CN106854450A - Broken stone water permeability pavement solvent-free single-component polyurethane adhesive and preparation method thereof - Google Patents
Broken stone water permeability pavement solvent-free single-component polyurethane adhesive and preparation method thereof Download PDFInfo
- Publication number
- CN106854450A CN106854450A CN201611266232.7A CN201611266232A CN106854450A CN 106854450 A CN106854450 A CN 106854450A CN 201611266232 A CN201611266232 A CN 201611266232A CN 106854450 A CN106854450 A CN 106854450A
- Authority
- CN
- China
- Prior art keywords
- solvent
- water permeability
- component polyurethane
- broken stone
- polyurethane adhesive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to technical field of chemical synthesis, and in particular to a kind of broken stone water permeability pavement solvent-free single-component polyurethane adhesive and preparation method thereof.Broken stone water permeability pavement is made up with solvent-free single-component polyurethane adhesive of the following raw material:PPG, isocyanates, plasticizer, silane coupler, antioxidant, ultra-violet absorber, catalyst, latent curing agent.The present invention solves the problems, such as that organic solvent has penetrating odor and harm health because solvent-free, it is a kind of Environment-friendlyadhesive adhesive, because introducing silane coupler and latent curing agent improve the adhesive strength of one-package adhesive and solve the problems, such as to be solidified with bubble generation and curing rate is slow, and it is heat-resisting, it is low temperature resistant, there is simple to operate, the advantage of easy construction relative to two component adhesive.
Description
Technical field
The invention belongs to technical field of chemical synthesis, and in particular to a kind of broken stone water permeability pavement poly- ammonia of solvent-free single-component
Ester adhesive and preparation method thereof.
Background technology
The high speed development of modern city, supporting road traffic facility, earth's surface mat formation and manual construction thing increase, composition
The impermeable material of these structures such as cement, pitch, pavement bricks, metal etc. result in track, pavement, parking lot, wide
Often become fluid-tight hard ground, blocked the chance that rainwater penetrates soil so that rainwater fling rivers and creeks or tube and
Ground cannot be looped back, and these road surfaces lack water penetration and gas permeability has intercepted heat, the moisture of atmosphere and rainwash
Circulation, so-called " tropical island effect " is produced to the regulating power of urban surface temperature humidity so as to substantially reduce.
Water-permeable pavement and sub-surface cause the soil that permeated the ground under the water energy on road surface is rapid.Therefore, water penetration road
The laying in face can reduce water logging street, alleviate urban heat land effect.Adhesive is resin type water-permeable brick or the scene permeable road of laying
One of critical material that face makes, what is used at present is generally epoxy resin, phenolic resin, polyurethane etc..And epoxy resin is tough
Property it is poor, impact strength is low, and matter is crisp after solidification, and the color of phenolic resin is relatively deep, have certain fragility, be easily cracked, polyurethane adhesive
Stick possesses excellent shear strength and impact property, and possesses excellent flexible nature, excellent rubber property, can fit
Answer the bonding of different heat expansion coefficient base material, not only bonding force is strong, while also have excellent buffering, shock-absorbing function, low temperature and
Ultralow temperature performance exceedes the adhesive of every other type, it is adaptable to various structural bonding fields.
Chinese patent CN1995257A makees base-material with thermosetting epoxy resin, adds polyamide-based resin, absolute ethyl alcohol, oxygen
Base silane coupling agent, phenol accelerant and 2,4-DTBP, the porous pavement adhesive prepared at room temperature 24 hours
It is curable., with epoxy resin as base-material, fragility is big, and easy to crack, impact resistance is poor for the patent.
Chinese patent CN104004490A adds various functions resin to be prepared for curing rate soon with polyurethane as base material,
The double-component water-permeable brick adhesive such as mechanical property is good, but preparation process is more complicated, in-convenience in use.
The content of the invention
It is an object of the invention to provide a kind of broken stone water permeability pavement solvent-free single-component polyurethane adhesive, with applicable
Phase is long, intensity is high, quick solidifying and be difficult foaming, hardness good-toughness, good base adhesive power, simple to operate, easy construction
And the characteristics of environmental protection;Invention also provides the preparation side of broken stone water permeability pavement solvent-free single-component polyurethane adhesive
Method, it is scientific and reasonable, simple and easy to apply.
Broken stone water permeability pavement solvent-free single-component polyurethane adhesive of the present invention, by following percentage by weight
Raw material is made:
Described PPG is diethylene glycol for initiator, expoxy propane open loop, ethylene oxide-capped, degree of functionality are
2nd, molecular weight is the polyalcohol of 2000-3000, and degree of functionality is 3, number-average molecular weight in the polyalcohol or castor oil of 300-500
One or more.
Described isocyanates is one or two of MDI or polyphenyl polymethylene polyisocyanates.
Described plasticizer is environment-friendly epoxy carburetion fat, preferably ethyl hexyl ester of epoxidized soybean oil or epoxy acetyl linolenic acid
One or two in methyl esters.
Described silane coupler is isocynate silane coupling agent, preferred isocyanate base propyl-triethoxysilicane.
Described antioxidant is 1,3,5- trimethyls -2,4,6- three (3,5- di-t-butyl -4- hydroxy benzenes) benzene.
Described ultra-violet absorber is the 2,4- tert-butyl groups -6- (5- chlorinated benzotriazoles base -2) phenol.
One or more in described catalyst naphthenic acid rare earth, isooctoate of rare earth metal or bismuth naphthenate.
Described latent curing agent is oxazolidine class latent curing agent, preferably 2- isopropyls-N- ethoxys-oxazolidine ester type compound.
The preparation method of broken stone water permeability pavement solvent-free single-component polyurethane adhesive of the present invention, step is such as
Under:
(1) first load weighted PPG and plasticizer are added in reactor, are heated up, in 90-100 DEG C, vacuum-
Under the conditions of 0.1MPa, it is dehydrated 1-2 hours, 0.1% is less than to moisture;
(2) 30-45 DEG C is cooled to, isocyanates, antioxidant, ultra-violet absorber is added, it is anti-under the conditions of 70-90 DEG C of intensification
1-2.5h is answered, less than 70 DEG C are cooled to, silane coupler, catalyst and latent curing agent is added, 15-30min is stirred, 50 are cooled to
DEG C, barrelling is obtained product.
The present invention compared with prior art, has the advantages that:
The present invention solves the problems, such as that organic solvent has penetrating odor and harm health because solvent-free, is a kind of environmental protection
Type adhesive, improves the adhesive strength of one-package adhesive and solves and be solidified with because introducing silane coupler and latent curing agent
Bubble is produced and the slow problem of curing rate, and heat-resisting, low temperature resistant, has simple to operate, construction relative to two component adhesive
Convenient advantage.
Specific embodiment
The present invention is described further with reference to embodiments.
Embodiment 1
Single-component polyurethane adhesive 1000g is prepared, by PPG (the expoxy propane open loop, epoxy second of formula ratio
Alkane is blocked, and degree of functionality is 2, and molecular weight is the polyalcohol of 2000-3000) 350g, (degree of functionality is 3 to PPG, the equal molecule of number
Measuring the polyalcohol for 300-500) 80g and castor oil 70g and plasticizer (ethyl hexyl ester of epoxidized soybean oil) 100g normal temperature is added to reaction
In kettle, 100 DEG C are warmed up to, are dehydrated 1.5 hours (- 0.1MPa vacuums), moisture is less than 0.1%, is cooled to 40 DEG C, adds many benzene
Quito methylene polyisocyanates 300g, antioxidant 1,3,5- trimethyls -2,4,6- three (3,5- di-t-butyl -4- hydroxy benzenes) benzene
10g, ultra-violet absorber 2, the 4- tert-butyl groups -6- (5- chlorinated benzotriazoles base -2) phenol 10g react under the conditions of 80 DEG C of intensification
2h, cools to 65 DEG C, adds catalyst naphthenic acid rare earth 5g, NCO propyl-triethoxysilicane 50g, 2- of formula ratio
Isopropyl-N- ethoxys-oxazolidine ester type compound 15g, stir 20min, are cooled to 50 DEG C, barrelling.
Embodiment 2
Single-component polyurethane adhesive 1000g is prepared, by PPG (the expoxy propane open loop, epoxy second of formula ratio
Alkane is blocked, and degree of functionality is 2, and molecular weight is the polyalcohol of 2000-3000) 280g, (degree of functionality is 3 to PPG, the equal molecule of number
Measuring the polyalcohol for 300-500) 70g and castor oil 80g and plasticizer (ethyl hexyl ester of epoxidized soybean oil) 80g normal temperature is added to reactor
In, be warmed up to 100 DEG C, be dehydrated 1.5 hours (- 0.1MPa vacuums), moisture is less than 0.1%, is cooled to 40 DEG C, add MDI and
Polyphenyl polymethylene polyisocyanates distinguish 140 and 300g, (the tertiary fourths of 3,5- bis- of antioxidant 1,3,5- trimethyls -2,4,6- three
Base -4- hydroxy benzenes) benzene 5g, ultra-violet absorber 2, the 4- tert-butyl groups -6- (5- chlorinated benzotriazoles base -2) phenol 5g, heat up 80 DEG C
Under the conditions of react 2h, cool to 65 DEG C, add catalyst naphthenic acid rare earth 8g, the NCO propyl triethoxy of formula ratio
Silane 20g, 2- isopropyl-N- ethoxys-oxazolidine ester type compound 12g, stir 20min, are cooled to 50 DEG C, barrelling.
Embodiment 3
Single-component polyurethane adhesive 1000g is prepared, by PPG (the expoxy propane open loop, epoxy second of formula ratio
Alkane is blocked, and degree of functionality is 2, and molecular weight is the polyalcohol of 2000-3000) 300g, (degree of functionality is 3 to PPG, the equal molecule of number
Measuring the polyalcohol for 300-500) 100g and plasticizer (ethyl hexyl ester of epoxidized soybean oil) 80g normal temperature is added in reactor, is warmed up to
100 DEG C, 1.5 hours (- 0.1MPa vacuums) is dehydrated, moisture is less than 0.1%, is cooled to 40 DEG C, adds MDI and many phenyl how sub-
Methyl polyisocyanates distinguishes 70 and 300g, antioxidant 1,3,5- trimethyls -2,4,6- three (3,5- di-t-butyl -4- hydroxy benzenes)
Benzene 5g, ultra-violet absorber 2, the 4- tert-butyl groups -6- (5- chlorinated benzotriazoles base -2) phenol 5g react under the conditions of 80 DEG C of intensification
2h, cools to 65 DEG C, adds catalyst naphthenic acid rare earth 5g, NCO propyl-triethoxysilicane 30g, 2- of formula ratio
Isopropyl-N- ethoxys-oxazolidine ester type compound 15g, stir 20min, are cooled to 50 DEG C, barrelling.
Embodiment 4
Single-component polyurethane adhesive 1000g is prepared, by PPG (the expoxy propane open loop, epoxy second of formula ratio
Alkane is blocked, and degree of functionality is 2, and molecular weight is the polyalcohol of 2000-3000) 330g, castor oil 130g and plasticizer (epoxidized soybean oil
Misery ester) 80g normal temperature is added in reactor, is warmed up to 100 DEG C, is dehydrated 1.5 hours (- 0.1MPa vacuums), and moisture is less than
0.1%, 40 DEG C are cooled to, add MDI and polyphenyl polymethylene polyisocyanates to distinguish 90 and 290g, antioxidant 1,3,5- tri-
Methyl -2,4,6- three (3,5- di-t-butyl -4- hydroxy benzenes) benzene 5g, the ultra-violet absorber 2,4- tert-butyl groups -6- (5- chloro benzos
Triazolyl -2) phenol 5g, 2h is reacted under the conditions of 80 DEG C of intensification, 65 DEG C are cooled to, add the catalyst naphthenic acid rare earth of formula ratio
5g, NCO propyl-triethoxysilicane 40g, 2- isopropyl-N- ethoxys-oxazolidine ester type compound 25g, stirring
20min, is cooled to 50 DEG C, barrelling.
The product that embodiment 1-4 is obtained carries out quantitative measurement, the results are shown in Table 1.
The embodiment 1-4 product physical property tables of table 1
Embodiment 1 | Embodiment 2 | Embodiment 3 | Embodiment 4 | |
Applicable time min | 40 | 35 | 40 | 30 |
Shore hardness D | 29 | 45 | 30 | 35 |
Tensile strength MPa | 8.2 | 9.5 | 8.7 | 9.3 |
Elongation at break % | 146.3 | 159.4 | 170.9 | 145.8 |
Claims (10)
1. a kind of broken stone water permeability pavement solvent-free single-component polyurethane adhesive, it is characterised in that by following percentage by weight
Raw material is made:
2. broken stone water permeability pavement solvent-free single-component polyurethane adhesive according to claim 1, it is characterised in that institute
The PPG stated is diethylene glycol for initiator, expoxy propane open loop, ethylene oxide-capped, degree of functionality are that 2, molecular weight is
The polyalcohol of 2000-3000, degree of functionality is the one kind or many in the polyalcohol or castor oil that 3, number-average molecular weight is 300-500
Kind.
3. broken stone water permeability pavement solvent-free single-component polyurethane adhesive according to claim 1, it is characterised in that institute
The isocyanates stated is one or two of MDI or polyphenyl polymethylene polyisocyanates.
4. broken stone water permeability pavement solvent-free single-component polyurethane adhesive according to claim 1, it is characterised in that institute
The plasticizer stated is environment-friendly epoxy carburetion fat.
5. broken stone water permeability pavement solvent-free single-component polyurethane adhesive according to claim 1, it is characterised in that institute
The silane coupler stated is isocynate silane coupling agent.
6. broken stone water permeability pavement solvent-free single-component polyurethane adhesive according to claim 1, it is characterised in that institute
The antioxidant stated is 1,3,5- trimethyls -2,4,6- three (3,5- di-t-butyl -4- hydroxy benzenes) benzene.
7. broken stone water permeability pavement solvent-free single-component polyurethane adhesive according to claim 1, it is characterised in that institute
The ultra-violet absorber stated is the 2,4- tert-butyl groups -6- (5- chlorinated benzotriazoles base -2) phenol.
8. broken stone water permeability pavement solvent-free single-component polyurethane adhesive according to claim 1, it is characterised in that institute
One or more in catalyst naphthenic acid rare earth, isooctoate of rare earth metal or the bismuth naphthenate stated.
9. broken stone water permeability pavement solvent-free single-component polyurethane adhesive according to claim 1, it is characterised in that institute
The latent curing agent stated is oxazolidine class latent curing agent.
10. the preparation of any described broken stone water permeability pavement solvent-free single-component polyurethane adhesives of a kind of claim 1-9
Method, it is characterised in that step is as follows:
(1) first load weighted PPG and plasticizer are added in reactor, are heated up, in 90-100 DEG C, vacuum-
Under the conditions of 0.1MPa, it is dehydrated 1-2 hours, 0.1% is less than to moisture;
(2) 30-45 DEG C is cooled to, isocyanates, antioxidant, ultra-violet absorber is added, 1- is reacted under the conditions of 70-90 DEG C of intensification
2.5h, is cooled to less than 70 DEG C, adds silane coupler, catalyst and latent curing agent, stirs 15-30min, is cooled to 50 DEG C,
Barrelling is obtained product.