CN106854060A - A kind of ecological permeable bricks and preparation method thereof - Google Patents
A kind of ecological permeable bricks and preparation method thereof Download PDFInfo
- Publication number
- CN106854060A CN106854060A CN201611220462.XA CN201611220462A CN106854060A CN 106854060 A CN106854060 A CN 106854060A CN 201611220462 A CN201611220462 A CN 201611220462A CN 106854060 A CN106854060 A CN 106854060A
- Authority
- CN
- China
- Prior art keywords
- weight portions
- weight
- water
- admixture
- binder materials
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a kind of ecological permeable bricks and preparation method thereof, water-permeable brick includes Binder Materials, aggregate, additive and water, and by weight, the content of various materials is：The weight portion of Binder Materials 10 35, the weight portion of aggregate 60 80, the weight portion of additive 15 and the weight portion of water 2 30.Preparation method is：The mechanical activation of step one, admixture；The dual activation of thermokalite of step 2, admixture；Step 3, the mixing of Binder Materials and stirring；Step 4, water-permeable brick it is compressing；The maintenance of step 5, water-permeable brick.Beneficial effect：The water-permeable brick of excellent performance can be provided for market, the groundwater resources for increasingly lacking can be progressively supplemented, improve urban ecological environment, with good Social benefit and economic benefit.
Description
Technical field
The present invention relates to a kind of water-permeable brick and preparation method thereof, more particularly to a kind of ecological permeable bricks and preparation method thereof.
Background technology
Currently, with the development of the city, paving material requirements more and more higher, in recent years on urban development to surrounding
And the influence research that underground environment brings shows：Near cities underground water is reduced, and land subsidence, soil moisture content is low, flowers and plants tree
The growth of wood is suppressed.Researcher thinks relevant with urban ground structure.At present major part urban road in concrete and its
Its paving brick is all waterproof, impermeable gaseity.Causing the rainwater of nature, snow-broth can not effectively permeate the ground, and destroy life
State environment.Therefore the demand of the road pavement material of water-permeable and air permeable is increasing.Water-permeable brick because its structure memory is in continuous hole,
Rainwater or the snow-broth of thawing can be made to enter in underground in time, such that it is able to progressively supplement the underground water for increasingly lacking money
Source, improves urban ecological environment.
On the other hand, industrial expansion brings substantial amounts of industrial residue, and gangue, oil shale waste slag and iron tailings are more
The larger solid waste of common and storage, can apply to prepare construction material, but because its activity is relatively low, greatly limit
Application in construction material.
The content of the invention
The main object of the present invention is, in order to solve how effectively to supplement the groundwater resources for increasingly lacking, to improve city life
The problem of state environment；
Another object of the present invention is the problem for how effectively processing industrial residue.
The present invention in order to achieve the above object, a kind of ecological permeable bricks for solving the above problems and providing and its preparation side
Method.
The ecological permeable bricks that the present invention is provided include Binder Materials, aggregate, additive and water, by weight, various materials
The content of material is：Binder Materials 10-35 weight portions, aggregate 60-80 weight portions, additive 1-5 weight portions and water 2-30 weight portions.
Binder Materials by weight, adds 2-8 weight portions by admixture and cement composition in the admixture of 100 weight portions
Cement, gangue, oil shale waste slag, kaolin and NaOH are included in admixture, the content of materials various by weight is：
Gangue 30-40 weight portions, oil shale waste slag 30-40 weight portions, kaolin 20-30 weight portions and NaOH 1-5 weight portions, oil
Shale lime-ash is the shale ashes of formation after oil shale retorting and burning.
Aggregate is CHARACTERISTICS OF TAILINGS SAND or regeneration aggregate, and particle size range 0.3mm-4.75mm can also use equivalent river sand or artificial sand generation
Replace.
Additive is waterglass or alkaline excitation material.
The preparation method of the ecological permeable bricks that the present invention is provided, its method is as described below：
The mechanical activation of step one, admixture：By weight, gangue, the 30-40 weight portions of 30-40 weight portions are weighed
Oil shale waste slag and 20-30 weight portions kaolin mixing after use ball mill grinding 2-3h, it is and standby by 200 mesh square hole screens
With；
The dual activation of heat-alkali of step 2, admixture：The material that step one is prepared adds 1-5 weight by weight
The NaOH of part is mixed, and after stirring, being placed in be heated up in high temperature furnace carries out activation process, and activation temperature is 500-600 degree,
Soak time 2-3 hours, cooling down sealing was stand-by；
Step 3, the mixing of Binder Materials and stirring：The admixture that will be activated in step 2 adds cement to be mixed
Stirring, by weight, the admixture of 100 weight portions adds the cement of 2-8 weight portions, is well mixed stand-by；
Step 4, water-permeable brick it is compressing：The Binder Materials that to be prepared in step 3 add additive, coarse aggregate and
Water is mixed again, and by weight, the content of various materials is：Binder Materials 10-35 weight portions, aggregate 60-80 weight portions,
Additive 1-5 weight portions and water 2-30 weight portions, compressing on forcing press after being well mixed, briquetting pressure is 15-
30MPa, compressing rear natural drying；
The maintenance of step 5, water-permeable brick：Water-permeable brick after will be compressing is put into fog room maintenance, curing temperature 60-90
Degree, maintenance humidity is more than 95%, curing time 36-48h, is got product after the completion of maintenance.
Beneficial effects of the present invention：
Water-permeable brick provided by the present invention is non-sintered water-permeable brick, with gangue, oil shale waste slag as primary raw material, is passed through
Middle low-temperature activation treatment, improves reactivity, then is aided with a small amount of cement as Binder Materials, with iron tailings sand as aggregate, addition
A small amount of additive, water-permeable brick is obtained by compressing, maintenance, the present invention both solved solid waste it is active relatively low, mix
Amount minor issue, turn avoid high-sintering process, greatly reduce energy consumption.The water-permeable brick prepared using present invention process has saturating
Aqueous good, mechanical strength is high, excellent durability, the low feature of energy consumption, not only can for solve gangue, oil shale waste slag,
Environmental problem and problem of resource waste that the solid waste such as mine tailing are brought, and the permeable of excellent performance can be provided for market
Brick, can progressively supplement the groundwater resources for increasingly lacking, and improve urban ecological environment, with good social benefit and economy
Benefit.
Specific embodiment
Embodiment one：
The ecological permeable bricks that the present invention is provided include Binder Materials, aggregate, additive and water, by weight, various materials
The content of material is：The weight portion of Binder Materials 10, the weight portion of aggregate 60, the weight portion of additive 1 and the weight portion of water 2.
Binder Materials by weight, adds 2 weight portions by admixture and cement composition in the admixture of 100 weight portions
Cement, includes gangue, oil shale waste slag, kaolin and NaOH in admixture, the content of materials various by weight is：Coal
The weight portion of spoil 30, the weight portion of oil shale waste slag 40, the weight portion of kaolin 30 and the weight portions of NaOH 1, oil shale waste slag are oily page
The shale ashes formed after rock destructive distillation and burning.
Aggregate is CHARACTERISTICS OF TAILINGS SAND or regeneration aggregate, and particle size range 0.3mm-4.75mm can also use equivalent river sand or artificial sand generation
Replace.
Additive is waterglass or alkaline excitation material.
The preparation method of the ecological permeable bricks that the present invention is provided, its method is as described below：
The mechanical activation of step one, admixture：By weight, gangue, the oily page of 40 weight portions of 30 weight portions are weighed
Ball mill grinding 2-3h is used after the kaolin mixing of rock lime-ash and 30 weight portions, and it is standby by 200 mesh square hole screens；
The dual activation of heat-alkali of step 2, admixture：The material that step one is prepared adds 1 weight portion by weight
NaOH mix, after stirring, being placed in be heated up in high temperature furnace carries out activation process, and activation temperature is 500-600 degree, living
2-3 hours change time, cooling down sealing is stand-by；
Step 3, the mixing of Binder Materials and stirring：The admixture that will be activated in step 2 adds cement to be mixed
Stirring, by weight, the admixture of 100 weight portions adds the cement of 2 weight portions, is well mixed stand-by；
Step 4, water-permeable brick it is compressing：The Binder Materials that to be prepared in step 3 add additive, coarse aggregate and
Water is mixed again, and by weight, the content of various materials is：The weight portion of Binder Materials 10, the weight portion of aggregate 60, additive
1 weight portion and the weight portion of water 2, be well mixed after it is compressing on forcing press, briquetting pressure is 15-30MPa, it is compressing after
Spontaneously dry；
The maintenance of step 5, water-permeable brick：Water-permeable brick after will be compressing is put into fog room maintenance, curing temperature 60-90
Degree, maintenance humidity is more than 95%, curing time 36-48h, is got product after the completion of maintenance.
Embodiment two：
The ecological permeable bricks that the present invention is provided include Binder Materials, aggregate, additive and water, by weight, various materials
The content of material is：The weight portion of Binder Materials 35, the weight portion of aggregate 80, the weight portion of additive 5 and the weight portion of water 30.
Binder Materials by weight, adds 8 weight portions by admixture and cement composition in the admixture of 100 weight portions
Cement, includes gangue, oil shale waste slag, kaolin and NaOH in admixture, the content of materials various by weight is：Coal
The weight portion of spoil 40, the weight portion of oil shale waste slag 40, the weight portion of kaolin 20 and the weight portions of NaOH 5, oil shale waste slag are oily page
The shale ashes formed after rock destructive distillation and burning.
Aggregate is CHARACTERISTICS OF TAILINGS SAND or regeneration aggregate, and particle size range 0.3mm-4.75mm can also use equivalent river sand or artificial sand generation
Replace.
Additive is waterglass or alkaline excitation material.
The preparation method of the ecological permeable bricks that the present invention is provided, its method is as described below：
The mechanical activation of step one, admixture：By weight, gangue, the oily page of 40 weight portions of 40 weight portions are weighed
Ball mill grinding 2-3h is used after the kaolin mixing of rock lime-ash and 20 weight portions, and it is standby by 200 mesh square hole screens；
The dual activation of heat-alkali of step 2, admixture：The material that step one is prepared adds 5 weight portions by weight
NaOH mix, after stirring, being placed in be heated up in high temperature furnace carries out activation process, and activation temperature is 500-600 degree, living
2-3 hours change time, cooling down sealing is stand-by；
Step 3, the mixing of Binder Materials and stirring：The admixture that will be activated in step 2 adds cement to be mixed
Stirring, by weight, the admixture of 100 weight portions adds the cement of 8 weight portions, is well mixed stand-by；
Step 4, water-permeable brick it is compressing：The Binder Materials that to be prepared in step 3 add additive, coarse aggregate and
Water is mixed again, and by weight, the content of various materials is：The weight portion of Binder Materials 35, the weight portion of aggregate 80, additive
5 weight portions and the weight portion of water 30, compressing on forcing press after being well mixed, briquetting pressure is 15-30MPa, compressing
After spontaneously dry；
The maintenance of step 5, water-permeable brick：Water-permeable brick after will be compressing is put into fog room maintenance, curing temperature 60-90
Degree, maintenance humidity is more than 95%, curing time 36-48h, is got product after the completion of maintenance.
Embodiment three：
The ecological permeable bricks that the present invention is provided include Binder Materials, aggregate, additive and water, by weight, various materials
The content of material is：The weight portion of Binder Materials 25, the weight portion of aggregate 70, the weight portion of additive 3 and the weight portion of water 16.
Binder Materials by weight, adds 5 weight portions by admixture and cement composition in the admixture of 100 weight portions
Cement, includes gangue, oil shale waste slag, kaolin and NaOH in admixture, the content of materials various by weight is：Coal
The weight portion of spoil 35, the weight portion of oil shale waste slag 35, the weight portion of kaolin 30 and the weight portions of NaOH 3, oil shale waste slag are oily page
The shale ashes formed after rock destructive distillation and burning.
Aggregate is CHARACTERISTICS OF TAILINGS SAND or regeneration aggregate, and particle size range 0.3mm-4.75mm can also use equivalent river sand or artificial sand generation
Replace.
Additive is waterglass or alkaline excitation material.
The preparation method of the ecological permeable bricks that the present invention is provided, its method is as described below：
The mechanical activation of step one, admixture：By weight, gangue, the oily page of 35 weight portions of 35 weight portions are weighed
Ball mill grinding 2-3h is used after the kaolin mixing of rock lime-ash and 30 weight portions, and it is standby by 200 mesh square hole screens；
The dual activation of heat-alkali of step 2, admixture：The material that step one is prepared adds 3 weight portions by weight
NaOH mix, after stirring, being placed in be heated up in high temperature furnace carries out activation process, and activation temperature is 500-600 degree, living
2-3 hours change time, cooling down sealing is stand-by；
Step 3, the mixing of Binder Materials and stirring：The admixture that will be activated in step 2 adds cement to be mixed
Stirring, by weight, the admixture of 100 weight portions adds the cement of 5 weight portions, is well mixed stand-by；
Step 4, water-permeable brick it is compressing：The Binder Materials that to be prepared in step 3 add additive, coarse aggregate and
Water is mixed again, and by weight, the content of various materials is：The weight portion of Binder Materials 25, the weight portion of aggregate 70, additive
3 weight portions and the weight portion of water 16, compressing on forcing press after being well mixed, briquetting pressure is 15-30MPa, compressing
After spontaneously dry；
The maintenance of step 5, water-permeable brick：Water-permeable brick after will be compressing is put into fog room maintenance, curing temperature 60-90
Degree, maintenance humidity is more than 95%, curing time 36-48h, is got product after the completion of maintenance.
Claims (5)
1. a kind of ecological permeable bricks, it is characterised in that：Binder Materials, aggregate, additive and water are included, it is by weight, various
The content of material is：Binder Materials 10-35 weight portions, aggregate 60-80 weight portions, additive 1-5 weight portions and water 2-30 weight
Part.
2. a kind of ecological permeable bricks according to claim 1, it is characterised in that：Described Binder Materials is by admixture and water
Mud constitute, by weight, in the admixture of 100 weight portions add 2-8 weight portions cement, included in admixture gangue,
Oil shale waste slag, kaolin and NaOH, the content of materials various by weight is：Gangue 30-40 weight portions, oil shale waste slag
30-40 weight portions, kaolin 20-30 weight portions and NaOH 1-5 weight portions, after oil shale waste slag is for oil shale retorting and burning
The shale ashes of formation.
3. a kind of ecological permeable bricks according to claim 1, it is characterised in that：Described aggregate is CHARACTERISTICS OF TAILINGS SAND or Regenerated Bone
Material, particle size range 0.3mm-4.75mm can also be replaced with equivalent river sand or artificial sand.
4. a kind of ecological permeable bricks according to claim 1, it is characterised in that：Described additive is waterglass or alkalescence
Excitation material.
5. a kind of preparation method of ecological permeable bricks, it is characterised in that：Its method is as described below：
The mechanical activation of step one, admixture：By weight, gangue, the oil of 30-40 weight portions of 30-40 weight portions are weighed
Ball mill grinding 2-3h is used after the kaolin mixing of shale lime-ash and 20-30 weight portions, and it is standby by 200 mesh square hole screens；
The dual activation of heat-alkali of step 2, admixture：The material that step one is prepared adds 1-5 weight portions by weight
NaOH is mixed, and after stirring, being placed in be heated up in high temperature furnace carries out activation process, and activation temperature is 500-600 degree, activation
Time 2-3 hours, cooling down sealing was stand-by；
Step 3, the mixing of Binder Materials and stirring：The admixture that will be activated in step 2 adds cement to be mixed,
By weight, the admixture of 100 weight portions adds the cement of 2-8 weight portions, is well mixed stand-by；
Step 4, water-permeable brick it is compressing：The Binder Materials that will be prepared in step 3 adds additive, coarse aggregate and water again
Secondary to be mixed, by weight, the content of various materials is：It is Binder Materials 10-35 weight portions, aggregate 60-80 weight portions, additional
Agent 1-5 weight portions and water 2-30 weight portions, compressing on forcing press after being well mixed, briquetting pressure is 15-30MPa, pressure
Spontaneously dried after being made type；
The maintenance of step 5, water-permeable brick：Water-permeable brick after will be compressing is put into fog room maintenance, and curing temperature 60-90 degree is supported
Shield humidity is more than 95%, curing time 36-48h, is got product after the completion of maintenance.