CN107082982A - A kind of online three rollers laminating big flooring method of belt lock catch - Google Patents
A kind of online three rollers laminating big flooring method of belt lock catch Download PDFInfo
- Publication number
- CN107082982A CN107082982A CN201710325843.2A CN201710325843A CN107082982A CN 107082982 A CN107082982 A CN 107082982A CN 201710325843 A CN201710325843 A CN 201710325843A CN 107082982 A CN107082982 A CN 107082982A
- Authority
- CN
- China
- Prior art keywords
- laminating
- areas
- extruder
- online
- extrusion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of online three rollers laminating big flooring method of belt lock catch, is related to plastic-wood material production technical field, mainly including mixing process, extrusion and laminating process；Mixing process, required raw material components and group component are：PVC5 types 30 35%, coarse whiting 60 70%, PE waxes 0.03 0.07%, calcium zinc stabilizer 0.1 0.2%, modifier 0.1%, remaining be MBS, above each group component sum meet 100%.Beneficial effect：The complicated technology fitted again before solving, fully achieves the online integration of extrusion laminating, and great advantage is to be overlayed color film and wearing layer fusion using temperature, and 100% without glue and substantially increases peel strength.
Description
Technical field：
The present invention relates to plastic-wood material production technical field, more particularly to a kind of online three rollers laminating big floor system of belt lock catch
Standby technique.
Background technology：
Plastics Packaging Wastes seriously pollute environment, have impact on industrial and agricultural production, compromise human health and dynamic
The existence of plant.World's plastics annual production more than 200,000,000 tons, China plastics packaging materials 2007 more than 10,000,000 tons, this
A little plastic package materials and container are most of into solid waste after disposable.Plastics Packaging Wastes are lightweight,
Volume is big, quantity is more, it is difficult to degrade, and can not arbitrarily incinerate again, railway side, inland waters and cities and towns street is discarded in mostly small
Lane, accumulate over a long period " white pollution " band for having become startling.According to the relevant departments of the investigation 1000 tons of rubbish of Shanghai daily output is understood,
Plastic refuse accounts for 330 tons；12000 tons of rubbish is produced in Beijing daily, and plastic refuse accounts for 360 tons；Guangzhou daily output rubbish is about
6000 tons, plastic garbage accounts for 200 tons.
China's logging residue and producing material residue account for the 40% of Tree biomass, according to " the 11 of State Council approved
The m3/a of forest pathogen 2.5 hundred million are calculated during five ", and China will produce about 1.1 hundred million tons of felling, producing material residue every year.Separately
Outside, industrial wood waste calculates the annual production for also having up to 32,100,000 m3 by the 34.4% of log.At present, although forestry " three surplus things "
Utilization caused the attention of people, but worldwide development level and uneven.The wood of the developing countries such as China
Material comprehensive utilization ratio is only 50%~60%, and the wood comprehensive utilization rate of developed country is up to 80%~90%." three remain for forestry
The development and utilization situation of thing "：Forestry " three surplus things " generally bulk density is low, volume is big, and distribution is loose, is not easy to collect, stores up
Hide and transport, therefore traditional " three surplus things " processing mode mostly to abandon, burn or fill etc. based on plain mode on the spot.Mesh
Before, as people gradually step up to the attention rate of air and water quality, these traditional methods can not continue to continue to use.And pass through wood
The engineering and high performance of (bamboo) plastic material, the modification regeneration of waste plastic and bamboo wood chip resource make full use of, and can solve
Certainly waste or used plastics, the regeneration problem of bamboo wood working industry waste resource.
Floor is prepared during laminating, and the technique fitted again is extremely complex, it is difficult to fully achieve extrusion laminating online
Integration, using a large amount of glue, peel strength is relatively low.
The content of the invention：
The technical problems to be solved by the invention are the defect for overcoming prior art, it is further proposed that a kind of online three roller
The laminating big flooring method of belt lock catch.
The technical problems to be solved by the invention are realized using following technical scheme.
A kind of online three rollers laminating big flooring method of belt lock catch, it is characterised in that：Mainly include mixing process, extrusion
Process and laminating process；
Mixing process, required raw material components and group component are：
Above each group component sum meets 100%；
Mixing process：The step of including feeding, high pressure batch mixing, wherein feeding is that above-mentioned raw materials are proportionally added into elevating hopper
Interior, the temperature of high pressure batch mixing is 100-135 DEG C, and the time of high pressure batch mixing is 15-20 minutes；
Extrusion：Mixed material grain is transported to extruder, the machine barrel of extruder includes five areas, by feed end
To extruding end, the temperature in four areas is followed successively by 180-190 DEG C, 190-200 DEG C, 180-190 DEG C, 170-180 DEG C, 170-180 DEG C,
Pressure in 150 DEG C of merging core, the machine barrel connection vaccum-pumping equipment of extruder, machine barrel is 20MPa；Mold temperature 1-10 areas 180
DEG C, 190 DEG C of 11-12 areas, 150 DEG C of merging core；
Laminating process：Extruder is linked with three roller make-up machines, by extrusion sheet send into three roller make-up machine central rolls and lower roll it
Between, color film is then sent into sheet surface together with wearing layer and overlayed by high temperature progress fusion, three roll temperatures are followed successively by：Upper roller
70-80 DEG C, 80-90 DEG C of central roll, 90-100 DEG C of lower roll, extruded velocity 80-100cm/min.
Beneficial effect：The complicated technology fitted again before solving, fully achieves the online integration of extrusion laminating, maximum excellent
Point is to be overlayed color film and wearing layer fusion using temperature, and 100% without glue and substantially increases peel strength.
PVC stone-plastic plates and foamed board performance comparison
Embodiment：
In order that the technical means, the inventive features, the objects and the advantages of the present invention are easy to understand, tie below
Specific embodiment is closed, the present invention is expanded on further.
A kind of online three rollers laminating big flooring method of belt lock catch, mainly including mixing process, extrusion and laminating
Process；
Mixing process, required raw material components and group component are：
Above each group component sum meets 100%；
Mixing process：The step of including feeding, high pressure batch mixing, wherein feeding is that above-mentioned raw materials are proportionally added into elevating hopper
Interior, the temperature of high pressure batch mixing is 100-135 DEG C, and the time of high pressure batch mixing is 15-20 minutes；
Extrusion：Mixed material grain is transported to extruder, the machine barrel of extruder includes five areas, by feed end
To extruding end, the temperature in four areas is followed successively by 180-190 DEG C, 190-200 DEG C, 180-190 DEG C, 170-180 DEG C, 170-180 DEG C,
Pressure in 150 DEG C of merging core, the machine barrel connection vaccum-pumping equipment of extruder, machine barrel is 20MPa；Mold temperature 1-10 areas 180
DEG C, 190 DEG C of 11-12 areas, 150 DEG C of merging core；
Laminating process：Extruder is linked with three roller make-up machines, by extrusion sheet send into three roller make-up machine central rolls and lower roll it
Between, color film is then sent into sheet surface together with wearing layer and overlayed by high temperature progress fusion, three roll temperatures are followed successively by：Upper roller
70-80 DEG C, 80-90 DEG C of central roll, 90-100 DEG C of lower roll, extruded velocity 80-100cm/min.
It is preferred that 1：A kind of online three rollers laminating big flooring method of belt lock catch, mainly including mixing process, extrusion
With laminating process；
Mixing process, required raw material components and group component are：
Mixing process：The step of including feeding, high pressure batch mixing, wherein feeding is that above-mentioned raw materials are proportionally added into elevating hopper
Interior, the temperature of high pressure batch mixing is 100-135 DEG C, and the time of high pressure batch mixing is 15-20 minutes；
Extrusion：Mixed material grain is transported to extruder, the machine barrel of extruder includes five areas, by feed end
To extruding end, the temperature in four areas is followed successively by 180-190 DEG C, 190-200 DEG C, 180-190 DEG C, 170-180 DEG C, 170-180 DEG C,
Pressure in 150 DEG C of merging core, the machine barrel connection vaccum-pumping equipment of extruder, machine barrel is 20MPa；Mold temperature 1-10 areas 180
DEG C, 190 DEG C of 11-12 areas, 150 DEG C of merging core；
Laminating process：Extruder is linked with three roller make-up machines, by extrusion sheet send into three roller make-up machine central rolls and lower roll it
Between, color film is then sent into sheet surface together with wearing layer and overlayed by high temperature progress fusion, three roll temperatures are followed successively by：Upper roller
70-80 DEG C, 80-90 DEG C of central roll, 90-100 DEG C of lower roll, extruded velocity 80-100cm/min.
It is preferred that 2：A kind of online three rollers laminating big flooring method of belt lock catch, mainly including mixing process, extrusion
With laminating process；
Mixing process, required raw material components and group component are：
Mixing process：The step of including feeding, high pressure batch mixing, wherein feeding is that above-mentioned raw materials are proportionally added into elevating hopper
Interior, the temperature of high pressure batch mixing is 100-135 DEG C, and the time of high pressure batch mixing is 15-20 minutes；
Extrusion：Mixed material grain is transported to extruder, the machine barrel of extruder includes five areas, by feed end
To extruding end, the temperature in four areas is followed successively by 180-190 DEG C, 190-200 DEG C, 180-190 DEG C, 170-180 DEG C, 170-180 DEG C,
Pressure in 150 DEG C of merging core, the machine barrel connection vaccum-pumping equipment of extruder, machine barrel is 20MPa；Mold temperature 1-10 areas 180
DEG C, 190 DEG C of 11-12 areas, 150 DEG C of merging core；
Laminating process：Extruder is linked with three roller make-up machines, by extrusion sheet send into three roller make-up machine central rolls and lower roll it
Between, color film is then sent into sheet surface together with wearing layer and overlayed by high temperature progress fusion, three roll temperatures are followed successively by：Upper roller
70-80 DEG C, 80-90 DEG C of central roll, 90-100 DEG C of lower roll, extruded velocity 80-100cm/min.
General principle, principal character and the advantages of the present invention of the present invention has been shown and described above.The skill of the industry
Art personnel are it should be appreciated that the present invention is not limited to the above embodiments, and described in above-described embodiment and specification is explanation
The principle of the present invention, without departing from the spirit and scope of the present invention, various changes and modifications of the present invention are possible, these
Changes and improvements all fall within the protetion scope of the claimed invention.The claimed scope of the invention by appended claims and
Its equivalent thereof.
Claims (1)
1. a kind of online three rollers laminating big flooring method of belt lock catch, it is characterised in that：Mainly include mixing process, extruded
Journey and laminating process；
Mixing process, required raw material components and group component are：
Above each group component sum meets 100%；
Mixing process：The step of including feeding, high pressure batch mixing, wherein feeding is that above-mentioned raw materials are proportionally added into elevating hopper,
The temperature of high pressure batch mixing is 100-135 DEG C, and the time of high pressure batch mixing is 15-20 minutes；
Extrusion：Mixed material grain is transported to extruder, the machine barrel of extruder includes five areas, from feed end to squeezing
Go out end, the temperature in four areas is followed successively by 180-190 DEG C, 190-200 DEG C, 180-190 DEG C, 170-180 DEG C, 170-180 DEG C, interflow
Pressure in 150 DEG C of core, the machine barrel connection vaccum-pumping equipment of extruder, machine barrel is 20MPa；180 DEG C of mold temperature 1-10 areas,
190 DEG C of 11-12 areas, 150 DEG C of merging core；
Laminating process：Extruder is linked with three roller make-up machines, extrusion sheet is sent between three roller make-up machine central rolls and lower roll, so
Color film is sent into sheet surface together with wearing layer afterwards to overlay by high temperature progress fusion, three roll temperatures are followed successively by：Upper roller 70-80
DEG C, 80-90 DEG C of central roll, 90-100 DEG C of lower roll, extruded velocity 80-100cm/min.