CN106757666A - A kind of silk flosssilk wadding intertexture jacquard fabric anti-chiseling down technique - Google Patents

A kind of silk flosssilk wadding intertexture jacquard fabric anti-chiseling down technique Download PDF

Info

Publication number
CN106757666A
CN106757666A CN201611096619.2A CN201611096619A CN106757666A CN 106757666 A CN106757666 A CN 106757666A CN 201611096619 A CN201611096619 A CN 201611096619A CN 106757666 A CN106757666 A CN 106757666A
Authority
CN
China
Prior art keywords
flosssilk wadding
silk flosssilk
silk
fabric
chiseling down
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201611096619.2A
Other languages
Chinese (zh)
Inventor
魏庆刚
蔡仪新
姜云
朱敬江
刘艳红
赵娜
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Large Dyehouse Zibo Silk Group Co ltd
Original Assignee
Large Dyehouse Zibo Silk Group Co ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Large Dyehouse Zibo Silk Group Co ltd filed Critical Large Dyehouse Zibo Silk Group Co ltd
Priority to CN201611096619.2A priority Critical patent/CN106757666A/en
Publication of CN106757666A publication Critical patent/CN106757666A/en
Pending legal-status Critical Current

Abstract

A kind of silk flosssilk wadding intertexture jacquard fabric anti-chiseling down technique, belongs to silk flosssilk wadding interweaving product processing technique field.It is characterized in that:Using silk flosssilk wadding fabric, the weave specification of silk flosssilk wadding fabric is 22d/2 × 80s 173 × 195;Apply DOWN PROOF dressing liquid under the conditions of 108 ~ 113 DEG C using drying machine after the upper machine of silk flosssilk wadding fabric weaving, then a low-temperature curing 50s ~ 60s is carried out under the conditions of 137 ~ 142 DEG C, through 178 ~ 183 DEG C of temperature conditionss calenderings, then it is transferred to forming machine and is obtained final product in 178 ~ 183 DEG C of secondary 50s ~ 60s that bake.After the present invention is baked twice before and after, a network structure is formed in the surface hinge of silk flosssilk wadding product, can breathed freely, the frictional force between fiber is increased again, hinder the movement between each interlacing point of fiber, improve silk flosssilk wadding product anti-chiseling down finishing effect.

Description

A kind of silk flosssilk wadding intertexture jacquard fabric anti-chiseling down technique
Technical field
A kind of silk flosssilk wadding intertexture jacquard fabric anti-chiseling down technique, belongs to silk flosssilk wadding interweaving product processing technique field.
Background technology
The filler of eiderdown quilt is mainly eider down, and eider down is the belly in geese and ducks long, into the fine hair of reed flower shaped.Due to Eider down is a kind of animal protein fiber, compares cotton(Vegetative fiber element)Heat insulating ability is high, and is gathered on eider down nodular fibrous Ten million tiny stomata of triangle, can the convergent-divergent with temperature Change, produce temperature adjustment function, absorbable human body distributes flowing Hot gas, completely cut off cool ambient air invasion.The warmth retention property of eiderdown quilt is high, and elasticity is strong, and fluffy degree is high, and with light, soft, soft The characteristics of.Eiderdown quilt is breathed freely dry and comfortable, and hydrofuge is strong, not hardened, the moisture absorption diverging not possessed with other heat insulating materials it is good Performance, is referred to as " quilt that can be breathed ".Eiderdown quilt is durable in use, and it enables to nervous centralis to be stabilized, and enters quickly Sweet and beautiful dreamland, therefore cosmetically also having certain effect, " natural down goes out beauty by under " is also this reason.Eiderdown quilt is fitted For hyperpietic and pre- anti-rheumatism, arthritis.
Mentioned above, with the continuous improvement of people's living standard, the eiderdown quilt market space is very big, is needed extensively as people The daily necessities asked, and the both sides that the eiderdown quilt quilt cover made of silk flosssilk wadding jacquard fabric combines real silk and eider down is excellent Point, thus as high-end class product, it is deep to be pursued by European & American Market.But, due to the natural structure of jacquard fabric tissue, make It is poor into its fabric tightness, it is extremely difficult to DOWN PROOF and escapes effect.
Silk flosssilk wadding interweaving product wants have anti-chiseling down performance, it should meet two conditions:First, fabric will have sufficiently high close Degree, the space between interlacing point is the smaller the better;2nd, there are enough support forces between the interlacing point of fabric, it is impossible to move easily.
DOWN PROOF arrangement technical way in current industry to silk flosssilk wadding product is coating, and anti-plumage is applied in fabric face Suede resin finishing agent, block fiber between, the space between fabric tissue point.Although the anti-chiseling down effect of product is good after arranging, But it is airtight, the class of product is reduced, do not approved by market.Another method is calendering, by the pressure of roll, makes fibre Dimension become flat, reduce fiber between, the space between fabric tissue point, reach the purpose of anti-chiseling down.This way has the disadvantage The effect of anti-chiseling down is poor.
The content of the invention
The technical problem to be solved in the present invention is:Overcome the deficiencies in the prior art, there is provided one kind can breathe freely and anti-chiseling down Silk flosssilk wadding intertexture jacquard fabric anti-chiseling down technique.
The technical solution adopted for the present invention to solve the technical problems is:The silk flosssilk wadding intertexture jacquard fabric anti-chiseling down technique, It is characterized in that:Using silk flosssilk wadding fabric, the weave specification of silk flosssilk wadding fabric is:Warp is using 22 Denier, the combination of two monofilament Mulberry silk, parallel use 80s yarn count combed cotton yarns, thread count be 173 × 195;
Apply DOWN PROOF dressing liquid under the conditions of 108 ~ 113 DEG C using drying machine after the upper machine of silk flosssilk wadding fabric weaving, then 137 ~ A low-temperature curing 50s ~ 60s is carried out under the conditions of 142 DEG C, through 178 ~ 183 DEG C of temperature conditionss calenderings, then be transferred to forming machine 178 ~ 183 DEG C of secondary 50s ~ 60s that bake are obtained final product.
Silk flosssilk wadding intertexture jacquard fabric after anti-chiseling down PROCESS FOR TREATMENT of the invention can breathe freely and anti-chiseling down.The present invention is right When the anti-chiseling down performance of silk flosssilk wadding interweaving product is processed, with reference to anti-chiseling down resin finishing.Anti-chiseling down resin finishing in the present invention, it is premenstrual After low and high temperature is baked twice afterwards, a network structure is formed in the surface hinge of silk flosssilk wadding product, can breathed freely, fiber is increased again Between frictional force, hinder the movement between each interlacing point of fiber, improve silk flosssilk wadding product anti-chiseling down finishing effect.To improve Wearability, reaches feel, ventilative, shrink various index requests.After low-temperature curing, DOWN PROOF dressing liquid cuts with scissors in fabric face Chain is also incomplete, when postchannel process does calendering, is conducive to fiber extrusion to deform, between reduction fiber, between each interlacing point Space;After calendering, fiber is become flat, reduce fiber between, the space between fabric tissue point;Secondary high-temperature is baked is, DOWN PROOF dressing liquid forms network structure in the complete hinge of fabric face, hinders the movement between each interlacing point of fiber, reaches anti- Bore the effect that suede is arranged.The finished product made enters to its DOWN PROOF effect with reference to standard GB/T/T14272-2011 anti-chiseling down performances Row experiment, as a result reaches Standard.Reach anti-chiseling down effect, and 100% excellent properties for remaining silk fabric.
Preferably, the warp of described silk flosssilk wadding fabric is mulberry silk, and parallel is combed cotton yarn.Silk flosssilk wadding interweaving product will have Anti-chiseling down performance, first fabric will have sufficiently high density, and usual silk flosssilk wadding product warp uses 22d/2(22 Denier, two lists The combination of silk)Mulberry silk, parallel uses 80s(80 yarn counts, yarn count:Refer to every gram of length of yarn, i.e. number yarn higher is thinner, Evenness is better, otherwise namely the lower yarn of number is thicker.)Combed cotton yarn, thread count(The warp thread of middle arrangement per square inch With the radical of weft yarn)It is 173 × 195, digital woven is imaged using high density entirely, using multilayer " fish scale-shaped " eclipsed form filling density group Knit;It is with " multicolored interleaving combinations method ", using limited color silk form and aspect when longitude and latitude interweaves that high density images digital woven entirely The spatial mixing effect of generation.By Institutes Of Technology Of Zhejiang Li Jialin teaching inventive and apply.It is former using three first in the world Color color separation principle carries out emulating colored weaving, and technical merit is in first place in the world.From color situation of the silk no more than 6 kinds Under) fabric intertexture color reaches more than 2000 kinds, tissue density improves 8 times than traditional silk weaving picture brocade, and layer of structure extends 3 times, Color representation increases decades of times;The scheme developed can be applied to any species raw material.Particularly fineness is higher The cocoon fiber of 46.6dtex fiber numbers;Through close up to 100/more than cm, filling density is up to 190/more than cm;Intertexture density reaches every English Very little 250~300, fabric intertwined point every square centimeter reaches more than 11500.The present invention images number entirely using high density Weaving technology carries out woven silk flosssilk wadding fabric, and using multilayer " fish scale-shaped " eclipsed form filling density tissue, filling density is than normal weaving process Improve a lot, improve the spreadability of fabric, meet the gas permeability of fabric, anti-chiseling down performance is improve from institutional framework.
Preferably, described DOWN PROOF dressing liquid be castor oil-base aqueous polyurethane and acrylic acid acrylamide in mass ratio 5~7:1 compound.The present invention provides above-mentioned preferred DOWN PROOF dressing liquid, most strong to technique adaptability of the invention, Hinge state after low-temperature curing is especially suitable for the calendering operation under present invention process, fully ensures that fiber extrusion deforms, It is between fiber, the space between each interlacing point reaches minimum of the invention.
Preferably, a described low-temperature curing baking temperature is 140 DEG C.
Preferably, the temperature of described calendering is 180 DEG C.
Preferably, the described secondary temperature for baking is 180 DEG C.
Preferably, the temperature of described applying DOWN PROOF dressing liquid is 110 DEG C.
To various DOWN PROOF dressing liquids under above-mentioned preferred process conditions(Windproof dose)Adaptability it is most strong, can be preferably Ensure the gas permeability and DOWN PROOF performance of silk flosssilk wadding intertexture jacquard fabric.
Compared with prior art, a kind of silk flosssilk wadding intertexture jacquard fabric anti-chiseling down technique of the invention is had the advantage that It is:Silk flosssilk wadding intertexture jacquard fabric after anti-chiseling down PROCESS FOR TREATMENT of the invention can breathe freely and anti-chiseling down, solve traditional handicraft The ventilative problem that can not be had concurrently with anti-chiseling down of lower silk flosssilk wadding intertexture jacquard fabric.Anti-chiseling down performance of the present invention to silk flosssilk wadding interweaving product During treatment, it is initiative add before and after bake and bank up with earth operation twice, can preferably combine anti-chiseling down resin finishing.It is anti-drilling in the present invention Suede resin finishing, through front and rear after low and high temperature is baked twice, a network structure, Ji Nengtou is formed in the surface hinge of silk flosssilk wadding product Gas, increases the frictional force between fiber again, hinders the movement between each interlacing point of fiber, improves silk flosssilk wadding product anti-chiseling down Finishing effect.To improve wearability, feel, ventilative, shrink various index requests are reached.The finished product made is to its DOWN PROOF Effect is tested with reference to standard GB/T/T14272-2011 anti-chiseling down performances, as a result reaches Standard.Reach anti-drilling Suede effect, and the 100% excellent breathability energy for remaining silk fabric.
Specific embodiment
With reference to specific embodiment, the present invention will be further described, and wherein embodiment 1 is optimal implementation of the invention Example.
Wherein, embodiment 1 ~ 6 and cotton fabric fabric used by comparative example 1 ~ 3 are carried greatly in the big dyehouse silk group company in Zibo The weaving of flower division department.
Embodiment 1
The design of silk flosssilk wadding jacquard product is pasture and water, specification 22d/2 × 80s 173 × 195 in the present embodiment;
By below scheme:After fabric is practiced in vain through pre-treatment, DOWN PROOF is applied under the conditions of 110 DEG C using drying machine after machine in weaving Dressing liquid, then carries out a low-temperature curing 50s ~ 60s under the conditions of 140 DEG C, through 180 DEG C of temperature conditionss calenderings, then is transferred to calmly Type machine is obtained final product in 180 DEG C of secondary 50s ~ 60s that bake.
Embodiment 2
The design of silk flosssilk wadding jacquard product is Aguarius flower, specification 22d/2 × 80s 173 × 195 in the present embodiment;
By below scheme:After fabric is practiced in vain through pre-treatment, DOWN PROOF is applied under the conditions of 111 DEG C using drying machine after machine in weaving Dressing liquid, then carries out a low-temperature curing 50s ~ 60s under the conditions of 139 DEG C, through 181 DEG C of temperature conditionss calenderings, then is transferred to calmly Type machine is obtained final product in 181 DEG C of secondary 50s ~ 60s that bake.
Embodiment 3
The design of silk flosssilk wadding jacquard product is fringed iris, specification 22d/2 × 80s 173 × 195 in the present embodiment;
By below scheme:After fabric is practiced in vain through pre-treatment, DOWN PROOF is applied under the conditions of 109 DEG C using drying machine after machine in weaving Dressing liquid, then carries out a low-temperature curing 50s ~ 60s under the conditions of 141 DEG C, through 179 DEG C of temperature conditionss calenderings, then is transferred to calmly Type machine is obtained final product in 179 DEG C of secondary 50s ~ 60s that bake.
Embodiment 4
The design of silk flosssilk wadding jacquard product is fringed iris, specification 22d/2 × 80s 173 × 195 in the present embodiment;
By below scheme:After fabric is practiced in vain through pre-treatment, DOWN PROOF is applied under the conditions of 108 DEG C using drying machine after machine in weaving Dressing liquid, then carries out a low-temperature curing 50s ~ 60s under the conditions of 137 DEG C, through 178 DEG C of temperature conditionss calenderings, then is transferred to calmly Type machine is obtained final product in 178 DEG C of secondary 50s ~ 60s that bake.
Embodiment 5
The design of silk flosssilk wadding jacquard product is fringed iris, specification 22d/2 × 80s 173 × 195 in the present embodiment;
By below scheme:After fabric is practiced in vain through pre-treatment, DOWN PROOF is applied under the conditions of 113 DEG C using drying machine after machine in weaving Dressing liquid, then carries out a low-temperature curing 50s ~ 60s under the conditions of 142 DEG C, through 183 DEG C of temperature conditionss calenderings, then is transferred to calmly Type machine is obtained final product in 183 DEG C of secondary 50s ~ 60s that bake.
Comparative example 1
The design of silk flosssilk wadding jacquard product is pasture and water, specification 22d/2 × 80s 173 × 160 in the present embodiment;
By below scheme:After fabric is practiced in vain through pre-treatment, DOWN PROOF is applied under the conditions of 110 DEG C using drying machine after machine in weaving Dressing liquid, then carries out a low-temperature curing 50s ~ 60s under the conditions of 140 DEG C, through 180 DEG C of temperature conditionss calenderings, then is transferred to calmly Type machine is obtained final product in 180 DEG C of secondary 50s ~ 60s that bake.
Comparative example 2
The design of silk flosssilk wadding jacquard product is pasture and water, specification 22d/2 × 80s 173 × 195 in the present embodiment;
By below scheme:After fabric is practiced in vain through pre-treatment, DOWN PROOF is applied under the conditions of 110 DEG C using drying machine after machine in weaving Dressing liquid, through 180 DEG C of temperature conditionss calenderings, then is transferred to forming machine and is obtained final product in 180 DEG C of secondary 50s ~ 60s that bake.
Comparative example 3
The design of silk flosssilk wadding jacquard product is pasture and water, specification 22d/2 × 80s 173 × 195 in the present embodiment;
By below scheme:After fabric is practiced in vain through pre-treatment, DOWN PROOF is applied under the conditions of 110 DEG C using drying machine after machine in weaving Dressing liquid, then carries out a low-temperature curing 50s ~ 60s under the conditions of 140 DEG C, is obtained final product through 180 DEG C of temperature conditionss calenderings.
Performance test is tested
Feel is touched using artificial hand and judged, Air permenbility uses the digital air permeation volume gauges of YG461E(Ningbo textile Instrument Factory), reference Standard GB/T/T14272-2011 anti-chiseling down performances are tested, and washing shrinkage is pressed《GB/T8629-2001 washes change in size Rate》Tested.Items the results are shown in Table 1.
Table 1:Embodiment and comparative example properties test result
Explanation:Air permenbility refer in each embodiment and comparative example under identical pressure, fabric basis are passed through in the unit interval The gas volume of area.Ventilative numerical quantity is bigger, and anti-chiseling down effect is poorer.
The above, is only presently preferred embodiments of the present invention, is not the limitation for making other forms to the present invention, is appointed What those skilled in the art changed possibly also with the technology contents of the disclosure above or be modified as equivalent variations etc. Effect embodiment.But it is every without departing from technical solution of the present invention content, according to technical spirit of the invention to above example institute Any simple modification, equivalent variations and the remodeling made, still fall within the protection domain of technical solution of the present invention.

Claims (7)

1. a kind of silk flosssilk wadding intertexture jacquard fabric anti-chiseling down technique, it is characterised in that:Using silk flosssilk wadding fabric, the tissue of silk flosssilk wadding fabric is advised Lattice are:Warp uses 80s yarn count combed cotton yarns, thread count using 22 Denier, the mulberry silk of the combination of two monofilament, parallel It is 173 × 195;
Apply DOWN PROOF dressing liquid under the conditions of 108 ~ 113 DEG C using drying machine after the upper machine of silk flosssilk wadding fabric weaving, then 137 ~ A low-temperature curing 50s ~ 60s is carried out under the conditions of 142 DEG C, through 178 ~ 183 DEG C of temperature conditionss calenderings, then be transferred to forming machine 178 ~ 183 DEG C of secondary 50s ~ 60s that bake are obtained final product.
2. a kind of silk flosssilk wadding intertexture jacquard fabric anti-chiseling down technique according to claim 1, it is characterised in that:Described silk The warp of cotton grey cloth is mulberry silk, and parallel is combed cotton yarn.
3. a kind of silk flosssilk wadding intertexture jacquard fabric anti-chiseling down technique according to claim 1, it is characterised in that:Described anti-plumage Suede dressing liquid is castor oil-base aqueous polyurethane and acrylic acid acrylamide in mass ratio 5 ~ 7:1 compound.
4. a kind of silk flosssilk wadding intertexture jacquard fabric anti-chiseling down technique according to claim 1, it is characterised in that:It is described once The baking temperature of low-temperature curing is 140 DEG C.
5. a kind of silk flosssilk wadding intertexture jacquard fabric anti-chiseling down technique according to claim 1, it is characterised in that:Described calendering Temperature be 180 DEG C.
6. a kind of silk flosssilk wadding intertexture jacquard fabric anti-chiseling down technique according to claim 1, it is characterised in that:Described is secondary The temperature for baking is 180 DEG C.
7. a kind of silk flosssilk wadding intertexture jacquard fabric anti-chiseling down technique according to claim 1, it is characterised in that:Described applying The temperature of DOWN PROOF dressing liquid is 110 DEG C.
CN201611096619.2A 2016-12-02 2016-12-02 A kind of silk flosssilk wadding intertexture jacquard fabric anti-chiseling down technique Pending CN106757666A (en)