CN107098721A - 一种具有净化空气功能的保温材料及其制备方法 - Google Patents
一种具有净化空气功能的保温材料及其制备方法 Download PDFInfo
- Publication number
- CN107098721A CN107098721A CN201710425199.6A CN201710425199A CN107098721A CN 107098721 A CN107098721 A CN 107098721A CN 201710425199 A CN201710425199 A CN 201710425199A CN 107098721 A CN107098721 A CN 107098721A
- Authority
- CN
- China
- Prior art keywords
- parts
- purification function
- air purification
- insulation material
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
本发明提供一种具有净化空气功能的保温材料及其制备方法，涉及保温材料领域，具有净化空气功能的保温材料包括以下重量份的原料：硅酸钙粉14‑20份、花岗岩粉10‑28份、聚氨酯15‑17份、硅酸铝粉17‑23份、氧化镁5‑9份、矿物棉7‑13份、聚酯纤维4‑8份、竹炭21‑35份、膨润土7‑13份、海泡石粉9‑13份、酚醛泡沫15‑19份、蛭石11‑31份、废弃聚乙烯泡沫塑料15‑21份、硼纤维9‑15份、聚丙烯腈纤维13‑21份、水泥27‑35份、引气剂0.2‑0.4份、缓凝剂0.1‑0.7份、热稳定剂0.1‑0.3份、减水剂0.3‑0.7份、发泡剂0.2‑0.6份和水4‑8份；制备方法包括以下步骤：（1）称取原料、（2）焙烧、（3）粉碎、（4）搅拌、（5）加压成型、（6）烘干。本发明制得的具有净化空气功能的保温材料具有强度高、保温隔热性能好和环保节能的优点。
Description
技术领域
本发明属于保温材料领域，具体涉及一种具有净化空气功能的保温材料及其制备方法。
背景技术
随着社会进步和人民生活水平的提高，人们对建筑材料的要求越来越高，尤其是建筑材料中的保温材料，但是，在现有的保温材料中，存在着抗压强度低、抗拉强度低、保温效果一般以及达不到节能环保要求的问题。
2016年7月13日公告的中国专利文献一种保温隔热的建筑材料及其制备方法（授权公告号CN104261776B），所述的保温隔热的建筑材料包括以下重量份的原料：硅酸钙粉为14-21份、花岗岩粉为8-17份、聚氨酯为15-19份、硅酸铝粉为17-25份、氧化镁为5-11份、矿物棉为7-13份、聚酯纤维为4-9份。所述保温隔热的建筑材料的制备方法包括以下步骤：(1)取上述的各成分在搅拌罐中进行搅拌，搅拌均匀后备用；(2)将步骤(1)制备得到的混合均匀后的复合材料注入到成型模具中，加压成型；(3)将步骤(2)加压成型后的复合建筑材料再进行烘干，烘干温度为75℃，烘干时间为3h，烘干后制备得到保温隔热的建筑材料。
该发明在面对高标准要求的建筑时，对其配方仍需要进一步的改进，使其具有抗压强度高、抗拉强度高、保温隔热性能好和环保节能的特点。
发明内容
为了解决现有保温材料在应用于对抗压强度、抗拉强度、保温隔热和环保节能要求高的建筑上还存在着不足的问题，本发明的目的是提供一种具有净化空气功能的保温材料及其制备方法，制得的具有净化空气功能的保温材料具有抗压强度高、抗拉强度高、保温隔热性能好和环保节能的优点。
本发明提供了如下的技术方案：
一种具有净化空气功能的保温材料，包括以下重量份的原料：硅酸钙粉14-20份、花岗岩粉10-28份、聚氨酯15-17份、硅酸铝粉17-23份、氧化镁5-9份、矿物棉7-13份、聚酯纤维4-8份、竹炭21-35份、膨润土7-13份、海泡石粉9-13份、酚醛泡沫15-19份、蛭石11-31份、废弃聚乙烯泡沫塑料15-21份、硼纤维9-15份、聚丙烯腈纤维13-21份、水泥27-35份、引气剂0.2-0.4份、缓凝剂0.1-0.7份、热稳定剂0.1-0.3份、减水剂0.3-0.7份、发泡剂0.2-0.6份和水4-8份。
原料中添加了废弃聚乙烯泡沫塑料，废弃聚乙烯泡沫塑料长期搁置在城市，不仅占用城市用地，而且污染当地的环境，现将废弃聚乙烯泡沫塑料循环再利用，达到了节能环保的目的；废弃聚乙烯泡沫塑料具有缓冲性好、耐热性好、保温隔热性好和化学稳定性好的特点。
原料中添加了竹炭，竹炭为疏松多孔结构，其分子细密多孔，质地坚硬，具有很强的吸附能力，能够净化空气、消除异味、抑菌驱虫和呼吸调湿。
原料中添加了膨润土，膨润土具有吸湿性和膨胀性，在水介质中能分散成胶凝状和悬浮状，这种介质溶液具有一定的黏滞性、触变性和润滑性，能够与保温材料中的其他原料连接更加牢固，而且膨润土还具有对气体、液体和有机物质一定的吸附能力。
原料中添加了海泡石粉，海泡石是一种具层链状结构的含水富镁硅酸盐黏土矿物，具有质轻、保温隔热、绝缘、抗腐蚀和热稳定的优点。
原料中添加了酚醛泡沫，酚醛泡沫具有均匀的闭孔结构、导热系数低、绝热性好、成本低、难燃、低烟和耐高温的特点。
原料中添加了蛭石，蛭石是一种天然、无味、无毒且在高温下会膨胀的矿物质，在800-1000℃的温度下焙烧，体积会迅速膨胀，增大6-15倍，膨胀后的蛭石容重为100-200kg/m3,具有细小的空气隔层，导致其具有优良的保温性能，此外蛭石在吸附性、隔音性、抗冻性和耐火性上均表现良好。
原料中添加了硼纤维，硼纤维具有抗拉强度高、抗压缩性好和耐高温。
原料中添加了聚丙烯腈纤维，聚丙烯腈纤维具有弹性好、耐光、抗菌和保温性好的特点。
优选地，包括以下重量份的原料：硅酸钙粉17份、花岗岩粉19份、聚氨酯16份、硅酸铝粉20份、氧化镁7份、矿物棉10份、聚酯纤维6份、竹炭28份、膨润土10份、海泡石粉11份、酚醛泡沫17份、蛭石21份、废弃聚乙烯泡沫塑料18份、硼纤维12份、聚丙烯腈纤维17份、水泥31份、引气剂0.3份、缓凝剂0.4份、热稳定剂0.2份、减水剂0.5份、发泡剂0.4份和水6份。
优选地，所述引气剂为烷基苯磺酸盐类引气剂，提高具有净化空气功能的保温材料的原料流动性、可塑性以及降低具有净化空气功能的保温材料成品的导热系数。
优选地，所述缓凝剂为焦磷酸钠，焦磷酸钠能够降低水泥水化速度、水化热和延长凝结时间的特点。
优选地，所述热稳定剂为硬脂酸铝，能够提高保温材料的热稳性。
优选地，所述减水剂为木质素磺酸盐类减水剂，可以减少用水量的10-15%，改善混合浆料和易性。
优选地，所述发泡剂为碳酸氢钠，加热放出二氧化碳，发泡效果好，提高具有净化空气功能的保温材料的保温隔热性能。
一种具有净化空气功能的保温材料的制备方法，包括以下步骤：
（1）按照具有净化空气功能的保温材料原料的重量份数称取原料；
（2）将蛭石放入窑炉中焙烧20-30min，焙烧温度控制在800-1000℃，即得焙烧后的蛭石；
（3）将废弃聚乙烯泡沫塑料加入到粉碎机中粉碎，粉碎时间为15-20min，即得粉碎料；
（4）将步骤（2）中的焙烧后的蛭石、步骤（3）中的粉碎料、硅酸钙粉、花岗岩粉、聚氨酯、硅酸铝粉、氧化镁、矿物棉、聚酯纤维、竹炭、膨润土、海泡石粉、酚醛泡沫、硼纤维、聚丙烯腈纤维、水泥、引气剂、缓凝剂、热稳定剂、减水剂、发泡剂和水加入到搅拌机中搅拌，搅拌时间为35-40min，即得混合料；
（5）将步骤（4）中的混合料注入成型模具中，加压成型，即得成型料；
（6）将步骤（5）中的成型料进行烘干，烘干温度为75-80℃，烘干时间为4-5h，即得具有净化空气功能的保温材料。
本发明的有益效果是：
1、本发明制得的具有净化空气功能的保温材料具有抗压强度高、抗拉强度高、保温隔热性能好和环保节能的优点。
2、本发明的原料中添加了废弃聚乙烯泡沫塑料，废弃聚乙烯泡沫塑料长期搁置在城市，不仅占用城市用地，而且污染当地的环境，现将废弃聚乙烯泡沫塑料循环再利用，达到了节能环保的目的；废弃聚乙烯泡沫塑料具有缓冲性好、耐热性好、保温隔热性好和化学稳定性好的特点。
3、本发明的原料中添加了竹炭，竹炭为疏松多孔结构，其分子细密多孔，质地坚硬，具有很强的吸附能力，能够净化空气、消除异味、抑菌驱虫和呼吸调湿。
4、本发明的原料中添加了膨润土，膨润土具有吸湿性和膨胀性，在水介质中能分散成胶凝状和悬浮状，这种介质溶液具有一定的黏滞性、触变性和润滑性，能够与保温材料中的其他原料连接更加牢固，而且膨润土还具有对气体、液体和有机物质一定的吸附能力。
5、本发明的原料中添加了海泡石粉，海泡石是一种具层链状结构的含水富镁硅酸盐黏土矿物，具有质轻、保温隔热、绝缘、抗腐蚀和热稳定的优点。
6、本发明的原料中添加了酚醛泡沫，酚醛泡沫具有均匀的闭孔结构、导热系数低、绝热性好、成本低、难燃、低烟和耐高温的特点。
7、本发明的原料中添加了蛭石，蛭石是一种天然、无味、无毒且在高温下会膨胀的矿物质，在800-1000℃的温度下焙烧，体积会迅速膨胀，增大6-15倍，膨胀后的蛭石容重为100-200kg/m3,具有细小的空气隔层，导致其具有优良的保温性能，此外蛭石在吸附性、隔音性、抗冻性和耐火性上均表现良好。
8、本发明的原料中添加了硼纤维，硼纤维具有抗拉强度高、抗压缩性好和耐高温。
9、本发明的原料中添加了聚丙烯腈纤维，聚丙烯腈纤维具有弹性好、耐光、抗菌和保温性好的特点。
10、本发明中所述引气剂为烷基苯磺酸盐类引气剂，提高具有净化空气功能的保温材料的原料流动性、可塑性以及降低具有净化空气功能的保温材料成品的导热系数。
11、本发明中所述缓凝剂为焦磷酸钠，焦磷酸钠能够降低水泥水化速度、水化热和延长凝结时间的特点。
12、本发明中所述热稳定剂为硬脂酸铝，能够提高保温材料的热稳性。
13、本发明中所述减水剂为木质素磺酸盐类减水剂，可以减少用水量的10-15%，改善混合浆料和易性。
14、本发明中所述发泡剂为碳酸氢钠，加热放出二氧化碳，发泡效果好，提高具有净化空气功能的保温材料的保温隔热性能。
具体实施方式
实施例1
一种具有净化空气功能的保温材料，包括以下重量份的原料：硅酸钙粉17份、花岗岩粉19份、聚氨酯16份、硅酸铝粉20份、氧化镁7份、矿物棉10份、聚酯纤维6份、竹炭28份、膨润土10份、海泡石粉11份、酚醛泡沫17份、蛭石21份、废弃聚乙烯泡沫塑料18份、硼纤维12份、聚丙烯腈纤维17份、水泥31份、引气剂0.3份、缓凝剂0.4份、热稳定剂0.2份、减水剂0.5份、发泡剂0.4份和水6份。
原料中添加了废弃聚乙烯泡沫塑料，废弃聚乙烯泡沫塑料长期搁置在城市，不仅占用城市用地，而且污染当地的环境，现将废弃聚乙烯泡沫塑料循环再利用，达到了节能环保的目的；废弃聚乙烯泡沫塑料具有缓冲性好、耐热性好、保温隔热性好和化学稳定性好的特点。
原料中添加了竹炭，竹炭为疏松多孔结构，其分子细密多孔，质地坚硬，具有很强的吸附能力，能够净化空气、消除异味、抑菌驱虫和呼吸调湿。
原料中添加了膨润土，膨润土具有吸湿性和膨胀性，在水介质中能分散成胶凝状和悬浮状，这种介质溶液具有一定的黏滞性、触变性和润滑性，能够与保温材料中的其他原料连接更加牢固，而且膨润土还具有对气体、液体和有机物质一定的吸附能力。
原料中添加了海泡石粉，海泡石是一种具层链状结构的含水富镁硅酸盐黏土矿物，具有质轻、保温隔热、绝缘、抗腐蚀和热稳定的优点。
原料中添加了酚醛泡沫，酚醛泡沫具有均匀的闭孔结构、导热系数低、绝热性好、成本低、难燃、低烟和耐高温的特点。
原料中添加了蛭石，蛭石是一种天然、无味、无毒且在高温下会膨胀的矿物质，在800-1000℃的温度下焙烧，体积会迅速膨胀，增大6-15倍，膨胀后的蛭石容重为100-200kg/m3,具有细小的空气隔层，导致其具有优良的保温性能，此外蛭石在吸附性、隔音性、抗冻性和耐火性上均表现良好。
原料中添加了硼纤维，硼纤维具有抗拉强度高、抗压缩性好和耐高温。
原料中添加了聚丙烯腈纤维，聚丙烯腈纤维具有弹性好、耐光、抗菌和保温性好的特点。
引气剂为烷基苯磺酸盐类引气剂，提高具有净化空气功能的保温材料的原料流动性、可塑性以及降低具有净化空气功能的保温材料成品的导热系数。
缓凝剂为焦磷酸钠，焦磷酸钠能够降低水泥水化速度、水化热和延长凝结时间的特点。
热稳定剂为硬脂酸铝，能够提高保温材料的热稳性。
减水剂为木质素磺酸盐类减水剂，可以减少用水量的10-15%，改善混合浆料和易性。
发泡剂为碳酸氢钠，加热放出二氧化碳，发泡效果好，提高具有净化空气功能的保温材料的保温隔热性能。
一种具有净化空气功能的保温材料的制备方法，包括以下步骤：
（1）按照具有净化空气功能的保温材料原料的重量份数称取原料；
（2）将蛭石放入窑炉中焙烧20-30min，焙烧温度控制在800-1000℃，即得焙烧后的蛭石；
（3）将废弃聚乙烯泡沫塑料加入到粉碎机中粉碎，粉碎时间为15-20min，即得粉碎料；
（4）将步骤（2）中的焙烧后的蛭石、步骤（3）中的粉碎料、硅酸钙粉、花岗岩粉、聚氨酯、硅酸铝粉、氧化镁、矿物棉、聚酯纤维、竹炭、膨润土、海泡石粉、酚醛泡沫、硼纤维、聚丙烯腈纤维、水泥、引气剂、缓凝剂、热稳定剂、减水剂、发泡剂和水加入到搅拌机中搅拌，搅拌时间为35-40min，即得混合料；
（5）将步骤（4）中的混合料注入成型模具中，加压成型，即得成型料；
（6）将步骤（5）中的成型料进行烘干，烘干温度为75-80℃，烘干时间为4-5h，即得具有净化空气功能的保温材料。
实施例2
一种具有净化空气功能的保温材料，包括以下重量份的原料：硅酸钙粉14份、花岗岩粉10份、聚氨酯15份、硅酸铝粉17份、氧化镁5份、矿物棉7份、聚酯纤维4份、竹炭21份、膨润土7份、海泡石粉9份、酚醛泡沫15份、蛭石11份、废弃聚乙烯泡沫塑料15份、硼纤维9份、聚丙烯腈纤维13份、水泥27份、引气剂0.2份、缓凝剂0.1份、热稳定剂0.1份、减水剂0.3份、发泡剂0.2份和水4份。
原料中添加了废弃聚乙烯泡沫塑料，废弃聚乙烯泡沫塑料长期搁置在城市，不仅占用城市用地，而且污染当地的环境，现将废弃聚乙烯泡沫塑料循环再利用，达到了节能环保的目的；废弃聚乙烯泡沫塑料具有缓冲性好、耐热性好、保温隔热性好和化学稳定性好的特点。
原料中添加了竹炭，竹炭为疏松多孔结构，其分子细密多孔，质地坚硬，具有很强的吸附能力，能够净化空气、消除异味、抑菌驱虫和呼吸调湿。
原料中添加了膨润土，膨润土具有吸湿性和膨胀性，在水介质中能分散成胶凝状和悬浮状，这种介质溶液具有一定的黏滞性、触变性和润滑性，能够与保温材料中的其他原料连接更加牢固，而且膨润土还具有对气体、液体和有机物质一定的吸附能力。
原料中添加了海泡石粉，海泡石是一种具层链状结构的含水富镁硅酸盐黏土矿物，具有质轻、保温隔热、绝缘、抗腐蚀和热稳定的优点。
原料中添加了酚醛泡沫，酚醛泡沫具有均匀的闭孔结构、导热系数低、绝热性好、成本低、难燃、低烟和耐高温的特点。
原料中添加了蛭石，蛭石是一种天然、无味、无毒且在高温下会膨胀的矿物质，在800-1000℃的温度下焙烧，体积会迅速膨胀，增大6-15倍，膨胀后的蛭石容重为100-200kg/m3,具有细小的空气隔层，导致其具有优良的保温性能，此外蛭石在吸附性、隔音性、抗冻性和耐火性上均表现良好。
原料中添加了硼纤维，硼纤维具有抗拉强度高、抗压缩性好和耐高温。
原料中添加了聚丙烯腈纤维，聚丙烯腈纤维具有弹性好、耐光、抗菌和保温性好的特点。
引气剂为烷基苯磺酸盐类引气剂，提高具有净化空气功能的保温材料的原料流动性、可塑性以及降低具有净化空气功能的保温材料成品的导热系数。
缓凝剂为焦磷酸钠，焦磷酸钠能够降低水泥水化速度、水化热和延长凝结时间的特点。
热稳定剂为硬脂酸铝，能够提高保温材料的热稳性。
减水剂为木质素磺酸盐类减水剂，可以减少用水量的10-15%，改善混合浆料和易性。
发泡剂为碳酸氢钠，加热放出二氧化碳，发泡效果好，提高具有净化空气功能的保温材料的保温隔热性能。
一种具有净化空气功能的保温材料的制备方法，包括以下步骤：
（1）按照具有净化空气功能的保温材料原料的重量份数称取原料；
（2）将蛭石放入窑炉中焙烧20-30min，焙烧温度控制在800-1000℃，即得焙烧后的蛭石；
（3）将废弃聚乙烯泡沫塑料加入到粉碎机中粉碎，粉碎时间为15-20min，即得粉碎料；
（4）将步骤（2）中的焙烧后的蛭石、步骤（3）中的粉碎料、硅酸钙粉、花岗岩粉、聚氨酯、硅酸铝粉、氧化镁、矿物棉、聚酯纤维、竹炭、膨润土、海泡石粉、酚醛泡沫、硼纤维、聚丙烯腈纤维、水泥、引气剂、缓凝剂、热稳定剂、减水剂、发泡剂和水加入到搅拌机中搅拌，搅拌时间为35-40min，即得混合料；
（5）将步骤（4）中的混合料注入成型模具中，加压成型，即得成型料；
（6）将步骤（5）中的成型料进行烘干，烘干温度为75-80℃，烘干时间为4-5h，即得具有净化空气功能的保温材料。
实施例3
一种具有净化空气功能的保温材料，包括以下重量份的原料：硅酸钙粉20份、花岗岩粉28份、聚氨酯17份、硅酸铝粉23份、氧化镁9份、矿物棉13份、聚酯纤维8份、竹炭35份、膨润土13份、海泡石粉13份、酚醛泡沫19份、蛭石31份、废弃聚乙烯泡沫塑料21份、硼纤维15份、聚丙烯腈纤维21份、水泥35份、引气剂0.4份、缓凝剂0.7份、热稳定剂0.3份、减水剂0.7份、发泡剂0.6份和水8份。
原料中添加了废弃聚乙烯泡沫塑料，废弃聚乙烯泡沫塑料长期搁置在城市，不仅占用城市用地，而且污染当地的环境，现将废弃聚乙烯泡沫塑料循环再利用，达到了节能环保的目的；废弃聚乙烯泡沫塑料具有缓冲性好、耐热性好、保温隔热性好和化学稳定性好的特点。
原料中添加了竹炭，竹炭为疏松多孔结构，其分子细密多孔，质地坚硬，具有很强的吸附能力，能够净化空气、消除异味、抑菌驱虫和呼吸调湿。
原料中添加了膨润土，膨润土具有吸湿性和膨胀性，在水介质中能分散成胶凝状和悬浮状，这种介质溶液具有一定的黏滞性、触变性和润滑性，能够与保温材料中的其他原料连接更加牢固，而且膨润土还具有对气体、液体和有机物质一定的吸附能力。
原料中添加了海泡石粉，海泡石是一种具层链状结构的含水富镁硅酸盐黏土矿物，具有质轻、保温隔热、绝缘、抗腐蚀和热稳定的优点。
原料中添加了酚醛泡沫，酚醛泡沫具有均匀的闭孔结构、导热系数低、绝热性好、成本低、难燃、低烟和耐高温的特点。
原料中添加了蛭石，蛭石是一种天然、无味、无毒且在高温下会膨胀的矿物质，在800-1000℃的温度下焙烧，体积会迅速膨胀，增大6-15倍，膨胀后的蛭石容重为100-200kg/m3,具有细小的空气隔层，导致其具有优良的保温性能，此外蛭石在吸附性、隔音性、抗冻性和耐火性上均表现良好。
原料中添加了硼纤维，硼纤维具有抗拉强度高、抗压缩性好和耐高温。
原料中添加了聚丙烯腈纤维，聚丙烯腈纤维具有弹性好、耐光、抗菌和保温性好的特点。
引气剂为烷基苯磺酸盐类引气剂，提高具有净化空气功能的保温材料的原料流动性、可塑性以及降低具有净化空气功能的保温材料成品的导热系数。
缓凝剂为焦磷酸钠，焦磷酸钠能够降低水泥水化速度、水化热和延长凝结时间的特点。
热稳定剂为硬脂酸铝，能够提高保温材料的热稳性。
减水剂为木质素磺酸盐类减水剂，可以减少用水量的10-15%，改善混合浆料和易性。
发泡剂为碳酸氢钠，加热放出二氧化碳，发泡效果好，提高具有净化空气功能的保温材料的保温隔热性能。
一种具有净化空气功能的保温材料的制备方法，包括以下步骤：
（1）按照具有净化空气功能的保温材料原料的重量份数称取原料；
（2）将蛭石放入窑炉中焙烧20-30min，焙烧温度控制在800-1000℃，即得焙烧后的蛭石；
（3）将废弃聚乙烯泡沫塑料加入到粉碎机中粉碎，粉碎时间为15-20min，即得粉碎料；
（4）将步骤（2）中的焙烧后的蛭石、步骤（3）中的粉碎料、硅酸钙粉、花岗岩粉、聚氨酯、硅酸铝粉、氧化镁、矿物棉、聚酯纤维、竹炭、膨润土、海泡石粉、酚醛泡沫、硼纤维、聚丙烯腈纤维、水泥、引气剂、缓凝剂、热稳定剂、减水剂、发泡剂和水加入到搅拌机中搅拌，搅拌时间为35-40min，即得混合料；
（5）将步骤（4）中的混合料注入成型模具中，加压成型，即得成型料；
（6）将步骤（5）中的成型料进行烘干，烘干温度为75-80℃，烘干时间为4-5h，即得具有净化空气功能的保温材料。
对比例1
一种保温隔热的建筑材料，包括以下重量份的原料：硅酸钙粉17.5份、花岗岩粉20份、聚氨酯17份、硅酸铝粉21份、氧化镁8 份、矿物棉10份、聚酯纤维6.5份和水4份。
一种保温隔热的建筑材料的制备方法，包括以下步骤：
（1）按照保温隔热的建筑材料原料的重量份数称取原料；
（2）将硅酸钙粉、花岗岩粉、聚氨酯、硅酸铝粉、氧化镁、矿物棉、聚酯纤维和水加入到搅拌机中搅拌，搅拌时间为30-40min，即得混合料；
（3）将步骤（2）中的混合料注入成型模具中，加压成型，即得成型料；
（4）将步骤（3）中的成型料进行烘干，烘干温度为75-85℃，烘干时间为4-5h，即得具有净化空气功能的保温材料。
将实施例1、实施例2和实施例3制得具有净化空气功能的保温材料与对比例1制得的保温隔热的建筑材料进行性能测试，测试结果如表1所示：
| 指标 | 实施例1 | 实施例2 | 实施例3 | 对比例1 |
| 抗压强度（Mpa） | 45.1 | 41.2 | 35.6 | 30.7 |
| 抗拉强度（Mpa） | 46.8 | 42.1 | 36.8 | 30.9 |
| 导热系数（w/m﹒k） | 0.016 | 0.020 | 0.023 | 0.028 |
| 抗细菌性能(%) | 56 | 42 | 31 | 0 |
| 甲醛净化性能(%) | 98 | 90 | 84 | 0 |
从表1数据比较可以看出，本发明的优点是：
1、一种具有净化空气功能的保温材料及其制备方法，从测得的抗压强度值可以看出，实施例1-3的抗压强度值均高于对比例1，说明该具有净化空气功能的保温材料抗压强度高。
2、一种具有净化空气功能的保温材料及其制备方法，从测得的抗拉强度值可以看出，实施例1-3的抗拉强度值均高于对比例1，说明该具有净化空气功能的保温材料抗拉强度高。
3、一种具有净化空气功能的保温材料及其制备方法，从测得的导热系数可以看出，实施例1-3的导热系数均低于对比例1，说明该具有净化空气功能的保温材料保温效果好。
4、一种具有净化空气功能的保温材料及其制备方法，从测得的抗细菌性能和甲醛净化性能可以看出，实施例1-3的抗细菌性能和甲醛净化性能均高于对比例1，说明该具有净化空气功能的保温材料的环保效果好。
5、一种具有净化空气功能的保温材料及其制备方法，从测得的各个指标的数据可以看出，实施例1均优于实施例2、实施例3和对比例1，说明该具有净化空气功能的保温材料的原料配方和制备方法的合理性。
以上所述仅为本发明的优选实施例而已，并不用于限制本发明，尽管参照前述实施例对本发明进行了详细的说明，对于本领域的技术人员来说，其依然可以对前述各实施例所记载的技术方案进行修改，或者对其中部分技术特征进行等同替换，凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。
Claims (8)
1.一种具有净化空气功能的保温材料，其特征在于，包括以下重量份的原料：硅酸钙粉14-20份、花岗岩粉10-28份、聚氨酯15-17份、硅酸铝粉17-23份、氧化镁5-9份、矿物棉7-13份、聚酯纤维4-8份、竹炭21-35份、膨润土7-13份、海泡石粉9-13份、酚醛泡沫15-19份、蛭石11-31份、废弃聚乙烯泡沫塑料15-21份、硼纤维9-15份、聚丙烯腈纤维13-21份、水泥27-35份、引气剂0.2-0.4份、缓凝剂0.1-0.7份、热稳定剂0.1-0.3份、减水剂0.3-0.7份、发泡剂0.2-0.6份和水4-8份。
2.根据权利要求1所述的具有净化空气功能的保温材料，其特征在于，包括以下重量份的原料：硅酸钙粉17份、花岗岩粉19份、聚氨酯16份、硅酸铝粉20份、氧化镁7份、矿物棉10份、聚酯纤维6份、竹炭28份、膨润土10份、海泡石粉11份、酚醛泡沫17份、蛭石21份、废弃聚乙烯泡沫塑料18份、硼纤维12份、聚丙烯腈纤维17份、水泥31份、引气剂0.3份、缓凝剂0.4份、热稳定剂0.2份、减水剂0.5份、发泡剂0.4份和水6份。
3.根据权利要求1所述的具有净化空气功能的保温材料，其特征在于：所述引气剂为烷基苯磺酸盐类引气剂。
4.根据权利要求1所述的具有净化空气功能的保温材料，其特征在于：所述缓凝剂为焦磷酸钠。
5.根据权利要求1所述的具有净化空气功能的保温材料，其特征在于：所述热稳定剂为硬脂酸铝。
6.根据权利要求1所述的具有净化空气功能的保温材料，其特征在于：所述减水剂为木质素磺酸盐类减水剂。
7.根据权利要求1所述的具有净化空气功能的保温材料，其特征在于：所述发泡剂为碳酸氢钠。
8.一种如权利要求1—7任意一项所述的具有净化空气功能的保温材料的制备方法，其特征在于，包括以下步骤：
（1）按照具有净化空气功能的保温材料原料的重量份数称取原料；
（2）将蛭石放入窑炉中焙烧20-30min，焙烧温度控制在800-1000℃，即得焙烧后的蛭石；
（3）将废弃聚乙烯泡沫塑料加入到粉碎机中粉碎，粉碎时间为15-20min，即得粉碎料；
（4）将步骤（2）中的焙烧后的蛭石、步骤（3）中的粉碎料、硅酸钙粉、花岗岩粉、聚氨酯、硅酸铝粉、氧化镁、矿物棉、聚酯纤维、竹炭、膨润土、海泡石粉、酚醛泡沫、硼纤维、聚丙烯腈纤维、水泥、引气剂、缓凝剂、热稳定剂、减水剂、发泡剂和水加入到搅拌机中搅拌，搅拌时间为35-40min，即得混合料；
（5）将步骤（4）中的混合料注入成型模具中，加压成型，即得成型料；
（6）将步骤（5）中的成型料进行烘干，烘干温度为75-80℃，烘干时间为4-5h，即得具有净化空气功能的保温材料。