CN106995307A - A kind of coal sauce glaze tea small cup porcelain and preparation method thereof - Google Patents

A kind of coal sauce glaze tea small cup porcelain and preparation method thereof Download PDF

Info

Publication number
CN106995307A
CN106995307A CN201710331908.4A CN201710331908A CN106995307A CN 106995307 A CN106995307 A CN 106995307A CN 201710331908 A CN201710331908 A CN 201710331908A CN 106995307 A CN106995307 A CN 106995307A
Authority
CN
China
Prior art keywords
parts
glaze
porcelain
coal
sauce
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710331908.4A
Other languages
Chinese (zh)
Inventor
张双昆
黄丽君
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Dehua New Jun Cheng Ceramic Arts And Crafts Co Ltd
Original Assignee
Dehua New Jun Cheng Ceramic Arts And Crafts Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Dehua New Jun Cheng Ceramic Arts And Crafts Co Ltd filed Critical Dehua New Jun Cheng Ceramic Arts And Crafts Co Ltd
Priority to CN201710331908.4A priority Critical patent/CN106995307A/en
Publication of CN106995307A publication Critical patent/CN106995307A/en
Pending legal-status Critical Current

Abstract

The invention discloses a kind of coal sauce glaze tea small cup porcelain and preparation method thereof, glaze is manufactured by the raw material of following parts by weight:Potassium feldspar, calcium carbonate, barium carbonate, zinc oxide, silica, iron oxide.Extended to using the manufacture technique on domestic ceramics and craft artistic pottery and porcelain, improve the attractive in appearance and added value of product, be a new method, new breakthrough, new technology, simultaneously, glaze after burning till can watch the glaze of one layer of gold diamond under jewelry mirror, dazzling as stars all over the sky.

Description

A kind of coal sauce glaze tea small cup porcelain and preparation method thereof
【Technical field】
The present invention relates to porcelain field, more particularly to a kind of coal sauce glaze tea small cup porcelain and preparation method thereof.
【Background technology】
China's ceramics are with a long history, between Wan Yunian, and the mankind create original pottery in life is settled down with water, soil, fire Device;Period flourishing age Tang and Song Dynasty, ceramics develops on an unprecedented scale, an ancient unit of weight, you, official, brother, fixed turn into five big generally acknowledged porcelain;Pottery glaze is to aoxidize Copper reduction coloring produced by magical transmutation and unrivalled porcelain woods;30 years after reform and opening-up, the development of the pottery art work was unprecedented It is flourishing;State's gift pottery becomes a name cards of China and is world known.Its thick and heavy history culture inside information and magnificent abundant Transmutation romantic charm is by dilution treasure of the honor for " vertical to have roll in riches, not as pottery one ".
21st century allows the mankind to enter the post-industrial civilization epoch, ceaselessly exploits and result in industrialized production Energy crisis, greenhouse effects, environmental pollution, safe diet also come one after another, and more have visual pollution also nibbling the spirit of people Soul.Therefore, the development of post-industrial civilization follows the course of nature gravely with greater need for people, pursues brief reality, rather than numerous and diverse luxurious China, but the method for cooking of coal sauce glaze tea small cup porcelain is still defective at present, is extended to using the manufacture technique of the present invention On domestic ceramics and craft artistic pottery and porcelain, the attractive in appearance and added value of product is improved.Therefore, a kind of it is proposed that coal sauce glaze tea small cup Porcelain and preparation method thereof.
【The content of the invention】
It is a primary object of the present invention to provide a kind of coal sauce glaze tea small cup porcelain and preparation method thereof, can effectively it solve The problem of in background technology.
To achieve the above object, the technical scheme taken of the present invention is:
A kind of coal sauce glaze tea small cup porcelain, glaze is manufactured by the raw material of following parts by weight:
70-75 parts of potassium feldspar, 10-20 parts of calcium carbonate, 1-5 parts of barium carbonate, 4-8 parts of zinc oxide, 10-20 parts of silica, oxidation 5-10 parts of iron.
Further, the glaze parts by weight are as follows:70 parts of potassium feldspar, 10 parts of calcium carbonate, 1 part of barium carbonate, zinc oxide 4 Part, 10 parts of silica, 5 parts of iron oxide.
Further, the glaze parts by weight are as follows:72 parts of potassium feldspar, 15 parts of calcium carbonate, 2 parts of barium carbonate, zinc oxide 6 Part, 15 parts of silica, 7 parts of iron oxide.
Further, the glaze parts by weight are as follows:75 parts of potassium feldspar, 20 parts of calcium carbonate, 5 parts of barium carbonate, zinc oxide 8 Part, 20 parts of silica, 10 parts of iron oxide.
The preparation method of coal sauce glaze tea small cup porcelain, comprises the following steps:
Step one:It is prepared by glaze, soil
(1) whole raw materials chosen, eluriated, drying, crushing, crossing 35 mesh sieves, it is standby after above-mentioned raw materials sieving.
(2) add water ball milling, ball after raw material is weighed according to formula:Water=1:1.2 weight ratio adds water, and Ball-milling Time is 48 Hour, obtain glaze slip.
(3) soil is crossed into 300 mesh sieves, adds water and walk is made, it is ensured that walk moisture content reaches 20%-25%, then anti- Preserved in the environment of tide.
Step 2:3 assembly bodies are made, carries out after preliminary trimming, is burnt in temperature is 1300 to 1500 DEG C of cave dwelling System (optimum temperature is 1380 DEG C), the firing time is 10-15 hours (the optimal firing time is 13 hours).
Step 3:Glaze spraying
Chosen in 3 assembly bodies of step 2 without deformation, ftracture, the base substrate of iron spot defect, and polish, sweep off floating dust Afterwards, muffle painting is blowed and sprayed, then, again in 800 DEG C of low-firings, is painted afterwards, and adds colored glaze water, is dried afterwards.
Step 4:Fire
After drying, firing semi-finished product show space pattern by pattern in 800 DEG C of environment, then spray glaze pulp material .
Further, the firing Best Times in the step 2 are 13 hours, wherein 0 DEG C -800 DEG C, fire 5 hours, Burnt for oxidation, fire 3 hours for 800 DEG C -1000 DEG C and burnt for slightly reduction, it 5 hours is that moderate reduction is burnt to fire for 800 DEG C -1000 DEG C, And reduce flame and be about 10 centimeters, to 1380 DEG C of end.
Compared with prior art, the present invention has the advantages that:Daily pottery is extended to using the manufacture technique On porcelain and craft artistic pottery and porcelain, the attractive in appearance and added value of product is improved, is a new method, new breakthrough, new technology, meanwhile, burn Glaze after can watch the glaze of one layer of gold diamond under jewelry mirror, dazzling as stars all over the sky.
【Embodiment】
To be easy to understand the technical means, the inventive features, the objects and the advantages of the present invention, with reference to Embodiment, is expanded on further the present invention.
A kind of coal sauce glaze tea small cup porcelain, glaze is manufactured by the raw material of following parts by weight:
70-75 parts of potassium feldspar, 10-20 parts of calcium carbonate, 1-5 parts of barium carbonate, 4-8 parts of zinc oxide, 10-20 parts of silica, oxidation 5-10 parts of iron.
The preparation method of coal sauce glaze tea small cup porcelain, comprises the following steps:
Step one:It is prepared by glaze, soil
(1) whole raw materials chosen, eluriated, drying, crushing, crossing 35 mesh sieves, it is standby after above-mentioned raw materials sieving.
(2) add water ball milling, ball after raw material is weighed according to formula:Water=1:1.2 weight ratio adds water, and Ball-milling Time is 48 Hour, obtain glaze slip.
(3) soil is crossed into 300 mesh sieves, adds water and walk is made, it is ensured that walk moisture content reaches 20%-25%, then anti- Preserved in the environment of tide.
Step 2:3 assembly bodies are made, carries out after preliminary trimming, is burnt in temperature is 1300 to 1500 DEG C of cave dwelling System (optimum temperature is 1380 DEG C), the firing time is 10-15 hours (the optimal firing time is 13 hours).
Step 3:Glaze spraying
Chosen in 3 assembly bodies of step 2 without deformation, ftracture, the base substrate of iron spot defect, and polish, sweep off floating dust Afterwards, muffle painting is blowed and sprayed, then, again in 800 DEG C of low-firings, is painted afterwards, and adds colored glaze water, is dried afterwards.
Step 4:Fire
After drying, firing semi-finished product show space pattern by pattern in 800 DEG C of environment, then spray glaze pulp material .
Further, the firing Best Times in the step 2 are 13 hours, wherein 0 DEG C -800 DEG C, fire 5 hours, Burnt for oxidation, fire 3 hours for 800 DEG C -1000 DEG C and burnt for slightly reduction, it 5 hours is that moderate reduction is burnt to fire for 800 DEG C -1000 DEG C, And reduce flame and be about 10 centimeters, to 1380 DEG C of end.
Embodiment 1:
The glaze parts by weight are as follows:70 parts of potassium feldspar, 10 parts of calcium carbonate, 1 part of barium carbonate, 4 parts of zinc oxide, silica 10 Part, 5 parts of iron oxide.
Embodiment 2:
The glaze parts by weight are as follows:72 parts of potassium feldspar, 15 parts of calcium carbonate, 2 parts of barium carbonate, 6 parts of zinc oxide, silica 15 Part, 7 parts of iron oxide.
Embodiment 3:
The glaze parts by weight are as follows:75 parts of potassium feldspar, 20 parts of calcium carbonate, 5 parts of barium carbonate, 8 parts of zinc oxide, silica 20 Part, 10 parts of iron oxide.
Extended to using the manufacture technique on domestic ceramics and craft artistic pottery and porcelain, improve the attractive in appearance and additional of product Value, is a new method, new breakthrough, new technology, meanwhile, the glaze after burning till can watch one layer of gold diamond under jewelry mirror As glaze, it is dazzling as stars all over the sky.
The general principle and principal character and advantages of the present invention of the present invention has been shown and described above.The technology of the industry Personnel are it should be appreciated that the present invention is not limited to the above embodiments, and the simply explanation described in above-described embodiment and specification is originally The principle of invention, without departing from the spirit and scope of the present invention, various changes and modifications of the present invention are possible, these changes Change and improvement all fall within the protetion scope of the claimed invention.The claimed scope of the invention by appended claims and its Equivalent thereof.

Claims (6)

1. a kind of coal sauce glaze tea small cup porcelain, it is characterised in that glaze is manufactured by the raw material of following parts by weight:
70-75 parts of potassium feldspar, 10-20 parts of calcium carbonate, 1-5 parts of barium carbonate, 4-8 parts of zinc oxide, 10-20 parts of silica, iron oxide 5- 10 parts.
2. coal sauce glaze tea small cup porcelain according to claim 1, it is characterised in that the glaze parts by weight are as follows:Potassium is long 70 parts of stone, 10 parts of calcium carbonate, 1 part of barium carbonate, 4 parts of zinc oxide, 10 parts of silica, 5 parts of iron oxide.
3. coal sauce glaze tea small cup porcelain according to claim 1, it is characterised in that the glaze parts by weight are as follows:Potassium is long 72 parts of stone, 15 parts of calcium carbonate, 2 parts of barium carbonate, 6 parts of zinc oxide, 15 parts of silica, 7 parts of iron oxide.
4. coal sauce glaze tea small cup porcelain according to claim 1, it is characterised in that the glaze parts by weight are as follows:Potassium is long 75 parts of stone, 20 parts of calcium carbonate, 5 parts of barium carbonate, 8 parts of zinc oxide, 20 parts of silica, 10 parts of iron oxide.
5. the preparation method of coal sauce glaze tea small cup porcelain, it is characterised in that comprise the following steps:
Step one:It is prepared by glaze, soil
(1) whole raw materials chosen, eluriated, drying, crushing, crossing 35 mesh sieves, it is standby after above-mentioned raw materials sieving.
(2) add water ball milling, ball after raw material is weighed according to formula:Water=1:1.2 weight ratio adds water, and Ball-milling Time is 48 small When, obtain glaze slip.
(3) soil is crossed into 300 mesh sieves, adds water and walk is made, it is ensured that walk moisture content reaches 20%-25%, then in protection against the tide Preserved in environment.
Step 2:3 assembly bodies are made, carries out after preliminary trimming, is fired (most in temperature is 1300 to 1500 DEG C of cave dwelling Good temperature is 1380 DEG C), the firing time is 10-15 hours (the optimal firing time is 13 hours).
Step 3:Glaze spraying
Chosen in 3 assembly bodies of step 2 without deformation, ftracture, the base substrate of iron spot defect, and polish, sweep off after floating dust, blow Glaze spraying is color, then, again in 800 DEG C of low-firings, paints afterwards, and adds colored glaze water, dries afterwards.
Step 4:Fire
After drying, firing semi-finished product show space pattern by pattern in 800 DEG C of environment, then spray glaze pulp material i.e. Can.
6. the preparation method of coal sauce glaze tea small cup porcelain according to claim 5, it is characterised in that in the step 2 It is 13 hours to fire Best Times, wherein 0 DEG C -800 DEG C, fire 5 hours, burnt for oxidation, 800 DEG C of -1000 DEG C of firings 3 hours are Slightly reduce and burn, it 5 hours is moderate reduction burning to fire for 800 DEG C -1000 DEG C, and reduce flame and be about 10 centimeters, to 1380 DEG C Terminate.
CN201710331908.4A 2017-05-11 2017-05-11 A kind of coal sauce glaze tea small cup porcelain and preparation method thereof Pending CN106995307A (en)