CN106751552A - A kind of strength modified heat-shrinkable film of anti-puncture high with double-decker and preparation method thereof - Google Patents
A kind of strength modified heat-shrinkable film of anti-puncture high with double-decker and preparation method thereof Download PDFInfo
- Publication number
- CN106751552A CN106751552A CN201610986960.9A CN201610986960A CN106751552A CN 106751552 A CN106751552 A CN 106751552A CN 201610986960 A CN201610986960 A CN 201610986960A CN 106751552 A CN106751552 A CN 106751552A
- Authority
- CN
- China
- Prior art keywords
- double
- shrinkable film
- melt
- modified heat
- antioxidant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of strength modified heat-shrinkable film of anti-puncture high with double-decker and preparation method thereof;The strength modified heat-shrinkable film of anti-puncture high uses double-layer structural:Internal layer and outer layer;Outer layer is made up of following raw material:Polyethylene terephthalate polymer, polyvinyl chloride, inorganic filler stone flour, Its Compatibilizing Technology, non-toxic organic tin stabilizer;Internal layer is made up of following raw material:EVAc, glass powder, antioxidant, plasticizer.Film of the invention is a kind of anti-puncture intensity high, the heat shrink films of the splendid way contracting of transparency, have the advantages that the high grade of transparency and contractile function are strong simultaneously, steadiness is good in packaging process, reduce the breakage in transportation, collapse, the phenomenon such as Bales Off, most of self-action, the requirement of auto-manual system package packing machine are adapted to, foreign export, papermaking, hardware, plastics chemical industry, building materials, food pharmaceuticals industry is can be widely used in.
Description
Technical field
The invention belongs to heat shrink wrap material field, and in particular to a kind of anti-puncture intensity high with double-decker changes
Thermal shrinkage film and preparation method thereof.
Background technology
Heat-shrinkable film is a kind of new heat shrink wrap material;This material can not only reduce packaging production cost, fortune
Defeated cost, reduction packaging volume, also because of the shelf life that it has transparency higher, good printing performance, increases product, competition
Consumer's sight can be rapidly caught in fierce market, cater to consumer demand.Thus obtained extensively in European and American developed countries
Pay attention to and apply.Heat-shrinkable film is widely used in food, medicine, sterilizing dinnerware, stationery sports goods, process gift, printed matter, five
The external packing of golden plastic products, telephone set, electronic apparatus etc. various products, especially in anomalistic object article or commodity
Combined type (boundling) packaging aspect, can meet commodity it is moistureproof dust-proof, touch-proof substitute for another surreptitiously, the function such as transparent display, and can increase
Plus product appearance attraction, it can also be used to instead of all kinds of cartons, packing cost is not only saved, and meet packaging trend.Shrink
Film (bag) can be processed into:The abnormity sack such as flat mouth bag, circular arc bag, trapezoidal bag, stereoscopic bag.More shrink film is used at present
It is PVC, PE, PP, next has PVDC, PET, EVA, chlorinated rubber etc..
Multi-layer co-extruded shrink film is the two-way drawing of a kind of new high shrinkage developed on the basis of POF shrink films in recent years
Shrink film is stretched, it can make the physical and mechanical properties of product change.Matched somebody with somebody by different in multi-layer co-extruded shrink film production
Side's design and degree of cross linking control can be obtained the product of different performance requirement, be adapted to different packaging facilities and product.This hair
Bright to have good stability there is provided one kind, equilibrium is shunk, and the anti-puncture intensity high of the double-decker such as good percentage elongation, transparency be high changes
Thermal shrinkage film and preparation method thereof.
The content of the invention
It is strength modified that 1st technical problem to be solved by this invention is to provide a kind of anti-puncture high with double-decker
Heat-shrinkable film.
2nd technical problem to be solved by this invention is the preparation method of above-mentioned modified heat-shrinkable film.
The problem that the present invention is solved is a kind of strength modified heat-shrinkable film of anti-puncture high with double-decker, the film
Using double-layer structural:Internal layer and outer layer;Outer layer is made up of the raw material of following parts by weight meter:PET is polymerized
Thing 75-85, polyvinyl chloride 10-18, inorganic filler stone flour 2-4, Its Compatibilizing Technology 2-4, non-toxic organic tin stabilizer 0.2-1;
Internal layer is made up of the raw material of following parts by weight meter:Vinyl-vinyl acetate copolymer 80-90, glass powder 5-12, antioxidant 5-
8th, plasticizer 0.2-1.
The specifications and models of the glass powder are E (C) MG-250C.
The inorganic filler stone flour is the one kind in active calcium carbonate powder, talcum powder or blanc fixe.
The Its Compatibilizing Technology is modified polyacrylate or m- isopropenyl -2,2- dimethyl benzoyl isocyanates.
The non-toxic organic tin stabilizer is in thiol methyl tin ST-181, organotin ST-182, organotin ST-189
It is a kind of.
The plasticizer is dibutyl phthalate or dioctyl phthalate.
The antioxidant is selected from antioxidant 1010, antioxidant 1076, irgasfos 168, antioxidant 264, antioxidant 1099
One kind.
The preparation method of above-mentioned modified heat-shrinkable film, comprises the following steps:
A) dried process:By polyethylene terephthalate polymer, polyvinyl chloride, vinyl-vinyl acetate copolymer
4-5h is dried with 100-120 DEG C of temperature by fluid bed and obtains dry feedstock;
B) melting extrusion:By inorganic filler stone flour, Its Compatibilizing Technology, non-toxic organic tin stabilizer and by step a)
Polyethylene terephthalate polymer, the polyvinyl chloride of dried process are heated to molten in being added to main extruder in proportion
State, through being filtrated to get as the main frame melt of outer layer;Be proportionally added into subsidiary extruder glass powder, plasticizer, antioxidant and
By the vinyl-vinyl acetate copolymer of dried process in step a), obtained as interior by after melting, vacuumize process
The auxiliary crowded melt of layer;Main crowded melt and auxiliary crowded melt converge extrusion in double-deck die head;Wherein main extruder melt temperature is
250-260 DEG C, subsidiary extruder melt temperature is 200-220 DEG C, converges extrusion temperature for 220-240 DEG C;
C) it is cast slab:The blend melt of melting extrusion enters rack-style by melt metering pump, filter, melt pipe
It is cast to after die head on cooler drum and forms slab;Wherein, the cooling water temperature of cooler drum is controlled at 20-30 DEG C;
D) simple tension:The slab that will be obtained via step c) carries out cross directional stretch while hot by being reheated after preheating
With the treatment of longitudinal stretching multiple;Wherein, the preheating temperature of stretching is 90-100 DEG C, and the time is 15-30min, and draft temperature is
105-115 DEG C, draw ratio is 3-4 times;
E) wind, cut:By the film of simple tension by thickness measuring, traction winding, cutting obtains the heat of double-layer structural
Shrinkable film finished product.
Beneficial effects of the present invention:The strength modified heat-shrinkable film of anti-puncture high of double-decker of the invention has following
Advantage:
1st, excellent self-adhesive energy;
2nd, good pliability and draftability, looping ability are strong;
3rd, anti-puncture intensity high;
4th, the high grade of transparency and glossiness;
5th, contractile function is strong, and retraction tightness is good;
6th, wrapping material part entirety steadiness is good, reduce the breakage in transportation, collapse, the phenomenon such as Bales Off.
Specific embodiment
Specific embodiment of the invention is illustrated below.It should be appreciated that specific implementation described herein
Mode is merely to illustrate and explain the present invention, and is not intended to limit the invention.In embodiment, PET polymerization
Thing, polyvinyl chloride, vinyl-vinyl acetate copolymer, glass powder, antioxidant 1010,1076, talcum powder, blanc fixe, adjacent benzene
Dibutyl carboxylic acid, dioctyl phthalate are Gaede chemical industry net commercially available product;Thiol methyl tin ST-181, organotin ST-182
It is Sheng Teng macromolecular materials Co., Ltd of Foshan City commercially available product.
Embodiment 1
A kind of strength modified heat-shrinkable film of anti-puncture high with double-decker, the film uses double-layer structural:Internal layer
And outer layer;Outer layer is made up of the raw material of following parts by weight meter:Polyethylene terephthalate polymer 82, polyvinyl chloride 12,
Talcum powder 3, modified polyacrylate 2.5, thiol methyl tin ST-181 0.5;Internal layer by following parts by weight meter raw material group
Into:Vinyl-vinyl acetate copolymer 83, glass powder 10, antioxidant 1010 6.5, dibutyl phthalate 0.5.
The preparation method of above-mentioned modified heat-shrinkable film, comprises the following steps:
A) dried process:By polyethylene terephthalate polymer, polyvinyl chloride, vinyl-vinyl acetate copolymer
4h is dried with 110 DEG C of temperature by fluid bed and obtains dry feedstock;
B) melting extrusion:By inorganic filler stone flour, Its Compatibilizing Technology, non-toxic organic tin stabilizer and by step a)
Polyethylene terephthalate polymer, the polyvinyl chloride of dried process are heated to molten in being added to main extruder in proportion
State, through being filtrated to get as the main frame melt of outer layer;Be proportionally added into subsidiary extruder glass powder, plasticizer, antioxidant and
By the vinyl-vinyl acetate copolymer of dried process in step a), obtained as interior by after melting, vacuumize process
The auxiliary crowded melt of layer;Main crowded melt and auxiliary crowded melt converge extrusion in double-deck die head;Wherein main extruder melt temperature is 250
DEG C, subsidiary extruder melt temperature is 210 DEG C, converges extrusion temperature for 230 DEG C;
C) it is cast slab:The blend melt of melting extrusion enters rack-style by melt metering pump, filter, melt pipe
It is cast to after die head on cooler drum and forms slab;Wherein, the cooling water temperature of cooler drum is controlled at 28 DEG C;
D) simple tension:The slab that will be obtained via step c) carries out cross directional stretch while hot by being reheated after preheating
With the treatment of longitudinal stretching multiple;Wherein, the preheating temperature of stretching is 95 DEG C, and the time is 25min, and draft temperature is 110 DEG C, stretching
Multiple is 3 times;
E) wind, cut:By the film of simple tension by thickness measuring, traction winding, cutting obtains the heat of double-layer structural
Shrinkable film finished product.
Embodiment 2
A kind of strength modified heat-shrinkable film of anti-puncture high with double-decker, the film uses double-layer structural:Internal layer
And outer layer;Outer layer is made up of the raw material of following parts by weight meter:Polyethylene terephthalate polymer 80, polyvinyl chloride 13,
Blanc fixe 2, modified polyacrylate 4, organotin ST-182 1;Internal layer is made up of the raw material of following parts by weight meter:Ethene-
Vinyl acetate copolymer 82, glass powder 10, antioxidant 1076 7, dioctyl phthalate 1.
The preparation method of above-mentioned modified heat-shrinkable film, comprises the following steps:
A) dried process:By polyethylene terephthalate polymer, polyvinyl chloride, vinyl-vinyl acetate copolymer
5h is dried with 120 DEG C of temperature by fluid bed and obtains dry feedstock;
B) melting extrusion:By inorganic filler stone flour, Its Compatibilizing Technology, non-toxic organic tin stabilizer and by step a)
Polyethylene terephthalate polymer, the polyvinyl chloride of dried process are heated to molten in being added to main extruder in proportion
State, through being filtrated to get as the main frame melt of outer layer;Be proportionally added into subsidiary extruder glass powder, plasticizer, antioxidant and
By the vinyl-vinyl acetate copolymer of dried process in step a), obtained as interior by after melting, vacuumize process
The auxiliary crowded melt of layer;Main crowded melt and auxiliary crowded melt converge extrusion in double-deck die head;Wherein main extruder melt temperature is 260
DEG C, subsidiary extruder melt temperature is 220 DEG C, converges extrusion temperature for 240 DEG C;
C) it is cast slab:The blend melt of melting extrusion enters rack-style by melt metering pump, filter, melt pipe
It is cast to after die head on cooler drum and forms slab;Wherein, the cooling water temperature of cooler drum is controlled at 30 DEG C;
D) simple tension:The slab that will be obtained via step c) carries out cross directional stretch while hot by being reheated after preheating
With the treatment of longitudinal stretching multiple;Wherein, the preheating temperature of stretching is 100 DEG C, and the time is 30min, and draft temperature is 115 DEG C, is drawn
Multiple is stretched for 4 times;
E) wind, cut:By the film of simple tension by thickness measuring, traction winding, cutting obtains the heat of double-layer structural
Shrinkable film finished product.
The technical parameter of the strength modified heat-shrinkable film of anti-puncture high of the double-decker prepared using the present invention is as follows:
Claims (8)
1. a kind of strength modified heat-shrinkable film of anti-puncture high with double-decker, it is characterised in that the film is using double-deck
Construction:Internal layer and outer layer;Outer layer is made up of the raw material of following parts by weight meter:Polyethylene terephthalate polymer 75-85,
Polyvinyl chloride 10-18, inorganic filler stone flour 2-4, Its Compatibilizing Technology 2-4, non-toxic organic tin stabilizer 0.2-1;Internal layer by with
The raw material composition of lower parts by weight meter:Vinyl-vinyl acetate copolymer 80-90, glass powder 5-12, antioxidant 5-8, plasticizer
0.2-1。
2. a kind of strength modified heat-shrinkable film of anti-puncture high with double-decker according to claim 1, its feature
It is:The specifications and models of the glass powder are E (C) MG-250C.
3. a kind of strength modified heat-shrinkable film of anti-puncture high with double-decker according to claim 1, its feature
It is:The inorganic filler stone flour is the one kind in active calcium carbonate powder, talcum powder or blanc fixe.
4. a kind of strength modified heat-shrinkable film of anti-puncture high with double-decker according to claim 1, its feature
It is:The Its Compatibilizing Technology is modified polyacrylate or m- isopropenyl -2,2- dimethyl benzoyl isocyanates.
5. a kind of strength modified heat-shrinkable film of anti-puncture high with double-decker according to claim 1, its feature
It is:The non-toxic organic tin stabilizer is in thiol methyl tin ST-181, organotin ST-182, organotin ST-189
Kind.
6. a kind of strength modified heat-shrinkable film of anti-puncture high with double-decker according to claim 1, its feature
It is:The plasticizer is dibutyl phthalate or dioctyl phthalate.
7. a kind of strength modified heat-shrinkable film of anti-puncture high with double-decker according to claim 1, its feature
It is:The antioxidant is selected from antioxidant 1010, antioxidant 1076, irgasfos 168, antioxidant 264, antioxidant 1099
Kind.
8. a kind of strength modified heat-shrinkable film of anti-puncture high with double-decker described in claim 1-7 any one
Preparation method, it is characterised in that comprise the following steps:
A) dried process:Polyethylene terephthalate polymer, polyvinyl chloride, vinyl-vinyl acetate copolymer are passed through
Fluid bed dries 4-5h and obtains dry feedstock with 100-120 DEG C of temperature;
B) melting extrusion:By inorganic filler stone flour, Its Compatibilizing Technology, non-toxic organic tin stabilizer and by step a) dry
Polyethylene terephthalate polymer, the polyvinyl chloride for the treatment of are heated to molten condition in being added to main extruder in proportion,
Through being filtrated to get as the main frame melt of outer layer;Glass powder, plasticizer, antioxidant and process are proportionally added into subsidiary extruder
The vinyl-vinyl acetate copolymer of dried process in step a), obtains as internal layer by after melting, vacuumize process
Auxiliary crowded melt;Main crowded melt and auxiliary crowded melt converge extrusion in double-deck die head;Wherein main extruder melt temperature is 250-260
DEG C, subsidiary extruder melt temperature is 200-220 DEG C, converges extrusion temperature for 220-240 DEG C;
C) it is cast slab:The blend melt of melting extrusion enters hanger-style die by melt metering pump, filter, melt pipe
After be cast on cooler drum and form slab;Wherein, the cooling water temperature of cooler drum is controlled at 20-30 DEG C;
D) simple tension:The slab that will be obtained via step c) carries out cross directional stretch and indulges while hot by being reheated after preheating
Processed to draw ratio;Wherein, the preheating temperature of stretching is 90-100 DEG C, and the time is 15-30min, and draft temperature is 105-115
DEG C, draw ratio is 3-4 times;
E) wind, cut:By the film of simple tension by thickness measuring, traction winding, cutting obtains the thermal contraction of double-layer structural
Finished film.