CN106854412A - A kind of wear-resisting antifouling double-component polyurethane coating and preparation method thereof - Google Patents
A kind of wear-resisting antifouling double-component polyurethane coating and preparation method thereof Download PDFInfo
- Publication number
- CN106854412A CN106854412A CN201611133840.0A CN201611133840A CN106854412A CN 106854412 A CN106854412 A CN 106854412A CN 201611133840 A CN201611133840 A CN 201611133840A CN 106854412 A CN106854412 A CN 106854412A
- Authority
- CN
- China
- Prior art keywords
- coating
- component
- wear
- polyurethane
- white
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses wear-resisting antifouling double-component polyurethane coating of one kind and preparation method thereof, it is formulated by the raw material of following weight portion:Polyoxypropyleneglycol 70 80, hexamethylene diisocyanate 140 150, sorbierite 46, monoethanolamine 24, acrylate 79, dipropylene glycol dibenzoate 56, peroxidating trimethylacetic acid tertiary butyl ester 23 etc..The present invention is coordinated as film forming matter using polyurethane, acrylate etc., the present invention is possessed good film forming characteristics;The raw materials such as sub-white corundum fine powder, white graphite, the aluminium titanates of addition, can be in the presence of polypropylene glycol, sodium metnylene bis-naphthalene sulfonate, uniformly, it is dispersed stably in coating, the abrasive resistance of coating can be strengthened, the raw materials such as dipropylene glycol dibenzoate, the tridecafluoro-n-octyltriethoxysilane of addition, can improve antifouling, the water resistance of coating.
Description
Technical field
The present invention relates to a kind of coating, a kind of wear-resisting antifouling double-component polyurethane coating and its preparation are concretely related to
Method.
Background technology
Polyurethane coating is a class coating more typical at present, can be divided into bicomponent polyurethane coating and single group segregation ammonia
Ester paint.Bicomponent polyurethane coating is usually to be made up of isocyanate prepolymer and hydroxy-containing resin two parts, commonly referred to
Curing agent component and host component.The various types of this class coating, range of application is also very wide, according to the difference of hydroxy-containing component
The kinds such as acroleic acid polyurethane, alcohol acid and polyurethane, polyester-polyurethane, polyether-polyurethane, epoxy polyurethane can be divided into.Typically all have
There are good mechanical performance, solids content higher, the performance of each side all relatively good, be a class rising at present
Coating variety.Main application direction has woodwork coating, automobile repairing paint, anticorrosive paint, floor paint, electronic paint, extraordinary painting
Material, polyurethane water-proof paint etc..One-can urethane coating mainly has urethane oil paint, moisture solidification polyurethane coating, closing
The kinds such as type polyurethane coating.Application surface is wide not as two-component coating, is mainly used in floor paint, anticorrosive paint, pre- coiled material and applies
Material etc., its overall performance is comprehensive not as two-component coating.Because coating generally requires the outer surface for being attached to object, so can be through
Often rubbed by other objects, or adhered to by some dirts, influenceed attractive in appearance, it is therefore desirable to a kind of wear-resisting Anti-fouling polyurethanes coating.
The content of the invention
It is an object of the invention to provide wear-resisting antifouling double-component polyurethane coating of one kind and preparation method thereof.
To reach above-mentioned purpose, the technical solution used in the present invention is:
A kind of wear-resisting antifouling double-component polyurethane coating, is formulated by the raw material of following weight portion:Polyoxypropyleneglycol 70-
80th, hexamethylene diisocyanate 140-150, sorbierite 4-6, monoethanolamine 2-4, acrylate 7-9, dipropylene glycol hexichol
Formic acid esters 5-6, peroxidating trimethylacetic acid tertiary butyl ester 2-3, cobalt naphthenate 1-2, polypropylene glycol 12-14, sub-white corundum fine powder 14-
16th, white graphite 6-8, inulin lauryl carbamate 7-9, tridecafluoro-n-octyltriethoxysilane 3-5, Lime Hypophosphate 4-
7th, aluminium titanates 6-8, Tissuemat E 8-10, HEMC 4-7, sodium metnylene bis-naphthalene sulfonate 2-3, polyoxypropylene are sweet
Oily ether 3-6, pentaerythritol stearic acid ester 2 5-8, calcium stearate 7-9, cetyl dimethicone 8-10, propandiol butyl ether
5-7, polyvinylpyrrolidone 2-4, appropriate deionized water.
A kind of preparation method of wear-resisting antifouling double-component polyurethane coating, comprises the following steps:
(1)It is 1: 2-3 mixing according to mol ratio by polyoxypropyleneglycol, hexamethylene diisocyanate, in nitrogen atmosphere
60-80min is reacted in 55-75 DEG C, sorbierite is added, NCO/OH mol ratios are 1.2-1.4 in regulation system, anti-at 60-80 DEG C
100-150min is answered, monoethanolamine is subsequently adding, 40-60min is reacted at 40-60 DEG C, obtain base polyurethane prepolymer for use as;
(2)Sequentially add acrylate, dipropylene glycol dibenzoate, peroxidating uncle penta by weight in a kettle.
Sour tertiary butyl ester, cobalt naphthenate, polypropylene glycol, then stirring heat up, and treat that temperature is raised to 65 DEG C of disposable addition polyurethane before
Performed polymer, then temperature is raised to 85-90 DEG C, 40-50 DEG C is cooled to after insulation reaction 2-3h, obtain final product component A;
(3)To addition sub-white corundum fine powder, white graphite, inulin lauryl carbamate, the second of ten trifluoro octyl group three in mill
TMOS, Lime Hypophosphate, aluminium titanates, Tissuemat E, HEMC, sodium metnylene bis-naphthalene sulfonate, polyoxy third
Alkene glycerin ether, pentaerythritol stearic acid ester 2, calcium stearate, cetyl dimethicone, propandiol butyl ether, polyethylene pyrrole
The raw materials such as pyrrolidone, are vacuumized after mixing 8-10min at a temperature of 130-150 DEG C, and 80-100min is stood under vacuum condition,
Then 45-50 μm of fineness is ground to using three-roller, obtains B component;
(4)Component A and B component are pressed 1:(0.4-0.5)Ratio mixing after, add appropriate ionized water be well mixed, i.e.,
Obtain the coating.
Beneficial effects of the present invention:
The present invention is coordinated as film forming matter using polyurethane, acrylate etc., the present invention is possessed good film forming characteristics;Add
Plus the raw material such as sub-white corundum fine powder, white graphite, aluminium titanates, can in the presence of polypropylene glycol, sodium metnylene bis-naphthalene sulfonate,
Uniformly, it is dispersed stably in coating, can strengthens the abrasive resistance of coating, the dipropylene glycol dibenzoate of addition,
The raw materials such as tridecafluoro-n-octyltriethoxysilane, can improve antifouling, the water resistance of coating.
Specific embodiment
Technical scheme of the present invention is further described with reference to specific embodiment.
Embodiment 1:
A kind of wear-resisting antifouling double-component polyurethane coating, by following weight portion(kg)Raw material be formulated:PPOX two
Alcohol 70, hexamethylene diisocyanate 140, sorbierite 4, monoethanolamine 2, acrylate 7, dipropylene glycol dibenzoate 5,
Peroxidating trimethylacetic acid tertiary butyl ester 2, cobalt naphthenate 1, polypropylene glycol 12, sub-white corundum fine powder 14, white graphite 6, inulin lauryl base
Carbamate 7, tridecafluoro-n-octyltriethoxysilane 3, Lime Hypophosphate 4, aluminium titanates 6, Tissuemat E 8, hydroxyethyl methyl
Cellulose 4, sodium metnylene bis-naphthalene sulfonate 2, polypropylene glycerol aether 3, pentaerythritol stearic acid ester 25, calcium stearate 7, spermaceti
Base dimethyl silicone polymer 8, propandiol butyl ether 5, polyvinylpyrrolidone 2, appropriate deionized water.
A kind of preparation method of wear-resisting antifouling double-component polyurethane coating, comprises the following steps:
(1)It is 1: 2-3 mixing according to mol ratio by polyoxypropyleneglycol, hexamethylene diisocyanate, in nitrogen atmosphere
60-80min is reacted in 55-75 DEG C, sorbierite is added, NCO/OH mol ratios are 1.2-1.4 in regulation system, anti-at 60-80 DEG C
100-150min is answered, monoethanolamine is subsequently adding, 40-60min is reacted at 40-60 DEG C, obtain base polyurethane prepolymer for use as;
(2)Sequentially add acrylate, dipropylene glycol dibenzoate, peroxidating uncle penta by weight in a kettle.
Sour tertiary butyl ester, cobalt naphthenate, polypropylene glycol, then stirring heat up, and treat that temperature is raised to 65 DEG C of disposable addition polyurethane before
Performed polymer, then temperature is raised to 85-90 DEG C, 40-50 DEG C is cooled to after insulation reaction 2-3h, obtain final product component A;
(3)To addition sub-white corundum fine powder, white graphite, inulin lauryl carbamate, the second of ten trifluoro octyl group three in mill
TMOS, Lime Hypophosphate, aluminium titanates, Tissuemat E, HEMC, sodium metnylene bis-naphthalene sulfonate, polyoxy third
Alkene glycerin ether, pentaerythritol stearic acid ester 2, calcium stearate, cetyl dimethicone, propandiol butyl ether, polyethylene pyrrole
The raw materials such as pyrrolidone, are vacuumized after mixing 8-10min at a temperature of 130-150 DEG C, and 80-100min is stood under vacuum condition,
Then 45-50 μm of fineness is ground to using three-roller, obtains B component;
(4)Component A and B component are pressed 1:(0.4-0.5)Ratio mixing after, add appropriate ionized water be well mixed, i.e.,
Obtain the coating.
Embodiment 2:
A kind of wear-resisting antifouling double-component polyurethane coating, by following weight portion(kg)Raw material be formulated:PPOX two
Alcohol 75, hexamethylene diisocyanate 145, sorbierite 5, monoethanolamine 3, acrylate 8, dipropylene glycol dibenzoate
5.5th, peroxidating trimethylacetic acid tertiary butyl ester 2.5, cobalt naphthenate 1.5, polypropylene glycol 13, sub-white corundum fine powder 15, white graphite 7, chrysanthemum
Powder lauryl carbamate 8, tridecafluoro-n-octyltriethoxysilane 4, Lime Hypophosphate 5.5, aluminium titanates 7, Tissuemat E 9,
HEMC 5.5, sodium metnylene bis-naphthalene sulfonate 2.5, polypropylene glycerol aether 4.5, pentaerythritol stearic acid ester 2
6.5th, calcium stearate 8, cetyl dimethicone 9, propandiol butyl ether 6, polyvinylpyrrolidone 3, appropriate deionized water.
Preparation method is with embodiment 1.
Embodiment 3:
A kind of wear-resisting antifouling double-component polyurethane coating, it is characterised in that by following weight portion(kg)Raw material be formulated:It is poly-
Propylene oxide glycol 80, hexamethylene diisocyanate 150, sorbierite 6, monoethanolamine 4, acrylate 9, dipropylene glycol two
Benzoic ether 6, peroxidating trimethylacetic acid tertiary butyl ester 3, cobalt naphthenate 2, polypropylene glycol 14, sub-white corundum fine powder 16, white graphite 8,
Inulin lauryl carbamate 9, tridecafluoro-n-octyltriethoxysilane 5, Lime Hypophosphate 7, aluminium titanates 8, Tissuemat E
10th, HEMC 7, sodium metnylene bis-naphthalene sulfonate 3, polypropylene glycerol aether 6, pentaerythritol stearic acid ester 28,
Calcium stearate 9, cetyl dimethicone 10, propandiol butyl ether 7, polyvinylpyrrolidone 4, appropriate deionized water.
Preparation method is with embodiment 1.
The performance test results of wear-resisting Anti-fouling polyurethanes coating are as shown in the table obtained in above-described embodiment 1-3:
The performance test results of wear-resisting Anti-fouling polyurethanes coating obtained in the embodiment 1-3 of table 1
Embodiment 1 | Embodiment 2 | Embodiment 3 | |
Abrasion loss, mg | 2.2 | 1.7 | 1.9 |
Coating water contact angle, ° | 104.6 | 105.8 | 102.7 |
Coating oil contact angle, ° | 56 | 59 | 57 |
Coating light transmittance, % | 90.4 | 92.3 | 91.8 |
Claims (2)
1. a kind of wear-resisting antifouling double-component polyurethane coating, it is characterised in that be formulated by the raw material of following weight portion:Polyoxy
Change propylene glycol 70-80, hexamethylene diisocyanate 140-150, sorbierite 4-6, monoethanolamine 2-4, acrylate 7-9, one
Contracting dipropylene glycol dibenzoate 5-6, peroxidating trimethylacetic acid tertiary butyl ester 2-3, cobalt naphthenate 1-2, polypropylene glycol 12-14, Asia
White fused alumina fine powder 14-16, white graphite 6-8, inulin lauryl carbamate 7-9, tridecafluoro-n-octyltriethoxysilane 3-5,
Lime Hypophosphate 4-7, aluminium titanates 6-8, Tissuemat E 8-10, HEMC 4-7, sodium metnylene bis-naphthalene sulfonate 2-
3rd, polypropylene glycerol aether 3-6, pentaerythritol stearic acid ester 2 5-8, calcium stearate 7-9, cetyl dimethicone 8-
10th, propandiol butyl ether 5-7, polyvinylpyrrolidone 2-4, appropriate deionized water.
2. a kind of preparation method of wear-resisting antifouling double-component polyurethane coating according to claim 1, it is characterised in that bag
Include following steps:
(1)It is 1: 2-3 mixing according to mol ratio by polyoxypropyleneglycol, hexamethylene diisocyanate, in nitrogen atmosphere
60-80min is reacted in 55-75 DEG C, sorbierite is added, NCO/OH mol ratios are 1.2-1.4 in regulation system, anti-at 60-80 DEG C
100-150min is answered, monoethanolamine is subsequently adding, 40-60min is reacted at 40-60 DEG C, obtain base polyurethane prepolymer for use as;
(2)Sequentially add acrylate, dipropylene glycol dibenzoate, peroxidating uncle penta by weight in a kettle.
Sour tertiary butyl ester, cobalt naphthenate, polypropylene glycol, then stirring heat up, and treat that temperature is raised to 65 DEG C of disposable addition polyurethane before
Performed polymer, then temperature is raised to 85-90 DEG C, 40-50 DEG C is cooled to after insulation reaction 2-3h, obtain final product component A;
(3)To addition sub-white corundum fine powder, white graphite, inulin lauryl carbamate, the second of ten trifluoro octyl group three in mill
TMOS, Lime Hypophosphate, aluminium titanates, Tissuemat E, HEMC, sodium metnylene bis-naphthalene sulfonate, polyoxy third
Alkene glycerin ether, pentaerythritol stearic acid ester 2, calcium stearate, cetyl dimethicone, propandiol butyl ether, polyethylene pyrrole
The raw materials such as pyrrolidone, are vacuumized after mixing 8-10min at a temperature of 130-150 DEG C, and 80-100min is stood under vacuum condition,
Then 45-50 μm of fineness is ground to using three-roller, obtains B component;
(4)Component A and B component are pressed 1:(0.4-0.5)Ratio mixing after, add appropriate ionized water be well mixed, i.e.,
Obtain the coating.