CN106584643A - Light honeycomb outer wall plate - Google Patents
Light honeycomb outer wall plate Download PDFInfo
- Publication number
- CN106584643A CN106584643A CN201611126120.1A CN201611126120A CN106584643A CN 106584643 A CN106584643 A CN 106584643A CN 201611126120 A CN201611126120 A CN 201611126120A CN 106584643 A CN106584643 A CN 106584643A
- Authority
- CN
- China
- Prior art keywords
- parts
- component
- light
- polystyrene
- sludge
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a light honeycomb outer wall plate, and belongs to the technical field of chemical artificial stone. The light honeycomb outer wall plate is prepared in the manner that by mass, the following components are mixed, pressing is conducted in a die cavity under the pressure ranging from 100 kgkg/cm<2> to 140 kgkg/cm<2>, the mixture and the die cavity are placed in a constant-temperature and constant-humidity box with the humidity ranging from 90% to 100% and the temperature being 20+/-2 DEG C to be cured for 8 h, and after die stripping, curing continues in a curing box till the set age is reached. The first component is 36-60 parts of a mixture obtained after sludge produced by a domestic waste water plant and dry coal ash and slag are blended and stirred in a half-to-half manner, wherein the content of water of the sludge ranges from 60% to 80%. The second component is 30-60 parts of dry building garbage scrap powder with the diameter being below 15 mm through crushing. The third component is 25-36 parts of cement. The fourth component is 0.5-1.5 parts of polystyrene ball particles. The fifth component is 2-7 parts of steel fiber. According to the light honeycomb outer wall plate, the sludge generated by the domestic waste water plant and the polystyrene particles can be comprehensively utilized for preparing light building blocks free of secondary pollution.
Description
Technical field
The present invention relates to a kind of light-duty Side fascia of Nidus Vespae, belongs to artificial stone technical field in chemistry.
Background technology
A large amount of sanitary sewage disposals are filled out in current city --- precipitating sludge Jing after pressure, filter predrainage moisture content still 60-85% it
Between（Containing water of crystallization）Sludge silt because wherein containing the harmful substance such as heavy metal, various places government forbids to fill on the spot, though it is useful
Chemical method dehydration fed to boiler is burned or disposed by cement plant, but its amount of clearing up is far from meeting yield.
It is the also difficult crystalloid water for evaporating of exposure in the sun to be full of big portion in 80% moisture content in domestic sewage factory sludge
Body, even if be exposed to the sun can only also dissipate a small amount of crystalloid water body, and is up to 80% town domestic sewage factory sludge to moisture content
To reduce its moisture content（Even if by 80% to 60% moisture content）, the input of its required energy and fund seriously loses more than gain,
And secondary pollution is also extremely difficult avoids.Therefore, disposal and the recycling of reasonable environmental protection how are carried out to sludge, is individual very big
Problem.
Meanwhile, according to the applicant understood, modified styrene polymer is widely used, and has brought many convenience, but due to
Waste polystyrene is difficult to compress and degrades, and the environmental pollution that causes to used foamed plastics of people lacks and enough recognizes
Know, used used foamed plastics product arbitrarily abandoned, polystyrene has the characteristic such as ageing-resistant, difficult degradation, anticorrosive again,
Serious harm is caused to environment, also becomes a great problem of garbage disposal.
The content of the invention
The technical problem to be solved in the present invention is not enough for prior art, proposes that a kind of comprehensive utilization domestic sewage factory is produced
Raw sludge and waste polystyrene are producing the light-duty light-duty Side fascia of Nidus Vespae of non-secondary pollution.
The present invention is that the technical scheme for solving above-mentioned technical problem proposition is：A kind of light-duty Side fascia of Nidus Vespae, its feature exists
In：After the light-duty Side fascia of the Nidus Vespae is by mass by following components mixing, in mold cavity under 100-140kgkg/cm2 pressure
After compacting, and humidity is placed in together with mold cavity：90-100%, temperature are maintenance in 20 ± 2 DEG C of climatic chamber 8 hours,
Continue to conserve in curing box to setting age after the demoulding and form,
Component one：The sludge and dry coal lime-ash that the domestic sewage factory of aqueous 60%-80% is produced half-and-half blends the compound after stirring：
36-60 parts；
Component two：It is broken into the dry building waste bits powder of below 15mm：30-60 parts；
Component three：Cement：25-36 parts；
Component four：Polystyrene ball granule 0.5-1.5 parts；
Component five：Steel fibre：2-7 parts.
The working mechanism and beneficial effect of the light-duty Side fascia technical scheme of Nidus Vespae disclosed in the invention described above is presented below：
1）The sludge and dry coal lime-ash produced by the domestic sewage factory by the aqueous 60%-80% of 36-60 parts half-and-half blends stirring
Afterwards, with 30-60 parts the dry building waste bits powder for being broken into below 15mm, the cement of 25-36 parts, the 0.4- of 0.5-1 parts
The polystyrene ball granule of 0.7mm particle diameters and the steel fibre of 2-7 parts carry out dispensing, by hydraulic press with 100-140kgkg/
Compound densification molding in mold cavity is made to combine densification between exterior wall plate body material granule, sludge crystallization by the hydraulic coupling of cm2
Water participates in having the moistening effect of watering concurrently during hydrated cementitious；Easily incorporated and perpendicular solid cement system is formed after fully wrapped around other material of cement
Product, make to be diluted in terms of dry mash micro heavy class nuisance contained by the sludge powder for only accounting for 9% or so and polystyrene circle
Ball particle is blocked in being difficult to analyse the Behavior of Hardened Cement Paste of solution, it is possible to use it is relatively light same that sludge and polystyrene produce building block overall weight
When again secondary pollution is not caused to environment；2）Because Side fascia is than relatively thin and roomy, therefore steel fibre is referred and synthesized, make high intensity and mix
Enter the high-quality product of steel fibre；3）The light-duty Side fascia of this Nidus Vespae, is not only able to a large amount of dredgings using produced by annual and becomes silted up
Mud and waste plastic foam, and and substantially reduce the permeability of solidified after-product, while avoid being produced because of air storage
Raw harmful gass, greatly eliminate the environmental pollution that both garbages bring, and produce very big social benefit.
The change of above-mentioned technical proposal is：The polystyrene ball granule is the poly- of the 0.4-0.7mm particle diameters of 0.5-1 parts
Styrene ball granule, the polystyrene ball granule of the 0.7-1.0mm particle diameters of 0.6-0.9 parts, the 1.0- of 0.7-1.1 parts
The polystyrene ball granule of the polystyrene ball granule of 1.2mm particle diameters or the 1.2-1.8mm particle diameters of 1.2-1.5 parts.
Specific embodiment
Embodiment
A kind of light-duty Side fascia of Nidus Vespae of the present embodiment, the light-duty Side fascia of the Nidus Vespae is mixed by mass by following components
Afterwards, under 100-140kgkg/cm2 pressure after die cavity pressing, and humidity is placed in together with mold cavity：90-100%、
Temperature continues to conserve in curing box to setting age after the demoulding and forms to conserve 8 hours in 20 ± 2 DEG C of climatic chamber,
Typically age is set as 28 days.
Component one：The sludge and dry coal lime-ash that the domestic sewage factory of aqueous 60%-80% is produced half-and-half blends mixed after stirring
Close material：36-60 parts；
Component two：It is broken into the dry building waste bits powder of below 15mm：30-60 parts；
Component three：Cement：25-36 parts；
Component four：Polystyrene ball granule 0.5-1.5 parts；
Component five：Steel fibre：2-7 parts.
The polystyrene ball granule of the present embodiment be the 0.4-0.7mm particle diameters of 0.5-1 parts polystyrene ball granule,
The polystyrene ball granule of the 0.7-1.0mm particle diameters of 0.6-0.9 parts, the polystyrene of the 1.0-1.2mm particle diameters of 0.7-1.1 parts
The polystyrene ball granule of the 1.2-1.8mm particle diameters of ball granule or 1.2-1.5 parts.
The present invention is not limited to above-described embodiment.The technical scheme that all employing equivalents are formed, all falling within the present invention will
The protection domain asked.
Claims (2)
1. the light-duty Side fascia of a kind of Nidus Vespae, it is characterised in that：After the light-duty Side fascia of the Nidus Vespae is by mass by following components mixing,
Under 100-140kgkg/cm2 pressure after die cavity pressing, and humidity is placed in together with mold cavity：90-100%, temperature
To conserve 8 hours in 20 ± 2 DEG C of climatic chambers, continue to be conserved in curing box to setting age forming after the demoulding,
Component one：The sludge and dry coal lime-ash that the domestic sewage factory of aqueous 60%-80% is produced half-and-half blends the compound after stirring：
36-60 parts；
Component two：It is broken into the dry building waste bits powder of below 15mm：30-60 parts；
Component three：Cement：25-36 parts；
Component four：Polystyrene ball granule 0.5-1.5 parts；
Component five：Steel fibre：2-7 parts.
2. the light-duty Side fascia of Nidus Vespae as claimed in claim 1, it is characterised in that：The polystyrene ball granule is 0.5-1
Polystyrene ball granule, the polystyrene ball of the 0.7-1.0mm particle diameters of 0.6-0.9 parts of the 0.4-0.7mm particle diameters of part
The polyphenyl of the 1.2-1.8mm particle diameters of grain, the polystyrene ball granule of the 1.0-1.2mm particle diameters of 0.7-1.1 parts or 1.2-1.5 parts
Ethylene ball granule.