CN106674827A - 一种多功能电力施工用管材 - Google Patents
一种多功能电力施工用管材 Download PDFInfo
- Publication number
- CN106674827A CN106674827A CN201611164505.7A CN201611164505A CN106674827A CN 106674827 A CN106674827 A CN 106674827A CN 201611164505 A CN201611164505 A CN 201611164505A CN 106674827 A CN106674827 A CN 106674827A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- power construction
- mesh
- resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种多功能电力施工用管材,由以下组分组成:氟橡胶、酮醛树脂、PVC树脂粉、聚酯氨基甲酸酯树脂、聚丙烯树脂、二甲基甲酰胺、聚乙酸乙烯酯乳液、聚甘油蓖麻醇酯、二乙二醇丁醚、聚醋酸乙烯乳液、茶多酚、二溴二甲基乙内酰脲、多菌灵、氰乙基纤维素、双十八烷基二甲基氯化铵、锆酸钠粉末、碳酸锶粉末、硅酸镁粉末、淀粉丙烯酰胺、海藻酸、硫酸铝、腐殖酸钠、磷酸二氢铵、十溴二苯乙烷、六氢化邻苯二甲酸酐、三甘醇二异辛酸酯、磷酸三甲酚酯、木质素磺酸钠、丁烯二酸酐、甲基丙烯酸月桂酯、脂肪酸甘油酯。本发明多种配料相互混合,形成新型的复合增韧增强体系,韧性、刚度、弹性模量性能指标较好,大大提高产品的抗老化性能和使用性能。
Description
技术领域
本发明涉及一种多功能电力施工用管材,属于电力施工技术领域。
背景技术
电力施工安装中,经常需要用到多种管材,以便电线或者其他电力产品利用管材安装,起到保护和美观作用,一般的管材使用,效果不佳,影响其使用寿命,也没有更多的保护功能,有必要采用合适方式改进。
发明内容
本发明的目的在于提供一种多功能电力施工用管材,以便更好地实现多功能电力施工用管材的使用功能,改善产品的韧性、刚度、弹性模量,提高产品的抗老化性能和使用性能,并使得产品具有较好的耐腐蚀、抗菌阻燃效果。
为了实现上述目的,本发明的技术方案如下。
一种多功能电力施工用管材,由以下质量份数的组分组成:氟橡胶24~28份、酮醛树脂22~26份、PVC树脂粉22~26份、聚酯氨基甲酸酯树脂20~24份、聚丙烯树脂22~26份、二甲基甲酰胺22~26份、聚乙酸乙烯酯乳液20~24份、聚甘油蓖麻醇酯22~26份、二乙二醇丁醚22~26份、聚醋酸乙烯乳液20~24份、茶多酚20~24份、二溴二甲基乙内酰脲20~24份、多菌灵22~26份、氰乙基纤维素20~24份、双十八烷基二甲基氯化铵18~22份、锆酸钠粉末22~26份、碳酸锶粉末20~24份、硅酸镁粉末18~22份、淀粉丙烯酰胺20~24份、海藻酸18~22份、硫酸铝18~22份、腐殖酸钠18~22份、磷酸二氢铵16~20份、十溴二苯乙烷12~16份、六氢化邻苯二甲酸酐10~14份、三甘醇二异辛酸酯10~14份、磷酸三甲酚酯10~14份、木质素磺酸钠10~14份、丁烯二酸酐10~14份、甲基丙烯酸月桂酯10~14份、脂肪酸甘油酯10~14份。
进一步地,上述多功能电力施工用管材,由以下质量份数的组分组成:氟橡胶24份、酮醛树脂22份、PVC树脂粉22份、聚酯氨基甲酸酯树脂20份、聚丙烯树脂22份、二甲基甲酰胺22份、聚乙酸乙烯酯乳液20份、聚甘油蓖麻醇酯22份、二乙二醇丁醚22份、聚醋酸乙烯乳液20份、茶多酚20份、二溴二甲基乙内酰脲20份、多菌灵22份、氰乙基纤维素20份、双十八烷基二甲基氯化铵18份、锆酸钠粉末22份、碳酸锶粉末20份、硅酸镁粉末18份、淀粉丙烯酰胺20份、海藻酸18份、硫酸铝18份、腐殖酸钠18份、磷酸二氢铵16份、十溴二苯乙烷12份、六氢化邻苯二甲酸酐10份、三甘醇二异辛酸酯10份、磷酸三甲酚酯10份、木质素磺酸钠10份、丁烯二酸酐10份、甲基丙烯酸月桂酯10份、脂肪酸甘油酯10份。
进一步地,上述多功能电力施工用管材,由以下质量份数的组分组成:氟橡胶26份、酮醛树脂24份、PVC树脂粉24份、聚酯氨基甲酸酯树脂22份、聚丙烯树脂24份、二甲基甲酰胺24份、聚乙酸乙烯酯乳液22份、聚甘油蓖麻醇酯24份、二乙二醇丁醚24份、聚醋酸乙烯乳液22份、茶多酚22份、二溴二甲基乙内酰脲22份、多菌灵24份、氰乙基纤维素22份、双十八烷基二甲基氯化铵20份、锆酸钠粉末24份、碳酸锶粉末22份、硅酸镁粉末20份、淀粉丙烯酰胺22份、海藻酸20份、硫酸铝20份、腐殖酸钠20份、磷酸二氢铵18份、十溴二苯乙烷14份、六氢化邻苯二甲酸酐12份、三甘醇二异辛酸酯12份、磷酸三甲酚酯12份、木质素磺酸钠12份、丁烯二酸酐12份、甲基丙烯酸月桂酯12份、脂肪酸甘油酯12份。
进一步地,上述多功能电力施工用管材,由以下质量份数的组分组成:氟橡胶28份、酮醛树脂26份、PVC树脂粉26份、聚酯氨基甲酸酯树脂24份、聚丙烯树脂26份、二甲基甲酰胺26份、聚乙酸乙烯酯乳液24份、聚甘油蓖麻醇酯26份、二乙二醇丁醚26份、聚醋酸乙烯乳液24份、茶多酚24份、二溴二甲基乙内酰脲24份、多菌灵26份、氰乙基纤维素24份、双十八烷基二甲基氯化铵22份、锆酸钠粉末26份、碳酸锶粉末24份、硅酸镁粉末22份、淀粉丙烯酰胺24份、海藻酸22份、硫酸铝22份、腐殖酸钠22份、磷酸二氢铵20份、十溴二苯乙烷16份、六氢化邻苯二甲酸酐14份、三甘醇二异辛酸酯14份、磷酸三甲酚酯14份、木质素磺酸钠14份、丁烯二酸酐14份、甲基丙烯酸月桂酯14份、脂肪酸甘油酯14份。
进一步地,所述锆酸钠粉末由三种粒径目数的粉体组成,其粒径目数分别为30~50目、50~100目、100~140目,上述三种粉体的混合质量比例为4~12∶4~8∶1。
进一步地,所述硅酸镁粉末由三种粒径目数的粉体组成,其粒径目数分别为30~50目、50~80目、80~100目,上述三种粉体的混合质量比例为7~17∶2~8∶1。
进一步地,所述脂肪酸甘油酯的粘度在25℃为120~160mpa.s。
进一步地,所述硫酸铝由三种粒径目数的粉体组成,其粒径目数分别为20~50目、50~70目、70~120目,上述三种粉体的混合质量比例为2~6∶3~8∶1。
进一步地,所述聚醋酸乙烯乳的粘度在25℃为80~120mpa.s。
进一步地,上述多功能电力施工用管材制备方法步骤如下:
(1)将所述质量份数的氟橡胶、酮醛树脂、PVC树脂粉、聚酯氨基甲酸酯树脂、聚丙烯树脂、二甲基甲酰胺、聚乙酸乙烯酯乳液、聚甘油蓖麻醇酯、二乙二醇丁醚、聚醋酸乙烯乳液、茶多酚、二溴二甲基乙内酰脲、多菌灵、氰乙基纤维素、双十八烷基二甲基氯化铵、锆酸钠粉末、碳酸锶粉末、硅酸镁粉末、淀粉丙烯酰胺、海藻酸、硫酸铝予以混合,超声高速分散,超声波频率为20~40KHz,分散速度5000~5400r/min,分散时间为30~60min;
(2)加入所述质量份数的腐殖酸钠、磷酸二氢铵、十溴二苯乙烷、六氢化邻苯二甲酸酐、三甘醇二异辛酸酯,超声高速分散,超声波频率为20~35KHz,分散速度4800~5200r/min,分散时间为30~50min;
(3)加入所述质量份数的磷酸三甲酚酯、木质素磺酸钠、丁烯二酸酐、甲基丙烯酸月桂酯、脂肪酸甘油酯,超声高速分散,超声波频率为20~30KHz,分散速度4600~4800r/min,分散时间为20~40min;混合均匀后制得初级混合物;再将初级混合物加入到双螺杆挤出机中进行熔融混炼,得到所需混合物原料;
(4)将步骤(3)得到的混合物原料在挤出机中挤出,获得成品,其中,挤出条件为:料筒温度:184±2℃,合流芯温度:176±2℃,机头温度:190±5℃,牵引:0.6~0.9m/min,主机转速:25~30转/分。
该发明的有益效果在于:本发明中的多功能电力施工用管材,由以下组分组成:氟橡胶、酮醛树脂、PVC树脂粉、聚酯氨基甲酸酯树脂、聚丙烯树脂、二甲基甲酰胺、聚乙酸乙烯酯乳液、聚甘油蓖麻醇酯、二乙二醇丁醚、聚醋酸乙烯乳液、茶多酚、二溴二甲基乙内酰脲、多菌灵、氰乙基纤维素、双十八烷基二甲基氯化铵、锆酸钠粉末、碳酸锶粉末、硅酸镁粉末、淀粉丙烯酰胺、海藻酸、硫酸铝、腐殖酸钠、磷酸二氢铵、十溴二苯乙烷、六氢化邻苯二甲酸酐、三甘醇二异辛酸酯、磷酸三甲酚酯、木质素磺酸钠、丁烯二酸酐、甲基丙烯酸月桂酯、脂肪酸甘油酯。本发明多种配料相互混合,形成新型的复合增韧增强体系,韧性、刚度、弹性模量性能指标较好,大大提高产品的抗老化性能和使用性能,具有较好的耐腐蚀、抗菌阻燃效果好,绝缘性能佳,综合性能佳,使用效果好。
具体实施方式
下面结合实施例对本发明的具体实施方式进行描述,以便更好的理解本发明。
实施例1
本实施例中的多功能电力施工用管材,由以下质量份数的组分组成:氟橡胶24份、酮醛树脂22份、PVC树脂粉22份、聚酯氨基甲酸酯树脂20份、聚丙烯树脂22份、二甲基甲酰胺22份、聚乙酸乙烯酯乳液20份、聚甘油蓖麻醇酯22份、二乙二醇丁醚22份、聚醋酸乙烯乳液20份、茶多酚20份、二溴二甲基乙内酰脲20份、多菌灵22份、氰乙基纤维素20份、双十八烷基二甲基氯化铵18份、锆酸钠粉末22份、碳酸锶粉末20份、硅酸镁粉末18份、淀粉丙烯酰胺20份、海藻酸18份、硫酸铝18份、腐殖酸钠18份、磷酸二氢铵16份、十溴二苯乙烷12份、六氢化邻苯二甲酸酐10份、三甘醇二异辛酸酯10份、磷酸三甲酚酯10份、木质素磺酸钠10份、丁烯二酸酐10份、甲基丙烯酸月桂酯10份、脂肪酸甘油酯10份。
所述锆酸钠粉末由三种粒径目数的粉体组成,其粒径目数分别为30~50目、50~100目、100~140目,上述三种粉体的混合质量比例为4∶4∶1。
所述硅酸镁粉末由三种粒径目数的粉体组成,其粒径目数分别为30~50目、50~80目、80~100目,上述三种粉体的混合质量比例为7∶2∶1。
所述脂肪酸甘油酯的粘度在25℃为120mpa.s。
所述硫酸铝由三种粒径目数的粉体组成,其粒径目数分别为20~50目、50~70目、70~120目,上述三种粉体的混合质量比例为2∶3∶1。
所述聚醋酸乙烯乳的粘度在25℃为80mpa.s。
上述多功能电力施工用管材制备方法步骤如下:
(1)将所述质量份数的氟橡胶、酮醛树脂、PVC树脂粉、聚酯氨基甲酸酯树脂、聚丙烯树脂、二甲基甲酰胺、聚乙酸乙烯酯乳液、聚甘油蓖麻醇酯、二乙二醇丁醚、聚醋酸乙烯乳液、茶多酚、二溴二甲基乙内酰脲、多菌灵、氰乙基纤维素、双十八烷基二甲基氯化铵、锆酸钠粉末、碳酸锶粉末、硅酸镁粉末、淀粉丙烯酰胺、海藻酸、硫酸铝予以混合,超声高速分散,超声波频率为20kHz,分散速度5400r/min,分散时间为60min;
(2)加入所述质量份数的腐殖酸钠、磷酸二氢铵、十溴二苯乙烷、六氢化邻苯二甲酸酐、三甘醇二异辛酸酯,超声高速分散,超声波频率为20kHz,分散速度5200r/min,分散时间为50min;
(3)加入所述质量份数的磷酸三甲酚酯、木质素磺酸钠、丁烯二酸酐、甲基丙烯酸月桂酯、脂肪酸甘油酯,超声高速分散,超声波频率为20kHz,分散速度4800r/min,分散时间为40min;混合均匀后制得初级混合物;再将初级混合物加入到双螺杆挤出机中进行熔融混炼,得到所需混合物原料;
(4)将步骤(3)得到的混合物原料在挤出机中挤出,获得成品,其中,挤出条件为:料筒温度:184±2℃,合流芯温度:176±2℃,机头温度:190±5℃,牵引:0.6~0.9m/min,主机转速:25~30转/分。
实施例2
本实施例中的多功能电力施工用管材,由以下质量份数的组分组成:氟橡胶26份、酮醛树脂24份、PVC树脂粉24份、聚酯氨基甲酸酯树脂22份、聚丙烯树脂24份、二甲基甲酰胺24份、聚乙酸乙烯酯乳液22份、聚甘油蓖麻醇酯24份、二乙二醇丁醚24份、聚醋酸乙烯乳液22份、茶多酚22份、二溴二甲基乙内酰脲22份、多菌灵24份、氰乙基纤维素22份、双十八烷基二甲基氯化铵20份、锆酸钠粉末24份、碳酸锶粉末22份、硅酸镁粉末20份、淀粉丙烯酰胺22份、海藻酸20份、硫酸铝20份、腐殖酸钠20份、磷酸二氢铵18份、十溴二苯乙烷14份、六氢化邻苯二甲酸酐12份、三甘醇二异辛酸酯12份、磷酸三甲酚酯12份、木质素磺酸钠12份、丁烯二酸酐12份、甲基丙烯酸月桂酯12份、脂肪酸甘油酯12份。
所述锆酸钠粉末由三种粒径目数的粉体组成,其粒径目数分别为30~50目、50~100目、100~140目,上述三种粉体的混合质量比例为8∶6∶1。
所述硅酸镁粉末由三种粒径目数的粉体组成,其粒径目数分别为30~50目、50~80目、80~100目,上述三种粉体的混合质量比例为12∶5∶1。
所述脂肪酸甘油酯的粘度在25℃为140mpa.s。
所述硫酸铝由三种粒径目数的粉体组成,其粒径目数分别为20~50目、50~70目、70~120目,上述三种粉体的混合质量比例为4∶5∶1。
所述聚醋酸乙烯乳的粘度在25℃为100mpa.s。
上述多功能电力施工用管材制备方法步骤如下:
(1)将所述质量份数的氟橡胶、酮醛树脂、PVC树脂粉、聚酯氨基甲酸酯树脂、聚丙烯树脂、二甲基甲酰胺、聚乙酸乙烯酯乳液、聚甘油蓖麻醇酯、二乙二醇丁醚、聚醋酸乙烯乳液、茶多酚、二溴二甲基乙内酰脲、多菌灵、氰乙基纤维素、双十八烷基二甲基氯化铵、锆酸钠粉末、碳酸锶粉末、硅酸镁粉末、淀粉丙烯酰胺、海藻酸、硫酸铝予以混合,超声高速分散,超声波频率为30kHz,分散速度5200r/min,分散时间为45min;
(2)加入所述质量份数的腐殖酸钠、磷酸二氢铵、十溴二苯乙烷、六氢化邻苯二甲酸酐、三甘醇二异辛酸酯,超声高速分散,超声波频率为27kHz,分散速度5000r/min,分散时间为40min;
(3)加入所述质量份数的磷酸三甲酚酯、木质素磺酸钠、丁烯二酸酐、甲基丙烯酸月桂酯、脂肪酸甘油酯,超声高速分散,超声波频率为25kHz,分散速度4700r/min,分散时间为30min;混合均匀后制得初级混合物;再将初级混合物加入到双螺杆挤出机中进行熔融混炼,得到所需混合物原料;
(4)将步骤(3)得到的混合物原料在挤出机中挤出,获得成品,其中,挤出条件为:料筒温度:184±2℃,合流芯温度:176±2℃,机头温度:190±5℃,牵引:0.6~0.9m/min,主机转速:25~30转/分。
实施例3
本实施例中的多功能电力施工用管材,由以下质量份数的组分组成:氟橡胶28份、酮醛树脂26份、PVC树脂粉26份、聚酯氨基甲酸酯树脂24份、聚丙烯树脂26份、二甲基甲酰胺26份、聚乙酸乙烯酯乳液24份、聚甘油蓖麻醇酯26份、二乙二醇丁醚26份、聚醋酸乙烯乳液24份、茶多酚24份、二溴二甲基乙内酰脲24份、多菌灵26份、氰乙基纤维素24份、双十八烷基二甲基氯化铵22份、锆酸钠粉末26份、碳酸锶粉末24份、硅酸镁粉末22份、淀粉丙烯酰胺24份、海藻酸22份、硫酸铝22份、腐殖酸钠22份、磷酸二氢铵20份、十溴二苯乙烷16份、六氢化邻苯二甲酸酐14份、三甘醇二异辛酸酯14份、磷酸三甲酚酯14份、木质素磺酸钠14份、丁烯二酸酐14份、甲基丙烯酸月桂酯14份、脂肪酸甘油酯14份。
所述锆酸钠粉末由三种粒径目数的粉体组成,其粒径目数分别为30~50目、50~100目、100~140目,上述三种粉体的混合质量比例为12∶8∶1。
所述硅酸镁粉末由三种粒径目数的粉体组成,其粒径目数分别为30~50目、50~80目、80~100目,上述三种粉体的混合质量比例为17∶8∶1。
所述脂肪酸甘油酯的粘度在25℃为160mpa.s。
所述硫酸铝由三种粒径目数的粉体组成,其粒径目数分别为20~50目、50~70目、70~120目,上述三种粉体的混合质量比例为6∶8∶1。
所述聚醋酸乙烯乳的粘度在25℃为120mpa.s。
上述多功能电力施工用管材制备方法步骤如下:
(1)将所述质量份数的氟橡胶、酮醛树脂、PVC树脂粉、聚酯氨基甲酸酯树脂、聚丙烯树脂、二甲基甲酰胺、聚乙酸乙烯酯乳液、聚甘油蓖麻醇酯、二乙二醇丁醚、聚醋酸乙烯乳液、茶多酚、二溴二甲基乙内酰脲、多菌灵、氰乙基纤维素、双十八烷基二甲基氯化铵、锆酸钠粉末、碳酸锶粉末、硅酸镁粉末、淀粉丙烯酰胺、海藻酸、硫酸铝予以混合,超声高速分散,超声波频率为40kHz,分散速度5000r/min,分散时间为30min;
(2)加入所述质量份数的腐殖酸钠、磷酸二氢铵、十溴二苯乙烷、六氢化邻苯二甲酸酐、三甘醇二异辛酸酯,超声高速分散,超声波频率为35kHz,分散速度4800r/min,分散时间为30min;
(3)加入所述质量份数的磷酸三甲酚酯、木质素磺酸钠、丁烯二酸酐、甲基丙烯酸月桂酯、脂肪酸甘油酯,超声高速分散,超声波频率为30kHz,分散速度4600r/min,分散时间为20min;混合均匀后制得初级混合物;再将初级混合物加入到双螺杆挤出机中进行熔融混炼,得到所需混合物原料;
(4)将步骤(3)得到的混合物原料在挤出机中挤出,获得成品,其中,挤出条件为:料筒温度:184±2℃,合流芯温度:176±2℃,机头温度:190±5℃,牵引:0.6~0.9m/min,主机转速:25~30转/分。
针对实施例1、实施例2和实施例3中的产品和某市售产品进行性能测量,所测得的数据如表1和表2所示。防火阻燃等级测试采用UL94标准。
表1性能测试结果
由表1可见,本发明产品具有较好的耐腐蚀、防火阻燃、防霉变、抗菌绝缘性能。
表2
性能测量 | 实施例1 | 实施例2 | 实施例3 | 对照组 |
屈服强度(MPa) | 38 | 42 | 41 | 25 |
拉伸弹性模量(MPa) | 2775 | 2848 | 2675 | 1354 |
弯曲弹性模量(GPa) | 2.6 | 2.9 | 2.5 | 1.5 |
抗压强度(MPa) | 115 | 122 | 118 | 42 |
纵向延伸率(%) | 1.8 | 1.9 | 1.7 | 9.9 |
管壁粗糙度(μm) | 90 | 82 | 89 | 151 |
导热系数λ(W/m·k) | 0.15 | 0.13 | 0.13 | 0.11 |
由表2可见,本发明产品具有较好的屈服强度、拉伸弹性模量,抗压强度高,纵向延伸率号,导热效果佳。
以上所述是本发明的优选实施方式,应当指出,对于本技术领域的普通技术人员来说,在不脱离本发明原理的前提下,还可以做出若干改进和润饰,这些改进和润饰也视为本发明的保护范围。
Claims (10)
1.一种多功能电力施工用管材,其特征在于:由以下质量份数的组分组成:氟橡胶24~28份、酮醛树脂22~26份、PVC树脂粉22~26份、聚酯氨基甲酸酯树脂20~24份、聚丙烯树脂22~26份、二甲基甲酰胺22~26份、聚乙酸乙烯酯乳液20~24份、聚甘油蓖麻醇酯22~26份、二乙二醇丁醚22~26份、聚醋酸乙烯乳液20~24份、茶多酚20~24份、二溴二甲基乙内酰脲20~24份、多菌灵22~26份、氰乙基纤维素20~24份、双十八烷基二甲基氯化铵18~22份、锆酸钠粉末22~26份、碳酸锶粉末20~24份、硅酸镁粉末18~22份、淀粉丙烯酰胺20~24份、海藻酸18~22份、硫酸铝18~22份、腐殖酸钠18~22份、磷酸二氢铵16~20份、十溴二苯乙烷12~16份、六氢化邻苯二甲酸酐10~14份、三甘醇二异辛酸酯10~14份、磷酸三甲酚酯10~14份、木质素磺酸钠10~14份、丁烯二酸酐10~14份、甲基丙烯酸月桂酯10~14份、脂肪酸甘油酯10~14份。
2.根据权利要求1所述的多功能电力施工用管材,其特征在于:所述多功能电力施工用管材由以下质量份数的组分组成:氟橡胶24份、酮醛树脂22份、PVC树脂粉22份、聚酯氨基甲酸酯树脂20份、聚丙烯树脂22份、二甲基甲酰胺22份、聚乙酸乙烯酯乳液20份、聚甘油蓖麻醇酯22份、二乙二醇丁醚22份、聚醋酸乙烯乳液20份、茶多酚20份、二溴二甲基乙内酰脲20份、多菌灵22份、氰乙基纤维素20份、双十八烷基二甲基氯化铵18份、锆酸钠粉末22份、碳酸锶粉末20份、硅酸镁粉末18份、淀粉丙烯酰胺20份、海藻酸18份、硫酸铝18份、腐殖酸钠18份、磷酸二氢铵16份、十溴二苯乙烷12份、六氢化邻苯二甲酸酐10份、三甘醇二异辛酸酯10份、磷酸三甲酚酯10份、木质素磺酸钠10份、丁烯二酸酐10份、甲基丙烯酸月桂酯10份、脂肪酸甘油酯10份。
3.根据权利要求1所述的多功能电力施工用管材,其特征在于:所述多功能电力施工用管材由以下质量份数的组分组成:氟橡胶26份、酮醛树脂24份、PVC树脂粉24份、聚酯氨基甲酸酯树脂22份、聚丙烯树脂24份、二甲基甲酰胺24份、聚乙酸乙烯酯乳液22份、聚甘油蓖麻醇酯24份、二乙二醇丁醚24份、聚醋酸乙烯乳液22份、茶多酚22份、二溴二甲基乙内酰脲22份、多菌灵24份、氰乙基纤维素22份、双十八烷基二甲基氯化铵20份、锆酸钠粉末24份、碳酸锶粉末22份、硅酸镁粉末20份、淀粉丙烯酰胺22份、海藻酸20份、硫酸铝20份、腐殖酸钠20份、磷酸二氢铵18份、十溴二苯乙烷14份、六氢化邻苯二甲酸酐12份、三甘醇二异辛酸酯12份、磷酸三甲酚酯12份、木质素磺酸钠12份、丁烯二酸酐12份、甲基丙烯酸月桂酯12份、脂肪酸甘油酯12份。
4.根据权利要求1所述的多功能电力施工用管材,其特征在于:所述多功能电力施工用管材由以下质量份数的组分组成:氟橡胶28份、酮醛树脂26份、PVC树脂粉26份、聚酯氨基甲酸酯树脂24份、聚丙烯树脂26份、二甲基甲酰胺26份、聚乙酸乙烯酯乳液24份、聚甘油蓖麻醇酯26份、二乙二醇丁醚26份、聚醋酸乙烯乳液24份、茶多酚24份、二溴二甲基乙内酰脲24份、多菌灵26份、氰乙基纤维素24份、双十八烷基二甲基氯化铵22份、锆酸钠粉末26份、碳酸锶粉末24份、硅酸镁粉末22份、淀粉丙烯酰胺24份、海藻酸22份、硫酸铝22份、腐殖酸钠22份、磷酸二氢铵20份、十溴二苯乙烷16份、六氢化邻苯二甲酸酐14份、三甘醇二异辛酸酯14份、磷酸三甲酚酯14份、木质素磺酸钠14份、丁烯二酸酐14份、甲基丙烯酸月桂酯14份、脂肪酸甘油酯14份。
5.根据权利要求1所述的多功能电力施工用管材,其特征在于:所述锆酸钠粉末由三种粒径目数的粉体组成,其粒径目数分别为30~50目、50~100目、100~140目,上述三种粉体的混合质量比例为4~12∶4~8∶1。
6.根据权利要求1所述的多功能电力施工用管材,其特征在于:所述硅酸镁粉末由三种粒径目数的粉体组成,其粒径目数分别为30~50目、50~80目、80~100目,上述三种粉体的混合质量比例为7~17∶2~8∶1。
7.根据权利要求1所述的多功能电力施工用管材,其特征在于:所述脂肪酸甘油酯的粘度在25℃为120~160mpa.s。
8.根据权利要求1所述的多功能电力施工用管材,其特征在于:所述硫酸铝由三种粒径目数的粉体组成,其粒径目数分别为20~50目、50~70目、70~120目,上述三种粉体的混合质量比例为2~6∶3~8∶1。
9.根据权利要求1所述的多功能电力施工用管材,其特征在于:所述聚醋酸乙烯乳的粘度在25℃为80~120mpa.s。
10.根据权利要求1所述的多功能电力施工用管材,其特征在于:所述多功能电力施工用管材制备方法步骤如下:
(1)将所述质量份数的氟橡胶、酮醛树脂、PVC树脂粉、聚酯氨基甲酸酯树脂、聚丙烯树脂、二甲基甲酰胺、聚乙酸乙烯酯乳液、聚甘油蓖麻醇酯、二乙二醇丁醚、聚醋酸乙烯乳液、茶多酚、二溴二甲基乙内酰脲、多菌灵、氰乙基纤维素、双十八烷基二甲基氯化铵、锆酸钠粉末、碳酸锶粉末、硅酸镁粉末、淀粉丙烯酰胺、海藻酸、硫酸铝予以混合,超声高速分散,超声波频率为20~40KHz,分散速度约5000~5400r/min,分散时间为30~60min;
(2)加入所述质量份数的腐殖酸钠、磷酸二氢铵、十溴二苯乙烷、六氢化邻苯二甲酸酐、三甘醇二异辛酸酯,超声高速分散,超声波频率为20~35KHz,分散速度为约4800~5200r/min,分散时间为30~50min;
(3)加入所述质量份数的磷酸三甲酚酯、木质素磺酸钠、丁烯二酸酐、甲基丙烯酸月桂酯、脂肪酸甘油酯,超声高速分散,超声波频率为20~30KHz,分散速度为约4600~4800r/min,分散时间为20~40min;混合均匀后制得初级混合物;再将初级混合物加入到双螺杆挤出机中进行熔融混炼,得到所需混合物原料;
(4)将步骤(3)得到的混合物原料在挤出机中挤出,获得成品,其中,挤出条件为:料筒温度:184±2℃,合流芯温度:176±2℃,机头温度:190±5℃,牵引:0.6~0.9m/min,主机转速:25~30转/分。