CN107035084A - The manufacture craft of the microballoon foaming Noctilucent decoration material of building interior trim - Google Patents

The manufacture craft of the microballoon foaming Noctilucent decoration material of building interior trim Download PDF

Info

Publication number
CN107035084A
CN107035084A CN201610914289.7A CN201610914289A CN107035084A CN 107035084 A CN107035084 A CN 107035084A CN 201610914289 A CN201610914289 A CN 201610914289A CN 107035084 A CN107035084 A CN 107035084A
Authority
CN
China
Prior art keywords
microballoon
interior trim
noctilucent
decoration material
noctilucence
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610914289.7A
Other languages
Chinese (zh)
Inventor
孙晋生
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Xuzhou Casting Biological Technology Co Ltd
Original Assignee
Xuzhou Casting Biological Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Xuzhou Casting Biological Technology Co Ltd filed Critical Xuzhou Casting Biological Technology Co Ltd
Priority to CN201610914289.7A priority Critical patent/CN107035084A/en
Publication of CN107035084A publication Critical patent/CN107035084A/en
Pending legal-status Critical Current

Abstract

A kind of manufacture craft for the Noctilucent decoration material that foamed the invention discloses microballoon for building interior trim, there is body paper production, Silk Procossing, bonding, application and microballoon foaming, press polish, noctilucence masking liquid to prepare and spray and shear step for it, final that the microballoon foaming Noctilucent decoration material for business club building interior trim being made up of original paper layer, silk layer, microballoon foamed material layer and noctilucence painting liquid layer is made.The manufacture craft cost of microballoon foaming Noctilucent decoration material of the present invention is relatively low, technique is easy, and be combined to improve interior trim class, physical strength and usage cycles with antibacterial body paper by silk fabrics first, pass through the application of noctilucence masking liquid, substantially increase the light illumination of building interior trim, advantage with energy-conserving and environment-protective, and compared with commercially available interior material, its flexible anti-tensile degree, bursting strength, environmental protection grade, antibacterial and mouldproof grade, life cycle and full moon noctilucence illumination are respectively provided with significant advantage.

Description

The manufacture craft of the microballoon foaming Noctilucent decoration material of building interior trim
Technical field
The present invention relates to building interior trim decoration material field, and in particular to the microballoon for business club building interior trim foams The manufacture craft of Noctilucent decoration material.
Background technology
At present, further abundant with material life, people are to shelter and consumption place such as club, KTV boxes, meeting The environmental requirement in the Room etc. is also significantly improved, and environmental-protecting performance, anti-microbial property, intensity and endurance quality, the dress of interior trim are embodied in emphatically Adorn in terms of class and light illumination, it is not enough yet with existing interior material one side antibacterial and mouldproof performance, on the one hand fill Decorations class is difficult to satisfactory to both parties, generally existing performance defect with Costco Wholesale.In addition, existing consumption place for example club, KTV boxes, Conference hall etc. in the presence of needing powerful lighting apparatus to improve the phenomenon of indoor light illumination, which greatly enhances electric energy into This, thus the use of high-power illumination equipment is reduced, it is a great problem urgently to be resolved hurrily to save the energy.
The content of the invention
The invention aims to provide, a kind of cost is relatively low, technique is easy, disclosure satisfy that client's performance requirement and section About the energy for business club building interior trim microballoon foam Noctilucent decoration material manufacture craft.
The purpose of the present invention is achieved through the following technical solutions（All numbers referred to, percentage composition are equal in specification To be calculated by mass）：A kind of manufacture craft of microballoon foaming Noctilucent decoration material for business club building interior trim, processing step It is rapid as follows：
（1）Body paper is produced：Using true qualities silver-containing antibacterial needle-leaved wood fibre material as raw material, wet method is manufactured paper with pulp on drainage cartridge type paper machine Without vertically and horizontally poor body paper, the wherein quantification of 70-80g/m of body paper2；
（2）Silk Procossing：Using antibacterial filamentary silver and waxy luster staple as raw material, using the silk face of Suzhou embroidery gimmick formation plover grid pattern Material, wherein the weight accounting of antibacterial filamentary silver are 5-10wt%；
（3）Bonding：Using environment-friendly adhesive by step（2）In silk fabrics be bonded in step（1）In body paper surface, formed Quantification of 90-100g/m2Substrate layer；
（4）Apply and microballoon foaming：Microballoon expanded material is applied to step（3）In base material layer surface, and use infrared ray Drying system carries out coated and dried foaming, forms microballoon foamed material layer, and the microballoon expanded material is the hair of island type structure Foam material, wherein island are that the modeling spherical particle and silica gel particle of organic alkane formation are mixed, and sea is Lauxite and trimerization The thermo-plastic mixture of melamine resin formation；
（5）Press polish：Soft calendaring is carried out to foamed material layer using paper calender roll, makes its surface uniform ground, is easy to following process；
（6）Noctilucence masking liquid is prepared：Epoxy resin is added in stirred tank and acrylate is stirred mixing, is continuously added Glass microballoon and wax, are warming up to after 50-60 DEG C and are stirred 40-60min with magnetic rotor, further add noctilucent powder, It is sufficiently mixed, adds the noctilucence masking liquid for forming that solid content is 15-25% after solvent；
（7）Spraying：By step（6）In noctilucence masking liquid dilution thicken after applied using high-pressure atomization paint finishing to step（5） Sheet surface after press polish, forms the microballoon foaming Noctilucent decoration material that liquid layer is applied containing noctilucence after drying；
（8）Shearing：According to required specification, by step（7）In microballoon foaming Noctilucent decoration material tailoring shearing after be used as business The interior trim of club building.
The step（1）In true qualities silver-containing antibacterial needle-leaved wood fibre material in silver content be 2wt%.
The step（1）In the quantification of 75g/m of body paper2。
The step（2）In antibacterial filamentary silver weight accounting be 8wt%.
The step（3）In environment-friendly adhesive be the natural gum that boils of glutinous rice.
The step（3）The quantification of 95g/m of substrate layer of middle formation2。
The step（4）In microballoon expanded material average particulate diameter be 20-30 μm, meso-position radius be 25 μm, foaming Temperature is 160-180 DEG C, and foamed time is 2-4h.
The step（6）In noctilucence masking liquid composition be：30 parts of epoxy resin, 40 parts of acrylic resin, glass microballoon 20 Part, 10 parts of wax, 15 parts of noctilucent powder, solvent is enough.
The step（6）In warming temperature be 55 DEG C, magnetic rotor mixing time be 50min, noctilucence apply fluid solid content For 20%.
The quantification of 110-130g/m of obtained microballoon foaming Noctilucent decoration material2, flexible anti-tensile degree is 16.5- 18.5kN/m, bursting strength is 580-680kPa, and environmental protection grade is E0Level, antibacterial and mouldproof grade is excellent, and life cycle reaches 7-9 Year, full moon noctilucence illumination is 4.5-6.5 luxs.
The present invention has the following advantages that compared with prior art：Cost is relatively low, and technique is easy, and first by silk fabrics It is combined to improve interior trim class, physical strength and usage cycles with antibacterial body paper, by the application of noctilucence masking liquid, greatly improves The light illumination of building interior trim, the advantage with energy-conserving and environment-protective, and compared with commercially available interior material is its flexible anti-tensile degree, resistance to Broken degree, environmental protection grade, antibacterial and mouldproof grade, life cycle and full moon noctilucence illumination are respectively provided with significant advantage.
Embodiment：
In order to deepen the understanding of the present invention, below in conjunction with embodiment, the invention will be further described, and the embodiment is only used In explaining the present invention, it is not intended to limit the scope of the present invention..
A kind of manufacture craft of microballoon foaming Noctilucent decoration material for business club building interior trim, procedure of processing is such as Under：
（1）Body paper is produced：Using true qualities silver-containing antibacterial needle-leaved wood fibre material as raw material, wet method is manufactured paper with pulp on drainage cartridge type paper machine Without vertically and horizontally poor body paper, the wherein quantification of 70-80g/m of body paper2；
（2）Silk Procossing：Using antibacterial filamentary silver and waxy luster staple as raw material, using the silk face of Suzhou embroidery gimmick formation plover grid pattern Material, wherein the weight accounting of antibacterial filamentary silver are 5-10wt%；
（3）Bonding：Using environment-friendly adhesive by step（2）In silk fabrics be bonded in step（1）In body paper surface, formed Quantification of 90-100g/m2Substrate layer；
（4）Apply and microballoon foaming：Microballoon expanded material is applied to step（3）In base material layer surface, and use infrared ray Drying system carries out coated and dried foaming, forms microballoon foamed material layer, and the microballoon expanded material is the hair of island type structure Foam material, wherein island are that the modeling spherical particle and silica gel particle of organic alkane formation are mixed, and sea is Lauxite and trimerization The thermo-plastic mixture of melamine resin formation；
（5）Press polish：Soft calendaring is carried out to foamed material layer using paper calender roll, makes its surface uniform ground, is easy to following process；
（6）Noctilucence masking liquid is prepared：Epoxy resin is added in stirred tank and acrylate is stirred mixing, is continuously added Glass microballoon and wax, are warming up to after 50-60 DEG C and are stirred 40-60min with magnetic rotor, further add noctilucent powder, It is sufficiently mixed, adds the noctilucence masking liquid for forming that solid content is 15-25% after solvent；
（7）Spraying：By step（6）In noctilucence masking liquid dilution thicken after applied using high-pressure atomization paint finishing to step（5） Sheet surface after press polish, forms the microballoon foaming Noctilucent decoration material that liquid layer is applied containing noctilucence after drying；
（8）Shearing：According to required specification, by step（7）In microballoon foaming Noctilucent decoration material tailoring shearing after be used as business The interior trim of club building.
The step（1）In true qualities silver-containing antibacterial needle-leaved wood fibre material in silver content be 2wt%.
The step（1）In the quantification of 75g/m of body paper2。
The step（2）In antibacterial filamentary silver weight accounting be 8wt%.
The step（3）In environment-friendly adhesive be the natural gum that boils of glutinous rice.
The step（3）The quantification of 95g/m of substrate layer of middle formation2。
The step（4）In microballoon expanded material average particulate diameter be 20-30 μm, meso-position radius be 25 μm, foaming Temperature is 160-180 DEG C, and foamed time is 2-4h.
The step（6）In noctilucence masking liquid composition be：30 parts of epoxy resin, 40 parts of acrylic resin, glass microballoon 20 Part, 10 parts of wax, 15 parts of noctilucent powder, solvent is enough.
The step（6）In warming temperature be 55 DEG C, magnetic rotor mixing time be 50min, noctilucence apply fluid solid content For 20%.
The quantification of 110-130g/m of obtained microballoon foaming Noctilucent decoration material2, flexible anti-tensile degree is 16.5- 18.5kN/m, bursting strength is 580-680kPa, and environmental protection grade is E0Level, antibacterial and mouldproof grade is excellent, and life cycle reaches 7-9 Year, full moon noctilucence illumination is 4.5-6.5 luxs.
Embodiment 1
A kind of manufacture craft of microballoon foaming Noctilucent decoration material for business club building interior trim, procedure of processing is as follows：
（1）Body paper is produced：Using true qualities argentiferous 2wt% antibacterial needle-leaved wood fibre materials as raw material, the wet method on drainage cartridge type paper machine Manufacture paper with pulp without vertically and horizontally poor body paper, the wherein quantification of 70g/m of body paper2；
（2）Silk Procossing：Using antibacterial filamentary silver and waxy luster staple as raw material, using the silk face of Suzhou embroidery gimmick formation plover grid pattern Material, wherein the weight accounting of antibacterial filamentary silver are 5wt%；
（3）Bonding：The natural gum boiled using glutinous rice is by step（2）In silk fabrics be bonded in step（1）In base paper sheet Face, forms quantification of 90g/m2Substrate layer；
（4）Apply and microballoon foaming：Microballoon expanded material is applied to step（3）In base material layer surface, and use infrared ray Drying system carries out coated and dried foaming, forms microballoon foamed material layer, and the microballoon expanded material is the hair of island type structure Foam material, wherein island are that the modeling spherical particle and silica gel particle of organic alkane formation are mixed, and sea is Lauxite and trimerization The thermo-plastic mixture of melamine resin formation, the average particulate diameter of the microballoon expanded material is 20-30 μm, and meso-position radius are 25 μ M, blowing temperature is 160 DEG C, and foamed time is 2h；
（5）Press polish：Soft calendaring is carried out to foamed material layer using paper calender roll, makes its surface uniform ground, is easy to following process；
（6）Noctilucence masking liquid is prepared：30 parts of epoxy resin is added in stirred tank and 40 parts of acrylate is stirred mixing, 10 parts of 20 parts of glass microballoon and wax are continuously added, 40min is stirred with magnetic rotor after being warming up to 50 DEG C, is further added 15 parts of noctilucent powder, is sufficiently mixed, and adds the noctilucence masking liquid for forming that solid content is 15% after sufficient solvent；
（7）Spraying：By step（6）In noctilucence masking liquid dilution thicken after applied using high-pressure atomization paint finishing to step（5） Sheet surface after press polish, forms the microballoon foaming Noctilucent decoration material that liquid layer is applied containing noctilucence after drying；
（8）Shearing：According to required specification, by step（7）In microballoon foaming Noctilucent decoration material tailoring shearing after be used as business The interior trim of club building.
The quantification of 110g/m of obtained microballoon foaming Noctilucent decoration material2, flexible anti-tensile degree is 16.5kN/m, resistance to broken Spend for 580kPa, environmental protection grade is E0Level, antibacterial and mouldproof grade is excellent, and life cycle was up to 7 years, and full moon noctilucence illumination is 4.5 Lux.
Embodiment 2
A kind of manufacture craft of microballoon foaming Noctilucent decoration material for business club building interior trim, procedure of processing is as follows：
（1）Body paper is produced：Using true qualities argentiferous 2wt% antibacterial needle-leaved wood fibre materials as raw material, the wet method on drainage cartridge type paper machine Manufacture paper with pulp without vertically and horizontally poor body paper, the wherein quantification of 75g/m of body paper2；
（2）Silk Procossing：Using antibacterial filamentary silver and waxy luster staple as raw material, using the silk face of Suzhou embroidery gimmick formation plover grid pattern Material, wherein the weight accounting of antibacterial filamentary silver are 8wt%；
（3）Bonding：The natural gum boiled using glutinous rice is by step（2）In silk fabrics be bonded in step（1）In base paper sheet Face, forms quantification of 95g/m2Substrate layer；
（4）Apply and microballoon foaming：Microballoon expanded material is applied to step（3）In base material layer surface, and use infrared ray Drying system carries out coated and dried foaming, forms microballoon foamed material layer, and the microballoon expanded material is the hair of island type structure Foam material, wherein island are that the modeling spherical particle and silica gel particle of organic alkane formation are mixed, and sea is Lauxite and trimerization The thermo-plastic mixture of melamine resin formation, the average particulate diameter of the microballoon expanded material is 20-30 μm, and meso-position radius are 25 μ M, blowing temperature is 170 DEG C, and foamed time is 3h；
（5）Press polish：Soft calendaring is carried out to foamed material layer using paper calender roll, makes its surface uniform ground, is easy to following process；
（6）Noctilucence masking liquid is prepared：30 parts of epoxy resin is added in stirred tank and 40 parts of acrylate is stirred mixing, 10 parts of 20 parts of glass microballoon and wax are continuously added, 50min is stirred with magnetic rotor after being warming up to 55 DEG C, is further added 15 parts of noctilucent powder, is sufficiently mixed, and adds the noctilucence masking liquid for forming that solid content is 20% after sufficient solvent；
（7）Spraying：By step（6）In noctilucence masking liquid dilution thicken after applied using high-pressure atomization paint finishing to step（5） Sheet surface after press polish, forms the microballoon foaming Noctilucent decoration material that liquid layer is applied containing noctilucence after drying；
（8）Shearing：According to required specification, by step（7）In microballoon foaming Noctilucent decoration material tailoring shearing after be used as business The interior trim of club building.
The quantification of 120g/m of obtained microballoon foaming Noctilucent decoration material2, flexible anti-tensile degree is 17.5kN/m, resistance to broken Spend for 630kPa, environmental protection grade is E0Level, antibacterial and mouldproof grade is excellent, and life cycle was up to 8 years, and full moon noctilucence illumination is 5.5 Lux.
Embodiment 3
A kind of manufacture craft of microballoon foaming Noctilucent decoration material for business club building interior trim, procedure of processing is as follows：
（1）Body paper is produced：Using true qualities argentiferous 2wt% antibacterial needle-leaved wood fibre materials as raw material, the wet method on drainage cartridge type paper machine Manufacture paper with pulp without vertically and horizontally poor body paper, the wherein quantification of 80g/m of body paper2；
（2）Silk Procossing：Using antibacterial filamentary silver and waxy luster staple as raw material, using the silk face of Suzhou embroidery gimmick formation plover grid pattern Material, wherein the weight accounting of antibacterial filamentary silver are 10wt%；
（3）Bonding：The natural gum boiled using glutinous rice is by step（2）In silk fabrics be bonded in step（1）In base paper sheet Face, forms quantification of 100g/m2Substrate layer；
（4）Apply and microballoon foaming：Microballoon expanded material is applied to step（3）In base material layer surface, and use infrared ray Drying system carries out coated and dried foaming, forms microballoon foamed material layer, and the microballoon expanded material is the hair of island type structure Foam material, wherein island are that the modeling spherical particle and silica gel particle of organic alkane formation are mixed, and sea is Lauxite and trimerization The thermo-plastic mixture of melamine resin formation, the average particulate diameter of the microballoon expanded material is 20-30 μm, and meso-position radius are 25 μ M, blowing temperature is 180 DEG C, and foamed time is 4h；
（5）Press polish：Soft calendaring is carried out to foamed material layer using paper calender roll, makes its surface uniform ground, is easy to following process；
（6）Noctilucence masking liquid is prepared：30 parts of epoxy resin is added in stirred tank and 40 parts of acrylate is stirred mixing, 10 parts of 20 parts of glass microballoon and wax are continuously added, 60min is stirred with magnetic rotor after being warming up to 60 DEG C, is further added 15 parts of noctilucent powder, is sufficiently mixed, and adds the noctilucence masking liquid for forming that solid content is 25% after sufficient solvent；
（7）Spraying：By step（6）In noctilucence masking liquid dilution thicken after applied using high-pressure atomization paint finishing to step（5） Sheet surface after press polish, forms the microballoon foaming Noctilucent decoration material that liquid layer is applied containing noctilucence after drying；
（8）Shearing：According to required specification, by step（7）In microballoon foaming Noctilucent decoration material tailoring shearing after be used as business The interior trim of club building.
The quantification of 130g/m of obtained microballoon foaming Noctilucent decoration material2, flexible anti-tensile degree is 18.5kN/m, resistance to broken Spend for 680kPa, environmental protection grade is E0Level, antibacterial and mouldproof grade is excellent, and life cycle was up to 9 years, and full moon noctilucence illumination is 6.5 Lux.
Microballoon foaming Noctilucent decoration material and the commercially available interior material performance comparison such as following table of the present invention：
Performance indications It is commercially available Embodiment 1 Embodiment 2 Embodiment 3
It is quantitative（g/m2） 120 110 120 130
Flexible anti-tensile degree（kN/m） 14.5 16.5 17.5 18.5
Bursting strength（kPa） 480 580 630 680
Environmental protection grade（Level） E1 E0 E0 E0
Antibacterial and mouldproof grade（Level） It is excellent It is excellent It is excellent It is excellent
Life cycle（Year） 5 7 8 9
Full moon noctilucence illumination（Tekes） 2.5 4.5 5.5 6.5
Note：Full moon noctilucence illumination refers to the light illumination after full moon environment next month light irradiation interior material in above table.
As shown above, its superior performance of the invention compared with commercially available interior material.It is mainly reflected in that cost is relatively low, technique Simplicity, and be combined to improve interior trim class, physical strength and usage cycles with antibacterial body paper by silk fabrics first, pass through night The application of light masking liquid, substantially increases the light illumination of building interior trim, the advantage with energy-conserving and environment-protective, and its flexible anti-tensile degree, Bursting strength, environmental protection grade, antibacterial and mouldproof grade, life cycle and full moon noctilucence illumination are respectively provided with significant advantage.
Above-mentioned embodiment is only the present invention preferably technical scheme, other any Spirit Essences without departing from the present invention With the change made under action principle, modification, replacement, combine, simplify, should be equivalent substitute mode, be included in this hair Within bright protection domain.

Claims (10)

  1. The manufacture craft of Noctilucent decoration material 1. a kind of microballoon for building interior trim foams, it is characterised in that procedure of processing is such as Under：
    （1）Body paper is produced：Using true qualities silver-containing antibacterial needle-leaved wood fibre material as raw material, wet method is manufactured paper with pulp on drainage cartridge type paper machine Without vertically and horizontally poor body paper, the wherein quantification of 70-80g/m of body paper2；
    （2）Silk Procossing：Using antibacterial filamentary silver and waxy luster staple as raw material, using the silk face of Suzhou embroidery gimmick formation plover grid pattern Material, wherein the weight accounting of antibacterial filamentary silver are 5-10wt% or so；
    （3）Bonding：Using environment-friendly adhesive by step（2）In silk fabrics be bonded in step（1）In body paper surface, formed Quantification of 90-100g/m2Substrate layer；
    （4）Apply and microballoon foaming：Microballoon expanded material is applied to step（3）In base material layer surface, and use infrared ray Drying system carries out coated and dried foaming, forms microballoon foamed material layer, and the microballoon expanded material is the hair of island type structure Foam material, wherein island are that the modeling spherical particle and silica gel particle of organic alkane formation are mixed, and sea is Lauxite and trimerization The thermo-plastic mixture of melamine resin formation；
    （5）Press polish：Soft calendaring is carried out to foamed material layer using paper calender roll, makes its surface uniform ground, is easy to following process；
    （6）Noctilucence masking liquid is prepared：Epoxy resin is added in stirred tank and acrylate is stirred mixing, is continuously added Glass microballoon and wax, are warming up to after 50-60 DEG C or so and are stirred 40-60min with magnetic rotor, further add luminescent powder End, is sufficiently mixed, and adds the noctilucence masking liquid for forming that solid content is 15-25% after solvent；
    （7）Spraying：By step（6）In noctilucence masking liquid dilution thicken after applied using high-pressure atomization paint finishing to step（5） Sheet surface after press polish, forms the microballoon foaming Noctilucent decoration material that liquid layer is applied containing noctilucence after drying；
    （8）Shearing：According to required specification, by step（7）In microballoon foaming Noctilucent decoration material tailoring shearing after be used as business The interior trim of club building.
  2. The manufacture craft of Noctilucent decoration material 2. a kind of microballoon for building interior trim according to claim 1 foams, its It is characterised by, step（1）In true qualities silver-containing antibacterial needle-leaved wood fibre material in silver content be about 2wt%.
  3. The manufacture craft of Noctilucent decoration material 3. a kind of microballoon for building interior trim according to claim 1 foams, its It is characterised by, step（1）In the quantification of 75g/m of body paper2。
  4. The manufacture craft of Noctilucent decoration material 4. a kind of microballoon for building interior trim according to claim 1 foams, its It is characterised by, step（2）In antibacterial filamentary silver weight accounting be 8wt%.
  5. The manufacture craft of Noctilucent decoration material 5. a kind of microballoon for building interior trim according to claim 1 foams, its It is characterised by, step（3）In environment-friendly adhesive be the natural gum that boils of glutinous rice.
  6. The manufacture craft of Noctilucent decoration material 6. a kind of microballoon for building interior trim according to claim 1 foams, its It is characterised by, step（3）The quantification of 95g/m of substrate layer of middle formation2。
  7. The making of Noctilucent decoration material 7. a kind of microballoon for business club building interior trim according to claim 1 foams Technique, it is characterised in that step（4）In microballoon expanded material average particulate diameter be 20-30 μm, meso-position radius be 25 μm, Blowing temperature is 160-180 DEG C, and foamed time is 2-4h.
  8. The manufacture craft of Noctilucent decoration material 8. a kind of microballoon for building interior trim according to claim 1 foams, its It is characterised by, step（6）In noctilucence masking liquid composition be：30 parts of epoxy resin, 40 parts of acrylic resin, 20 parts of glass microballoon, 10 parts of wax, 15 parts of noctilucent powder, solvent is enough.
  9. The manufacture craft of Noctilucent decoration material 9. a kind of microballoon for building interior trim according to claim 1 foams, its It is characterised by, step（6）In warming temperature be 55 DEG C, magnetic rotor mixing time be 50min, noctilucence apply fluid solid content be 20%。
  10. The system of Noctilucent decoration material 10. a kind of microballoon of institute's building interior trim according to any one of claim 1-9 foams Make technique, it is characterised in that the quantification of 110-130g/m of obtained microballoon foaming Noctilucent decoration material2, flexible anti-tensile degree is 16.5-18.5kN/m, bursting strength is 580-680kPa, and environmental protection grade is E0Level, antibacterial and mouldproof grade is excellent, and life cycle reaches 7-9, full moon noctilucence illumination is 4.5-6.5 luxs.
CN201610914289.7A 2016-10-20 2016-10-20 The manufacture craft of the microballoon foaming Noctilucent decoration material of building interior trim Pending CN107035084A (en)