CN106833522A - A kind of flange butterfly butterfly plate grinding agent - Google Patents
A kind of flange butterfly butterfly plate grinding agent Download PDFInfo
- Publication number
- CN106833522A CN106833522A CN201710143828.6A CN201710143828A CN106833522A CN 106833522 A CN106833522 A CN 106833522A CN 201710143828 A CN201710143828 A CN 201710143828A CN 106833522 A CN106833522 A CN 106833522A
- Authority
- CN
- China
- Prior art keywords
- parts
- butterfly
- butterfly plate
- micro mist
- grinding agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of flange butterfly butterfly plate grinding agent, the flange butterfly butterfly plate grinding agent is made up of the raw material of following weight portion：70 80 parts of chromium oxide micro mist, 30 35 parts of iron oxide micro mist, 16 22 parts of corundum powder, 40 50 parts of glycerine, 10 15 parts of alcohol, 30 40 parts of paraffin, 8 12 parts of oxirane, 58 parts of sodium tripolyphosphate, 25 parts of dibutyl hydroxy toluene.Flange butterfly butterfly plate grinding agent of the invention is using the relatively soft chromium oxide of material and iron oxide micro mist as main material, so grinding agent will not cause larger abrasion when grinding to butterfly plate, grinding agent grinding simultaneously can also form protective filmy layer after terminating on butterfly plate surface, the direct corrosion butterfly plate of extraneous corrosive substance is avoided, the service life of butterfly plate is extended.
Description
Technical field
The present invention relates to valve manufacture field, more precisely, being a kind of flange butterfly butterfly plate grinding agent.
Background technology
Flange form butterfly valve design structure is novel, and overall dimensions are small, lightweight.Butterfly plate opens and closes rapid, operation using double eccentric
Portable power saving；Fricton-tight friction between butterfly plate and sealing ring, sealing surface is wear-resistant, long service life, sealed reliable, easily adjustment.Method
Blue formula butterfly valve is vertical plank frame, and valve rod is monoblock type metal hard-sealing, the sealing ring of valve for flexible graphite plate with it is stainless
Steel plate composite structure, on valve body, butterfly plate sealing surface weld deposit stainless steel.The sealing ring of flexible sealing valve is butyronitrile rubber
The materials such as glue/fluorubber, are mounted on butterfly plate.Valve body and valve seat built-up welding stainless steel.Flange butterfly butterfly plate in use
Contacted with internal flow for a long time, butterfly plate surface is easily stained with dirt even by corrosion.Existing butterfly plate grinding agent can be effective
The spot on removal butterfly plate surface, but it is larger to butterfly plate surface damage, and the protective layer on butterfly plate surface is more easily damaged, and subsequently uses
During the probability that is corroded of butterfly plate become big, shorten the service life of butterfly plate.
The content of the invention
The present invention mainly solve prior art existing for technical problem so that provide it is a kind of to butterfly plate have protection make
Flange butterfly butterfly plate grinding agent.
Above-mentioned technical problem of the invention is mainly what is be addressed by following technical proposals：
A kind of flange butterfly butterfly plate grinding agent, is made up of the raw material of following weight portion：
70-80 parts of chromium oxide micro mist, 30-35 parts of iron oxide micro mist, corundum powder 16-22 parts, glycerine 40-50 parts, alcohol
10-15 parts, paraffin 30-40 parts, oxirane 8-12 parts, sodium tripolyphosphate 5-8 parts, dibutyl hydroxy toluene 2-5 parts.
The preparation method of the flange butterfly butterfly plate grinding agent is：
1. reactor, temperature in the kettle is added to be increased to 70-75 DEG C, be sufficiently stirred for 15-20 in glycerine, paraffin, oxirane
Minute, chromium oxide micro mist, iron oxide micro mist, corundum powder are continuously added, temperature is reduced to 50-55 DEG C, is sufficiently stirred for 10-15 points
Clock, natural cooling；
2. container is poured the mixture into, alcohol, sodium tripolyphosphate, dibutyl hydroxy toluene is added under normal temperature, stir 10-15
Obtained final product after minute.
Used as preferred embodiments of the present invention, the flange butterfly butterfly plate grinding agent is made up of the raw material of following weight portion：
76 parts of chromium oxide micro mist, 33 parts of iron oxide micro mist, 19 parts of corundum powder, 44 parts of glycerine, 12 parts of alcohol, paraffin 37
Part, 10 parts of oxirane, 6.5 parts of sodium tripolyphosphate, 3 parts of dibutyl hydroxy toluene.
Flange butterfly butterfly plate grinding agent of the invention is using the relatively soft chromium oxide of material and iron oxide micro mist as master
Raw material, such grinding agent will not cause larger abrasion when grinding to butterfly plate, while grinding agent grinding may be used also after terminating
Protective filmy layer is formed with butterfly plate surface, it is to avoid the extraneous direct corrosion butterfly plate of corrosive substance, extend the use longevity of butterfly plate
Life.
Specific embodiment
The preferred embodiments of the present invention are described in detail below so that advantages and features of the invention can be easier to by
It will be appreciated by those skilled in the art that apparent clearly being defined so as to be made to protection scope of the present invention.
[embodiment 1]
70 parts of chromium oxide micro mist, 30 parts of iron oxide micro mist, 16 parts of corundum powder, 40 parts of glycerine, alcohol 10 are taken by weight
Part, 30 parts of paraffin, 8 parts of oxirane, 5 parts of sodium tripolyphosphate, 2 parts of dibutyl hydroxy toluene.
Add reactor, temperature in the kettle to be increased to 70 DEG C, be sufficiently stirred for 15 minutes in glycerine, paraffin, oxirane, continue
Chromium oxide micro mist, iron oxide micro mist, corundum powder are added, temperature is reduced to 50 DEG C, is sufficiently stirred for 10 minutes, natural cooling.
Container is poured the mixture into, alcohol, sodium tripolyphosphate, dibutyl hydroxy toluene are added under normal temperature, stirred 10 minutes
After obtain final product.
[embodiment 2]
80 parts of chromium oxide micro mist, 35 parts of iron oxide micro mist, 22 parts of corundum powder, 50 parts of glycerine, alcohol 15 are taken by weight
Part, 40 parts of paraffin, 12 parts of oxirane, 8 parts of sodium tripolyphosphate, 5 parts of dibutyl hydroxy toluene.
Add reactor, temperature in the kettle to be increased to 75 DEG C, be sufficiently stirred for 20 minutes in glycerine, paraffin, oxirane, continue
Chromium oxide micro mist, iron oxide micro mist, corundum powder are added, temperature is reduced to 55 DEG C, is sufficiently stirred for 15 minutes, natural cooling.
Container is poured the mixture into, alcohol, sodium tripolyphosphate, dibutyl hydroxy toluene are added under normal temperature, stirred 15 minutes
After obtain final product.
The above, specific embodiment only of the invention, but protection scope of the present invention is not limited thereto, and it is any
The change or replacement expected without creative work, should all be included within the scope of the present invention.Therefore, it is of the invention
Protection domain should be determined by the scope of protection defined in the claims.
Claims (2)
1. a kind of flange butterfly butterfly plate grinding agent, it is characterised in that be made up of the raw material of following weight portion：
70-80 parts of chromium oxide micro mist, 30-35 parts of iron oxide micro mist, corundum powder 16-22 parts, glycerine 40-50 parts, alcohol 10-15
Part, paraffin 30-40 parts, oxirane 8-12 parts, sodium tripolyphosphate 5-8 parts, dibutyl hydroxy toluene 2-5 parts；
The preparation method of the flange butterfly butterfly plate grinding agent is：
1. reactor, temperature in the kettle is added to be increased to 70-75 DEG C, be sufficiently stirred for 15-20 minutes in glycerine, paraffin, oxirane,
Chromium oxide micro mist, iron oxide micro mist, corundum powder are continuously added, temperature is reduced to 50-55 DEG C, be sufficiently stirred for 10-15 minutes, from
So cooling；
2. container is poured the mixture into, alcohol, sodium tripolyphosphate, dibutyl hydroxy toluene is added under normal temperature, stirred 10-15 minutes
After obtain final product.
2. flange butterfly butterfly plate grinding agent according to claim 1, it is characterised in that by the raw material system of following weight portion
Into：
76 parts of chromium oxide micro mist, 33 parts of iron oxide micro mist, 19 parts of corundum powder, 44 parts of glycerine, 12 parts of alcohol, 37 parts of paraffin, ring
10 parts of oxidative ethane, 6.5 parts of sodium tripolyphosphate, 3 parts of dibutyl hydroxy toluene.