CN107160520A - A kind of solid wood door and window is embossed preparation technology with timber - Google Patents
A kind of solid wood door and window is embossed preparation technology with timber Download PDFInfo
- Publication number
- CN107160520A CN107160520A CN201710528652.6A CN201710528652A CN107160520A CN 107160520 A CN107160520 A CN 107160520A CN 201710528652 A CN201710528652 A CN 201710528652A CN 107160520 A CN107160520 A CN 107160520A
- Authority
- CN
- China
- Prior art keywords
- timber
- base material
- window
- solid wood
- preparation technology
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Preparation technology is embossed with timber the invention discloses a kind of solid wood door and window, is comprised the following steps：The selection of timber, the processing of material, the polishing of base material, the processing of base material, the damp and hot sofening treatment of material, material modification processing, the dewater treatment of substrate modified, the sizing of substrate modified moulding press resin.The solid wood door and window can carry out control with timber embossing preparation technology from source, improve output quality, by being modified processing to timber, prepared using the lossless mould pressing method of wood element, assign its excellent dimensionally stable, crack resistence, high density, high case hardness and structural behaviour etc., and early stage selection timber and the details for handling the solid wood door and window for enabling to make are more preferable, quality is higher.
Description
Technical field
The invention belongs to door and window embossing technology field, and in particular to a kind of solid wood door and window is embossed preparation technology with timber.
Background technology
Door and window is the essential part in house, by door and window can with outside world exchange and conmmunication, while door and window
Sunlight is brought to us and warm, resists the wind and rain and noise in the external world.Solid wood door and window is with simple and unsophisticated, environmentally friendly, elegant and poised for spy
Point, it is deep to be liked by common people.The outward appearance of door and window also embodies a kind of taste of life, and present people is more and more to be liked in reality
Wood-door window is embossed, and the door and window so made is more beautiful, and sheet material is in Milling Process, the process of generation space pattern
In, the transverse fiber of timber can cause material chi by substantial amounts of cut-out, the easy moisture absorption of so exposed lumen and cell membrane
Very little unstable, product is yielding, and timber band mechanical property is poor in addition, and when external environment amplitude of variation is big, material is easily opened
Split.Meanwhile, exposed part wood transverse section large percentage outwardly, substantial amounts of larger-size pore, lumen can cause to apply
Paint, the excessive permeation of oil in decorations, coating effect are poor, influence attractive in appearance.And manual type or mechanical engraving processing mode, input
Cost is high, and work efficiency is poor, and the qualification rate of product is low, and existing timber embossing preparation technology can not carry out handle from source
Close, cause follow-up making to go wrong, so we need a new solid wood door and window with timber be embossed preparation technology come
Solve the above problems, meet the demand of people.
The content of the invention
Preparation technology is embossed with timber it is an object of the invention to provide a kind of solid wood door and window, to solve above-mentioned background technology
The problem of middle proposition.
To achieve the above object, the present invention provides following technical scheme：A kind of solid wood door and window is embossed preparation technology with timber,
Comprise the following steps：
（1）The selection of timber：Different timber influence particularly evident to embossing element quality, and we can select the measured timber of matter,
It can also be selected simultaneously according to color within doors；
（2）The processing of material：The Wood surface of selection is simply handled, then will be treated according to fixed size
Timber is sawed into base material；
（3）The polishing of base material：The surface of base material is polished smooth using polishing paper, the feelings for uneven and wooden thorn occur are not allowed
Condition；
（4）The processing of base material：The wood chip of the substrate surface after polishing is blown off using air gun, then its surface is wiped with wet cloth
Totally, a period of time is then placed；
（5）The damp and hot sofening treatment of material：Base material is placed in 60-90 DEG C of hot water 2 days, then entered in drying process device
Row drying process, controls the moisture content of base material below 20%；
（6）Material modification processing：Base material after damp and hot and moisture control is handled is immersed in thermosetting resin modifying agent
Middle 2h carries out the impregnation process of resin, to obtain substrate modified；
（7）The dewater treatment of substrate modified：Low temperature dewatering by substrate modified as less than 45 DEG C is handled, and makes moisture content near
10% once；
（8）Substrate modified moulding press resin is shaped：Substrate modified after dehydration is placed on hot pressing in metal fever pressing mold, hot pressing
Temperature range is 110-150 DEG C, and the time of hot pressing is 4-6min.
It is preferred that, the thermosetting resin content range of described thermosetting resin modifying agent is 15%-45%.
It is preferred that, the impregnation process uses vacuum pressed processing method.
It is preferred that, described is to be wiped off the bark of Wood surface with scraper to the simple processing of Wood surface progress, then
Its surface is simply polished using sanding apparatus, smooth, light is made it appear to.
It is preferred that, the step（2）In sawing be to carry out sawing with portable electric saw.
The technique effect and advantage of the present invention：The solid wood door and window can carry out handle with timber embossing preparation technology from source
Control, improves output quality, by being modified processing to timber, is prepared, assigned using the lossless mould pressing method of wood element
Give its excellent dimensionally stable, crack resistence, high density, high case hardness and structural behaviour etc., and early stage selection timber
More preferable with the details for handling the solid wood door and window for enabling to make, quality is higher.
Embodiment
It is clearly and completely described below in conjunction with the technical scheme in the embodiment of the present invention, it is clear that described reality
It is only a part of embodiment of the invention to apply example, rather than whole embodiments.Based on the embodiment in the present invention, this area is general
The every other embodiment that logical technical staff is obtained under the premise of creative work is not made, belongs to what the present invention was protected
Scope.
Embodiment 1
A kind of solid wood door and window is embossed preparation technology with timber, comprises the following steps：
（1）The selection of timber：Different timber influence particularly evident to embossing element quality, and we can select the measured timber of matter,
It can also be selected simultaneously according to color within doors；
（2）The processing of material：The Wood surface of selection is simply handled, then will be treated according to fixed size
Timber is sawed into base material；
（3）The polishing of base material：The surface of base material is polished smooth using polishing paper, the feelings for uneven and wooden thorn occur are not allowed
Condition；
（4）The processing of base material：The wood chip of the substrate surface after polishing is blown off using air gun, then its surface is wiped with wet cloth
Totally, a period of time is then placed；
（5）The damp and hot sofening treatment of material：Base material is placed in 60 DEG C of hot water 2 days, then carried out in drying process device
Drying process, controls the moisture content of base material below 20%；
（6）Material modification processing：Base material after damp and hot and moisture control is handled is immersed in thermosetting resin modifying agent
Middle 2h carries out the impregnation process of resin, to obtain substrate modified；
（7）The dewater treatment of substrate modified：Low temperature dewatering by substrate modified as less than 45 DEG C is handled, and makes moisture content near
10% once；
（8）Substrate modified moulding press resin is shaped：Substrate modified after dehydration is placed on hot pressing in metal fever pressing mold, hot pressing
Temperature range is 110-150 DEG C, and the time of hot pressing is 4-6min.
A kind of above-mentioned solid wood door and window is embossed preparation technology with timber, wherein, the thermosetting of described thermosetting resin modifying agent
Property resin content scope is 15%-45%.
A kind of above-mentioned solid wood door and window is embossed preparation technology with timber, wherein, the impregnation process uses vacuum pressed
Processing method.
A kind of above-mentioned solid wood door and window is embossed preparation technology with timber, wherein, it is described that Wood surface is simply handled
It is to be wiped off the bark of Wood surface with scraper, then its surface is simply polished using sanding apparatus, it is taken a fancy to
Remove smooth, light.
A kind of above-mentioned solid wood door and window is embossed preparation technology with timber, wherein, the step（2）In sawing be with portable
Electric saw carries out sawing.
Embodiment 2
A kind of solid wood door and window is embossed preparation technology with timber, comprises the following steps：
（1）The selection of timber：Different timber influence particularly evident to embossing element quality, and we can select the measured timber of matter,
It can also be selected simultaneously according to color within doors；
（2）The processing of material：The Wood surface of selection is simply handled, then will be treated according to fixed size
Timber is sawed into base material；
（3）The polishing of base material：The surface of base material is polished smooth using polishing paper, the feelings for uneven and wooden thorn occur are not allowed
Condition；
（4）The processing of base material：The wood chip of the substrate surface after polishing is blown off using air gun, then its surface is wiped with wet cloth
Totally, a period of time is then placed；
（5）The damp and hot sofening treatment of material：Base material is placed in 75 DEG C of hot water 2 days, then carried out in drying process device
Drying process, controls the moisture content of base material below 20%；
（6）Material modification processing：Base material after damp and hot and moisture control is handled is immersed in thermosetting resin modifying agent
Middle 2h carries out the impregnation process of resin, to obtain substrate modified；
（7）The dewater treatment of substrate modified：Low temperature dewatering by substrate modified as less than 45 DEG C is handled, and makes moisture content near
10% once；
（8）Substrate modified moulding press resin is shaped：Substrate modified after dehydration is placed on hot pressing in metal fever pressing mold, hot pressing
Temperature range is 110-150 DEG C, and the time of hot pressing is 4-6min.
A kind of above-mentioned solid wood door and window is embossed preparation technology with timber, wherein, the thermosetting of described thermosetting resin modifying agent
Property resin content scope is 15%-45%.
A kind of above-mentioned solid wood door and window is embossed preparation technology with timber, wherein, the impregnation process uses vacuum pressed
Processing method.
A kind of above-mentioned solid wood door and window is embossed preparation technology with timber, wherein, it is described that Wood surface is simply handled
It is to be wiped off the bark of Wood surface with scraper, then its surface is simply polished using sanding apparatus, it is taken a fancy to
Remove smooth, light.
A kind of above-mentioned solid wood door and window is embossed preparation technology with timber, wherein, the step（2）In sawing be with portable
Electric saw carries out sawing.
Embodiment 3
A kind of solid wood door and window is embossed preparation technology with timber, comprises the following steps：
（1）The selection of timber：Different timber influence particularly evident to embossing element quality, and we can select the measured timber of matter,
It can also be selected simultaneously according to color within doors；
（2）The processing of material：The Wood surface of selection is simply handled, then will be treated according to fixed size
Timber is sawed into base material；
（3）The polishing of base material：The surface of base material is polished smooth using polishing paper, the feelings for uneven and wooden thorn occur are not allowed
Condition；
（4）The processing of base material：The wood chip of the substrate surface after polishing is blown off using air gun, then its surface is wiped with wet cloth
Totally, a period of time is then placed；
（5）The damp and hot sofening treatment of material：Base material is placed in 90 DEG C of hot water 2 days, then carried out in drying process device
Drying process, controls the moisture content of base material below 20%；
（6）Material modification processing：Base material after damp and hot and moisture control is handled is immersed in thermosetting resin modifying agent
Middle 2h carries out the impregnation process of resin, to obtain substrate modified；
（7）The dewater treatment of substrate modified：Low temperature dewatering by substrate modified as less than 45 DEG C is handled, and makes moisture content near
10% once；
（8）Substrate modified moulding press resin is shaped：Substrate modified after dehydration is placed on hot pressing in metal fever pressing mold, hot pressing
Temperature range is 110-150 DEG C, and the time of hot pressing is 4-6min.
A kind of above-mentioned solid wood door and window is embossed preparation technology with timber, wherein, the thermosetting of described thermosetting resin modifying agent
Property resin content scope is 15%-45%.
A kind of above-mentioned solid wood door and window is embossed preparation technology with timber, wherein, the impregnation process uses vacuum pressed
Processing method.
A kind of above-mentioned solid wood door and window is embossed preparation technology with timber, wherein, it is described that Wood surface is simply handled
It is to be wiped off the bark of Wood surface with scraper, then its surface is simply polished using sanding apparatus, it is taken a fancy to
Remove smooth, light.
A kind of above-mentioned solid wood door and window is embossed preparation technology with timber, wherein, the step（2）In sawing be with portable
Electric saw carries out sawing.
Finally it should be noted that：The preferred embodiments of the present invention are the foregoing is only, are not intended to limit the invention,
Although the present invention is described in detail with reference to the foregoing embodiments, for those skilled in the art, it still may be used
To be modified to the technical scheme described in foregoing embodiments, or equivalent substitution is carried out to which part technical characteristic,
Within the spirit and principles of the invention, any modification, equivalent substitution and improvements made etc., should be included in the present invention's
Within protection domain.
Claims (5)
1. a kind of solid wood door and window is embossed preparation technology with timber, it is characterised in that：Comprise the following steps：
（1）The selection of timber：Different timber influence particularly evident to embossing element quality, and we can select the measured timber of matter,
It can also be selected simultaneously according to color within doors；
（2）The processing of material：The Wood surface of selection is simply handled, then will be treated according to fixed size
Timber is sawed into base material；
（3）The polishing of base material：The surface of base material is polished smooth using polishing paper, the feelings for uneven and wooden thorn occur are not allowed
Condition；
（4）The processing of base material：The wood chip of the substrate surface after polishing is blown off using air gun, then its surface is wiped with wet cloth
Totally, a period of time is then placed；
（5）The damp and hot sofening treatment of material：Base material is placed in 60-90 DEG C of hot water 2 days, then entered in drying process device
Row drying process, controls the moisture content of base material below 20%；
（6）Material modification processing：Base material after damp and hot and moisture control is handled is immersed in thermosetting resin modifying agent
Middle 2h carries out the impregnation process of resin, to obtain substrate modified；
（7）The dewater treatment of substrate modified：Low temperature dewatering by substrate modified as less than 45 DEG C is handled, and makes moisture content near
10% once；
（8）Substrate modified moulding press resin is shaped：Substrate modified after dehydration is placed on hot pressing in metal fever pressing mold, hot pressing
Temperature range is 110-150 DEG C, and the time of hot pressing is 4-6min.
2. a kind of solid wood door and window according to claim 1 is embossed preparation technology with timber, it is characterised in that：Described thermosetting
The thermosetting resin content range of property modifier is 15%-45%.
3. a kind of solid wood door and window according to claim 1 is embossed preparation technology with timber, it is characterised in that：At the dipping
Reason uses vacuum pressed processing method.
4. a kind of solid wood door and window according to claim 1 is embossed preparation technology with timber, it is characterised in that：It is described to timber
It is to be wiped off the bark of Wood surface with scraper that surface, which carries out simple processing, then carries out letter to its surface using sanding apparatus
Single polishing, makes it appear to smooth, light.
5. a kind of solid wood door and window according to claim 1 is embossed preparation technology with timber, it is characterised in that：The step
（2）In sawing be to carry out sawing with portable electric saw.