CN107044247A - 一种吸音门 - Google Patents

一种吸音门 Download PDF

Info

Publication number
CN107044247A
CN107044247A CN201710295116.6A CN201710295116A CN107044247A CN 107044247 A CN107044247 A CN 107044247A CN 201710295116 A CN201710295116 A CN 201710295116A CN 107044247 A CN107044247 A CN 107044247A
Authority
CN
China
Prior art keywords
door
plate
al2o3
sound
zsm
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201710295116.6A
Other languages
English (en)
Other versions
CN107044247B (zh
Inventor
刘志伟
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Sichuan LONGSHANG Wood Industry Co., Ltd
Original Assignee
Changle Net Able New Mstar Technology Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Changle Net Able New Mstar Technology Ltd filed Critical Changle Net Able New Mstar Technology Ltd
Priority to CN201710295116.6A priority Critical patent/CN107044247B/zh
Publication of CN107044247A publication Critical patent/CN107044247A/zh
Application granted granted Critical
Publication of CN107044247B publication Critical patent/CN107044247B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种吸音门,包括门前板、门后板以及中间板,所述的中间板包括框架以及安装在框架里的吸音板,所述的门前板表面均匀排布有圆形凹槽。本发明由门前板、门后板以及中间板,门前板表面均匀排布有圆形凹槽,吸纳声波效果好,其次具有吸音板,吸音板由特殊工艺制备的NiO‑ZSM‑5/γ‑Al2O3制备而成,吸音系数能达到0.96,使得整个门的吸音效果十分显著,综合吸音系数达到0.99。

Description

一种吸音门
技术领域
[0001] 本发明涉及一种吸音门,属于日常生活领域。
背景技术
[0002] 在人们的生活和工作中,经常需要独立或私密的空间,例如办公、会议或休息等所 需要的场所,因此房间的隔音效果就显得非常重要。在室内采用隔音材料是一种降低噪音 污染的有效手段,目前市场上出售的房间门大多有经过隔音处理,具备一定的隔音功能,但 是当遇到音响声音较大时,或者与门有一定接触以及产生震动时,其隔音效果就比较差,这 样会给周围的人造成影响。因此,如何开发一种具有优异隔音效果的房间门是所要解决的 问题。
发明内容
[0003] 针对上述现有技术存在的问题,本发明提供一种吸音门,吸音效果好。
[0004] 为了实现上述目的,本发明采用的技术方案是:一种吸音门,包括门前板、门后板 以及中间板,所述的中间板包括框架以及安装在框架里的吸音板,所述的门前板表面均匀 排布有圆形凹槽。
[0005] 门前板还安装有门把手。
[0006] 所述的吸音板由改性Ni〇-ZSM-5/ γ -A1203材料制备组成。
[0007] 本发明由门前板、门后板以及中间板,门前板表面均匀排布有圆形凹槽,吸纳声波 效果好,其次具有吸音板,吸音板由特殊工艺制备的Ni0-ZSM-5/y-A1203制备而成,吸音系 数能达到0.96,使得整个门的吸音效果十分显著,综合吸音系数达到0.99。
附图说明
[0008] 图1是本发明的示意图。
[0009] 1、门前板,2、门后板,3、框架,4、吸音板,5、门把手。
具体实施方式
[0010] 下面结合附图和实施例对本发明作进一步说明。
[0011] —种吸音门,包括门前板1、门后板2以及中间板,所述的中间板包括框架3以及安 装在框架里的吸音板4,所述的门前板表面均匀排布有圆形凹槽。
[0012] 门前板还安装有门把手5。
[0013] 所述的吸音板由改性Ni〇-ZSM-5/ γ -A1203材料制备组成。
[0014] 本发明由门前板、门后板以及中间板,门前板表面均匀排布有圆形凹槽,吸纳声波 效果好,其次具有吸音板,吸音板由特殊工艺制备的分子筛制备而成,吸音系数能达到 〇. 96,使得整个门的吸音效果十分显著,综合吸音系数达到0.99。
[0015] 改性Ni〇-ZSM-5/ γ -Α1203材料制备方法如下:
[0016] 实施例I
[0017] γ-Α1203:硝酸镍:异丙醇铝的质量比为=4:1:2时,88丫41203,28硝酸镍,48异 丙醇铝;
[0018] 步骤1、首先将γ-Α1203,硝酸镍,15ml 2mol/L氢氧化钠,15ml无水乙醇在超声波 震荡下90°C油浴超声2h除杂;
[0019] 步骤2、将IOml硅溶胶,异丙醇铝,200ml去离子水,7ml液体模板剂三乙胺在超声波 震荡水浴90°C2h除杂;
[0020] 步骤3、将硅溶胶滴加到烧瓶中,然后滴加去离子水,无水乙醇,氢氧化钠以每分钟 20滴速度滴加,并同时磁力搅拌油浴加热3h;
[0021] 步骤4、将异丙醇铝加到上述溶液中,然后在滴加模板剂三乙胺以每分钟30滴速度 滴加,在滴加同时进行磁力搅拌油浴加热80 °C 2h;
[0022] 步骤6、将γ -A1203加入到上述溶液中,在磁力搅拌油浴加热90°C3h制成凝胶液;
[0023] 步骤7、将凝胶液在空气中老化12h;
[0024] 步骤8、将凝胶液通过引流器倒入聚四氟乙烯为内衬的反应釜中,然后将反应釜放 入到微波反应器中以l〇kap/min的速度升压到230kpa,温度以12°C/min的速度升至150°C, 在氦气氛围下晶化12h;
[0025] 步骤9、然后在离心分离机下离心分离,干燥,最后在马弗炉中第一次预烧,在45 % C02+55%N2气氛下,时间为30分钟,温度500°C,然后第二次预烧时间为60分钟,N2气氛下, 温度大约700°C,负压0.05MPa,最后第三次预烧,时间为50分钟,温度600°(:,0.0510^,在 30 % Ar+30 % C02+40 % CO气氛下;
[0026] 得到改性25]\1-5/丫41203材料;
[0027] 步骤10、将硝酸镍溶解在去离子水中,通过浸渍法,将制得的改性ZSM-5/ γ -A120 材料浸渍在硝酸镍溶液里磁力搅拌油浴加热90°C4h,空气中静置12h后,放入旋转蒸发器中 90 °C下真空旋蒸至水分蒸干,得到的材料前躯体在电热鼓风干燥箱中110 °C下干燥2h;
[0028] 步骤11、最后在马弗炉中充足空气氛围下煅烧9h,得到Ni〇-ZSM-5/ γ -A1203材料。
[0029] 实施例2
[0030] 制备方法与实施例1相同;不同之处在于,γ_Α1203:硝酸镍:异丙醇铝的质量比为 =4:3:2,8g γ -Α1203,6g硝酸镍,4g异丙醇铝。
[0031] 实施例3
[0032] 制备方法与实施例1相同;不同之处在于,T-A1203:硝酸镍:异丙醇铝的质量比为 =4:1:3,8g γ -六1203,28硝酸镍,68异丙醇错。
[0033] 实施例4
[0034] 制备方法与实施例1相同;不同之处在于,γ-Α1203:硝酸镍:异丙醇铝的质量比为 =5:1:2,IOg γ -Α1203,2g硝酸镍,4g异丙醇铝。
[0035] 实施例5
[0036] 制备方法与实施例1相同;不同之处在于,γ-Α1203:硝酸镍:异丙醇铝的质量比为 =4:1:4,8g γ -Α1203,2g硝酸镍,8g异丙醇铝。
[0037] 实施例6
[0038] 制备方法与实施例1相同;不同之处在于,T-A1203:硝酸镍:异丙醇铝的质量比为 =2:1:2,4g γ -A1203,2g硝酸镍,4g异丙醇铝。
[0039] 实施例7
[0040] 制备方法与实施例1相同;不同之处在于,γ-Α1203:硝酸镍:异丙醇铝的质量比为 =1:1:1,4g γ -Α1203,24g硝酸镍,4g异丙醇铝。
[0041] 实施例8
[0042] 制备方法与实施例1相同;不同之处在于,γ-Α1203:硝酸镍:异丙醇铝的质量比为 =3:1:2,6g γ -Α1203,2g硝酸镍,4g异丙醇铝。
[0043] 对比例2 γ-Al203:硝酸镍:异丙醇铝的质量比为=4:1:2时,8gy-Al203,2g硝酸 镍,4g异丙醇铝,步骤1、首先将γ_Α1203,硝酸镍,15ml 2mol/L氢氧化钠,15ml无水乙醇在 超声波震荡下90°C油浴超声2h除杂;
[0044] 步骤2、将IOml硅溶胶,异丙醇铝,200ml去离子水,7ml液体模板剂三乙胺在超声波 震荡水浴90°C2h除杂;
[0045] 步骤3、将硅溶胶滴加到烧瓶中,然后滴加去离子水,无水乙醇,氢氧化钠以每分钟 20滴速度滴加,并同时搅拌油浴加热3h;
[0046] 步骤4、将异丙醇铝加到上述溶液中,然后在滴加模板剂三乙胺以每分钟30滴速度 滴加,在滴加同时进行磁力搅拌油浴加热80 °C 2h;
[0047] 步骤6、将γ -A1203加入到上述溶液中,在磁力搅拌油浴加热90°C3h制成凝胶液;
[0048] 步骤7、将凝胶液在空气中老化12h;
[0049] 步骤8、将凝胶液通过引流器倒入聚四氟乙烯为内衬的反应釜中,然后将反应釜放 入到微波反应器中以l〇kap/min的速度升压到230kpa,温度以12°C/min的速度升至150°C, 在氦气氛围下晶化12h;
[0050] 步骤9、然后在离心分离机下离心分离,干燥,最后在马弗炉中第一次预烧,在45 % ⑶2+55%N2气氛下,时间为30分钟,温度500°C,然后第二次预烧时间为60分钟,温度大约 700°C,负压0.05MPa,最后第三次预烧,时间为50分钟,温度600°C,0.05MPa,在30 %Ar+30% C02+40%C0 气氛下;
[0051] 得到改性25]\1-5/丫41203材料;
[0052] 步骤10、将硝酸镍溶解在去离子水中,通过浸渍法,将制得的ZSM-5/ γ -A120材料 浸渍在硝酸镍溶液里搅拌油浴加热90 °C4h,空气中静置12h后,放入旋转蒸发器中90°C下真 空旋蒸至水分蒸干,得到的材料前躯体在电热鼓风干燥箱中11〇 °C下干燥2h;
[0053] 步骤11、最后在马弗炉中充足空气氛围下煅烧9h,得到Ni〇-ZSM-5/ γ -A1203材料。
[0054] 对比例2 γ -Α1203:异丙醇铝的质量比为=4:2时,8g γ -Α1203,4g异丙醇铝,
[0055] 步骤1、首先将y-A1203,15ml 2mol/L氢氧化钠,15ml无水乙醇在超声波震荡下90 °(:油浴超声2h除杂;
[0056] 步骤2、将IOml硅溶胶,异丙醇铝,200ml去离子水,7ml液体模板剂三乙胺在超声波 震荡水浴90°C2h除杂;
[0057] 步骤3、将硅溶胶滴加到烧瓶中,然后滴加去离子水,无水乙醇,氢氧化钠以每分钟 20滴速度滴加,并同时搅拌油浴加热3h;
[0058] 步骤4、将异丙醇铝加到上述溶液中,然后在滴加模板剂三乙胺以每分钟30滴速度 滴加,在滴加同时进行磁力搅拌油浴加热80 °C 2h;
[0059] 步骤6、将γ -A1203加入到上述溶液中,在磁力搅拌油浴加热90°C3h制成凝胶液;
[0060] 步骤7、将凝胶液在空气中老化12h;
[0061] 步骤8、将凝胶液通过引流器倒入聚四氟乙烯为内衬的反应釜中,然后将反应釜放 入到微波反应器中以l〇kap/min的速度升压到230kpa,温度以12°C/min的速度升至150°C, 在氦气氛围下晶化12h;
[0062] 步骤9、然后在离心分离机下离心分离,干燥,最后在马弗炉中充足空气氛围下煅 烧9h,得到ZSM-5/ γ -A1203材料。
[0063] 对比例3: γ-Α1203:硝酸镍:异丙醇铝的质量比为=4:1:2时,88丫41203,28硝酸 镍,4g异丙醇铝;步骤1、首先将γ_Α1203,硝酸镍,15ml 2mol/L氢氧化钠,15ml无水乙醇在 超声波震荡下90°C油浴超声2h除杂;
[0064] 步骤2、将IOml硅溶胶,异丙醇铝,200ml去离子水,7ml液体模板剂三乙胺在超声波 震荡水浴90°C2h除杂;
[0065] 步骤3、将硅溶胶滴加到烧瓶中,然后滴加去离子水,无水乙醇,氢氧化钠以每分钟 20滴速度滴加,并同时磁力搅拌油浴加热3h;
[0066] 步骤4、将异丙醇铝加到上述溶液中,然后在滴加模板剂三乙胺以每分钟30滴速度 滴加,在滴加同时进行磁力搅拌油浴加热80 °C 2h;
[0067] 步骤6、将γ -A1203加入到上述溶液中,在磁力搅拌油浴加热90°C3h制成凝胶液;
[0068] 步骤7、将凝胶液在空气中老化12h;
[0069] 步骤8、将凝胶液通过引流器倒入聚四氟乙烯为内衬的反应釜中,然后将反应釜放 入到微波反应器中以l〇kap/min的速度升压到230kpa,温度以12°C/min的速度升至150°C, 在氦气氛围下晶化12h;
[0070] 步骤9、然后在离心分离机下离心分离,干燥,最后在马弗炉中煅烧得到ZSM-5/ γ -Al 203材料;
[0071] 步骤10、将硝酸镍溶解在去离子水中,通过浸渍法,将制得的ZSM-5/ γ -A120材料 浸渍在硝酸镍溶液里磁力搅拌油浴加热90 °C4h,空气中静置12h后,放入旋转蒸发器中90°C 下真空旋蒸至水分蒸干,得到的材料前躯体在电热鼓风干燥箱中110 °C下干燥2h;
[0072] 步骤11、最后在马弗炉中充足空气氛围下煅烧9h,得到Ni〇-ZSM-5/ γ -A1203材料。
[0073] 试验对比:
[0074] 参照国标85-85,驻波管吸音系数与声阻率测量规范,测试试样的驻波管吸音系 数。
[0075] 测试吸音板均制成厚度1厘米的板状结构。
Figure CN107044247AD00061
Figure CN107044247AD00071
[0077]可见实施例1制备的材料相对于其他组别具有非常好的吸音效果,大大提高了整 个门的吸音效果,可见制备过程中的γ_Α1203:硝酸镍:异丙醇铝的质量比,磁性搅拌、以及 预烧的气体氛围等因素对于制备出来材料的吸音起到促进的作用。

Claims (4)

1. 一种吸音门,包括门前板、门后板以及中间板,所述的中间板包括框架以及安装在框 架里的吸音板,所述的门前板表面均匀排布有圆形凹槽。
2. 根据权利要求1所述的一种吸音门,其特征在于,门前板还安装有门把手。
3. 根据权利要求1所述的一种吸音门,其特征在于,所述的吸音板由改性M0-ZSM-5/ γ-Al203材料制备组成。
4. 根据权利要求3所述的一种吸音门,其特征在于,所述的改性Ni〇-ZSM-5/ γ -A1203材 料制备工艺保罗: 步骤1、首先将γ_Α1203,硝酸镍,氢氧化钠,无水乙醇在超声波震荡下90°C油浴超声除 杂; 步骤2、将硅溶胶,异丙醇铝,去离子水,液体模板剂三乙胺在超声波震荡水浴90°C除 杂; 步骤3、将硅溶胶滴加到烧瓶中,然后滴加去离子水,无水乙醇,氢氧化钠以每分钟20滴 速度滴加,并同时磁力搅拌油浴加热; 步骤4、将异丙醇铝加到上述溶液中,然后在滴加模板剂三乙胺以每分钟30滴速度滴 加,在滴加同时进行磁力搅拌油浴加热; 步骤6、将γ -Al203加入到上述溶液中,在磁力搅拌油浴加热制成凝胶液; 步骤7、将凝胶液在空气中老化12h; 步骤8、将凝胶液通过引流器倒入聚四氟乙烯为内衬的反应釜中,然后将反应釜放入到 微波反应器中以l〇kap/min的速度升压到230kpa,温度以12°C/min的速度升至150°C,在氦 气氛围下晶化12h; 步骤9、然后在离心分离机下离心分离,干燥,最后在马弗炉中预烧; 得到改性ZSM-5/ γ -A1203材料; 步骤10、将硝酸镍溶解在去离子水中,通过浸渍法,将制得的改性ZSM-5/ γ -Α120材料 浸渍在硝酸镍溶液里磁力搅拌油浴加热空气中静置12h后,放入旋转蒸发器中90°C下真空 旋蒸至水分蒸干,得到的材料前躯体在电热鼓风干燥箱中11〇 °C下干燥2h; 步骤11、最后在马弗炉中充足空气氛围下煅烧9h,得到Ni〇-ZSM-5/ γ -A1203材料。
CN201710295116.6A 2017-04-28 2017-04-28 一种吸音门 Active CN107044247B (zh)