CN107021684A - A kind of aging-resistant flame-proof clay for being used to bond stone material and composite - Google Patents
A kind of aging-resistant flame-proof clay for being used to bond stone material and composite Download PDFInfo
- Publication number
- CN107021684A CN107021684A CN201710350117.6A CN201710350117A CN107021684A CN 107021684 A CN107021684 A CN 107021684A CN 201710350117 A CN201710350117 A CN 201710350117A CN 107021684 A CN107021684 A CN 107021684A
- Authority
- CN
- China
- Prior art keywords
- parts
- component
- epoxy resin
- aging
- dry
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a kind of aging-resistant flame-proof clay for being used to bond stone material and composite, it is made up of the component of A, B, C tri-, according to the mass fraction, three components composition is as follows respectively：Component A：150 parts of cement, 20 parts of stone flour, 20 parts of iron sand；B component：20~30 parts of epoxy resin, A20 parts of dry-hang glue, diluent；C components：20~25 parts of curing agent, dry-hang glue B20~25 part.This is used for the aging-resistant flame-proof clay for bonding stone material and composite, and with good fire resistance, anti-aging, adhesive effect and good heat-insulation effect, intensity height, good toughness, cost durable in use are low.Raw material is cheap and easily-available, wide using scope, available for the repairing of building and ornament materials compound sticking, joint filling etc..Mechanical each field is can also be used for use.
Description
Technical field
It is more particularly to a kind of to be used to bond stone material and composite the present invention relates to stone material and composite bonding field
Aging-resistant flame-proof clay.
Background technology
Marble slabs quality is graceful, and texture is quaint and elegant attractive in appearance, frequently as building inner-outer wall, ground, ceiling, windowsill and
The finishing material of desktop, sanitary equipment.With the improvement and the lifting of artistic appreciation of people's living standard, this finishing material is used
Quantity is increasing.China rises with stone industries to go to the world with stone material product, the technology that marble is combined with base material
In rapid advances.But existing bonding cement slow curing, easy aging, easy firing, impact resistance is poor, and effect of heat insulation is poor, influence
Adhesive strength, does not meet environmental requirement, and plasticization effect is difficult to persistently, there is improved necessity really.
The content of the invention
Based on this, it is necessary to provide a kind of aging-resistant flame-proof clay for being used to bond stone material and composite.
A kind of aging-resistant flame-proof clay for being used to bond stone material and composite, is made up of the component of A, B, C tri-, by mass parts
Number meter, three components composition is as follows respectively：
Component A：
150 parts of cement, 20 parts of stone flour, 20 parts of iron sand；
B component：
20~30 parts of epoxy resin, A20 parts of dry-hang glue, diluent
C components：
20~25 parts of curing agent, dry-hang glue B20~25 part
Further, application method is：
(1) the husky separately storage of the cement of component A, building stones, iron, without using without diluent.
(2) epoxy resin of B component, dry-hang glue A, diluent are separately deposited, without using without curing agent and dry-hang glue
B；
(3) curing agent of C components and dry-hang glue B are separately deposited；
(4) the step of making the aging-resistant flame-proof clay be：The epoxy resin of B component and dry-hang glue A are mixed, then added
Enter the dry-hang glue B of C components and stir, then add the curing agent of C components, add component A and stir, be eventually adding dilution
Agent, stirs.
Further, the epoxy resin uses unmodified epoxy resin, polyurethane-modified epoxy resin or poly- third
One or more in the ester modified epoxy resin of olefin(e) acid.
Further, the diluent is epoxide resin reactive diluent or epoxy resin non-activated thinner, its middle ring
Oxygen resin reactive diluents include ethylene glycol diglycidylether, phenyl glycidyl ether, polypropylene glycol diglycidyl ether, benzyl
Base glycidol ether, o-tolyl glycidol ether or neopentylglycol diglycidyl ether；Epoxy resin non-activated thinner bag
Include dibutyl phthalate or dioctyl phthalate；The diluent uses one or more therein.
Further, the curing agent uses one kind in aliphatic modified amine, alicyclic modified amine or polyamide.
It is above-mentioned to be used to bond the aging-resistant flame-proof clay of stone material and composite, with good fire resistance, anti-aging,
Adhesive effect and good heat-insulation effect, intensity height, good toughness, cost durable in use are low.Raw material is cheap and easily-available, wide using scope, can
For the repairing of building and ornament materials compound sticking, joint filling etc..Mechanical each field is can also be used for use.
Embodiment
Presently preferred embodiments of the present invention is described in detail below so that advantages and features of the invention can be easier to by
It will be appreciated by those skilled in the art that apparent clearly being defined so as to be made to protection scope of the present invention.
The epoxy resin of the present invention uses unmodified epoxy resin, polyurethane-modified epoxy resin or polyacrylate
One or more in modified epoxy resin.Diluent is epoxide resin reactive diluent or epoxy resin inactive diluents
Agent, wherein epoxide resin reactive diluent include ethylene glycol diglycidylether, phenyl glycidyl ether, polypropylene glycol two and shunk
Glycerin ether, benzyl glycidyl ether, o-tolyl glycidol ether or neopentylglycol diglycidyl ether；Epoxy resin is nonactive
Diluent includes dibutyl phthalate or dioctyl phthalate；The diluent uses one or more therein.
Curing agent uses one kind in aliphatic modified amine, alicyclic modified amine or polyamide.
Cement in the present invention was used no more than 30 days dates of manufacture.
After testing, the epoxide equivalent of epoxy resin is 210-244g/mol, and softening point is 15-23 DEG C, and viscosity is 6-10 DEG C,
Easy saponification chlorine≤0.5%, 200≤mg/kg of inorganic chlorine, fugitive constituent≤1.0%, color and luster number 3≤.
Embodiment 1：
A kind of aging-resistant flame-proof clay for being used to bond stone material and composite, is made up of the component of A, B, C tri-, by mass parts
Number meter, three components composition is as follows respectively：
Component A：
150 parts of cement, 20 parts of stone flour, 20 parts of iron sand；
B component：
20~30 parts of epoxy resin, A20 parts of dry-hang glue, diluent
C components：
20 parts of curing agent, B20 parts of dry-hang glue
Further, application method is：
(1) the husky separately storage of the cement of component A, building stones, iron, without using without diluent.
(2) epoxy resin of B component, dry-hang glue A, diluent are separately deposited, without using without curing agent and dry-hang glue
B；
(3) curing agent of C components and dry-hang glue B are separately deposited；
(4) the step of making the aging-resistant flame-proof clay be：By mass fraction, by the epoxy resin of B component and dry-hang glue A
Mixing, is subsequently added into the dry-hang glue B of C components and stirs, and then adds the curing agent of C components, adds component A and stir, most
After add diluent, stir.
In the present embodiment, the component of A, B, C tri- carries out cooperation solidification with mass parts, starts solidification after 6~8 hours, 48 is small
When after be fully cured.
Embodiment 2：
A kind of aging-resistant flame-proof clay for being used to bond stone material and composite, is made up of the component of A, B, C tri-, by mass parts
Number meter, three components composition is as follows respectively：
Component A：
150 parts of cement, 20 parts of stone flour, 20 parts of iron sand；
B component：
20~30 parts of epoxy resin, A20 parts of dry-hang glue, diluent
C components：
22.5 parts of curing agent, B22.5 parts of dry-hang glue
Further, application method is：
(1) the husky separately storage of the cement of component A, building stones, iron, without using without diluent.
(2) epoxy resin of B component, dry-hang glue A, diluent are separately deposited, without using without curing agent and dry-hang glue
B；
(3) curing agent of C components and dry-hang glue B are separately deposited；
(4) the step of making the aging-resistant flame-proof clay be：By mass fraction, by the epoxy resin of B component and dry-hang glue A
Mixing, is subsequently added into the dry-hang glue B of C components and stirs, and then adds the curing agent of C components, adds component A and stir, most
After add diluent, stir.
In the present embodiment, the component of A, B, C tri- carries out cooperation solidification with mass parts, starts solidification after 6~8 hours, 48 is small
When after be fully cured.
Embodiment 3：
A kind of aging-resistant flame-proof clay for being used to bond stone material and composite, is made up of the component of A, B, C tri-, by mass parts
Number meter, three components composition is as follows respectively：
Component A：
150 parts of cement, 20 parts of stone flour, 20 parts of iron sand；
B component：
20~30 parts of epoxy resin, A20 parts of dry-hang glue, diluent
C components：
25 parts of curing agent, B25 parts of dry-hang glue
Further, application method is：
(1) the husky separately storage of the cement of component A, building stones, iron, without using without diluent.
(2) epoxy resin of B component, dry-hang glue A, diluent are separately deposited, without using without curing agent and dry-hang glue
B；
(3) curing agent of C components and dry-hang glue B are separately deposited；
(4) the step of making the aging-resistant flame-proof clay be：By mass fraction, by the epoxy resin of B component and dry-hang glue A
Mixing, is subsequently added into the dry-hang glue B of C components and stirs, and then adds the curing agent of C components, adds component A and stir, most
After add diluent, stir.
In the present embodiment, the component of A, B, C tri- carries out cooperation solidification with mass parts, starts solidification after 6~8 hours, 48 is small
When after be fully cured.
Embodiment described above only expresses the several embodiments of the present invention, and it describes more specific and detailed, but simultaneously
Therefore the limitation to the scope of the claims of the present invention can not be interpreted as.It should be pointed out that for one of ordinary skill in the art
For, without departing from the inventive concept of the premise, various modifications and improvements can be made, these belong to the guarantor of the present invention
Protect scope.Therefore, the protection domain of patent of the present invention should be determined by the appended claims.
Claims (5)
1. a kind of aging-resistant flame-proof clay for being used to bond stone material and composite, it is characterised in that by the component group of A, B, C tri-
Into according to the mass fraction, three components composition is as follows respectively：
Component A：
150 parts of cement, 20 parts of stone flour, 20 parts of iron sand；
B component：
20~30 parts of epoxy resin, A20 parts of dry-hang glue, diluent
C components：
20~25 parts of curing agent, dry-hang glue B20~25 part.
2. it is used for the aging-resistant flame-proof clay for bonding stone material and composite according to claim 1, it is characterised in that it makes
It is with method：
(1) the husky separately storage of the cement of component A, building stones, iron, without using without diluent.
(2) epoxy resin of B component, dry-hang glue A, diluent are separately deposited, without using without curing agent and dry-hang glue B；
(3) curing agent of C components and dry-hang glue B are separately deposited；
(4) the step of making the aging-resistant flame-proof clay be：The epoxy resin of B component and dry-hang glue A are mixed, C is subsequently added into
The dry-hang glue B of component is simultaneously stirred, and is then added the curing agent of C components, is added component A and stir, be eventually adding diluent, stir
Mix uniform.
3. it is used for the aging-resistant flame-proof clay for bonding stone material and composite according to claim 1, it is characterised in that described
Epoxy resin is used in unmodified epoxy resin, polyurethane-modified epoxy resin or polyacrylate modified epoxy resin
One or more.
4. it is used for the aging-resistant flame-proof clay for bonding stone material and composite according to claim 1, it is characterised in that described
Diluent is epoxide resin reactive diluent or epoxy resin non-activated thinner, and wherein epoxide resin reactive diluent includes second
Hexanediol diglycidyl ether, phenyl glycidyl ether, polypropylene glycol diglycidyl ether, benzyl glycidyl ether, o-tolyl
Glycidol ether or neopentylglycol diglycidyl ether；Epoxy resin non-activated thinner includes dibutyl phthalate or neighbour
Dioctyl phthalate；The diluent uses one or more therein.
5. it is used for the aging-resistant flame-proof clay for bonding stone material and composite according to claim 1, it is characterised in that described
Curing agent uses one kind in aliphatic modified amine, alicyclic modified amine or polyamide.