CN106747659A - A kind of heat-resistant porcelain glaze - Google Patents
A kind of heat-resistant porcelain glaze Download PDFInfo
- Publication number
- CN106747659A CN106747659A CN201510804721.2A CN201510804721A CN106747659A CN 106747659 A CN106747659 A CN 106747659A CN 201510804721 A CN201510804721 A CN 201510804721A CN 106747659 A CN106747659 A CN 106747659A
- Authority
- CN
- China
- Prior art keywords
- parts
- heat
- resistant porcelain
- stone
- raw material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of heat-resistant porcelain glaze, its raw material is grouped into by each group of following weight fraction：57~63 parts of spodumene of calcining, 15~22 parts of quartz, 1~4 part of ripe talcum, Jiangxi black talc washes 4~10 parts of mud, 5~9 parts of Suzhou soil, 0~3 part of barium carbonate, your 0~6 part of stone, 0~2 part of manganese stone；Heat-resistant porcelain glaze product is prepared with heat-resistant porcelain glaze raw material of the present invention, glaze paint is bright and clean smooth, good with base substrate conjugation, not easy to crack, can be used on naked light, 420 DEG C to 20 DEG C heat exchanges of thermal shock resistance are not split once, water absorption rate≤0.8%.
Description
Technical field
The present invention relates to domestic ceramics technical field, more particularly, to a kind of heat-resistant porcelain glaze and preparation method thereof.
Background technology
The firing of crockery and apply and have long history in China, its various shapes, colorful, feel are refrigerant fine and smooth, easily washing, deep to be liked by compatriots.The universal resistance to heat shocks of ceramic product in the market, especially ceramic cooker is not high, when product is heated suddenly（Or catch a cold）Expand（Or shrink）When, thermal stress is produced because each several part deformation is restricted mutually, when thermal stress exceedes product internal bond strength, product glaze layer can be produced splits or peels off, and causes product rejection to reuse.
The content of the invention
It is an object of the invention to overcome the shortcomings of raw material in existing Production of Ceramics, there is provided a kind of heat-resistant porcelain glaze and preparation method thereof.
The object of the invention is achieved by the following technical programs：
A kind of heat-resistant porcelain glaze is provided, its raw material weight percentage composition：57~63 parts of spodumene of calcining, 15~22 parts of quartz, 1~4 part of ripe talcum, Jiangxi black talc washes 4~10 parts of mud, 5~9 parts of Suzhou soil, 0~3 part of barium carbonate, your 0~6 part of stone, 0~2 part of manganese stone.
Its raw material weight percentage is constituted：60 parts of spodumene of calcining, 20 parts of quartz, 2 parts of ripe talcum, Jiangxi black talc washes 8 parts of mud, 8 parts of Suzhou soil, 2 parts of barium carbonate, your 0.3 part of stone, 0.5 part of manganese stone.
The preparation method of heat-resistant porcelain glaze, comprises the following steps：
Household china raw material is taken by weight ratio, with ball：Water：Material=2：0.8：1 ratio enters ball milling, and fineness mores than 0.03~0.05% for 10000-hole sieve, and on the basis of gross mass, addition mass percent is 3~9% cobalt black toners, and 6~9% zirconium silicates, fineness tails over 0.5~0.7%, obtains glaze slip for 400 mesh sieves.
The glaze slip that will be obtained glazing on biscuit, enters kiln oxidation and fires, and obtains finished product.
Compared with prior art, the invention has the advantages that：The product glaze paint for burning out is bright and clean smooth, good with base substrate conjugation, not easy to crack, can be used on naked light, and 420 DEG C to 20 DEG C heat exchanges of thermal shock resistance are not split once, water absorption rate≤0.8%.
Specific embodiment
With reference to specific embodiment, the present invention is further illustrated.
Embodiment 1
Present embodiment discloses a kind of heat-resistant porcelain glaze, its raw material weight percentage composition：60 parts of spodumene of calcining, 20 parts of quartz, 2 parts of ripe talcum, Jiangxi black talc washes 8 parts of mud, 8 parts of Suzhou soil, 2 parts of barium carbonate, your 0.3 part of stone, 0.5 part of manganese stone.
The preparation method of the heat-resistant porcelain glaze, comprises the following steps：
Household china raw material is taken by weight ratio, with ball：Water：Material=2：0.8：1 ratio enters ball milling, and fineness mores than 0.04% for 10000-hole sieve, and on the basis of gross mass, addition mass percent is 6% cobalt black toner, and 8% zirconium silicate, fineness tails over 0.6%, obtains glaze slip for 400 mesh sieves.
Embodiment 2
Present embodiment discloses a kind of heat-resistant porcelain glaze, its raw material weight percentage composition：57 parts of spodumene of calcining, 15 parts of quartz, 1 part of ripe talcum, Jiangxi black talc washes 4 parts of mud, 5 parts of Suzhou soil, 1 part of barium carbonate, your 2 parts of stone, 1 part of manganese stone.
The preparation method of the heat-resistant porcelain glaze, comprises the following steps：
Household china raw material is taken by weight ratio, with ball：Water：Material=2：0.8：1 ratio enters ball milling, and fineness mores than 0.03% for 10000-hole sieve, and on the basis of gross mass, addition mass percent is 3% cobalt black toner, and 6% zirconium silicate, fineness tails over 0.5%, obtains glaze slip for 400 mesh sieves.
Embodiment 3
Present embodiment discloses a kind of heat-resistant porcelain glaze, its raw material weight percentage composition：63 parts of spodumene of calcining, 22 parts of quartz, 4 parts of ripe talcum, Jiangxi black talc washes 10 parts of mud, 9 parts of Suzhou soil, 3 parts of barium carbonate, your 6 parts of stone, 2 parts of manganese stone.
The preparation method of the heat-resistant porcelain glaze, comprises the following steps：
Household china raw material is taken by weight ratio, with ball：Water：Material=2：0.8：1 ratio enters ball milling, and fineness mores than 0.05% for 10000-hole sieve, and on the basis of gross mass, addition mass percent is 9% cobalt black toner, and 9% zirconium silicate, fineness tails over 0.7%, obtains glaze slip for 400 mesh sieves.
Embodiment 4
Present embodiment discloses a kind of heat-resistant porcelain glaze, its raw material weight percentage composition：62 parts of spodumene of calcining, 18 parts of quartz, 2 parts of ripe talcum, Jiangxi black talc washes 8 parts of mud, 7 parts of Suzhou soil.
The preparation method of the heat-resistant porcelain glaze, comprises the following steps：
Household china raw material is taken by weight ratio, with ball：Water：Material=2：0.8：1 ratio enters ball milling, and fineness mores than 0.04% for 10000-hole sieve, and on the basis of gross mass, addition mass percent is 5% cobalt black toner, and 7% zirconium silicate, fineness is 400 mesh screen residues 0.6%, obtains glaze slip.
Embodiment 5
Present embodiment discloses a kind of heat-resistant porcelain glaze, its raw material weight percentage composition：61 parts of spodumene of calcining, 21 parts of quartz, 3 parts of ripe talcum, Jiangxi black talc washes 6 parts of mud, 8 parts of Suzhou soil, your 5 parts of stone, 1 part of manganese stone.
The preparation method of the heat-resistant porcelain glaze, comprises the following steps：
Household china raw material is taken by weight ratio, with ball：Water：Material=2：0.8：1 ratio enters ball milling, and fineness mores than 0.04% for 10000-hole sieve, and on the basis of gross mass, addition mass percent is 4% cobalt black toner, and 8% zirconium silicate, fineness tails over 0.7%, obtains glaze slip for 400 mesh sieves.
Embodiment 6
Present embodiment discloses a kind of heat-resistant porcelain glaze, its raw material weight percentage composition：58 parts of spodumene of calcining, 21 parts of quartz, 2 parts of ripe talcum, Jiangxi black talc washes 5 parts of mud, 6 parts of Suzhou soil, 2 parts of barium carbonate, your 3 parts of stone, 0.8 part of manganese stone.
The preparation method of the heat-resistant porcelain glaze, comprises the following steps：
Household china raw material is taken by weight ratio, with ball：Water：Material=2：0.8：1 ratio enters ball milling, and fineness mores than 0.05% for 10000-hole sieve, and on the basis of gross mass, addition mass percent is 8% cobalt black toner, and 9% zirconium silicate, fineness tails over 0.6%, obtains glaze slip for 400 mesh sieves.
Claims (3)
1. a kind of heat-resistant porcelain glaze, it is characterised in that its raw material weight percentage is constituted：57~63 parts of spodumene of calcining, 15~22 parts of quartz, 1~4 part of ripe talcum, Jiangxi black talc washes 4~10 parts of mud, 5~9 parts of Suzhou soil, 0~3 part of barium carbonate, your 0~6 part of stone, 0~2 part of manganese stone.
2. heat-resistant porcelain glaze according to claim 1, it is characterised in that its raw material weight percentage is constituted：60 parts of spodumene of calcining, 20 parts of quartz, 2 parts of ripe talcum, Jiangxi black talc washes 8 parts of mud, 8 parts of Suzhou soil, 2 parts of barium carbonate, your 0.3 part of stone, 0.5 part of manganese stone.
3. the preparation method of heat-resistant porcelain glaze described in claim 1 or 2, it is characterised in that comprise the following steps：Household china raw material is taken by weight ratio, with ball：Water：Material=2：0.8：1 ratio enters ball milling, and fineness mores than 0.03~0.05% for 10000-hole sieve, and on the basis of gross mass, addition mass percent is 3~9% cobalt black toners, and 6~9% zirconium silicates, fineness tails over 0.5~0.7%, obtains glaze slip for 400 mesh sieves.