CN106810152A - 一种高分散性的再生eps粒子掺杂硅酸盐水泥复合发泡保温板及其制备方法 - Google Patents

一种高分散性的再生eps粒子掺杂硅酸盐水泥复合发泡保温板及其制备方法 Download PDF

Info

Publication number
CN106810152A
CN106810152A CN201611175356.4A CN201611175356A CN106810152A CN 106810152 A CN106810152 A CN 106810152A CN 201611175356 A CN201611175356 A CN 201611175356A CN 106810152 A CN106810152 A CN 106810152A
Authority
CN
China
Prior art keywords
regeneration eps
regeneration
polymolecularity
preparation
shell oil
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201611175356.4A
Other languages
English (en)
Inventor
吴传兴
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Maanshan Jiechuang Plastic Science & Technology Co Ltd
Original Assignee
Maanshan Jiechuang Plastic Science & Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Maanshan Jiechuang Plastic Science & Technology Co Ltd filed Critical Maanshan Jiechuang Plastic Science & Technology Co Ltd
Priority to CN201611175356.4A priority Critical patent/CN106810152A/zh
Publication of CN106810152A publication Critical patent/CN106810152A/zh
Withdrawn legal-status Critical Current

Abstract

本发明公开了一种高分散性的再生EPS粒子掺杂硅酸盐水泥复合发泡保温板，该发泡保温板将成本低廉的废旧聚苯乙烯泡沫塑料进行改性处理，得到具有良好回弹韧性、低热膨胀系数和耐温性更强的再生EPS粒子，并利用掺杂腰果壳油摩擦粉的丙烯酸酯乳液在再生EPS粒子表面包覆改性，改性后的再生EPS粒子与水泥浆料具有良好的界面结合性，分散悬浮性更佳，腰果壳油摩擦粉增进了其与水泥浆料的把持力，有效的避免了团聚，提高发泡气孔率，其与硅酸盐水泥、尾矿渣、海泡石纤维等原料协同作用，经过发泡处理后最终制得了具有优异隔热保温、阻燃抗震的保温板，产品经济耐用，高效环保，应用前景良好。

Description

一种高分散性的再生EPS粒子掺杂硅酸盐水泥复合发泡保温 板及其制备方法
技术领域
本发明涉及水泥发泡保温板技术领域，尤其涉及一种高分散性的再生EPS粒子掺杂硅酸盐水泥复合发泡保温板及其制备方法。
背景技术
在建筑外面建立外墙保温系统是建筑行业节能减排的一个重要举措，同时建立外墙保温系统可以避免产生热桥；还能根据季节变化调节室内温度，避免室内外温差对墙体造成损害，影响使用安全及寿命。现在市面上的外墙保温材料基本为：酚醛、岩棉板、玻璃棉板、聚苯板、挤塑板、超薄真空绝热板等等。其中，岩棉、玻化微珠的成本较高，而酚醛、聚苯板、挤塑板等防火性能严重不足，安全隐患多，因此对比看来水泥发泡保温板具有更为优良的综合性能，更适用于作为建筑外墙保温材料。
水泥发泡保温板是以水泥、粉煤灰、矿渣、硅灰等原料经化学发泡剂发泡而成，原料的选取及工艺将直接影响到产品的性能，目前市场上的水泥发泡材料质量参差不齐，在粘结强度、耐水性、耐老化性等方面存在不足。《复合EPS颗粒发泡水泥发泡保温板的研究》一文将硅酸盐水泥与改性EPS颗粒混合发泡，制成了一种无机/有机复合保温材料，具有良好的保温、耐水、阻燃效果，然而EPS颗粒刚性较高，易脆易裂，热膨胀系数较大，容易变形开裂，直接影响复合板材的使用性能，因此需要对其进一步改性，以提高其使用性能。
发明内容
本发明目的就是为了弥补已有技术的缺陷，提供一种高分散性的再生EPS粒子掺杂硅酸盐水泥复合发泡保温板及其制备方法。
本发明是通过以下技术方案实现的：
一种高分散性的再生EPS粒子掺杂硅酸盐水泥复合发泡保温板，该发泡保温板由以下重量份的原料制成：硅酸盐水泥30-40、粉煤灰15-20、200-500目尾矿渣8-10、海泡石纤维5-8、再生EPS粒子30-40、十二水合磷酸氢二钠2-3、腰果壳油摩擦粉0.4-0.5、丙烯酸酯乳液3-5、木质素磺酸钠0.01-0.02、浓度为20-25%的双氧水5-6、水适量。
所述的再生EPS粒子由以下重量份的原料制成：废旧聚苯乙烯泡沫塑料粒子20-30、硅烷偶联剂0.5-1、TPE热塑性弹性体5-8、400-600目磷酸锆钠陶瓷粉体8-10、氮气4-5；制备方法为：将废旧聚苯乙烯泡沫塑料粒子、硅烷偶联剂、TPE热塑性弹性体、磷酸锆钠陶瓷粉体送入喂料系统中混合均匀，随后投入双螺杆挤出机中熔融混合，并注入氮气进行发泡处理，最后熔体经双螺杆挤出机挤出造粒筛分，粒度控制在≤1mm，即得。
所述的一种高分散性的再生EPS粒子掺杂硅酸盐水泥复合发泡保温板的制备方法为：
（1）取4-5重量份的水，加入木质素磺酸钠，搅拌至其完全溶解后加入腰果壳油摩擦粉，超声振荡分散40-50min，随后加入丙烯酸酯乳液，继续搅拌混合30-40min，随后将配置的混合溶液均匀喷涂到再生EPS粒子表面，喷涂完毕后用50-60℃热风干燥处理20-30min，得腰果壳油摩擦粉包覆改性的再生EPS粒子备用；
（2）将硅酸盐水泥、粉煤灰、尾矿渣、海泡石纤维、十二水合磷酸氢二钠一起投入高速混料机中，加入适量的水，高速搅拌混合5-6min后投入步骤（1）制备的腰果壳油摩擦粉包覆改性的再生EPS粒子，继续搅拌混合4-5min，最后再加入双氧水，快速搅拌混合4-5s后将混合浆料浇注入模成型，经发泡静停、养护、脱模后即得所述发泡保温板。
本发明将成本低廉的废旧聚苯乙烯泡沫塑料进行改性处理，得到具有良好回弹韧性、低热膨胀系数和耐温性更强的再生EPS粒子，并利用掺杂腰果壳油摩擦粉的丙烯酸酯乳液在再生EPS粒子表面包覆改性，改性后的再生EPS粒子与水泥浆料具有良好的界面结合性，分散悬浮性更佳，腰果壳油摩擦粉增进了其与水泥浆料的把持力，有效的避免了团聚，提高发泡气孔率，其与硅酸盐水泥、尾矿渣、海泡石纤维等原料协同作用，经过发泡处理后最终制得了具有优异隔热保温、阻燃抗震的保温板，产品经济耐用，高效环保，应用前景良好。
具体实施方式
一种高分散性的再生EPS粒子掺杂硅酸盐水泥复合发泡保温板，该发泡保温板由以下重量份的原料制成：硅酸盐水泥30、粉煤灰15、200目尾矿渣8、海泡石纤维5、再生EPS粒子30、十二水合磷酸氢二钠2、腰果壳油摩擦粉0.4、丙烯酸酯乳液3、木质素磺酸钠0.01、浓度为20%的双氧水5、水适量。
其中再生EPS粒子由以下重量份的原料制成：废旧聚苯乙烯泡沫塑料粒子20、硅烷偶联剂0.5、TPE热塑性弹性体5、400目磷酸锆钠陶瓷粉体8、氮气4；制备方法为：将废旧聚苯乙烯泡沫塑料粒子、硅烷偶联剂、TPE热塑性弹性体、磷酸锆钠陶瓷粉体送入喂料系统中混合均匀，随后投入双螺杆挤出机中熔融混合，并注入氮气进行发泡处理，最后熔体经双螺杆挤出机挤出造粒筛分，粒度控制在≤1mm，即得。
该复合发泡保温板的制备方法为：
（1）取4重量份的水，加入木质素磺酸钠，搅拌至其完全溶解后加入腰果壳油摩擦粉，超声振荡分散40min，随后加入丙烯酸酯乳液，继续搅拌混合30min，随后将配置的混合溶液均匀喷涂到再生EPS粒子表面，喷涂完毕后用50℃热风干燥处理20min，得腰果壳油摩擦粉包覆改性的再生EPS粒子备用；
（2）将硅酸盐水泥、粉煤灰、尾矿渣、海泡石纤维、十二水合磷酸氢二钠一起投入高速混料机中，加入适量的水，高速搅拌混合5min后投入步骤（1）制备的腰果壳油摩擦粉包覆改性的再生EPS粒子，继续搅拌混合4min，最后再加入双氧水，快速搅拌混合4s后将混合浆料浇注入模成型，经发泡静停、养护、脱模后即得所述发泡保温板。
制得的保温板根据相关标准进行性能测试，测试结果为：
密度：210.3kg/m3；导热系数：0.028W/(m2.k)；抗压强度：1.14MPa；吸水率：4.12%；阻燃等级：A。

Claims (3)

1.一种高分散性的再生EPS粒子掺杂硅酸盐水泥复合发泡保温板，其特征在于，该发泡保温板由以下重量份的原料制成：硅酸盐水泥30-40、粉煤灰15-20、200-500目尾矿渣8-10、海泡石纤维5-8、再生EPS粒子30-40、十二水合磷酸氢二钠2-3、腰果壳油摩擦粉0.4-0.5、丙烯酸酯乳液3-5、木质素磺酸钠0.01-0.02、浓度为20-25%的双氧水5-6、水适量。
2.如权利要求1所述的一种高分散性的再生EPS粒子掺杂硅酸盐水泥复合发泡保温板，其特征在于，所述的再生EPS粒子由以下重量份的原料制成：废旧聚苯乙烯泡沫塑料粒子20-30、硅烷偶联剂0.5-1、TPE热塑性弹性体5-8、400-600目磷酸锆钠陶瓷粉体8-10、氮气4-5；制备方法为：将废旧聚苯乙烯泡沫塑料粒子、硅烷偶联剂、TPE热塑性弹性体、磷酸锆钠陶瓷粉体送入喂料系统中混合均匀，随后投入双螺杆挤出机中熔融混合，并注入氮气进行发泡处理，最后熔体经双螺杆挤出机挤出造粒筛分，粒度控制在≤1mm，即得。
3.如权利要求1所述的一种高分散性的再生EPS粒子掺杂硅酸盐水泥复合发泡保温板的制备方法，其特征在于，所述的制备方法为：
（1）取4-5重量份的水，加入木质素磺酸钠，搅拌至其完全溶解后加入腰果壳油摩擦粉，超声振荡分散40-50min，随后加入丙烯酸酯乳液，继续搅拌混合30-40min，随后将配置的混合溶液均匀喷涂到再生EPS粒子表面，喷涂完毕后用50-60℃热风干燥处理20-30min，得腰果壳油摩擦粉包覆改性的再生EPS粒子备用；
（2）将硅酸盐水泥、粉煤灰、尾矿渣、海泡石纤维、十二水合磷酸氢二钠一起投入高速混料机中，加入适量的水，高速搅拌混合5-6min后投入步骤（1）制备的腰果壳油摩擦粉包覆改性的再生EPS粒子，继续搅拌混合4-5min，最后再加入双氧水，快速搅拌混合4-5s后将混合浆料浇注入模成型，经发泡静停、养护、脱模后即得所述发泡保温板。
CN201611175356.4A 2016-12-19 2016-12-19 一种高分散性的再生eps粒子掺杂硅酸盐水泥复合发泡保温板及其制备方法 Withdrawn CN106810152A (zh)