochemical industry And there is wide application in domestic life field.In recent years, developing rapidly with building trade, people progressively attempt to change Become the single decoration functions of Ceramic Tiles, assign its more utility function.
The content of the invention
It is an object of the invention to for weak point of the prior art, proposition is a kind of to strengthen the ceramics of total balance of the body Product and preparation method thereof, the ceramic, which has, can strengthen the function of total balance of the body.
For up to this purpose, the present invention uses following technical scheme:
It is a kind of to strengthen the ceramic of total balance of the body, calculate by weight, ceramic component includes:Dongxing sand 30-38 Part, pure white sand 33-45 parts, bright sand 10-15 parts of good fortune, 70-90 parts of quartz sand, 35-50 parts of nine eyestone shale, magnetic iron ore 25-40 Part, 15-25 parts of white clay, 10-15 parts of kerosene shale ash, 24-38 parts of serpentine, 16-25 parts of olivine, 10-15 parts of waste mortar, solidifying ash 14-22 parts of rock, 15-20 parts of sludge dry powder, 12-18 parts of bauxite, 10-14 parts of magnesium borate crystal whisker, 10-15 parts of red mud, slag are micro- 17-23 parts of powder.
Further, calculate by weight, ceramic component includes:35 parts of Dongxing sand, 40 parts of pure white sand, good fortune are bright 13 parts of sand, 80 parts of quartz sand, 40 parts of nine eyestone shale, 30 parts of magnetic iron ore, 20 parts of white clay, 13 parts of kerosene shale ash, serpentine 30 It is part, 20 parts of olivine, 12 parts of waste mortar, 16 parts of tufa stone, 16 parts of sludge dry powder, 15 parts of bauxite, 12 parts of magnesium borate crystal whisker, red 13 parts of mud, 20 parts of slag micro powder.
A kind of method for preparing the above-mentioned ceramic that can strengthen total balance of the body, including step are as follows:
A, raw material preparation;Sand 30-38 parts of Dongxing, pure white sand 33-45 parts, bright sand 10-15 parts of good fortune, 70-90 parts, nine of quartz sand 35-50 parts of stone shale, 25-40 parts of magnetic iron ore, 15-25 parts of white clay, 10-15 parts of kerosene shale ash, 24-38 parts of serpentine, olive 16-25 parts of stone, 10-15 parts of waste mortar, 14-22 parts of tufa stone, 15-20 parts of sludge dry powder, 12-18 parts of bauxite, antifungin are brilliant 10-14 parts of palpus, 10-15 parts of red mud, 17-23 parts of progress mixing outfits of slag micro powder, obtain resulting mixture A1;B, ball milling;Institute State mixture A1 and water(By weight 2:1)Add and mixed grinding is carried out in ball mill, form slurry B1;C, mist projection granulating; It is dried in the spray drying tower for the slurry B1 injections, granulates, forms powder C1;D, punch forming;The powder Expect that C1 adds stamping machine and carries out cloth, punch forming, obtain ceramic tile blank D1;E, calcining;The ceramic tile blank D1 is put into kiln Calcined in stove, obtain Ceramic Tiles E1.
Beneficial effects of the present invention:1. the ceramic that the present invention is realized has strong positive magnetic field energy, it can reconcile Human magnetic field, enhancing human body vim and vigour circulation, increases body immunity, promotes the mediation of body and mind, human body is obtained the happy of exception, Make people energetic, mood is optimistic, vigorous, while Ceramic Tiles of the present invention have intensity high, water absorption rate is low, wearability is good, The advantages of shock resistance is good, can strengthen the function of total balance of the body, meet the market demand.
Embodiment
Technical scheme is further illustrated below by embodiment.
Embodiment 1:
A kind of method for preparing the described ceramic that can strengthen total balance of the body, including step are as follows:
A, raw material preparation;30 parts of Dongxing sand, 33 parts of pure white sand, 10 parts of the bright sand of good fortune, 70 parts of quartz sand, 35 parts of nine eyestone shale, 25 parts of magnetic iron ore, 15 parts of white clay, 10 parts of kerosene shale ash, 24 parts of serpentine, 16 parts of olivine, 10 parts of waste mortar, tufa stone 14 Part, 15 parts of sludge dry powder, 12 parts of bauxite, 10 parts of magnesium borate crystal whisker, 10 parts of red mud, 17 parts of progress mixing outfits of slag micro powder, Obtain resulting mixture A1;B, ball milling;The mixture A1 and water(By weight 2:1)Progress mixing in ball mill is added to grind Mill, forms slurry B1;C, mist projection granulating;Slurry B1 injections are dried to it in the spray drying tower, granulated, are formed Powder C1;D, punch forming;The powder C1 is added stamping machine and carries out cloth, punch forming, ceramic tile blank D1 is obtained;E, forge Burn;The ceramic tile blank D1 is put into kiln and calcined, Ceramic Tiles E1 is obtained.
Embodiment 2:A kind of method for preparing the described ceramic that can strengthen total balance of the body, including step are as follows:
A, raw material preparation;38 parts of Dongxing sand, 45 parts of pure white sand, 15 parts of the bright sand of good fortune, 90 parts of quartz sand, 50 parts of nine eyestone shale, 40 parts of magnetic iron ore, 25 parts of white clay, 15 parts of kerosene shale ash, 24-38 parts of serpentine, 5 parts of olivine, 15 parts of waste mortar, tufa stone 22 parts, 20 parts of sludge dry powder, 18 parts of bauxite, 14 parts of magnesium borate crystal whisker, 15 parts of red mud, 23 parts of slag micro powder carry out mixing and match somebody with somebody It is standby, obtain resulting mixture A1;B, ball milling;The mixture A1 and water(By weight 2:1)Add and mixed in ball mill Grinding, forms slurry B1;C, mist projection granulating;Slurry B1 injections are dried to it in the spray drying tower, granulated, shape Into powder C1;D, punch forming;The powder C1 is added stamping machine and carries out cloth, punch forming, ceramic tile blank D1 is obtained;E、 Calcining;The ceramic tile blank D1 is put into kiln and calcined, Ceramic Tiles E1 is obtained.
Embodiment 3:
A kind of method for preparing the described ceramic that can strengthen total balance of the body, including step are as follows:
A, raw material preparation;35 parts of Dongxing sand, 40 parts of pure white sand, 13 parts of the bright sand of good fortune, 80 parts of quartz sand, 40 parts of nine eyestone shale, 30 parts of magnetic iron ore, 20 parts of white clay, 13 parts of kerosene shale ash, 30 parts of serpentine, 20 parts of olivine, 12 parts of waste mortar, tufa stone 16 Part, 16 parts of sludge dry powder, 15 parts of bauxite, 12 parts of magnesium borate crystal whisker, 13 parts of red mud, 20 parts of progress mixing outfits of slag micro powder, Obtain resulting mixture A1;B, ball milling;The mixture A1 and water(By weight 2:1)Progress mixing in ball mill is added to grind Mill, forms slurry B1;C, mist projection granulating;Slurry B1 injections are dried to it in the spray drying tower, granulated, are formed Powder C1;D, punch forming;The powder C1 is added stamping machine and carries out cloth, punch forming, ceramic tile blank D1 is obtained;E, forge Burn;The ceramic tile blank D1 is put into kiln and calcined, Ceramic Tiles E1 is obtained.
The technical principle of the present invention is described above in association with specific embodiment.These descriptions are intended merely to explain the present invention's Principle, and limiting the scope of the invention can not be construed in any way.Based on explanation herein, the technology of this area Personnel, which would not require any inventive effort, can associate other embodiments of the present invention, and these modes are fallen within Within protection scope of the present invention.

Claims (3)

1. a kind of can strengthen the ceramic of total balance of the body, it is characterised in that:Calculate by weight, ceramic component bag Include:Sand 30-38 parts of Dongxing, pure white sand 33-45 parts, bright sand 10-15 parts of good fortune, 70-90 parts of quartz sand, 35-50 parts of nine eyestone shale, 25-40 parts of magnetic iron ore, 15-25 parts of white clay, 10-15 parts of kerosene shale ash, 24-38 parts of serpentine, 16-25 parts of olivine, antiquated sand 10-15 parts of slurry, 14-22 parts of tufa stone, 15-20 parts of sludge dry powder, 12-18 parts of bauxite, 10-14 parts of magnesium borate crystal whisker, red mud 10-15 parts, 17-23 parts of slag micro powder.
2. according to claim 1 can strengthen the ceramic of total balance of the body, it is characterised in that:Calculate by weight, Ceramic component includes:35 parts of Dongxing sand, 40 parts of pure white sand, 13 parts of the bright sand of good fortune, 80 parts of quartz sand, 40 parts of nine eyestone shale, 30 parts of magnetic iron ore, 20 parts of white clay, 13 parts of kerosene shale ash, 30 parts of serpentine, 20 parts of olivine, 12 parts of waste mortar, tufa stone 16 Part, 16 parts of sludge dry powder, 15 parts of bauxite, 12 parts of magnesium borate crystal whisker, 13 parts of red mud, 20 parts of slag micro powder.
3. a kind of method of the ceramic that can strengthen total balance of the body prepared described in claim 1-2, it is characterised in that:Including Step is as follows:A, raw material preparation;Sand 30-38 parts of Dongxing, pure white sand 33-45 parts, bright sand 10-15 parts of good fortune, quartz sand 70-90 Part, 35-50 parts of nine eyestone shale, 25-40 parts of magnetic iron ore, 15-25 parts of white clay, 10-15 parts of kerosene shale ash, serpentine 24-38 Part, 16-25 parts of olivine, 10-15 parts of waste mortar, 14-22 parts of tufa stone, 15-20 parts of sludge dry powder, 12-18 parts of bauxite, boron Sour 10-14 parts of magnesium whisker, 10-15 parts of red mud, 17-23 parts of progress mixing outfits of slag micro powder, obtain resulting mixture A1;B, ball Mill;The mixture A1 and water(By weight 2:1)Add and mixed grinding is carried out in ball mill, form slurry B1;C, spraying Granulation;Slurry B1 injections are dried to it in the spray drying tower, granulated, powder C1 is formed;D, punch forming; The powder C1 adds stamping machine and carries out cloth, punch forming, obtains ceramic tile blank D1;E, calcining;The ceramic tile blank D1 It is put into kiln and is calcined, obtains Ceramic Tiles E1.
CN201710549485.3A 2017-07-07 2017-07-07 It is a kind of to strengthen ceramic of total balance of the body and preparation method thereof Withdrawn CN107162570A (en)