CN106760358A - A kind of baking vanish antibacterial decorative panel - Google Patents
A kind of baking vanish antibacterial decorative panel Download PDFInfo
- Publication number
- CN106760358A CN106760358A CN201510808952.0A CN201510808952A CN106760358A CN 106760358 A CN106760358 A CN 106760358A CN 201510808952 A CN201510808952 A CN 201510808952A CN 106760358 A CN106760358 A CN 106760358A
- Authority
- CN
- China
- Prior art keywords
- baking vanish
- layer
- base material
- decorative panel
- antibacterial
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Baking vanish layer and the antibiotic layer on base material are set in turn in from outside to inside the invention discloses a kind of baking vanish antibacterial decorative panel, including base material and edge；Base material is made up of following raw material：String, portland cement, flyash, vinal, lime stone, kaolin, potassium silicate, tungsten sulfide, calcium sulfate, ABS resin emulsion, hydroxy stearic acid isodecyl ester；Described antibiotic layer is TiO2Photocatalyst material, Nano Silver mix the mixture layer of composition with Formaldehyde decomposition active ingredient.The beneficial effects of the invention are as follows：Durability is good, antibacterial and mouldproof, intensity are high, sound absorption sound insulation, density are strong, good penetrability, low cost；The stable performance of Nano Silver, not volatile, by ionization, sustainedly and stably release silver ion enters in bacterial body the silver of nanoscale, so as to keep antibacterial functions for a long time；TiO2Photocatalyst material is produced under the irradiation of sunshine or visible ray and is similar to photosynthetic catalytic reaction, forms oxidability extremely strong hydroxyl free radical and active oxygen.
Description
Technical field
The present invention relates to board technology field, particularly a kind of baking vanish antibacterial decorative panel.
Background technology
Various volatile organic matters and harmful microorganism are there is in the living environment of people, the physical and mental health of people is directly affected.The antimildew and antibacterial agent of past people's chemicals is sprayed at the surrounding in room, thereby solve the air quality problems in room, and the toxicity of common antimildew and antibacterial agent is larger, heat-resisting, endurance quality is poor, and being sprayed at floor and surface of decorative plate easily makes it change colour and influence attractive in appearance.
The content of the invention
A kind of shortcoming it is an object of the invention to overcome prior art, there is provided the baking vanish antibacterial decorative panel of environment purification and air.
The purpose of the present invention is achieved through the following technical solutions：A kind of baking vanish antibacterial decorative panel, including base material and edge are set in turn in baking vanish layer and the antibiotic layer on base material from outside to inside；Described baking vanish layer is resin, Hydroxylated acrylic resin, anti-settling thickener, solvent and filler by weight 20-30：5-10：5-10：5-10：The mixture layer of 50-70 mixing compositions, described base material by following weight than raw material be made：String 30-35, portland cement 25-35, flyash 45-50, vinal 2-4, lime stone 5-10, kaolin 10-15, potassium silicate 1-1.5, tungsten sulfide 0.5-1, calcium sulfate 0.3-0.6, ABS resin emulsion 15-20, hydroxy stearic acid isodecyl ester 10-15；Described antibiotic layer is TiO2Photocatalyst material, Nano Silver and Formaldehyde decomposition active ingredient are by weight 10-20：2-5：The mixture layer of 5-10 mixing compositions.
Described Formaldehyde decomposition active ingredient includes one or more mixture in chitin, nanometer silicon chip or tourmaline powder.
Described baking vanish layer is resin, Hydroxylated acrylic resin, anti-settling thickener, solvent and filler by weight 25：8：8：8：The mixture layer of 60 mixing compositions.
Described base material by following weight than raw material be made：String 33, portland cement 30, flyash 48, vinal 3, lime stone 6, kaolin 12, potassium silicate 1.2, tungsten sulfide 0.8, calcium sulfate 0.5, ABS resin emulsion 17, hydroxy stearic acid isodecyl ester 13.
Described antibiotic layer is TiO2Photocatalyst material, Nano Silver and Formaldehyde decomposition active ingredient are by weight 15：3：The mixture layer of 7 mixing compositions.
The present invention has advantages below：
Baking vanish layer is easier to adhere to, and improves operating efficiency 50%, saves manpower and materials cost, and with larger commercial value, base material has that good durability, antibacterial and mouldproof, intensity high, sound absorption sound insulation, density is strong, good penetrability, low cost and other advantages；The stable performance of Nano Silver, not volatile, by ionization, sustainedly and stably release silver ion enters in bacterial body the silver of nanoscale, so as to keep antibacterial functions for a long time；TiO2Photocatalyst material is produced under the irradiation of sunshine or visible ray and is similar to photosynthetic catalytic reaction, and the oxygen and hydrone in air are excited, and forms oxidability extremely strong hydroxyl free radical and active oxygen.The extremely strong free radical of these oxidabilities can catch and kill the planktonic bacteria in air, and remove that cigarette is smelly, rubbish is smelly, sludge is smelly, and organic pollution is constantly degraded into free of contamination water and carbon dioxide etc., so as to reach the purpose of environment purification and air.
Brief description of the drawings
Fig. 1 is structural representation of the invention.
In figure, 1- base materials, 2- antibiotic layers, 3- baking vanish layer.
Specific embodiment
Below in conjunction with the accompanying drawings and embodiment the present invention will be further described：
Embodiment 1：
As shown in figure 1, a kind of baking vanish antibacterial decorative panel, including base material 1 and edge are set in turn in baking vanish layer 3 and the antibiotic layer 2 on base material 1 from outside to inside；Described baking vanish layer 3 is resin, Hydroxylated acrylic resin, anti-settling thickener, solvent and filler by weight 25：8：8：8：The mixture layer of 60 mixing compositions；Described base material 1 by following weight than raw material be made：String 33, portland cement 30, flyash 48, vinal 3, lime stone 6, kaolin 12, potassium silicate 1.2, tungsten sulfide 0.8, calcium sulfate 0.5, ABS resin emulsion 17, hydroxy stearic acid isodecyl ester 13, described antibiotic layer 2 are TiO2Photocatalyst material, Nano Silver and Formaldehyde decomposition active ingredient are by weight 15：3：The mixture layer of 7 mixing compositions.
Described Formaldehyde decomposition active ingredient includes one or more mixture in chitin, nanometer silicon chip or tourmaline powder.
Base material 1 has that durability is good, antibacterial and mouldproof, intensity high, sound absorption sound insulation, density are strong, good penetrability, low cost and other advantages；The stable performance of Nano Silver, not volatile, by ionization, sustainedly and stably release silver ion enters in bacterial body the silver of nanoscale, so as to keep antibacterial functions for a long time； TiO2Photocatalyst material is produced under the irradiation of sunshine or visible ray and is similar to photosynthetic catalytic reaction, and the oxygen and hydrone in air are excited, and forms oxidability extremely strong hydroxyl free radical and active oxygen.The extremely strong free radical of these oxidabilities can catch and kill the planktonic bacteria in air, and remove that cigarette is smelly, rubbish is smelly, sludge is smelly, and organic pollution is constantly degraded into free of contamination water and carbon dioxide etc., so as to reach the purpose of environment purification and air.
Embodiment 2：
As shown in figure 1, a kind of baking vanish antibacterial decorative panel, including base material 1 and edge are set in turn in baking vanish layer 3 and the antibiotic layer 2 on base material 1 from outside to inside；Described baking vanish layer 3 is resin, Hydroxylated acrylic resin, anti-settling thickener, solvent and filler by weight 20：5：5：5：The mixture layer of 50 mixing compositions；Described base material 1 by following weight than raw material be made：String 30, portland cement 25, flyash 45, vinal 2, lime stone 5, kaolin 10, potassium silicate 1, tungsten sulfide 0.5, calcium sulfate 0.3, ABS resin emulsion 15, hydroxy stearic acid isodecyl ester 10, described antibiotic layer 2 are TiO2Photocatalyst material, Nano Silver and Formaldehyde decomposition active ingredient are by weight 10：2：The mixture layer of 5 mixing compositions.
Described Formaldehyde decomposition active ingredient includes one or more mixture in chitin, nanometer silicon chip or tourmaline powder.
Base material 1 has that durability is good, antibacterial and mouldproof, intensity high, sound absorption sound insulation, density are strong, good penetrability, low cost and other advantages；The stable performance of Nano Silver, not volatile, by ionization, sustainedly and stably release silver ion enters in bacterial body the silver of nanoscale, so as to keep antibacterial functions for a long time；TiO2Photocatalyst material is produced under the irradiation of sunshine or visible ray and is similar to photosynthetic catalytic reaction, and the oxygen and hydrone in air are excited, and forms oxidability extremely strong hydroxyl free radical and active oxygen.The extremely strong free radical of these oxidabilities can catch and kill the planktonic bacteria in air, and remove that cigarette is smelly, rubbish is smelly, sludge is smelly, and organic pollution is constantly degraded into free of contamination water and carbon dioxide etc., so as to reach the purpose of environment purification and air.
Embodiment 3：
As shown in figure 1, a kind of baking vanish antibacterial decorative panel, including base material 1 and edge are set in turn in baking vanish layer 3 and the antibiotic layer 2 on base material 1 from outside to inside；Described baking vanish layer 3 is resin, Hydroxylated acrylic resin, anti-settling thickener, solvent and filler by weight 30：10：10：10：The mixture layer of 70 mixing compositions；Described base material 1 by following weight than raw material be made：String 35, portland cement 35, flyash 50, vinal 4, lime stone 10, kaolin 15, potassium silicate 1.5, tungsten sulfide 1, calcium sulfate 0.6, ABS resin emulsion 20, hydroxy stearic acid isodecyl ester 15, described antibiotic layer 2 are TiO2Photocatalyst material, Nano Silver and Formaldehyde decomposition active ingredient are by weight 20：5：The mixture layer of 10 mixing compositions.
Described Formaldehyde decomposition active ingredient includes one or more mixture in chitin, nanometer silicon chip or tourmaline powder.
Base material 1 has that durability is good, antibacterial and mouldproof, intensity high, sound absorption sound insulation, density are strong, good penetrability, low cost and other advantages；The stable performance of Nano Silver, not volatile, by ionization, sustainedly and stably release silver ion enters in bacterial body the silver of nanoscale, so as to keep antibacterial functions for a long time；TiO2Photocatalyst material is produced under the irradiation of sunshine or visible ray and is similar to photosynthetic catalytic reaction, and the oxygen and hydrone in air are excited, and forms oxidability extremely strong hydroxyl free radical and active oxygen.The extremely strong free radical of these oxidabilities can catch and kill the planktonic bacteria in air, and remove that cigarette is smelly, rubbish is smelly, sludge is smelly, and organic pollution is constantly degraded into free of contamination water and carbon dioxide etc., so as to reach the purpose of environment purification and air.
Claims (5)
1. a kind of baking vanish antibacterial decorative panel, it is characterised in that：Including base material（1）Base material is set in turn in from outside to inside with edge（1）On baking vanish layer（3）And antibiotic layer（2）；Described baking vanish layer（3）It is resin, Hydroxylated acrylic resin, anti-settling thickener, solvent and filler 20-30 by weight：5-10：5-10：5-10：The mixture layer of 50-70 mixing compositions, described base material（1）By following weight than raw material be made：String 30-35, portland cement 25-35, flyash 45-50, vinal 2-4, lime stone 5-10, kaolin 10-15, potassium silicate 1-1.5, tungsten sulfide 0.5-1, calcium sulfate 0.3-0.6, ABS resin emulsion 15-20, hydroxy stearic acid isodecyl ester 10-15；Described antibiotic layer（2）It is TiO2Photocatalyst material, Nano Silver and Formaldehyde decomposition active ingredient are by weight 10-20：2-5：The mixture layer of 5-10 mixing compositions.
2. a kind of baking vanish antibacterial decorative panel according to claim 1, it is characterised in that：Described Formaldehyde decomposition active ingredient includes one or more mixture in chitin, nanometer silicon chip or tourmaline powder.
3. a kind of baking vanish antibacterial decorative panel according to claim 1, it is characterised in that：Described baking vanish layer（3）It is resin, Hydroxylated acrylic resin, anti-settling thickener, solvent and filler by weight 25：8：8：8：The mixture layer of 60 mixing compositions.
4. a kind of baking vanish antibacterial decorative panel according to claim 1, it is characterised in that：Described base material（1）By following weight than raw material be made：String 33, portland cement 30, flyash 48, vinal 3, lime stone 6, kaolin 12, potassium silicate 1.2, tungsten sulfide 0.8, calcium sulfate 0.5, ABS resin emulsion 17, hydroxy stearic acid isodecyl ester 13.
5. a kind of baking vanish antibacterial decorative panel according to claim 1, it is characterised in that：Described antibiotic layer（2）It is TiO2Photocatalyst material, Nano Silver and Formaldehyde decomposition active ingredient are by weight 15：3：The mixture layer of 7 mixing compositions.