CN106801344A - A kind of quaternary ammonium base class water-soluble polyamide resins artificial leather manufacture method - Google Patents
A kind of quaternary ammonium base class water-soluble polyamide resins artificial leather manufacture method Download PDFInfo
- Publication number
- CN106801344A CN106801344A CN201510832442.7A CN201510832442A CN106801344A CN 106801344 A CN106801344 A CN 106801344A CN 201510832442 A CN201510832442 A CN 201510832442A CN 106801344 A CN106801344 A CN 106801344A
- Authority
- CN
- China
- Prior art keywords
- quaternary ammonium
- artificial leather
- paint
- base class
- ammonium base
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of quaternary ammonium base class water-soluble polyamide resins artificial leather manufacture method, it is to use quaternary ammonium base class water-soluble polyamide resins to configure to cover with paint, lacquer, colour wash, etc. slurry, then slurry will be covered with paint, lacquer, colour wash, etc. to cover with paint, lacquer, colour wash, etc. in artificial leather base fabric surface, the polyamide artificial leather for being dyeed by dyeing treatment again, covering with paint, lacquer, colour wash, etc. slurry includes the component of following mass parts:100 parts of quaternary ammonium base class water-soluble polyamide resins, 20~120 parts of dimethylformamide, 20~120 parts of acetone.Quaternary ammonium base class water-soluble polyamide resins are used as artificial leather top finishing material, dyeing process can be carried out with dyestuff, color effects by that can obtain dyestuff coloring after dyeing treatment, make product have the characteristics of bright-colored, coating permeability is good, surface color fastness is high, color animal migration is small.
Description
Technical field
The invention belongs to polyamide artificial leather preparation method technical field, and in particular to a kind of quaternary ammonium for being easy to dye
The manufacture method of base class water-soluble polyamide resins artificial leather.
Background technology
Surface has the artificial leather of dyestuff coloring effect, and its bright in luster, transparency is high, is applied to the fashion such as case and bag women's shoes
It is loved by people on product, but conventional synthesis leather generally uses pigment coloring mode, it is impossible to and reaching dyestuff coloring is had
Effect, although dyestuff coloring effect can be obtained using the manufacture method that the coloring of dyestuff water colouring agent is added in coating material,
But this manufacture method can bring serious colour migration to move, poor color fastness, the problems such as cost price is high, making for product is constrained
With.
In traditional synthetic leather manufacturing process, mill base, toner and organic dyestuff, metal network need to be added in coating paste
The coloring materials such as dyestuff are closed, so that assign finished leather different colors, but coat colorization feel is partially hard, and coloring formula is once
It is determined that after, coating is presented solid color, and gloss and color and luster are dull, without the stereovision such as the depth, light and shade, new and old.Exploitation is just
In dyeing artificial leather be those skilled in the art need thinking problem.
The content of the invention
The technical problems to be solved by the invention are directed to above-mentioned prior art and provide a kind of polyamide people be easy to and dye
Fabricate-leather, can be dyeed with dyestuff, and product has the characteristics of bright-colored, coating permeability is good, surface color fastness is high.
The present invention the used technical scheme that solves the above problems is:A kind of quaternary ammonium base class water-soluble polyamide resins are artificial
Leather manufacture method, is to use quaternary ammonium base class water-soluble polyamide resins to configure to cover with paint, lacquer, colour wash, etc. slurry, then will cover with paint, lacquer, colour wash, etc. slurry and covers with paint, lacquer, colour wash, etc. in people
Fabricate-leather scrim surfaces, then the polyamide artificial leather dyeed by dyeing treatment;
Covering with paint, lacquer, colour wash, etc. slurry includes the component of following mass parts:
100 parts of quaternary ammonium base class water-soluble polyamide resins
20~60 parts of water.
Preferably, the covering with paint is to make surface technology by release liners dry method quaternary ammonium base class water soluble polyamide surface layer is fitted
Onto artificial leather wet half-finished product.
Preferably described covering with paint is that quaternary ammonium base class water soluble polyamide is covered with paint, lacquer, colour wash, etc. into slurry with surface printing method to cover with paint, lacquer, colour wash, etc. in artificial
Revolutionary cadre's method surface of semi-finished.
Preferably, the covering with paint is that quaternary ammonium base class water soluble polyamide is applied into finish coat with rolling method to be coated with to artificial leather base
Cloth surface of semi-finished.
Described dyeing
Polyamide artificial leather in the present invention is easy to dyeing, and dyeing processing mode includes pad dyeing, dye gigging, overflow dyeing or gas
Stream dyeing.
Compared with prior art, the advantage of the invention is that:Using quaternary ammonium base class water-soluble polyamide resins as artificial
Leather top finishing material, can carry out dyeing process with dyestuff, the color effects by that can obtain dyestuff coloring after dyeing treatment,
Make product that there is the characteristics of bright-colored, coating permeability is good, surface color fastness is high, color animal migration is small, contaminated with common artificial leather
Form and aspect are fewer than dyestuff usage amount, and dyeing time is very short, and dyeing can be completed compared with low temperature, dyeing relatively simple, cost
Relatively low, energy saving.
Specific embodiment
The present invention is described in further detail with reference to embodiments.
Embodiment 1
Quaternary ammonium base class water-soluble polyamide resins artificial leather manufacture method, is configured using quaternary ammonium base class water-soluble polyamide resins
Slurry is covered with paint, lacquer, colour wash, etc., slurry then will be covered with paint, lacquer, colour wash, etc. and is covered with paint, lacquer, colour wash, etc. in artificial leather base fabric surface, foregoing covering with paint is to make surface technology by release liners dry method
Quaternary ammonium base class water soluble polyamide surface layer is fitted in artificial leather wet half-finished product, then dyeed by pad dyeing treatment
Polyamide artificial leather.
Covering with paint, lacquer, colour wash, etc. slurry includes the component of following mass parts:
100 parts of quaternary ammonium base class water-soluble polyamide resins
20 parts of water.
Embodiment 2
Quaternary ammonium base class water-soluble polyamide resins artificial leather manufacture method, is configured using quaternary ammonium base class water-soluble polyamide resins
Slurry is covered with paint, lacquer, colour wash, etc., slurry then will be covered with paint, lacquer, colour wash, etc. and be covered with paint, lacquer, colour wash, etc. in artificial leather base fabric surface, foregoing covering with paint is to use surface printing method by quaternary ammonium base class
Water soluble polyamide is covered with paint, lacquer, colour wash, etc. slurry and is covered with paint, lacquer, colour wash, etc. in artificial leather dry method surface of semi-finished, then the polyamides dyeed by dye gigging treatment
Amine artificial leather.
Covering with paint, lacquer, colour wash, etc. slurry includes the component of following mass parts:
100 parts of quaternary ammonium base class water-soluble polyamide resins
60 parts of water.
Embodiment 3
Quaternary ammonium base class water-soluble polyamide resins artificial leather manufacture method, is configured using quaternary ammonium base class water-soluble polyamide resins
Slurry is covered with paint, lacquer, colour wash, etc., slurry then will be covered with paint, lacquer, colour wash, etc. and be covered with paint, lacquer, colour wash, etc. in artificial leather base fabric surface, foregoing covering with paint is to use rolling method by quaternary ammonium base class water
Soluble polyamide painting finish coat coating arrives artificial leather base fabric's surface of semi-finished, then by gathering that airflow dyeing treatment is dyeed
Acid amides artificial leather.
Covering with paint, lacquer, colour wash, etc. slurry includes the component of following mass parts:
100 parts of quaternary ammonium base class water-soluble polyamide resins
40 parts of water.
Embodiment 4
Quaternary ammonium base class water-soluble polyamide resins artificial leather manufacture method, is configured using quaternary ammonium base class water-soluble polyamide resins
Slurry is covered with paint, lacquer, colour wash, etc., slurry then will be covered with paint, lacquer, colour wash, etc. and be covered with paint, lacquer, colour wash, etc. in artificial leather base fabric surface, foregoing covering with paint is to use surface printing method by quaternary ammonium base class
Water soluble polyamide is covered with paint, lacquer, colour wash, etc. slurry and is covered with paint, lacquer, colour wash, etc. in artificial leather dry method surface of semi-finished, then processes what is dyeed by overflow dyeing
Polyamide artificial leather.
Covering with paint, lacquer, colour wash, etc. slurry includes the component of following mass parts:
100 parts of quaternary ammonium base class water-soluble polyamide resins
60 parts of water.
Claims (5)
1. a kind of quaternary ammonium base class water-soluble polyamide resins artificial leather manufacture method, it is characterised in that:It is to use quaternary ammonium base class water
Slurry is covered with paint, lacquer, colour wash, etc. in soluble polyamide configuration, then will be covered with paint, lacquer, colour wash, etc. slurry and is covered with paint, lacquer, colour wash, etc. in artificial leather base fabric surface, then is processed by dyeing
The polyamide artificial leather for being dyeed,
Covering with paint, lacquer, colour wash, etc. slurry includes the component of following mass parts:
100 parts of quaternary ammonium base class water-soluble polyamide resins
20~60 parts of water.
2. quaternary ammonium base class water-soluble polyamide resins artificial leather manufacture method according to claim 1, it is characterised in that:Institute
State covering with paint be by release liners dry method make surface technology by quaternary ammonium base class water soluble polyamide surface layer fit to artificial leather wet method half into
On product.
3. quaternary ammonium base class water-soluble polyamide resins artificial leather manufacture method according to claim 1, it is characterised in that:Institute
It is that quaternary ammonium base class water soluble polyamide is covered with paint, lacquer, colour wash, etc. into slurry with surface printing method to cover with paint, lacquer, colour wash, etc. in artificial leather dry method surface of semi-finished to state covering with paint.
4. quaternary ammonium base class water-soluble polyamide resins artificial leather manufacture method according to claim 1, it is characterised in that:Institute
It is that quaternary ammonium base class water soluble polyamide is applied into finish coat with rolling method to be coated with to artificial leather base fabric's surface of semi-finished to state covering with paint.
5. quaternary ammonium base class water-soluble polyamide resins artificial leather manufacture method according to claim 1, it is characterised in that:Institute
It is pad dyeing, dye gigging, overflow dyeing or airflow dyeing to state dyeing treatment.