CN106757678A - Woven cotton bag polyolefin cartographic bi-bomb fabric continuous production processes - Google Patents

Woven cotton bag polyolefin cartographic bi-bomb fabric continuous production processes Download PDF

Info

Publication number
CN106757678A
CN106757678A CN201611014434.2A CN201611014434A CN106757678A CN 106757678 A CN106757678 A CN 106757678A CN 201611014434 A CN201611014434 A CN 201611014434A CN 106757678 A CN106757678 A CN 106757678A
Authority
CN
China
Prior art keywords
concentration
cartographic
bomb
cotton bag
continuous production
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201611014434.2A
Other languages
Chinese (zh)
Other versions
CN106757678B (en
Inventor
王德振
许秋生
张战旗
齐元章
仲伟浩
王辉
邵珠珍
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Lufeng Weaving and Dyeing Co Ltd
Original Assignee
Lufeng Weaving and Dyeing Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Lufeng Weaving and Dyeing Co Ltd filed Critical Lufeng Weaving and Dyeing Co Ltd
Priority to CN201611014434.2A priority Critical patent/CN106757678B/en
Publication of CN106757678A publication Critical patent/CN106757678A/en
Application granted granted Critical
Publication of CN106757678B publication Critical patent/CN106757678B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

It is radially pure cotton bag polyolefin elastic fibers the present invention relates to a kind of woven cotton bag polyolefin cartographic bi-bomb fabric continuous production processes, broadwise is pure cotton bag polyolefin elastic fibers, and the fineness of elastic filament is 33D, 40D or 42D.Potential demand to adapt to Vehicles Collected from Market of the invention, realizes the production of woven cartographic bi-bomb fabric on continuous dyeing apparatus, by elastic moderate after dyeing and finishing treatment, fabric resilience is good, fabric footpath broadwise is shunk and reaches 0~3%, and fabric good stability of the dimension is soft.

Description

Woven cotton bag polyolefin cartographic bi-bomb fabric continuous production processes
Technical field
The invention belongs to technical field of textile printing, and in particular to a kind of woven cotton bag polyolefin cartographic bi-bomb fabric is continuous Production technology.
Background technology
Due to comfortable and easy to wear, retractility is good, can reduce constraint of the clothing to human motion, thus increasingly receives for stockinette To liking for people, the underlinen fabric of existing market is more with broadwise as stretch yarn, and cartographic bi-bomb fabric through broadwise because have It is flexible, to stretch freely, dress is more comfortable, and the accreditation of consumer is increasingly obtained at present, and market potential is huge, but currently The cartographic bi-bomb fabric in market with cotton/brocade, wash/the knitting fabric of the stretch yarn such as brocade based on, be mainly used in leisure fabric, swimsuit, Anorak, jeans etc., in the market there are no woven shirt class cartographic bi-bomb fabric.
Current people wish that woven underlinen fabric can also have for the comfortableness more and more higher worn, more clients The effect of cartographic bi-bomb, thus ensure people attend formal occasion can also activity freely, easily tackle various commercial activitys, Therefore in the market is very big for the potential demand amount of woven cartographic bi-bomb fabric.
Cartographic bi-bomb fabric in the market is generally knitting fabric, and this kind of fabric is how enterprising in the equipment of loose formula batch (-type) Row production, and woven fabric when process on continuous production equipment because there is tension force in radial direction, be radially difficult contraction, it is difficult to realize Radial elastic, so simultaneously few using the technology that continuous production equipment processes cartographic bi-bomb fabric in dyeing and finishing field.
The content of the invention
It is an object of the invention to provide a kind of woven cotton bag polyolefin cartographic bi-bomb fabric continuous production processes, to adapt to work as The potential demand in preceding market.Realize the production of woven cartographic bi-bomb fabric on continuous dyeing apparatus.By after dyeing and finishing treatment Elasticity is moderate, and fabric resilience is good, and fabric footpath broadwise is shunk and reaches 0~-3%, and fabric good stability of the dimension is soft.
Woven cotton bag polyolefin cartographic bi-bomb fabric continuous production processes of the present invention, are radially pure cotton bag polyolefin Elastic fibers, broadwise is pure cotton bag polyolefin elastic fibers, and the fineness of elastic filament is 33D, 40D or 42D.
Woven cotton bag polyolefin cartographic bi-bomb fabric continuous production processes include → desizing → kiering → oxygen bleaching → silk of singing Light → dye or brighten → softness → preshrunk manufacturing procedure.
The condition of softening step：The concentration of softening agent is 10~30g/L, upper overfeeding：12~18%, lower overfeeding -1%~- 0.3%, drying room temperature：100 DEG C~130 DEG C, 40~50m/min of speed enters cloth tension force 140-180N, and expanding is more than into cloth breadth 8~15cm, cropping overfeeding 4~5%, 80~120N of cropping tension force.
The condition of mercerizing process：The concentration of NaOH be 200~240g/L, mercerising expanding breadth be more than into cloth breadth 1~ 3cm, overfeeding 102%~104%, 200~220N of mercerising tension force.
The condition of shrinking processes：Pressure is away from 12~18mm, 97~103 DEG C of glue blanket temperature, 1.4~1.7bar of tension force, speed 30 ~45m/min；The condition of singeing step：105~115m/min of speed, 15~18mbar of flame intensity, it is positive to burn.
The condition of desizing operation：The concentration of desizing enzyme is 2~4g/L, and the concentration of bleeding agent is 3~7g/L, chelating agent it is dense It is 1~3g/L to spend, steam box decatize 98~100 DEG C of * 12~15min, 200~260N of tension force.
The condition of kiering operation：The concentration of NaOH is 38~45g/L；The concentration of refining agent is 4~7g/L；Bleeding agent it is dense It is 4~6g/L to spend, steam box decatize 98~100 DEG C of * 20~25min, 200~260N of tension force.
The condition of oxygen bleaching operation：The concentration of NaOH is 2~4g/L, H2O28~14g/L of concentration, the concentration of chelating agent is 8 ~12g/L, the concentration of stabilizer is 7~8g/L, and the concentration of bleeding agent is 4~6g/L, 98~100 DEG C * 20 of steam box decatize~ 25min, 200~260N of tension force.
Brighten the condition of operation：1~the 14g/L of concentration of brightening agent, 200~250N of tension force.
The condition of dyeing process：Pad dye liquor, infrared drying, hot-air seasoning, clot, tension force 200N.
Fixation liquid is padded, the concentration of fixation liquid composition NaOH is 10g/L, and the concentration of glauber salt is 200g/L, reservehao S Concentration is 2g/L.
Product Design Theory resilient radial is 17~20%, and the theoretical elasticity of broadwise is 20~24%.
The preferred FH-01 of described softening agent, the preferred PHC of desizing enzyme, the preferred MRZ of bleeding agent, the preferred SQ-A of chelating agent, refining The preferred UH of agent, the preferred MRZ of bleeding agent, the preferred SQ-A of chelating agent, the preferred FC-B of stabilizer, the preferred MRZ of bleeding agent, brightening agent are preferred BHA。
Wherein：
The manufacturer of softening agent is FH-01, and manufacturer is that Hensel steps Chemical trade Co., Ltd, desizing enzyme PHC Manufacturer is the manufacturer for holding high chemical industry Shanghai Co., Ltd high, penetrant m RZ to hold high chemical industry Shanghai Co., Ltd high, chelating The manufacturer of agent SQ-A is the manufacturer of Zibo Lu Rui Fine Chemical Co., Ltd, refining agent UH for high chemical industry Shanghai high has Limit company, the manufacturer of penetrant m RZ be hold high chemical industry Shanghai Co., Ltd high, chelating agent SQ-A manufacturer be Zibo Shandong Auspicious Fine Chemical Co., Ltd, the manufacturer of stabilizer FC-B are high chemical industry Shanghai Co., Ltd high, the production of penetrant m RZ Producer is to hold high chemical industry Shanghai Co., Ltd high, the preferred BHA manufacturers of brightening agent to hold high chemical industry Shanghai Co., Ltd high.
The actual conditions of woven cotton bag polyolefin cartographic bi-bomb fabric continuous production processes is as follows：
(1) singe：Speed 105~115m/min, 15~18mbar of flame intensity, it is positive to burn.
(2) desizing：The concentration of desizing enzyme PHC is 2~4g/L, and the concentration of penetrant m RZ3~7g/L, chelating agent SQ-A is 1 ~3g/L, steam box decatize 98~100 DEG C of * 12~15min, 200~260N of tension force.
(3) kiering：The concentration of NaOH is 38~45g/L；The concentration of refining agent is 4~7g/L；The concentration of penetrant m RZ is 4~6g/L, steam box decatize 98~100 DEG C of * 20~25min, 200~260N of tension force.
(4) oxygen bleaching：The concentration of NaOH is 2~4g/L, H2O28~14g/L of concentration, the concentration of chelating agent SQ-A for 8~ The concentration of 12g/L, stabilizer FC-B is 7~8g/L, and the concentration of penetrant m RZ is 4~6g/L, 98~100 DEG C * 20 of steam box decatize ~25min, 200~260N of tension force.
(5) mercerising：The concentration of NaOH is 200~240g/L, and mercerising expanding breadth is more than 1~3cm of Fabric width, overfeeding 102%~104%, 200~220N of mercerising tension force.
(6) brighten：1~14g/L of brightening agent, 200~250N of tension force.
The condition of dyeing process：Pad dye liquor, infrared drying, hot-air seasoning, clot, tension force 200N.
Fixation liquid is padded, the concentration of fixation liquid composition NaOH is 10g/L, and the concentration of glauber salt is 200g/L, reservehao S Concentration is 2g/L.
(7) it is soft：Implement on framing shaping machine, the concentration of softening agent is 10~30g/L, upper overfeeding：Under 12~18% Overfeeding -1%~-0.3%, drying room temperature：100 DEG C~130 DEG C, 40~50m/min of speed enters cloth tension force 140-180N, expanding It is more than into cloth 8~15cm of breadth, cropping overfeeding 4~5%, 80~120N of cropping tension force.
(8) preshrunk：Spray is opened, is pressed away from 12~18mm, 97~103 DEG C of glue blanket temperature, 1.4~1.7bar of tension force, speed 30 ~45m/min.
The present invention is engaged by stenter and mercerizing machine expanding and overfeeding, preshrinking machine shrinks, and each operation tension force control System reaches the contraction of radial direction, so that radial elastic is obtained, it is achieved thereby that woven cartographic bi-bomb fabric is in continous way equipment for dyeing and finishing On normal process.
Compared with prior art, the invention has the advantages that：
(1) production of woven cartographic bi-bomb fabric on continuous dyeing apparatus is realized, the big of four-side elasticity fabric can be realized Batch continuous prodution.
(2) 12%~15% is reached by the radial elastic after dyeing and finishing treatment, broadwise elasticity reaches 13~17%, and elasticity is returned More than 55% is reached again, and elasticity is moderate, and fabric resilience is good.
(3) fabric footpath broadwise is shunk and reaches 0~-3%, and fabric good stability of the dimension is soft.
Specific embodiment
With reference to embodiment, the present invention will be further described.
Embodiment 1
Fabric：XLA50 (42D) * XLA50 (42D) * 144*80*53/54 organize plain weave.
Fabric design elasticity：Radial elastic 19.8%, broadwise 23.2%.
Technological process：Singe → desizing → kiering → oxygen bleaching → mercerising → brighten → softness → preshrunk.
The condition of each operation is as follows：
(1) singe：Speed 110m/min flame intensity 15mbar, it is positive to burn；
(2) desizing：The concentration of desizing enzyme PHC (Ang Gao chemical industry (Shanghai) Co., Ltd.) is 3g/L, penetrant m RZ (high height Chemical industry (Shanghai) Co., Ltd.) concentration be 4g/L, the concentration of chelating agent SQ-A (Ang Gao chemical industry (Shanghai) Co., Ltd.) is 1g/ L, steam box decatize 100 DEG C of * 14min, tension force 220N；
(3) kiering：The concentration of NaOH is 38~45g/L；The concentration of refining agent UH is 4~7g/L；Penetrant m RZ (high height Chemical industry (Shanghai) Co., Ltd.) concentration be 4~6g/L, steam box decatize 100 DEG C of * 22min, tension force 220N；
(4) oxygen bleaching：The concentration of NaOH is 2g/L, H2O2Concentration 8g/L, chelating agent SQ-A (hold high chemical industry (Shanghai) high it is limited Company) concentration be 8g/L, the concentration of stabilizer FC-B (Ang Gao chemical industry (Shanghai) Co., Ltd.) is 7g/L, and penetrant m RZ is (high Chemical industry (Shanghai) Co., Ltd. high) concentration be 4/L, steam box decatize 100 DEG C of * 25min, tension force 220N；
(5) mercerising：The concentration of NaOH is 200g/L, mercerising expanding breadth 140cm, overfeeding 103%；Mercerising tension force 230N.
(6) brighten：The concentration of brightening agent BHT is 1g/L, tension force 220N.
(7) it is soft：Implement on framing shaping machine, the concentration of softening agent FH-01 (Hensel steps Chemical trade Co., Ltd) It is 30g/L, upper overfeeding：14% time overfeeding -0.8%, drying room temperature：100 DEG C, speed 50m/min enters cloth tension force 160N, expanding 143cm, cropping overfeeding 3%, cropping tension force 100N.
(8) preshrunk：Spray, pressure are opened away from 14mm, 100 DEG C of glue blanket temperature, tension force 1.4bar, speed 40m/min.
The radial elastic expected below by above-mentioned dyeing and finishing processing is 13.6%, and elastic recovery 57.2%, broadwise elasticity reaches 15.8%, 60.7%, radially shrink -2.7%, broadwise shrink -1.8%.
Embodiment 2
Fabric：MS40 (42D) * MS40 (42D) * 152*68*55/56 organize latitude galassing；
Fabric design elasticity：Radial elastic 17.8%, broadwise 21%；
Technological process：Singe → desizing → kiering → oxygen bleaching → mercerising → brighten → softness → preshrunk；
The condition of each operation is as follows：
(1) singe：Speed 105m/min flame intensity 18mbar, it is positive to burn；
(2) desizing：The concentration of desizing enzyme PHC (Ang Gao chemical industry (Shanghai) Co., Ltd.) is 4g/L, penetrant m RZ (high height Chemical industry (Shanghai) Co., Ltd.) concentration be 7g/L, the concentration of chelating agent SQ-A (Ang Gao chemical industry (Shanghai) Co., Ltd.) is 3g/ L, steam box decatize 100 DEG C of * 14min, tension force 260N；；
(3) kiering：The concentration of NaOH is 45g/L；The concentration of refining agent UH is 7g/L；Penetrant m RZ (high chemical industry high (on Sea) Co., Ltd) concentration be 6g/L, steam box decatize 100 DEG C of * 22min, tension force 260N；；
(4) oxygen bleaching：The concentration of NaOH is 2g/L, H2O2Concentration be 8g/L, chelating agent SQ-A (hold high chemical industry (Shanghai) high have Limit company) concentration be 8g/L, the concentration of stabilizer FC-B (Ang Gao chemical industry (Shanghai) Co., Ltd.) is 7g/L, penetrant m RZ The concentration of (Ang Gao chemical industry (Shanghai) Co., Ltd.) is 4/L, steam box decatize 100 DEG C of * 25min, tension force 260N；
(5) mercerising：The concentration of NaOH is 240g/L, mercerising expanding breadth 140cm, overfeeding 103%；Mercerising tension force 220N.
(6) brighten：The concentration of brightening agent BHT is 1g/L, tension force 250N.
(7) it is soft：Implement on framing shaping machine, the concentration of softening agent FH-01 is 15g/L, upper overfeeding：Surpass for 16% time Hello -1.0%, drying room temperature：130 DEG C, speed 50m/min enters cloth tension force 180N, expanding 143cm, cropping overfeeding 3~5% falls Cloth tension force 120N.
(8) preshrunk：Spray is opened, is pressed away from 12mm, 100 DEG C of glue blanket temperature, tension force 1.7bar, speed 45m/min.
The radial elastic expected below by above-mentioned dyeing and finishing processing is 12.6%, and elastic recovery 58.9%, broadwise elasticity reaches 14.6%, elastic recovery 63.8%, radially shrink -2.4%, broadwise shrink -2.3%.
Embodiment 3
Fabric：XLA60 (33D) * XLA60 (33D) * 190*110*53/54 organize 4/1 satin weave.
Fabric design elasticity：Radial elastic 18.4%, broadwise 21.3%.
Technological process：Singe → desizing → kiering → oxygen bleaching → mercerising → pad dye liquor → vapour steaming colour fixing → softness → pre- Contracting.
The condition of each operation is as follows：
(1) singe：Speed 115m/min flame intensity 15mbar, it is positive to burn；
(2) desizing：The concentration of desizing enzyme PHC (Ang Gao chemical industry (Shanghai) Co., Ltd.) is 2g/L, penetrant m RZ (high height Chemical industry (Shanghai) Co., Ltd.) concentration be 3g/L, the concentration of chelating agent SQ-A (Ang Gao chemical industry (Shanghai) Co., Ltd.) is 1g/ L, steam box decatize 100 DEG C of * 14min, tension force 200N；
(3) kiering：The concentration of NaOH is 38g/L；The concentration of refining agent UH is 4g/L；Penetrant m RZ (high chemical industry high (on Sea) Co., Ltd) concentration be 4g/L, steam box decatize 100 DEG C of * 22min, tension force 200N；
(4) oxygen bleaching：The concentration of NaOH is 2g/L, H2O2Concentration 8g/L, chelating agent SQ-A (hold high chemical industry (Shanghai) high it is limited Company) concentration be 8g/L, the concentration of stabilizer FC-B (Ang Gao chemical industry (Shanghai) Co., Ltd.) is 7g/L, and penetrant m RZ is (high Chemical industry (Shanghai) Co., Ltd. high) concentration be 4/L, steam box decatize 100 DEG C of * 20min, tension force 200N；
(5) mercerising：NaOH200g/L, mercerising expanding breadth 140cm, overfeeding 103%；Mercerising tension force 200N.
(6) dye liquor, infrared drying, hot-air seasoning, clot, tension force 200N are padded.
Fixation liquid is padded, the concentration of fixation liquid composition NaOH is 10g/L, and the concentration of glauber salt is 200g/L, reservehao S Concentration is 2g/L.
(8) it is soft：Implement on framing shaping machine, softening agent FH-01 (Hensel steps Chemical trade Co., Ltd) 10g/L, Upper overfeeding：18% time overfeeding -0.3%, drying room temperature：100 DEG C, speed 50m/min enters cloth tension force 140N, expanding 141cm, fall Cloth overfeeding 5%, cropping tension force 80N.
(9) preshrunk：Spray, pressure are opened away from 18mm, 100 DEG C of glue blanket temperature, tension force 1.4bar, speed 30m/min.
The radial elastic expected below by above-mentioned dyeing and finishing processing is 12.4%, and elastic recovery 56.9%, broadwise elasticity reaches 13.7%, elastic recovery 63.4%, radially shrink -2.8%, broadwise shrink -2.6%.

Claims (10)

1. a kind of woven cotton bag polyolefin cartographic bi-bomb fabric continuous production processes, it is characterised in that be radially pure cotton bag polyene Hydrocarbon elastic fibers, broadwise is pure cotton bag polyolefin elastic fibers, and the fineness of elastic filament is 33D, 40D or 42D.
2. a kind of woven cotton bag polyolefin cartographic bi-bomb fabric continuous production processes according to claim 1, its feature exists In woven cotton bag polyolefin cartographic bi-bomb fabric continuous production processes include → desizing → kiering → oxygen bleaching → mercerising → dye of singing Color brightens → softness → preshrunk manufacturing procedure.
3. a kind of woven cotton bag polyolefin cartographic bi-bomb fabric continuous production processes according to claim 2, its feature exists In the condition of softening step：The concentration of softening agent is 10~30g/L, upper overfeeding：12~18%, lower overfeeding -1%~-0.3%, Drying room temperature：100 DEG C~130 DEG C, 40~50m/min of speed enters cloth tension force 140-180N, expanding be more than into cloth breadth 8~ 15cm, cropping overfeeding 4~5%, 80~120N of cropping tension force.
4. a kind of woven cotton bag polyolefin cartographic bi-bomb fabric continuous production processes according to claim 2, its feature exists In the condition of mercerizing process：The concentration of NaOH is 200~240g/L, and mercerising expanding breadth is more than into cloth 1~3cm of breadth, overfeeding 102%~104%, 200~220N of mercerising tension force.
5. a kind of woven cotton bag polyolefin cartographic bi-bomb fabric continuous production processes according to claim 2, its feature exists In the condition of shrinking processes：Pressure is away from 12~18mm, 97~103 DEG C of glue blanket temperature, 1.4~1.7bar of tension force, 30~45m/ of speed min；The condition of singeing step：105~115m/min of speed, 15~18mbar of flame intensity, it is positive to burn.
6. a kind of woven cotton bag polyolefin cartographic bi-bomb fabric continuous production processes according to claim 2, its feature exists In the condition of desizing operation：The concentration of desizing enzyme is 2~4g/L, and the concentration of bleeding agent is 3~7g/L, and the concentration of chelating agent is 1 ~3g/L, steam box decatize 98~100 DEG C of * 12~15min, 200~260N of tension force.
7. a kind of woven cotton bag polyolefin cartographic bi-bomb fabric continuous production processes according to claim 2, its feature exists In the condition of kiering operation：The concentration of NaOH is 38~45g/L；The concentration of refining agent is 4~7g/L；The concentration of bleeding agent is 4 ~6g/L, steam box decatize 98~100 DEG C of * 20~25min, 200~260N of tension force.
8. a kind of woven cotton bag polyolefin cartographic bi-bomb fabric continuous production processes according to claim 2, its feature exists In the condition of oxygen bleaching operation：The concentration of NaOH is 2~4g/L, H2O28~14g/L of concentration, the concentration of chelating agent is 8~12g/ L, the concentration of stabilizer is 7~8g/L, and the concentration of bleeding agent is 4~6g/L, 98~100 DEG C of * 20~25min of steam box decatize, is opened 200~260N of power.
9. a kind of woven cotton bag polyolefin cartographic bi-bomb fabric continuous production processes according to claim 2, its feature exists In brightening the condition of operation：The concentration of brightening agent is 1~14g/L, 200~250N of tension force.
10. a kind of woven cotton bag polyolefin cartographic bi-bomb fabric continuous production processes according to claim 1 and 2, it is special Levy and be, Product Design Theory resilient radial is 17~20%, the theoretical elasticity of broadwise is 20~24%.
CN201611014434.2A 2016-11-15 2016-11-15 Woven cotton packet polyolefin cartographic bi-bomb fabric continuous production processes Active CN106757678B (en)