CN106948220A - Preparation method of humidity-constant quality-kept and flavor-kept cigarette paper and cigarette paper prepared therefrom - Google Patents

Preparation method of humidity-constant quality-kept and flavor-kept cigarette paper and cigarette paper prepared therefrom Download PDF

Info

Publication number
CN106948220A
CN106948220A CN201710288040.4A CN201710288040A CN106948220A CN 106948220 A CN106948220 A CN 106948220A CN 201710288040 A CN201710288040 A CN 201710288040A CN 106948220 A CN106948220 A CN 106948220A
Authority
CN
China
Prior art keywords
cigarette paper
cigarette
ceramic powder
paper
kept
Prior art date
Application number
CN201710288040.4A
Other languages
Chinese (zh)
Inventor
陈毕峰
陈慷磊
Original Assignee
广州市花都联华包装材料有限公司
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 广州市花都联华包装材料有限公司 filed Critical 广州市花都联华包装材料有限公司
Priority to CN201710288040.4A priority Critical patent/CN106948220A/en
Publication of CN106948220A publication Critical patent/CN106948220A/en

Abstract

The invention discloses a preparation method of humidity-constant quality-kept and flavor-kept cigarette paper, which comprises the following steps: adding ceramic material powder into the paper-making pulp of cigarette paper, mixing, and making into cigarette paper. The invention also discloses a humidity-constant quality-kept and flavor-kept cigarette paper prepared from the preparation method, which comprises a cigarette paper body, wherein the ceramic powder is distributed in the cigarette paper body. Through the addition of ceramic powder in the paper-making pulp of cigarette paper, the humidity-constant quality-kept and flavor-kept cigarette paper is prepared. The cigarette product packaged with the cigarette paper disclosed by the invention can absorb moisture in a high-temperature and high-humidity environment, and release moisture in a low-temperature and low-humidity environment, and the quality of cigarette is not reduced due to the duration of storage and the difference of relative humidity and temperature of the environment, so as to effectively balance the moisture of the cigarette product, and keep the quality of the cigarette product.

Description

一种恒湿保质保香烟用卷烟纸的制备方法及烟用卷烟纸 One kind of humidity quality cigarettes and tobacco preparation of cigarette paper wrapping paper

技术领域 FIELD

[0001] 本发明涉及一种纸品的制备方法,具体涉及一种具有恒湿、保质保香功能的烟用卷烟纸的制备方法。 [0001] The present invention relates to a method for preparing paper products, particularly relates to the quality and function of incense smoke preparation having a constant humidity, with cigarette paper. 此外,本发明还涉及一种由该制备方法制备得到的烟用卷烟纸。 The present invention further relates to one kind of the smoke obtained by a preparation method of cigarette paper. 属于造纸技术领域。 Belonging to the technical field of papermaking.

背景技术 Background technique

[0002] 烟用卷烟纸作为卷烟辅料,在卷烟制造中占据极为重要的位置。 [0002] As the cigarette smoke materials, it occupies a very important position in cigarette manufacture of cigarette paper. 烟用卷烟纸主要由木浆纤维和无机填料组成,其中,木浆纤维占整体重量的70%以上。 Smoke mainly composed of wood pulp fibers and an inorganic filler of cigarette paper, wherein the pulp fibers comprise more than 70% of the overall weight. 然而,当卷烟采用现有的卷烟纸包装完毕进入市场后,卷烟产品会随着存放时间长和存放的高温、高湿环境而发生霉变,又或者,卷烟产品会由于低温、低湿的存放环境而影响卷烟的品质。 However, when using conventional cigarette paper cigarette packaging is completed to enter the market, along with cigarette products will be stored for a long time and stored in high temperature and high humidity environment mildew, or, cigarette products due to the low temperature, low-humidity storage environment affect the quality of cigarettes. 因此,如何解决卷烟由于存放环境的相对湿度、温度差异而导致的卷烟品质的变化问题,一直是烟草领域亟待解决的问题。 So, how to solve the problem of cigarette cigarette quality changes due Storage relative humidity, the temperature difference caused, it has been a tobacco field problems to be solved.

发明内容 SUMMARY

[0003] 本发明的目的在于克服现有技术的不足,提供一种烟用卷烟纸的制备方法,通过该方法制备得到的烟用卷烟纸具有恒湿、保质保香功能。 [0003] The object of the present invention is to overcome the disadvantages of the prior art, there is provided a method of preparing a smoke cigarette paper, obtained by a method of preparing the smoke of cigarette paper having a constant humidity, the quality and fragrance function.

[0004] 为实现上述目的,本发明采用以下技术方案: [0004] To achieve the above object, the present invention employs the following technical solution:

[0005] 一种恒湿保质保香烟用卷烟纸的制备方法,其制备步骤包括:在所述卷烟纸的造纸纸浆中加入陶瓷材料粉末,混合搅拌均匀后制备成卷烟纸。 [0005] A humidity quality cigarettes prepared cigarette paper, which preparation step comprises: a ceramic material powder is added to the papermaking pulp in the cigarette paper, cigarette paper mixed with stirring to prepare a uniformly.

[0006] 优选的是:所述陶瓷粉末的细度为600目-1500目。 [0006] It is preferable that: the fineness of the ceramic powder is 600 mesh -1500 mesh.

[0007] 优选的是:所述陶瓷粉末的单体粒径为1M1-100M1,且所述陶瓷粉末的单体表面具有孔径小于1 nm的微孔。 [0007] Preferred are: the diameter of the ceramic powder is a monomer 1M1-100M1, the monomer and the surface of the ceramic powder having a pore size of less than in 1 nm.

[0008] 优选的是:所述陶瓷粉末的比表面积为30g/m2-2000g/m2。 [0008] It is preferable that: the specific surface area of ​​the ceramic powder is 30g / m2-2000g / m2.

[0009] 优选的是:所述陶瓷粉末的添加量为造纸纸浆重量的l_20wt %。 [0009] It is preferable that: the addition amount of papermaking pulp l_20wt% by weight of ceramic powder.

[0010] 本发明的另一目的在于提供一种由如上所述的制备方法制备得到恒湿保质保香烟用卷烟纸。 [0010] Another object of the present invention is to provide a constant humidity to obtain the quality of cigarette paper cigarette prepared by the preparation method as described above.

[0011] 优选的是:所述烟用卷烟纸包括卷烟纸本体,所述卷烟纸本体中分布有陶瓷粉末。 [0011] Preferred are: the smoke of cigarette paper comprising a body cigarette paper, said cigarette paper distributed ceramic powder body.

[0012] 优选的是:所述陶瓷粉末的细度为600目-1500目。 [0012] Preferred are: the fineness of the ceramic powder is 600 mesh -1500 mesh.

[0013] 优选的是:所述陶瓷粉末的单体粒径为lMi-lOOwii,且所述陶瓷粉末的单体表面具有孔径小于lnm的微孔。 [0013] Preferred are: the diameter of the ceramic powder is a monomer lMi-lOOwii, the monomer and the surface of the ceramic powder having a pore size of less than lnm.

[0014] 优选的是:所述陶瓷粉末的比表面积为30g/m2-2000g/m2。 [0014] Preferred are: the specific surface area of ​​the ceramic powder is 30g / m2-2000g / m2.

[0015] 本发明的有益效果在于,本发明通过在卷烟纸的造纸纸浆中加入陶瓷粉末可制得具有恒湿、保质保香功能的烟用卷烟纸。 [0015] Advantageous effects of the present invention, the present invention is papermaking pulp by the addition of the ceramic powder of the cigarette paper may be produced with constant humidity, the quality and function of incense smoke of cigarette paper. 采用该烟用卷烟纸包装卷烟产品,可实现卷烟产品存放在高温、高湿环境下时能吸收水分,而当存放于低温、低湿环境下时能释放水分,不会因存放时间的长短以及环境相对湿度、温度的差异而降低卷烟的质量。 The cigarette paper using the cigarette tobacco packaged product, can be achieved in a high temperature storage of the cigarette product, it can absorb moisture when the humidity environment, and when stored at a low temperature, low-humidity environment can release water when the length of time will not be stored and the environment relative humidity, the temperature difference decreases the quality of cigarettes. 从而能有效地平衡卷烟产品水分,保持卷烟产品的品质。 So that it can effectively balance the cigarette product moisture, keeping the quality of cigarette products.

附图说明 BRIEF DESCRIPTION

[0016] 图1示出了本发明所述的烟用卷烟纸的结构示意图。 [0016] FIG. 1 shows a schematic structure of the smoke of cigarette paper according to the present invention.

具体实施方式 Detailed ways

[0017] 下面结合附图对本发明的具体实施方式做进一步说明。 [0017] The following drawings further illustrate specific embodiments of the present invention binds.

[0018] 本发明提供了一种恒湿保质保香烟用卷烟纸的制备方法,其制备步骤包括:将陶瓷材料粉碎成陶瓷粉末后添加到卷烟纸的纸浆中,搅拌混合均匀后按照本领域已知的卷烟纸常规生产工艺制备成卷烟纸即可。 [0018] The present invention provides a humidistat quality cigarettes prepared cigarette paper, which preparation comprises the step of: pulverizing a ceramic material into a cigarette paper added to the pulp after the ceramic powder is uniformly mixed with stirring in accordance with the present art prepared in a conventional production process of a conventional cigarette paper into a cigarette paper can.

[0019] 其中,所述陶瓷粉末的细度为600目-1500目,或者,所述陶瓷粉末的单体粒径为ly m-10〇Mi,且所述陶瓷粉末的单体表面具有孔径小于lnm的微孔。 [0019] wherein the fineness of the ceramic powder is 600 mesh -1500 mesh, or the monomer diameter of the ceramic powder is ly m-10〇Mi, and the surface of the monomer having a pore diameter less than the ceramic powder the microporous lnm. 进一步地,所述陶瓷粉末的比表面积为30g/m2-2000g/m2。 Further, the specific surface area of ​​the ceramic powder 30g / m2-2000g / m2. 更进一步地,所述陶瓷粉末的添加量为卷烟纸纸浆重量的1-20wt% 〇 Furthermore, the cigarette paper pulp added in an amount by weight of ceramic powder square 1-20wt%

[0020] 通过如上所述的制备方法制备得到的烟用卷烟纸,其具有如图1所示的结构,包括卷烟纸本体1,其中,所述卷烟纸本体1中分布有陶瓷粉末11。 [0020] with a cigarette paper, which has the structure shown in FIG. 1 was prepared by the method described above for preparing tobacco obtained cigarette paper comprising a body 1, wherein the body of the cigarette paper 1 in the ceramic powder 11 is distributed. 优选的是,所述陶瓷粉末11均匀分布在所述卷烟纸本体1中。 Preferably, the ceramic powder 11 uniformly distributed in a body of the cigarette paper.

[0021] 实施例1 [0021] Example 1

[0022] —种恒湿保质保香烟用卷烟纸,包括卷烟纸本体1,其中,所述卷烟纸本体1中含有均匀分布的陶瓷粉末11。 [0022] - the quality and types of cigarettes hygrostat cigarette paper, cigarette paper comprising a body 1, wherein the cigarette paper contains a ceramic powder body 1 11 uniformly distributed. 所述卷烟纸的制造过程包括:将陶瓷材料粉碎成细度为6〇〇目的陶瓷粉末后,按lwt%的重量百分比添加到卷烟纸的造纸纸浆中,搅拌混合均匀后按照本领域已知的卷烟纸常规生产工艺制备成卷烟纸即可。 The cigarette paper manufacturing process comprises: a ceramic material is pulverized to a fineness of the ceramic powder 6〇〇 object, according to lwt% by weight of papermaking pulp added to the cigarette paper and, after stirring uniformly mixed according to the known art conventional cigarette paper production process can be prepared as a cigarette paper.

[0023] 实施例2 [0023] Example 2

[0024] 重复实施例1,其不同之处在于:所述陶瓷粉末的细度为1200目,且其加入量为卷烟纸的造纸纸浆重量的2〇wt%。 [0024] Example 1 was repeated, except that which: the fineness of 1200 mesh ceramic powder, and added in an amount of papermaking pulp 2〇wt% by weight of the cigarette paper.

[0025] 实施例3 [0025] Example 3

[0026] 重复实施例1,其不同之处在于:所述陶瓷粉末的细度为1500目,且其加入量为卷烟纸的造纸纸衆重量的15wt%。 [0026] Example 1 was repeated, except that which: the fineness of 1500 mesh ceramic powder, and added in an amount of papermaking all cigarette paper weight 15wt%.

[0027] 实施例4 [0027] Example 4

[0028] —种恒湿保质保香烟用卷烟纸,包括卷烟纸本体1,其中,所述卷烟纸本体1中含有均匀分布的陶瓷粉末11。 [0028] - the quality and types of cigarettes hygrostat cigarette paper, cigarette paper comprising a body 1, wherein the cigarette paper contains a ceramic powder body 1 11 uniformly distributed. 所述卷烟纸的制造过程包括:将单体粒径为且单体表面具有小于lnm的微孔的陶瓷粉末按l〇wt%的重量百分比添加到卷烟纸的造纸纸浆中,搅拌混合均匀后按照本领域已知的卷烟纸常规生产工艺制备成卷烟纸即可。 The cigarette paper manufacturing process comprising: a monomer having a particle size of less than lnm micropores of a ceramic powder and a monomeric surfactant l〇wt% by weight percentage added to the papermaking pulp cigarette paper and, after stirring uniformly mixed in accordance with cigarette paper known in the art conventional production process can be prepared as a cigarette paper.

[0029] 实施例5 [0029] Example 5

[0030] 重复实施例4,其不同之处在于:所述陶瓷粉末的单体粒径为50M1、且单体表面具有小于lnm的微孔,所述陶瓷粉末的加入量为卷烟纸的造纸纸浆重量的8%。 [0030] Example 4 was repeated, except that which: the monomer of 50m1 diameter of the ceramic powder, and a monomer having surface pores of less than lnm, the ceramic powder is added in an amount of papermaking pulp cigarette paper 8% by weight.

[0031] 实施例6 [0031] Example 6

[0032] 重复实施例4,其不同之处在于:所述陶瓷粉末的单体粒径为100M1,且单体表面具有小于lnm的微孔,所述陶瓷粉末的加入量为卷烟纸的造纸纸浆重量的ISwt%。 [0032] Example 4 was repeated, except that which: the monomer diameter of the ceramic powder is 100m1, and monomers having surface pores of less than lnm, the ceramic powder is added in an amount of papermaking pulp cigarette paper ISwt% by weight.

[0033] 实施例7 [0033] Example 7

[0034] 一种恒湿保质保香烟用卷烟纸,包括卷烟纸本体1,其中,所述卷烟纸本体1中含有均匀分布的陶瓷粉末11。 [0034] A humidity cigarette quality of cigarette paper, cigarette paper comprising a body 1, wherein the cigarette paper contains a ceramic powder body 1 11 uniformly distributed. 所述卷烟纸的制造过程包括:将比表面积为30m2/g的陶瓷粉末按12wt %的重量百分比添加到卷烟纸的造纸纸浆中,搅拌混合均匀后按照本领域己知的卷烟纸常规生产工艺制备成卷烟纸即可。 The cigarette paper manufacturing process comprising: a specific surface area of ​​30m2 / g ceramic powder according to 12wt% by weight of papermaking pulp added to the cigarette paper and, after stirring uniformly mixed prepared according to art known conventional cigarette paper production process into a cigarette paper can.

[0035] 实施例8 [0035] Example 8

[0036] 重复实施例7,其不同之处在于:所述陶瓷粉末的比表面积为5〇〇m2/g,且其加入量为卷烟纸造纸纸楽的l〇wt%。 [0036] Example 7 was repeated, except that which: the specific surface area of ​​the ceramic powder is 5〇〇m2 / g, and it was added in an amount of cigarette paper in papermaking yue l〇wt%.

[0037] 实施例9 [0037] Example 9

[0038] 重复实施例7,其不同之处在于:所述陶瓷粉末的比表面积为2〇〇〇m2/g,且其加入量为卷烟纸造纸纸浆的3wt%。 [0038] Example 7 was repeated, except that which: the specific surface area of ​​the ceramic powder is 2〇〇〇m2 / g, and it was added in an amount of 3wt% of papermaking pulp cigarette paper.

[0039] 实施例1〇 [0039] Example 1〇

[0040] 重复实施例7,其不同之处在于:所述陶瓷粉末的比表面积为13〇〇m2/g,且其加入量为卷烟纸造纸纸楽的7wt%。 [0040] Example 7 was repeated, except that which: the specific surface area of ​​the ceramic powder is 13〇〇m2 / g, and it was added in an amount of 7wt% of the cigarette paper papermaking yue.

[0041] 本发明己通过优选的实施方式进行了详尽的说明。 Hexyl [0041] The present invention has been described in detail by preferred embodiments. 然而,通过对前文的研读,对各实施方式的变化和增加也是本领域的一般技术人员所显而易见的。 However, the study of the foregoing, changes and additions to the various embodiments are those skilled in the art are apparent. 申请人的意图是所有这些变化和增加落在了本发明权利要求的保护范围中。 Applicants' intent is that all these changes and additions fall within the scope of the claims of the invention. 本文中使用的术语仅为对具体的实施例加以说明,其并非意在对本发明进行限制。 The terms used herein are merely specific examples of the embodiment will be described, it is not intended to be limiting of the invention. 除非另有定义,本文中使用的所有术语(包括技术术语和科学术语)均与本发明所属领域的一般技术人员的理解相同。 Unless otherwise defined, all terms (including technical and scientific terms) have the same understanding of the present invention, those of ordinary skill in the art. 任何对此产品进行的修饰与改良,在专利范围或范畴内同类或相近物质的替代与使用,均属于本发明专利保护范围。 Any modification and improvement for this product, with the same or alternatively in the scope of use or scope similar substances belong to the scope of protection of the present invention.

Claims (10)

1. 一种恒湿保质保香烟用卷烟纸的制备方法,其特征在于:包括以下步骤:包括在所述卷烟纸的造纸纸浆中加入陶瓷材料粉末,混合搅拌均匀后制备成卷烟纸。 A humidity quality cigarette wrapping paper preparation method, characterized by: comprising the steps of: including a ceramic material powder is added to the papermaking pulp in the cigarette paper, cigarette paper mixed with stirring to prepare a uniformly.
2. 根据权利要求1所述的制备方法,其特征在于:所述陶瓷粉末的细度为600目-1500 目。 2. The production method according to claim 1, wherein: the fineness of the ceramic powder is 600 mesh -1500 mesh.
3. 根据权利要求1所述的制备方法,其特征在于:所述陶瓷粉末的单体粒径为lwn-lOOy m,且所述陶瓷粉末的单体表面具有孔径小于lnm的微孔。 3. The production method according to claim 1, wherein: said monomer particle diameter of the ceramic powder is lwn-lOOy m, and the surface of the ceramic powder of the monomer having a pore size of less than lnm.
4. 根据权利要求1所述的制备方法,其特征在于:所述陶瓷粉末的比表面积为30g/m2-2000g/m2。 4. The production method according to claim 1, wherein: the specific surface area of ​​the ceramic powder is 30g / m2-2000g / m2.
5. 根据权利要求1-4中任意一项所述的制备方法,其特征在于:所述陶瓷粉末的添加量为造纸纸衆重量的l-20wt%。 The production method of any one of claims 1-4, characterized in that: the addition amount of l-20wt% by weight of all papermaking ceramic powder.
6. —种恒湿保质保香烟用卷烟纸,其特征在于:所述卷烟纸由如权利要求1-4中任意一项所述的制备方法制备得到。 6. - Species hygrostat cigarette quality of cigarette paper, wherein: the cigarette paper obtained by the preparation as claimed in any one of claims 1 to 4 prepared requirements.
7. 根据权利要求6所述的烟用卷烟纸,其特征在于:所述烟用卷烟纸包括卷烟纸本体, 所述卷烟纸本体中分布有陶瓷粉末。 The cigarette according to claim 6 of cigarette paper, characterized in that: said cigarette comprising a cigarette paper body cigarette paper, said cigarette paper distributed ceramic powder body.
8. 根据权利要求7所述的烟用卷烟纸,其特征在于:所述陶瓷粉末的细度为600目-1500 目。 8. The cigarette according to claim 7, wherein the cigarette paper, characterized in that: the fineness of the ceramic powder is 600 mesh -1500 mesh.
9. 根据权利要求7所述的烟用卷烟纸,其特征在于:所述陶瓷粉末的单体粒径为lwn-100M1,且所述陶瓷粉末的单体表面具有孔径小于lnm的微孔。 9. The cigarette according to claim 7, wherein the cigarette paper, characterized in that: said monomer particle diameter of the ceramic powder is lwn-100M1, the monomer and the surface of the ceramic powder having a pore size of less than lnm.
10. 根据权利要求7所述的烟用卷烟纸,其特征在于:所述陶瓷粉末的比表面积为30g/ m2—2000g/m2。 10. The cigarette according to claim 7 with the cigarette paper, characterized in that: the specific surface area of ​​the ceramic powder is 30g / m2-2000g / m2.
CN201710288040.4A 2017-04-27 2017-04-27 Preparation method of humidity-constant quality-kept and flavor-kept cigarette paper and cigarette paper prepared therefrom CN106948220A (en)