CN106988494A - The slurry coating process of full water-based simulated natural granite face effect - Google Patents
The slurry coating process of full water-based simulated natural granite face effect Download PDFInfo
- Publication number
- CN106988494A CN106988494A CN201710184543.7A CN201710184543A CN106988494A CN 106988494 A CN106988494 A CN 106988494A CN 201710184543 A CN201710184543 A CN 201710184543A CN 106988494 A CN106988494 A CN 106988494A
- Authority
- CN
- China
- Prior art keywords
- layer
- granite
- artificial granite
- aqueous
- varnish
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a kind of slurry coating process of full water-based simulated natural granite face effect, comprise the following steps：The basic unit for treating application is surface-treated, and makes its surface smoothness ＜ 2mm；In the aqueous alkali resistant wash coats of substrate surface roller coating, aqueous alkali resistant wash coats layer is obtained；In aqueous alkali resistant wash coats layer surface plaster aqueousance artificial granite slurry, surface drying simultaneously throws flat processing, obtains the first aqueousance artificial granite layer；First aqueousance artificial granite layer is polished, after dust removal process, plaster aqueousance artificial granite slurry obtains the second aqueousance artificial granite preformed layer；Natural minerals toner is shed on the second aqueousance artificial granite preformed layer, then plaster top layer, obtain artificial granite texture layer；Artificial granite texture layer is polished, after dust removal process, spray aqueous transparent varnish, obtain the first aqueous transparent layer of varnish；First aqueous transparent layer of varnish is polished, after dedusting, spray aqueous transparent varnish, obtain the second aqueous transparent layer of varnish.
Description
Technical field
The invention belongs to coating application technical field, more particularly to a kind of slurry of full water-based simulated natural granite face effect
Expect coating process.
Background technology
Granite is one of conventional TERRAZZO, and it is wide in variety, and color is various, can highlight the elegant of building.
Natural granite quality is hard, durable in use and easy maintenance, is the stone decoration material increasingly liked and pursued at present.So
And, because granite good in the deficient of resource, nature is fewer and fewer, the various expense costs that granite is exploited in addition are too
Height, causes mined granite selling price also to remain high.And can be to local air and nature during granite exploitation
There is destructive destruction in environment, the time for causing the recovery needs of surface vegetation after exploitation very long.Although in addition, granite is filled
Exterior material is welcome by consumer deeply, still, because natural granite plaque is from great and brittle, in transport and decoration construction mistake
Easily damaged in journey, meanwhile, it can not be decorated on high external wall of building surface, further be applied so as to limit it.Cause
This, develops a kind of slurry coating process of anti-natural granite surface effect and is particularly important.
The content of the invention
It is an object of the invention to provide a kind of slurry coating process of full water-based simulated natural granite face effect, it is intended to
Solve that natural granite resource is nervous, high cost, not environmentally and the problem of be not suitable for high-altitude outer wall operation.
The present invention is achieved in that a kind of slurry coating process of full water-based simulated natural granite face effect, including
Following steps：
The basic unit for treating application is surface-treated, and makes its surface smoothness ＜ 2mm；
The aqueous alkali resistant wash coats of the substrate surface roller coating after surface treated, 8 are dried in 20 DEG C of -40 DEG C of temperature
More than hour, aqueous alkali resistant wash coats layer is obtained；
Thrown while the aqueous alkali resistant wash coats layer surface plaster aqueousance artificial granite slurry, surface drying processing
Flat processing, is then dried more than 24 hours in 20 DEG C of -40 DEG C of temperature, obtains the first aqueousance artificial granite layer；
First aqueousance artificial granite layer is polished, after dust removal process, in first aqueousance artificial granite layer
Aqueousance artificial granite slurry described in plaster, in the micro- dry 5-10min of 20 DEG C of -40 DEG C of temperature, obtains the second aqueousance artificial granite pre-
Preparative layer；
Natural minerals toner is shed on the second aqueousance artificial granite preformed layer, then using batch knife plaster table
Layer, makes to shed the natural minerals toner on the second aqueousance artificial granite preformed layer and scatters and be embedded in second water
Property artificial granite preformed layer in, prepare coloured artificial granite texture, dried more than 48 hours in 20 DEG C~40 DEG C temperature, imitated
Granite texture layer；
Grinding process is carried out to the artificial granite texture layer, removed after the marks on surface that plaster is produced, dust removal process,
The artificial granite texture layer surface spraying aqueous transparent varnish, after 20 DEG C of -40 DEG C of temperature are dried more than 24 hours, obtains the
One aqueous transparent layer of varnish；
The first aqueous transparent layer of varnish is polished, after dedusting, in the first aqueous transparent varnish layer surface
Aqueous transparent varnish, after 20 DEG C of -40 DEG C of temperature are dried more than 24 hours, obtains the second aqueous transparent layer of varnish.
It is preferred that, the thickness of dry film of the aqueous alkali resistant wash coats layer is 20-30 microns.
It is preferred that, the thickness of dry film of the first aqueousance artificial granite layer is 0.5-0.8 millimeters.
It is preferred that, the thickness of the artificial granite texture layer is 0.5-0.8 millimeters.
It is preferred that, the thickness that the natural minerals toner is embedded in the second aqueousance artificial granite preformed layer is 20-40
Micron.
It is preferred that, the thickness of the first aqueous transparent layer of varnish is 20-50 microns.
It is preferred that, the thickness of the second aqueous transparent layer of varnish is 20-50 microns.
It is preferred that, the basic unit includes plasterboard, concrete inner-outer wall, plank, fiberboard, cement plate, Etta's plate, common
Brick wall etc..
It is preferred that, the aqueousance artificial granite slurry is the aqueous flat slurry #901 of chrysanthemum board.
It is preferred that, the aqueous transparent varnish is chrysanthemum board water varnish #FP495.
The slurry coating process for the full water-based simulated natural granite face effect that the present invention is provided, before not welding
Put, pass through some base stocks (aqueous alkali-resistant sealing primer, aqueousance artificial granite slurry, water varnish, natural toner), energy
Natural granite surface texture effect is visually imitated very much in various basic units, and it is environmentally friendly, cheap.The present invention is used
Full water paste carries out decoration application to building surface, can reach the surface texture effect of natural granite, not only effectively solves
Existing natural granite resource is nervous, high cost, not environmentally the problem of；Moreover, the aqueousance artificial granite slurry, the water
The adhesive force of property clear varnish is good, can be constructed in the basic unit of various material, obtain firm coating, so as to solve
The problem of natural granite is limited using field.
Brief description of the drawings
Fig. 1 is that the slurry coating process of the full water-based simulated natural granite face effect provided by the embodiment of the present invention 1 is obtained
The artificial granite surface effect figure arrived；
Fig. 2 is that the slurry coating process of the full water-based simulated natural granite face effect provided by the embodiment of the present invention 2 is obtained
The artificial granite surface effect figure arrived.
Embodiment
In order that technical problems, technical solutions and advantageous effects to be solved by the present invention are more clearly understood, below in conjunction with
Embodiment, the present invention will be described in further detail.It should be appreciated that specific embodiment described herein is only to explain
The present invention, is not intended to limit the present invention.
The embodiments of the invention provide a kind of slurry coating process of full water-based simulated natural granite face effect, including with
Lower step：
S01. the basic unit for treating application is surface-treated, and makes its surface smoothness ＜ 2mm；
S02. aqueous alkali resistant wash coats of the substrate surface roller coating after surface treated, in 20 DEG C of -40 DEG C of temperature
Dry more than 8 hours, obtain aqueous alkali resistant wash coats layer；
S03. in the aqueous alkali resistant wash coats layer surface plaster aqueousance artificial granite slurry, enter while surface drying processing
Row throws flat processing, is then dried more than 24 hours in 20 DEG C of -40 DEG C of temperature, obtains the first aqueousance artificial granite layer；
S04. first aqueousance artificial granite layer is polished, after dust removal process, on the described first aqueous Fang Hua hilllocks
Aqueousance artificial granite slurry described in the plaster of rock stratum, in the micro- dry 5-10min of 20 DEG C of -40 DEG C of temperature, obtains the second aqueous Fang Hua hilllocks
Rock preformed layer；
S05. natural minerals toner is shed on the second aqueousance artificial granite preformed layer, then using batch knife plaster
Top layer, makes to shed the natural minerals toner on the second aqueousance artificial granite preformed layer and scatters and be embedded in described second
In aqueousance artificial granite preformed layer, coloured artificial granite texture is prepared, dries more than 48 hours, obtains in 20 DEG C~40 DEG C temperature
Artificial granite texture layer；
S06. grinding process is carried out to the artificial granite texture layer, removes the marks on surface that plaster is produced, dust removal process
Afterwards, in the artificial granite texture layer surface spraying aqueous transparent varnish, after 20 DEG C of -40 DEG C of temperature are dried more than 24 hours,
Obtain the first aqueous transparent layer of varnish；
S07. the first aqueous transparent layer of varnish is polished, after dedusting, in the first aqueous transparent layer of varnish
Aqueous surface clear varnish, after 20 DEG C of -40 DEG C of temperature are dried more than 24 hours, obtains the second aqueous transparent layer of varnish.
The slurry coating process of full water-based simulated natural granite face effect provided in an embodiment of the present invention, is not destroying ring
On the premise of border, pass through some base stock (aqueous alkali-resistant sealing primer, aqueousance artificial granite slurry, water varnish, natural colours
Powder), natural granite surface texture effect can be visually imitated very much in various basic units, and also it is environmentally friendly, cheap.This hair
Bright embodiment carries out decoration application using full water paste to building surface, on the premise of not welding, using complete aqueous
Slurry carries out decoration application to building surface, and cost is low, can reach the surface texture effect of natural granite, not only effectively solves
Existing natural granite resource is nervous, high cost, not environmentally the problem of；Moreover, the aqueousance artificial granite slurry, the water
The adhesive force of property clear varnish is good, can be constructed in the basic unit of various material, obtain firm coating, so as to solve
The problem of natural granite is limited using field.
Specifically, in above-mentioned steps S01, the basic unit for treating application is surface-treated, make its surface smoothness ＜ 2mm,
So as to be conducive to the deposition of follow-up each coating, and each coating of subsequent deposition is caused to be respectively provided with preferable flatness.It is of the invention real
Apply the basic unit that example treats application, including but not limited to plasterboard, concrete inner-outer wall, plank, fiberboard, cement plate, Etta
Plate, common brick wall etc..
Specifically, when the basic unit is concrete walls, the detailed process of substrate surface processing is：Remove basic unit's table
The floating pine in face and hollowing, are filled up, after drying again with wall putty to the out-of-flatness of concrete surface or the place of hole
Concrete surface is integrally polished, the flatness on the surface of concrete is reached ＜ 2mm, so as to be follow-up aqueous alkali resistant sealing bottom
The deposition of paint provides smooth basic unit basis.
In above-mentioned steps S02, due to containing alkaline matter, the analysis of alkaline matter in the basic unit particularly concrete base layer
Go out, larger is influenceed on the aqueousance artificial granite slurry, can cause to deposit obtained aqueousance artificial granite coating accumulation of salt in the surface soil change flower, shadow
The quality and coating result of decorative coveringn are rung, the substrate surface roller coating of the embodiment of the present invention after surface treated is aqueous anti-
Alkali wash coats, so that the alkaline matter of the basic unit particularly concrete base layer release is carried out into sealing, it is to avoid it is to described
The adverse effect that aqueousance artificial granite slurry is brought.Roller coating instrument described in the embodiment of the present invention can use wool roller, certainly, no
It is limited to this.Aqueous alkali-resistant sealing primer described in the embodiment of the present invention is the aqueous alkali-resistant primer FP217 of chrysanthemum board.
The embodiment of the present invention obtains the aqueous alkali resistant wash coats layer of drying by drying the moisture gone in removing coating.Tool
Body, in the embodiment of the present invention, the drying temperature is unsuitable too high, if temperature is too high, coating cracking is easily caused, after influence
The deposition of continuous coating and the effect of Integral decoration layer.But drying enough fully to avoid remnants moisture from separating out, should cause
Decorative layer bubble, finally equally causes coating cracking；And drying is insufficient, is also unfavorable for the deposition of follow-up coating, it is impossible to obtain
Firm coating.In view of this, the embodiment of the present invention is dried more than 8 hours in 20 DEG C of -40 DEG C of temperature, obtains aqueous alkali resistant sealing
Prime coat.
It is preferred that, the thickness of dry film of the aqueous alkali resistant wash coats layer is 20-30 microns.If the aqueous alkali resistant sealing
The thickness of dry film of prime coat is excessively thin, then can not alkaline matter that effectively sealing is discharged from base material；If described aqueous anti-
The thickness of dry film of alkali wash coats layer is blocked up, not only bad for drying, and can influence upper strata granite adhesive force, be unfavorable for institute
State the deposition of aqueousance artificial granite slurry.
In above-mentioned steps S03, in the embodiment of the present invention, in order to obtain the surface effect of natural granite, it is necessary to aqueous
Toner, which is shed, on the coating of artificial granite slurry formation carries out texture processing.It is during texture processing, the toner is embedding
Enter to carry out intention plaster in corresponding coating to realize.When using one layer of aqueousance artificial granite slurry coating, if the coating
It is excessively thin, then during the toner insertion coating shed during texture processing, easily directly contact the aqueous alkali resistant wash coats
Layer, causes corresponding region to lack aqueousance artificial granite slurry, it is impossible to ensure the physics of the coating of aqueousance artificial granite slurry formation
The integrality of property and surface texture effect.But, when directly formation is one layer thicker on the aqueous alkali resistant wash coats layer
Aqueousance artificial granite slurry coating when, because thickness is blocked up, the moisture close to the aqueous alkali resistant wash coats layer is difficult to have
Drying, the moisture influence coating quality of residual are imitated, or even causes cracking.In view of this, the embodiment of the present invention is used and deposited twice
The mode of aqueous alkali resistant wash coats prepares the first aqueousance artificial granite layer and the second aqueousance artificial granite preformed layer respectively.
Wherein, the first aqueousance artificial granite layer is by the aqueous uniform plaster water of alkali resistant wash coats layer surface
Property artificial granite slurry formed, it is specific to be realized using batch knife plaster.Carry out throwing flat processing, the surface drying while surface drying is handled
The time of processing is 20-35min；Batch tool marks formed when flat processing uses polishing blade by plaster of throwing throw smooth, so as to have
Beneficial to the coating for forming even uniform.
Processing is further dried in coating, the first aqueousance artificial granite layer is obtained.Specifically, the embodiment of the present invention
In, the drying temperature is unsuitable too high, if drying temperature is too high, easily causes coating cracking, influences the deposition of follow-up coating
And the effect of Integral decoration layer.But drying enough fully to avoid remnants moisture from separating out, should cause decorative layer to produce gas
Bubble, finally equally causes coating cracking；And if drying is insufficient, is also unfavorable for the deposition of follow-up coating, it is impossible to obtain firm
Coating.In view of this, the embodiment of the present invention is dried more than 24 hours under 20 DEG C of -40 DEG C of temperature conditionss, obtains first aqueous imitative
Sial.
It is preferred that, the thickness of dry film of the first aqueousance artificial granite layer is 0.5-0.8 millimeters, from but regardless of localized site
Toner insertion is whether there is, can ensure that each site has certain aqueousance artificial granite thickness degree.
In above-mentioned steps S04, grinding process is carried out to first aqueousance artificial granite layer, can be realized using sand paper, tool
Body can select #400 sand paper.After first aqueousance artificial granite layer grinding homogeneity, dust removal process is carried out, in favor of follow-up painting
The deposition of layer.
In aqueousance artificial granite slurry described in first aqueousance artificial granite layer plaster, and carry out micro- drying process and obtain
Second aqueousance artificial granite preformed layer.Specifically, micro- drying is to dry 5-10min in 20 DEG C of -40 DEG C of temperature, so as to ensure
The second obtained aqueousance artificial granite preformed layer is conducive to the proper moisture of the texture processing.Humidity is too high or too low all
It is unfavorable for the progress of texture processing.
In step S03, S04 of the embodiment of the present invention, the aqueousance artificial granite slurry is the aqueous flat slurry #901 of chrysanthemum board.
In above-mentioned steps S05, natural minerals toner is shed on the second aqueousance artificial granite preformed layer, the day
Right mineral toner can choose assorted natural minerals toner according to actual needs, and the collocation mode of the natural minerals toner can be with
According to actual needs or intention is adjusted.Spray method of the embodiment of the present invention can be carried out with intention, the natural minerals color shed
Powder forms local extra play in the prefabricated layer surface of the second aqueousance artificial granite.Then using batch knife plaster top layer, make to shed
The natural minerals toner on the second aqueousance artificial granite preformed layer scatters and is embedded in the described second aqueous Fang Hua hilllocks
In rock preformed layer, coloured artificial granite texture is prepared.
Processing is further dried in coating after texture processing, artificial granite texture layer is obtained.Specifically, of the invention
In embodiment, the drying temperature is unsuitable too high, if drying temperature is too high, easily causes coating cracking, influences follow-up coating
Deposition and Integral decoration layer effect.But drying enough fully to avoid the remaining moisture of coating from separating out, should cause dress
Adorn layer and produce bubble, finally equally cause coating cracking；And if drying is insufficient, is also unfavorable for the deposition of follow-up coating, it is impossible to
Obtain firm coating.In view of this, the embodiment of the present invention is dried more than 24 hours under 20 DEG C of -40 DEG C of temperature conditionss, is obtained
Second aqueousance artificial granite layer.
It is preferred that, the thickness of the artificial granite texture layer is 0.5-0.8 millimeters, thereby may be ensured that the natural minerals
Toner is substantially embedded into, and then plaster forms naturally coloured anti-granite texture.It is further preferred that the natural minerals
The thickness that toner is embedded in the second aqueousance artificial granite preformed layer is 20-40 microns, so as to obtain preferable grain effect.
In above-mentioned steps S06, grinding process is carried out to the artificial granite texture layer, the surface trace that plaster is produced is removed
Mark, polishing mode can be using sand paper realization, specific preferably #400 mesh sand paper grinding, then dust removal process.
Further, in the artificial granite texture layer surface spraying aqueous transparent varnish, protective clear layer is formed.When
When, if directly in the artificial granite texture layer surface one layer of aqueous transparent varnish of formation, in aqueousance artificial granite slurry table
The aqueous transparent varnish coat of face deposition easily forms burr, and feel is bad.In view of this, the embodiment of the present invention by sinking twice
Aqueous clear varnish prepares protective layer.
In the artificial granite texture layer surface spraying aqueous transparent varnish, the first aqueous transparent layer of varnish is dried to obtain.
Specifically, in the embodiment of the present invention, the drying temperature is unsuitable too high, if temperature is too high, easily causes coating cracking, influences
The effect of deposition and the Integral decoration layer of follow-up coating.But drying enough fully to avoid remnants moisture from separating out, should be led
Decorative layer bubble is caused, coating cracking is finally equally caused；And drying is insufficient, is also unfavorable for the deposition of follow-up coating, it is impossible to obtain
Obtain firm coating.In view of this, the embodiment of the present invention is dried more than 24 hours under 20 DEG C of -40 DEG C of temperature conditionss, obtains the
One aqueous transparent layer of varnish.
It is preferred that, the thickness of the first aqueous transparent layer of varnish is 20-50 microns, and the preferred thickness is more beneficial for
The abundant volatilization of moisture in coating, forms fine and close coating.
In above-mentioned steps S07, the first aqueous transparent layer of varnish is polished, surface spikes are removed, mode of polishing
It can be realized using sand paper, specific preferably #400 mesh sand paper grinding, then dedusting.
In the first aqueous transparent layer of varnish aqueous surface clear varnish, carried out by the way of same with step S06
Drying process, obtains that surface is smooth, good hand touch the second aqueous transparent layer of varnish.
It is preferred that, the thickness of the second aqueous transparent layer of varnish is 20-50 microns, and the preferred thickness is more beneficial for
The abundant volatilization of moisture in coating, forms fine and close coating.
The preferred thickness of two layers of transparent clear, it is ensured that the protecting effect and transparency of transparent clear.
In above-mentioned steps S06, S07, it is preferred that the aqueous transparent varnish is chrysanthemum board water varnish #FP495.By it
The explanation of specification, after the 10% proportioning allotment uniformly that adds water, you can for roller coating.
Complete aqueous anti-granite face effect slurry coating process provided in an embodiment of the present invention is a kind of with complete aqueous painting
Expect artificial granite surface texture technique, it can reach natural granite surface effect, can be applied again in a variety of basic units
Work, while using the cost of the artificial granite surface effect obtained by present invention method with respect to pole for natural granite
To be cheap, the 1/5 of also not enough natural granite, the cost of decoration can be greatly reduced.In addition, the artificial granite surface effect
Basic unit can be for timber, fiberboard, plasterboard, cement plate, Etta's plate, brick wall, concrete wall surface etc., therefore, the imitative flower
Hilllock rock surface effect coating process have have a wide range of application, the quadruple advantage that full aqueous, environmental protective, with low cost, decorative effect are good.
Illustrated with reference to specific embodiment.
Embodiment 1
A kind of slurry coating process of full water-based simulated natural granite face effect, comprises the following steps：
S11. the surface of concrete base layer is handled, makes the surface smoothness ＜ 2mm of basic unit；
S12. with wool roller by the uniform roller coating of aqueous alkali-resistant primer in the basic unit, and in 20 DEG C~40 DEG C temperature
Dry 8 hours, form aqueous alkali resistant wash coats layer, the film thickness 20~30 of the aqueous alkali resistant wash coats layer after construction
Micron.
S13. with batch knife will aqueous anti-granite slurry equably plaster on the aqueous alkali resistant wash coats layer, and
20 DEG C~40 DEG C temperature are dried more than half an hour, form the first aqueousance artificial granite layer.The first aqueous Fang Hua hilllocks after construction
40~60 microns of the film thickness of rock stratum.
S14. after the first aqueousance artificial granite layer is dried, equably ground using #400 mesh sand paper, and dedusting.
By aqueous anti-granite slurry, equably plaster is dried on first aqueousance artificial granite layer, and in 20 DEG C~40 DEG C temperature
After 5~10 minutes, the second aqueousance artificial granite preformed layer is formed.The paint film of the second aqueousance artificial granite preformed layer after construction
Thickness is 40~60 microns.
S15. shed using the natural toner of yellow, red toner and the natural toner intention of black aqueous imitative above-mentioned second
On granite preformed layer, local extra play is formed, while using batch plaster top layer of knife up and down progressively, making to shed on top layer
Natural toner scatter and be embedded in the second aqueousance artificial granite preformed layer, and dried more than 48 hours in 20 DEG C~40 DEG C temperature,
Form naturally coloured artificial granite texture layer.The milli of film thickness 0.5~0.8 of the artificial granite texture layer after construction
Rice.
S16. after the drying varniss of the artificial granite texture layer, equably ground, ground using #400 mesh sand paper
After dedusting, wool roller roller coating aqueous transparent varnish is used on the artificial granite texture layer, and it is dry in 20 DEG C~40 DEG C temperature
Dry more than 24 hours, form the first aqueous transparent layer of varnish.The film thickness 20~50 of first aqueous transparent layer of varnish after construction
Micron.
S17. after the drying varniss of the first aqueous transparent layer of varnish, equably ground using #400 mesh sand paper,
Grind after dedusting, wool roller roller coating aqueous transparent varnish is used on the first aqueous transparent layer of varnish, and 20 DEG C~40
DEG C temperature is dried more than 24 hours, forms the second aqueous transparent layer of varnish.The paint film thickness of second aqueous transparent layer of varnish after construction
20~50 microns of degree.
In the embodiment of the present invention, the aqueous alkali-resistant sealing primer is the aqueous alkali-resistant primer FP217 of chrysanthemum board, by its explanation
The explanation of book is directly used in roller coating；
The aqueous anti-granite slurry is the aqueous flat slurry #901 of chrysanthemum board, is directly used in and criticizes by the explanation of its specification
Swing；
The aqueous transparent varnish is chrysanthemum board water varnish FP495, by the explanation of its specification, 10% is matched somebody with somebody according to adding water
After more uniform than allotment, you can for roller coating.
Based on the imitated natural granite surface obtained by the present embodiment artificial granite surface effect slurry coating process of the present invention
Effect is as shown in Figure 1.Fig. 1 shows that the lines of the artificial granite surface effect is similar to natural granite texture, surface pattern
Naturally it is uniform clear.
Embodiment 2
A kind of slurry coating process of full water-based simulated natural granite face effect, comprises the following steps：
S21. the surface of plasterboard base material is handled, makes the surface smoothness ＜ 2mm of base material；
S22. with wool roller by the uniform roller coating of aqueous alkali-resistant primer in the basic unit, and in 20 DEG C~40 DEG C temperature
Dry 8 hours, form aqueous alkali resistant wash coats layer.The film thickness 20~30 of the aqueous alkali resistant wash coats layer after construction
Micron.
S23. with batch knife will aqueous anti-granite slurry equably plaster on the aqueous alkali resistant wash coats layer, and
20 DEG C~40 DEG C temperature are dried more than half an hour, form the first aqueousance artificial granite layer.The first aqueous Fang Hua hilllocks after construction
40~60 microns of the film thickness of rock stratum.
S24. after the drying of the first aqueousance artificial granite layer, equably ground using #400 mesh sand paper, and remove
Dirt.By aqueous anti-granite slurry, equably plaster is on first aqueousance artificial granite layer, and in 20 DEG C~40 DEG C temperature
After drying 5~10 minutes, the second aqueousance artificial granite preformed layer is formed.The second aqueousance artificial granite preformed layer after construction
Film thickness is 40~60 microns.
S25. shed using the natural toner of yellow and the natural toner intention of black pre- in above-mentioned second aqueousance artificial granite
On preparative layer, local artificial granite texture layer is formed, while using batch knife gradually slight plaster top layer up and down, making to shed on top layer
Natural toner scatter and be embedded in the 3rd extra play, and dried more than 48 hours in 20 DEG C~40 DEG C temperature, formation naturally has
The anti-granite texture of color.0.5~0.8 millimeter of the film thickness of the artificial granite texture layer after construction.
S26. after the drying varniss of the artificial granite texture layer, equably ground, ground using #400 mesh sand paper
After dedusting, wool roller roller coating aqueous transparent varnish is used on the artificial granite texture layer, and it is dry in 20 DEG C~40 DEG C temperature
Dry more than 24 hours, form the first aqueous transparent layer of varnish.The film thickness 20~50 of first aqueous transparent layer of varnish after construction
Micron.
S27. after the drying varniss of the first aqueous transparent layer of varnish, equably ground using #400 mesh sand paper,
Grind after dedusting, wool roller roller coating aqueous transparent varnish is used on the first aqueous transparent layer of varnish, and 20 DEG C~40
DEG C temperature is dried more than 24 hours, forms the second aqueous transparent layer of varnish.The paint film thickness of second aqueous transparent layer of varnish after construction
20~50 microns of degree.
In the embodiment of the present invention, the aqueous alkali-resistant sealing primer is the aqueous alkali-resistant primer FP217 of chrysanthemum board, by its explanation
The explanation of book is directly used in roller coating；
The aqueous anti-granite slurry is the aqueous flat slurry #901 of chrysanthemum board, is directly used in and criticizes by the explanation of its specification
Swing；
The aqueous transparent varnish is chrysanthemum board water varnish FP495, by the explanation of its specification, 10% is matched somebody with somebody according to adding water
After more uniform than allotment, you can for roller coating.
Imitated natural granite obtained by being prepared based on the artificial granite surface effect slurry coating process of the present embodiment 2 of the present invention
Surface effect is as shown in Figure 2.Fig. 2 shows that the lines of the artificial granite is similar to natural granite texture, its surface is smooth,
Light, lines are naturally uniform clear.
The foregoing is merely illustrative of the preferred embodiments of the present invention, is not intended to limit the invention, all essences in the present invention
Any modifications, equivalent substitutions and improvements made within refreshing and principle etc., should be included in the scope of the protection.
Claims (10)
1. a kind of slurry coating process of full water-based simulated natural granite face effect, it is characterised in that comprise the following steps：
The basic unit for treating application is surface-treated, and makes its surface smoothness ＜ 2mm；
The aqueous alkali resistant wash coats of the substrate surface roller coating after surface treated, are dried 8 hours in 20 DEG C of -40 DEG C of temperature
More than, obtain aqueous alkali resistant wash coats layer；
Carry out throwing flat place while the aqueous alkali resistant wash coats layer surface plaster aqueousance artificial granite slurry, surface drying processing
Reason, is then dried more than 24 hours in 20 DEG C of -40 DEG C of temperature, obtains the first aqueousance artificial granite layer；
First aqueousance artificial granite layer is polished, after dust removal process, in first aqueousance artificial granite layer plaster
The aqueousance artificial granite slurry, in the micro- dry 5-10min of 20 DEG C of -40 DEG C of temperature, obtains the second aqueousance artificial granite preformed layer；
Natural minerals toner is shed on the second aqueousance artificial granite preformed layer, then using batch knife plaster top layer, made
Shed that the natural minerals toner on the second aqueousance artificial granite preformed layer scatters and to be embedded in described second aqueous imitative
In granite preformed layer, coloured artificial granite texture is prepared, is dried more than 48 hours in 20 DEG C~40 DEG C temperature, obtains Fang Hua hilllocks
Rock texture layer；
Grinding process is carried out to the artificial granite texture layer, removed after the marks on surface that plaster is produced, dust removal process, described
Artificial granite texture layer surface spraying aqueous transparent varnish, after 20 DEG C of -40 DEG C of temperature are dried more than 24 hours, obtains the first water
Property transparent clear；
The first aqueous transparent layer of varnish is polished, after dedusting, in the first aqueous transparent layer of varnish aqueous surface
Clear varnish, after 20 DEG C of -40 DEG C of temperature are dried more than 24 hours, obtains the second aqueous transparent layer of varnish.
2. the slurry coating process of full water-based simulated natural granite face effect as claimed in claim 1, it is characterised in that institute
The thickness of dry film for stating aqueous alkali resistant wash coats layer is 20-30 microns.
3. the slurry coating process of full water-based simulated natural granite face effect as claimed in claim 1, it is characterised in that institute
The thickness of dry film for stating the first aqueousance artificial granite layer is 0.5-0.8 millimeters.
4. the slurry coating process of full water-based simulated natural granite face effect as claimed in claim 1, it is characterised in that institute
The thickness for stating artificial granite texture layer is 0.5-0.8 millimeters.
5. the slurry coating process of full water-based simulated natural granite face effect as claimed in claim 1, it is characterised in that institute
The thickness stated in natural minerals toner insertion the second aqueousance artificial granite preformed layer is 20-40 microns.
6. the slurry coating process of full water-based simulated natural granite face effect as claimed in claim 1, it is characterised in that institute
The thickness for stating the first aqueous transparent layer of varnish is 20-50 microns.
7. the slurry coating process of full water-based simulated natural granite face effect as claimed in claim 1, it is characterised in that institute
The thickness for stating the second aqueous transparent layer of varnish is 20-50 microns.
8. the slurry coating process of full water-based simulated natural granite face effect as claimed in claim 1, it is characterised in that institute
Stating basic unit includes plasterboard, concrete inner-outer wall, plank, fiberboard, cement plate, Etta's plate, brick wall.
9. the slurry coating process of full water-based simulated natural granite face effect as claimed in claim 1, it is characterised in that institute
Aqueousance artificial granite slurry is stated for the aqueous flat slurry #901 of chrysanthemum board.
10. the slurry coating process of full water-based simulated natural granite face effect as claimed in claim 1, it is characterised in that
The aqueous transparent varnish is chrysanthemum board water varnish #FP495.