CN106701245A - 一种应用于新能源方面的秸秆生物质燃烧棒及其制备方法 - Google Patents

一种应用于新能源方面的秸秆生物质燃烧棒及其制备方法 Download PDF

Info

Publication number
CN106701245A
CN106701245A CN201710096056.5A CN201710096056A CN106701245A CN 106701245 A CN106701245 A CN 106701245A CN 201710096056 A CN201710096056 A CN 201710096056A CN 106701245 A CN106701245 A CN 106701245A
Authority
CN
China
Prior art keywords
parts
straw
rod
terms
new energy
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710096056.5A
Other languages
English (en)
Inventor
董地
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201710096056.5A priority Critical patent/CN106701245A/zh
Publication of CN106701245A publication Critical patent/CN106701245A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种应用于新能源方面的秸秆生物质燃烧棒，包括以下重量份的原料：麦秆40‑60份、稻壳20‑40份、烟草废弃物10‑30份、石蜡2‑8份、煤粉20‑30份、树叶10‑30份、污泥5‑15份、酵母1‑3份、竹屑1‑5份、三氧化二铁4‑10份；本发明还提出了一种应用于新能源方面的秸秆生物质燃烧棒的制备方法，包括以下步骤：S1，将麦秆通过打磨机粉碎为2‑4mm的碎料，并与竹屑混合，放入烘干炉，50‑70℃的条件下烘干3‑6h，得到混合物A；S2，将稻壳与烟草废弃物混合均匀，粉碎至1‑3mm，在60‑80℃的条件下烘干1‑3h，得到混合物B。本发明制备方法简单，制备的燃烧棒燃烧充分，可以有效缓解环境污染问题，发热值大，适合推广。

Description

一种应用于新能源方面的秸秆生物质燃烧棒及其制备方法
技术领域
本发明涉及燃烧棒技术领域，尤其涉及一种应用于新能源方面的秸秆生物质燃烧棒及其制备方法。
背景技术
生物质燃料是指将生物质材料燃烧作为燃料，一般主要是农林废弃物（如秸秆、锯末、甘蔗渣、稻糠等）。主要区别于化石燃料。在目前的国家政策和环保标准中，直接燃烧生物质属于高污染燃料，只在农村的大灶中使用，不允许在城市中使用。生物质燃料的应用，实际主要是生物质成型燃料，是将农林废物作为原材料，经过粉碎、混合、挤压、烘干等工艺，制成各种成型（如块状、颗粒状等）的，可直接燃烧的一种新型清洁燃料。目前秸秆生物质燃烧棒的发热值小，不易燃、燃烧不透彻，不利于大范围推广。
发明内容
基于背景技术存在的技术问题，本发明提出了一种应用于新能源方面的秸秆生物质燃烧棒及其制备方法。
本发明提出的一种应用于新能源方面的秸秆生物质燃烧棒，包括以下重量份的原料：麦秆40-60份、稻壳20-40份、烟草废弃物10-30份、石蜡2-8份、煤粉20-30份、树叶10-30份、污泥5-15份、酵母1-3份、竹屑1-5份、三氧化二铁4-10份。
优选地，包括以下重量份的原料：麦秆45-55份、稻壳25-35份、烟草废弃物15-25份、石蜡3-7份、煤粉22-28份、树叶15-25份、污泥7-13份、酵母1.5-2.5份、竹屑2-4份、三氧化二铁6-8份。
优选地，包括以下重量份的原料：麦秆50份、稻壳30份、烟草废弃物20份、石蜡5份、煤粉25份、树叶20份、污泥10份、酵母2份、竹屑3份、三氧化二铁7份。
优选地，所述麦秆、稻壳、烟草废弃物的重量比为45-55：25-35：15-25。
优选地，所述石蜡、煤粉、树叶的重量比为3-7：22-28：15-25。
优选地，所述污泥、酵母、竹屑的重量比为7-13：1.5-2.5：2-4。
本发明还提出了一种应用于新能源方面的秸秆生物质燃烧棒的制备方法，包括以下步骤：
S1，将麦秆通过打磨机粉碎为2-4mm的碎料，并与竹屑混合，放入烘干炉，50-70℃的条件下烘干3-6h，得到混合物A；
S2，将稻壳与烟草废弃物混合均匀，粉碎至1-3mm，在60-80℃的条件下烘干1-3h，得到混合物B；
S3，将混合物A与混合物B混合在一起，加入石蜡、煤粉、树叶、污泥、酵母和三氧化二铁，搅拌20-40min后，静置24-48h，转至压棒机中，用压棒机挤压成燃烧棒，取出后干燥至含水量为5-15％即可。
优选地，所述S2中，将稻壳与烟草废弃物混合均匀，粉碎至2mm，在70℃的条件下烘干2h，得到混合物B。
本发明中，将各原料进行粉碎，再进行后续处理，有助于最终产品的充分燃烧，三氧化二铁有效减少了二氧化硫的排放，将烟草废弃物当做原料，可以充分缓解废物的排放，酵母可以对混合的物料进行发酵，实现各原料的融合，保证燃烧充分，本发明制备方法简单，将各原料粉碎后以一定的顺序混合并烘干，经过酵母发酵后可以促进物质的分解，有利于燃烧棒的制备和使用，制备的燃烧棒燃烧充分，可以有效缓解环境污染问题，发热值大，适合推广。
具体实施方式
下面结合具体实施例对本发明作进一步解说。
实施例一
本发明提出的一种应用于新能源方面的秸秆生物质燃烧棒，包括以下重量份的原料：麦秆40份、稻壳20份、烟草废弃物10份、石蜡2份、煤粉20份、树叶10份、污泥5份、酵母1份、竹屑1份、三氧化二铁4份。
其制备方法包括以下步骤：
S1，将麦秆通过打磨机粉碎为2mm的碎料，并与竹屑混合，放入烘干炉，50℃的条件下烘干3h，得到混合物A；
S2，将稻壳与烟草废弃物混合均匀，粉碎至1mm，在60℃的条件下烘干1h，得到混合物B；
S3，将混合物A与混合物B混合在一起，加入石蜡、煤粉、树叶、污泥、酵母和三氧化二铁，搅拌20min后，静置24h，转至压棒机中，用压棒机挤压成燃烧棒，取出后干燥至含水量为5-15％即可。
实施例二
本发明提出的一种应用于新能源方面的秸秆生物质燃烧棒，包括以下重量份的原料：麦秆45份、稻壳25份、烟草废弃物15份、石蜡3份、煤粉22份、树叶15份、污泥7份、酵母1.5份、竹屑2份、三氧化二铁6份。
其制备方法包括以下步骤：
S1，将麦秆通过打磨机粉碎为2.5mm的碎料，并与竹屑混合，放入烘干炉，55℃的条件下烘干3.5h，得到混合物A；
S2，将稻壳与烟草废弃物混合均匀，粉碎至1.5mm，在65℃的条件下烘干1.5h，得到混合物B；
S3，将混合物A与混合物B混合在一起，加入石蜡、煤粉、树叶、污泥、酵母和三氧化二铁，搅拌25min后，静置28h，转至压棒机中，用压棒机挤压成燃烧棒，取出后干燥至含水量为5-15％即可。
实施例三
本发明提出的一种应用于新能源方面的秸秆生物质燃烧棒，包括以下重量份的原料：麦秆50份、稻壳30份、烟草废弃物20份、石蜡5份、煤粉25份、树叶20份、污泥10份、酵母2份、竹屑3份、三氧化二铁7份。
其制备方法包括以下步骤：
S1，将麦秆通过打磨机粉碎为3mm的碎料，并与竹屑混合，放入烘干炉，60℃的条件下烘干4h，得到混合物A；
S2，将稻壳与烟草废弃物混合均匀，粉碎至1-3mm，在70℃的条件下烘干2h，得到混合物B；
S3，将混合物A与混合物B混合在一起，加入石蜡、煤粉、树叶、污泥、酵母和三氧化二铁，搅拌30min后，静置36h，转至压棒机中，用压棒机挤压成燃烧棒，取出后干燥至含水量为5-15％即可。
实施例四
本发明提出的一种应用于新能源方面的秸秆生物质燃烧棒，包括以下重量份的原料：麦秆55份、稻壳35份、烟草废弃物25份、石蜡7份、煤粉28份、树叶25份、污泥13份、酵母2.5份、竹屑4份、三氧化二铁8份。
其制备方法包括以下步骤：
S1，将麦秆通过打磨机粉碎为3.5mm的碎料，并与竹屑混合，放入烘干炉，65℃的条件下烘干5h，得到混合物A；
S2，将稻壳与烟草废弃物混合均匀，粉碎至2.5mm，在75℃的条件下烘干2.5h，得到混合物B；
S3，将混合物A与混合物B混合在一起，加入石蜡、煤粉、树叶、污泥、酵母和三氧化二铁，搅拌35min后，静置42h，转至压棒机中，用压棒机挤压成燃烧棒，取出后干燥至含水量为5-15％即可。
实施例五
本发明提出的一种应用于新能源方面的秸秆生物质燃烧棒，包括以下重量份的原料：麦秆60份、稻壳40份、烟草废弃物30份、石蜡8份、煤粉30份、树叶30份、污泥15份、酵母3份、竹屑5份、三氧化二铁10份。
其制备方法包括以下步骤：
S1，将麦秆通过打磨机粉碎为4mm的碎料，并与竹屑混合，放入烘干炉，70℃的条件下烘干6h，得到混合物A；
S2，将稻壳与烟草废弃物混合均匀，粉碎至3mm，在80℃的条件下烘干3h，得到混合物B；
S3，将混合物A与混合物B混合在一起，加入石蜡、煤粉、树叶、污泥、酵母和三氧化二铁，搅拌40min后，静置48h，转至压棒机中，用压棒机挤压成燃烧棒，取出后干燥至含水量为5-15％即可。
检测本发明中实施例1-5中制备的燃烧棒的燃料热值，结果如下表：
实施例一 实施例二 实施例三 实施例四 实施例五
燃料热值 3270kj/kg 3340kj/kg 3380kj/kg 3310kj/kg 3280kj/kg
由上表可知，本发明的燃烧棒发热值高，适合推广。
以上所述，仅为本发明较佳的具体实施方式，但本发明的保护范围并不局限于此，任何熟悉本技术领域的技术人员在本发明揭露的技术范围内，根据本发明的技术方案及其发明构思加以等同替换或改变，都应涵盖在本发明的保护范围之内。

Claims (8)

1.一种应用于新能源方面的秸秆生物质燃烧棒，其特征在于，包括以下重量份的原料：麦秆40-60份、稻壳20-40份、烟草废弃物10-30份、石蜡2-8份、煤粉20-30份、树叶10-30份、污泥5-15份、酵母1-3份、竹屑1-5份、三氧化二铁4-10份。
2.根据权利要求1所述的一种应用于新能源方面的秸秆生物质燃烧棒，其特征在于，包括以下重量份的原料：麦秆45-55份、稻壳25-35份、烟草废弃物15-25份、石蜡3-7份、煤粉22-28份、树叶15-25份、污泥7-13份、酵母1.5-2.5份、竹屑2-4份、三氧化二铁6-8份。
3.根据权利要求1所述的一种应用于新能源方面的秸秆生物质燃烧棒，其特征在于，包括以下重量份的原料：麦秆50份、稻壳30份、烟草废弃物20份、石蜡5份、煤粉25份、树叶20份、污泥10份、酵母2份、竹屑3份、三氧化二铁7份。
4.根据权利要求1所述的一种应用于新能源方面的秸秆生物质燃烧棒，其特征在于，所述麦秆、稻壳、烟草废弃物的重量比为45-55：25-35：15-25。
5.根据权利要求1所述的一种应用于新能源方面的秸秆生物质燃烧棒，其特征在于，所述石蜡、煤粉、树叶的重量比为3-7：22-28：15-25。
6.根据权利要求1所述的一种应用于新能源方面的秸秆生物质燃烧棒，其特征在于，所述污泥、酵母、竹屑的重量比为7-13：1.5-2.5：2-4。
7.一种应用于新能源方面的秸秆生物质燃烧棒的制备方法，其特征在于，包括以下步骤：
S1，将麦秆通过打磨机粉碎为2-4mm的碎料，并与竹屑混合，放入烘干炉，50-70℃的条件下烘干3-6h，得到混合物A；
S2，将稻壳与烟草废弃物混合均匀，粉碎至1-3mm，在60-80℃的条件下烘干1-3h，得到混合物B；
S3，将混合物A与混合物B混合在一起，加入石蜡、煤粉、树叶、污泥、酵母和三氧化二铁，搅拌20-40min后，静置24-48h，转至压棒机中，用压棒机挤压成燃烧棒，取出后干燥至含水量为5-15％即可。
8.根据权利要求7所述的一种应用于新能源方面的秸秆生物质燃烧棒的制备方法，其特征在于，所述S2中，将稻壳与烟草废弃物混合均匀，粉碎至2mm，在70℃的条件下烘干2h，得到混合物B。
CN201710096056.5A 2017-02-22 2017-02-22 一种应用于新能源方面的秸秆生物质燃烧棒及其制备方法 Pending CN106701245A (zh)