CN106571101A - Anti-counterfeiting mark capable of being recognized through presentation of stereoscopic pattern, and manufacture method for same - Google Patents
Anti-counterfeiting mark capable of being recognized through presentation of stereoscopic pattern, and manufacture method for same Download PDFInfo
- Publication number
- CN106571101A CN106571101A CN201610849040.2A CN201610849040A CN106571101A CN 106571101 A CN106571101 A CN 106571101A CN 201610849040 A CN201610849040 A CN 201610849040A CN 106571101 A CN106571101 A CN 106571101A
- Authority
- CN
- China
- Prior art keywords
- diamagnetism
- magnetic
- ink
- counterfeiting mark
- space pattern
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides an anti-counterfeiting mark capable of being recognized through presentation of a stereoscopic pattern. The anti-counterfeiting mark is characterized in that the stereoscopic pattern is formed through combination of magnetic printing ink and oriented arrangement of magnetic orientation printing plates; the magnetic printing ink comprises paramagnetism printing ink or diamagnetism printing ink; the paramagnetism printing ink is a paint containing iron magnetic substances; the diamagnetism printing ink is a paint containing diamagnetism substances; the paramagnetism or diamagnetism printing ink contains the constituents including 10-95 parts by weight of film forming substances, 1-25 parts by weight of the paint which can be arranged in an oriented manner in a magnetic field and contains the iron magnetic substances or the diamagnetism substances, 1-10 parts by weight of assistant agent and 0-88 parts by weight of solvent; and the paint which contains the iron magnetic substances or diamagnetism substances takes reflecting-material paints as the base material; and the base material is covered by the iron magnetic substances or the diamagnetism substances. The image has the high concretization and stereoscopic sense; and the recognition manner of the mark is visualized and efficient.
Description
Technical field
The present invention relates to a kind of by the way that anti-counterfeiting mark that space pattern is identified and preparation method thereof is presented.
Background technology
Existing anti-counterfeiting technology is typically adopted in body surface includes that the method such as printing, embossing, radium-shine, hologram transfer is done
Go out special-effect to realize；Or some hide informations are implanted into by methods such as bar code, Quick Response Code, magnetic information records,
Again by specialty instrument come recognize carry out it is false proof.Special-effect is made by the method such as printing, embossing, radium-shine, hologram transfer,
Identification is simple, but is easily copied；Although and be implanted into hide information by way of carry out it is false proof be difficult it is counterfeit, very
Hardly possible is intuitively recognized, is generally required for by professional instrument.The present invention relates to a kind of be identified by the way that space pattern is presented
Anti-counterfeiting mark, because it relates to multinomial subject crossing, counterfeit difficulty is big, and counterfeit high cost；Simultaneously significant innervation can be presented
Stereoscopic visual effect, it is easy to recognize.
The content of the invention
The technical problem to be solved in the present invention is to provide a kind of by the way that the anti-counterfeiting mark that space pattern is identified is presented, figure
As tool as, third dimension is strong, mark identification mode is intuitively efficient.
It is a kind of by the way that the anti-counterfeiting mark that space pattern is identified is presented that the present invention is provided, and the anti-counterfeiting mark adopts magnetic
Property ink align with reference to magnetic orientation printing plate, formed space pattern：The magnetic ink includes paramagnetism ink or diamagnetism
Ink：The paramagnetism ink is the pigment containing ferromagnetic material；The diamagnetism ink is the pigment containing diamagnetic material；Institute
Paramagnetism or diamagnetism ink are stated including following components by weight：
10-95 parts of film forming matters, pigment containing ferromagnetic material or diamagnetic material that energy counter field is arranged in magnetic field
1-25 parts and auxiliary agent 1-10 parts and solvent 0-88 parts；
The pigment containing ferromagnetic material or diamagnetic material with reflectorized material class pigment as base material, the base material overlying
Ferromagnetic material or diamagnetic material.
As further improvement of the invention：The ferromagnetic material is brown iron oxide；The diamagnetic material is inverse magnetic
Property metal, the diamagnetism metal is nanometer diamagnetism metal, and the nanometer diamagnetism metal is by the method system of arc discharge
It is standby to obtain.
As further improvement of the invention：By mass percentage, in the nanometer diamagnetism metal, the diamagnetism
Tenor is 2-17%.
As further improvement of the invention：It is described by mass percentage, the diamagnetism tenor be 6.5%.
As further improvement of the invention：The diamagnetism metal is selected from gold, silver, copper, bismuth, silicon dioxide, chlorination
The mixture of one or more in aluminum and/or zinc.
As further improvement of the invention：The film forming matter includes resin, oils and fatss, rubber, inorganic macromolecule material,
The resin is the mixture of one or more in epoxy resin, polyurethane, acrylic acid and celluosic resin.
As further improvement of the invention：The auxiliary agent is selected from silicone levelling agent, fluorine class levelling agent, organosilicon
Defoamer and adhesive agent.
As further improvement of the invention：The solvent is in esters, ketone, alcohols and ether organic solvent
The mixture of one or more.
The present invention also provides a kind of the anti-by be presented that space pattern is identified of suitable industrialized production simple to operate
Puppet mark manufacture method, it is characterised in that comprise the following steps：
1) above-mentioned magnetic ink by weight is coated in into printing mark sheet surface by spray painting or silk-screen；
2) it is coated with the mark sheet material of magnetic ink and places sizing in magnetic orientation printing plate, is formed and carry dynamic three-dimensional decorative pattern
Pattern；
3) the mark sheet material that surface has been formed dynamic three-dimensional decorative pattern is obtained finished product through high-temperature baking dry solidification.
As further improvement of the invention：The step 3) in drying mode be to be dried using UV photocurings.
Magnetic orientation printing plate affects the arrangement of magnetic ink the inside magnetic paint by forming magnetic field, and it can be Magnet；
Magnetic orientation printing plate particular design according to required pattern, pattern may be designed to decorative pattern, image, word etc..
Paramagnetism ink is the ink containing ferromagnetic material, and the anti-counterfeiting mark that it makes has very strong innervation, not
See with angle, three-dimensional line migration is obvious；The anti-counterfeiting mark of diamagnetism printing ink to manufacture has very strong concave-convex sense, as metal punching is cast
Effect：
The magnetic paint of paramagnetism ink is that the oxide of the ferrum on pearlescent pigment plated surface makes magnetic paint possess ferrum
Oxide can be by the characteristic of attraction, therefore magnetic ink can be produced using magnetic field to aligning for magnetic paint
Marvellous stereosopic printing effect.The stereoeffect that paramagnetism ink is presented be lines, geometrical pattern or some irregular take out
As space pattern, it is difficult to form the tool such as word, figure with concave-convex sense as pattern, the effect feature for being presented is with very strong
Light migration effect.
Diamagnetism ink is the ink containing diamagnetism pigment, and one is plated in reflective class surface of pigments using the method for chemistry
The materials with diamagnetism feature such as layer gold, silver, copper or zinc, reflectorized material base material is in tiny lamellar, with good reflective effect
Really；Produce concave-convex sense and be because the pigment with diamagnetic material, form concavo-convex inverse after the effect rearrangement in magnetic field
Magnetic paint layer, according to the principle of reflection of light the visual effect with strong concave-convex sense is finally presented.Diamagnetism metal face
The effect of material：There is magnetic reversal when certain metal in gold, silver, copper or zinc or metallic combination enter magnetic field, with Magnet not phase
Attract, but it is mutually exclusive.Gold, silver, copper, bismuth, silicon dioxide, aluminum chloride and/or zinc are included but is not limited in diamagnetism metal
In the mixture of one or more.Reflective class pigment includes but is not limited to pearlescent pigment, aluminium pigment, glass pigment.Reflective face
Material is coated with diamagnetic material by the method for chemistry, and the method for plating is water plating, plating, ion plating, Vacuum Deposition, chemical plating and relevant
The method of plating.
The more intuitive method for anti-counterfeit of a kind of vision that the present invention is provided, ferromagnetic pigments are in specific magnetic field along magnetic field side
To arrangement, diamagnetism pigment is arranged along magnetic direction as ferromagnetic material in specific magnetic field, but against magnetic
The direction oriented alignment of field, so as to form the appearance with strong stereo concave-convex.Simple to operate, form of construction work variation can
For：Various forms of construction work such as silk-screen, spraying, roller coating, showering, intaglio printing, offset printing, the curing mode of ink can be：From it is dry,
Heat cure, photocuring.
Description of the drawings
Fig. 1 is：It is a kind of by the way that anti-counterfeiting mark that space pattern is identified and preparation method thereof is presented that the present invention is provided
Process chart.
Fig. 2 is：It is a kind of by the way that anti-counterfeiting mark that space pattern is identified and preparation method thereof is presented that the present invention is provided
In diamagnetism ink design sketch.
Fig. 3 is：It is a kind of by the way that anti-counterfeiting mark that space pattern is identified and preparation method thereof is presented that the present invention is provided
In paramagnetism ink produce effect.
In Fig. 1：1st, sheet material is identified；2nd, magnetic orientation printing plate；3rd, drying device.
Specific embodiment
Below by way of a kind of anti-counterfeiting label being identified by presentation space pattern that specific embodiment is provided the present invention
Further more detailed description is done in knowledge and preparation method thereof：
Material is all molecular, and molecule is molecular by original.Electronics outside atomic nucleus ceaselessly does track fortune
Dynamic and spin motion, and nuclear spin, this all forms microcosmic electric current.Each microcosmic electric current load small equivalent to
Streamline circle, thus with certain magnetic moment.The magnetic moment of most of material atom cores is more much smaller than electron magnetic moment, can ignore not
Meter, therefore the magnetic of material is played a major role with electronic magnetic moment, especially its spin magnetic moment.The magnetic nature of material often with
The equivalent magnetic moment (or being called unit magnetic moment) and the intensity of magnetization of atom or molecule is illustrating.
In paramagnetism ink, the oxide of ferrum is coated with and obtained metal face on reflective class base material such as pearlescent pigment surface
Material, the metallic pigments possess the feature of the oxide of ferrum, can be tiny lamellar by attraction, form, there is reflecting effect.Should
Ink makes the metallic pigments rearrangement when the surface of magnetic field N/S contacts, work of the thin scutellate metallic pigments through magnetic field
After with arrangement, by ink coating effect of the reflection of light in ︶ radians depression.
When not having external magnetic field, the magnetic moment in atom cancels each other diamagnetic material, and the equivalent magnetic moment of atom is equal to zero,
Material does not externally show magnetic.In the presence of having external magnetic field, also will change around atomic nucleus rotating flow, original magnetic moment in atom
Poised state is destroyed, and a unbalanced magnetic moment is occurred in each atom.According to Lenz's law, this electronics is subject to magnetic
The effect of power, its angular momentum changes, i.e. the angular velocity of its rotation will be changed, thus the microcosmic electricity in atom is uneven
Magnetic moment and outer magnetic field direction conversely, so as to produce counter field arrangement phenomenon.Therefore, it is added with the pigment containing diamagnetic material
Ink makes pigment produce and repels and inversely arrange, the thin scutellate face with diamagnetic material when the surface of magnetic field N/S contacts
Expect through magnetic field effect arrangement after, by the reflection of light so as to be in ︵ radians project raised ink coating effect.
Diamagnetism metal is that the mixing such as last layer aluminum, gold, silver or single metal are plated on reflective class base material using chemical method, makes the face
Expect to be contacted on the surface of magnetic field N/S, when the ink/coating of the metallic pigments is added with, makes the metallic pigments produce and repel simultaneously
Reverse arrangement, so as to obtain the coating result of the ink/coating projected in ︵ radians.Reflective substrate material is in tiny lamellar, is had
There is good reflecting effect；Produce concave-convex sense and be because the pigment with diamagnetic material, through the effect rearrangement in magnetic field
Concavo-convex diamagnetism coat of colo(u)r is formed afterwards, and the effect of the vision with strong concave-convex sense is finally presented according to the principle of reflection of light
Really, and image can have as.
Test 1
The anti-counterfeiting mark being identified by presentation space pattern of this test, the anti-counterfeiting mark is tied using magnetic ink
Close magnetic orientation printing plate to align, form space pattern：The magnetic ink includes diamagnetism ink：The diamagnetism ink is
Pigment containing diamagnetic material；Diamagnetism ink includes following components by weight：
10 parts of film forming matters, in magnetic field can counter field arrangement 1 part of the pigment containing diamagnetic material and 1 part of auxiliary agents and molten
0 part of agent；
Wherein, with reflectorized material class pigment as base material, the base material overlying inverse magnetic to the pigment of the diamagnetic material
Property material.The diamagnetic material is diamagnetism metal, and the diamagnetism metal is nanometer diamagnetism metal, and the nanometer is against magnetic
Property metal is prepared by the method for arc discharge.
By mass percentage, in nanometer diamagnetism metal, diamagnetism tenor is 13%.
Diamagnetism metal is the mixture selected from gold, silver, copper, bismuth, silicon dioxide, aluminum chloride and/or zinc.The film forming matter
Matter includes resin, oils and fatss, rubber, inorganic macromolecule material, and the resin is selected from epoxy resin, polyurethane, acrylic acid and fibre
The mixture of the plain resin of dimension.Auxiliary agent is the mixture selected from organic silicon defoamer and adhesive agent.Solvent is ether organic solvent.Oil
Ink can be constructed by the way of roller coating.The curing mode of ink is carried out by the way of heat cure.
The technological process with reference to shown in Fig. 1, suitable industrialized production simple to operate by present space pattern be identified
Anti-counterfeiting mark manufacture method, comprise the following steps：
1) above-mentioned magnetic ink by weight is coated in into the surface of printing mark sheet material 1 by spray painting or silk-screen；2)
It is coated with the mark sheet material 1 of magnetic ink coating 4 and places sizing in magnetic orientation printing plate 2, is formed with dynamic three-dimensional decorative pattern
Pattern；3) the mark sheet material that surface has been formed dynamic three-dimensional decorative pattern is obtained by the high-temperature baking dry solidification of drying device 3
To finished product, as shown in Fig. 2 diamagnetism ink will be arranged in a raised sphere effect as button in this magnetic field
Really, the concave-convex effect or as casting in bronze.When not having external magnetic field, the magnetic moment in atom cancels each other diamagnetic material, former
The equivalent magnetic moment of son is equal to zero, and material does not externally show magnetic.In the presence of having external magnetic field, also will change around atomic nucleus rotating flow
Become, the poised state of original magnetic moment is destroyed in atom, and a unbalanced magnetic moment is occurred in each atom.According to Lenz
Law, this electronics is acted on by magnetic force, and its angular momentum changes, i.e. the angular velocity of its rotation will be changed, thus
The unbalanced magnetic moment of microcosmic electricity and outer magnetic field direction in atom is conversely, the phenomenon so as to produce counter field arrangement.Therefore, add
There is the pigment ink containing diamagnetic material when the surface of magnetic field N/S contacts, make pigment produce and repel and inversely arrange, tiny
The pigment of shape through magnetic field effect arrangement after, by the reflection of light so as to be in ︵ radians project raised ink coating
Effect.
Test 2
The anti-counterfeiting mark being identified by presentation space pattern of this test, the anti-counterfeiting mark is tied using magnetic ink
Close magnetic orientation printing plate to align, form space pattern：The magnetic ink includes paramagnetism ink：The paramagnetism ink is
Pigment containing ferromagnetic material；The paramagnetism ink includes following components by weight：
95 parts of film forming matters, can be along 25 parts of the pigment containing ferromagnetic material of magnetic field alignment and auxiliary agent 1-10 parts in magnetic field
With 88 parts of solvent；
Wherein, with reflectorized material class pigment as base material, the base material overlying ferrum to the pigment containing ferromagnetic material
Magnetisable material.Ferromagnetic material is brown iron oxide.
The film forming matter includes resin, and the resin is the mixture selected from epoxy resin and celluosic resin.Auxiliary agent
It is the mixture selected from silicone levelling agent, fluorine class levelling agent and adhesive agent.Solvent is organic selected from esters, alcohols and ethers
The mixture of solvent.Ink can be constructed by the way of silk-screen.The curing mode of ink is carried out by the way of heat cure.
With reference to shown in the process chart of Fig. 2, suitable industrialized production simple to operate by present space pattern carry out
The anti-counterfeiting mark manufacture method of identification, comprises the following steps：
1) above-mentioned magnetic ink by weight is coated in into the surface of printing mark sheet material 1 by spray painting or silk-screen；2)
It is coated with the mark sheet material of magnetic ink coating 4 and places sizing in magnetic orientation printing plate 2, forms the figure with dynamic three-dimensional decorative pattern
Case；3) the mark sheet material that surface has been formed dynamic three-dimensional decorative pattern is obtained through the transformation high-temperature baking dry solidification of device 3
Finished product, can only under identical magnetic field environment as shown in figure 3, paramagnetism ink has no idea to accomplish the effect that such font is highlighted
Realize that there is effect of shadow at font edge.In paramagnetism ink, the oxide of ferrum is coated with and obtained metal on pearlescent pigment surface
Pigment, the metallic pigments possess the feature of the oxide of ferrum, can be tiny lamellar by attraction, form, there is reflecting effect.
The ink makes the metallic pigments rearrangement when the surface of magnetic field N/S contacts, and thin scutellate metallic pigments are through magnetic field
After effect arrangement, by ink coating effect of the reflection of light in ︶ radians depression.
Embodiment 1
The anti-counterfeiting mark being identified by presentation space pattern of this test of the present embodiment, the anti-counterfeiting mark is adopted
Magnetic ink is aligned with reference to magnetic orientation printing plate, forms space pattern：The magnetic ink includes diamagnetism ink：It is described inverse
Magnetic ink is the pigment containing diamagnetic material；
15 parts of film forming matters, in magnetic field can counter field arrangement 5 parts of the pigment containing diamagnetic material and 2 parts of auxiliary agents and molten
2 parts of agent；
Wherein, the pigment containing diamagnetic material with reflectorized material class pigment as base material, inverse by the base material overlying
Magnetisable material.The diamagnetic material is diamagnetism metal, and the diamagnetism metal is nanometer diamagnetism metal, and the nanometer is inverse
Magnetic metal is prepared by the method for arc discharge.
By mass percentage, in nanometer diamagnetism metal, diamagnetism tenor is 2%.Diamagnetism metal be selected from
Gold.The film forming matter includes resin, and the resin is the mixture selected from epoxy resin, polyurethane.Solvent is that esters are organic
Solvent.Ink can be constructed by the way of silk-screen.The curing mode of ink is carried out by the way of heat cure.
The anti-counterfeiting mark manufacture method being identified by presentation space pattern of suitable industrialized production simple to operate, bag
Include following steps：
1) above-mentioned magnetic ink by weight is coated in into the surface of printing mark sheet material 1 by spray painting or silk-screen；2)
It is coated with the mark sheet material of magnetic ink coating 4 and places sizing in magnetic orientation printing plate 2, forms the figure with dynamic three-dimensional decorative pattern
Case；3) the mark sheet material that surface has been formed dynamic three-dimensional decorative pattern is obtained through the transformation high-temperature baking dry solidification of device 3
Finished product
Embodiment 2
The anti-counterfeiting mark being identified by presentation space pattern of this test, the anti-counterfeiting mark is tied using magnetic ink
Close magnetic orientation printing plate to align, form space pattern：The magnetic ink includes paramagnetism ink：The paramagnetism ink is
Pigment containing ferromagnetic material；
25 parts of film forming matters, in magnetic field can along 3 parts of 3 parts of the pigment containing ferromagnetic material of magnetic field alignment and auxiliary agent and
8 parts of solvent；
Wherein, with reflectorized material class pigment as base material, the base material overlying ferrum to the pigment containing ferromagnetic material
Magnetisable material.Ferromagnetic material is brown iron oxide.
The film forming matter includes resin, and the resin is the mixture selected from epoxy resin and celluosic resin.Auxiliary agent
It is the mixture selected from silicone levelling agent, fluorine class levelling agent.Solvent is organic molten selected from esters, ketone, alcohols and ethers
The mixture of agent.Ink can be constructed by the way of spraying.The curing mode of ink is carried out by the way of photocuring.
The anti-counterfeiting mark manufacture method being identified by presentation space pattern of suitable industrialized production simple to operate, bag
Include following steps：
1) above-mentioned magnetic ink by weight is coated in into the surface of printing mark sheet material 1 by spray painting or silk-screen；2)
It is coated with the mark sheet material of magnetic ink coating 4 and places sizing in magnetic orientation printing plate 2, forms the figure with dynamic three-dimensional decorative pattern
Case；3) the mark sheet material that surface has been formed dynamic three-dimensional decorative pattern is obtained through the transformation high-temperature baking dry solidification of device 3
Finished product
Embodiment 3
The anti-counterfeiting mark being identified by presentation space pattern of this test, the anti-counterfeiting mark is tied using magnetic ink
Close magnetic orientation printing plate to align, form space pattern：The magnetic ink includes diamagnetism ink：The diamagnetism ink is
Pigment containing diamagnetic material；
25 parts of film forming matters, in magnetic field can counter field arrangement 5 parts of the pigment containing diamagnetic material and 2 parts of auxiliary agents and molten
38 parts of agent；
Wherein, the pigment containing diamagnetic material with reflectorized material class pigment as base material, inverse by the base material overlying
Magnetisable material.The diamagnetic material is diamagnetism metal, and the diamagnetism metal is nanometer diamagnetism metal, and the nanometer is inverse
Magnetic metal is prepared by the method for arc discharge.
By mass percentage, in the nanometer diamagnetism metal, diamagnetism tenor is 6.5%.Diamagnetism metal
Be selected from bismuth, silicon dioxide, chlorination aluminum and zinc mixture.The film forming matter includes rubber.Auxiliary agent is to disappear selected from organosilicon
Mixture in infusion and adhesive agent.Solvent is the mixture selected from esters, ketone and ether organic solvent.Ink can be using rolling
The mode of painting is constructed.The curing mode of ink is carried out by the way of heat cure.
The anti-counterfeiting mark manufacture method being identified by presentation space pattern of suitable industrialized production simple to operate, bag
Include following steps：
1) above-mentioned magnetic ink by weight is coated in into the surface of printing mark sheet material 1 by spray painting or silk-screen；2)
It is coated with the mark sheet material of magnetic ink coating 4 and places sizing in magnetic orientation printing plate 2, forms the figure with dynamic three-dimensional decorative pattern
Case；3) the mark sheet material that surface has been formed dynamic three-dimensional decorative pattern is obtained through the transformation high-temperature baking dry solidification of device 3
Finished product
Embodiment 4
The anti-counterfeiting mark being identified by presentation space pattern of this test, the anti-counterfeiting mark is tied using magnetic ink
Close magnetic orientation printing plate to align, form space pattern：The magnetic ink includes diamagnetism ink：The diamagnetism ink is
Pigment containing diamagnetic material；
45 parts of film forming matters, in magnetic field can counter field arrangement 8 parts of the pigment containing diamagnetic material and 7 parts of auxiliary agents and molten
58 parts of agent；
Wherein, the pigment containing diamagnetic material with reflectorized material class pigment as base material, inverse by the base material overlying
Magnetisable material.The diamagnetic material is diamagnetism metal, and the diamagnetism metal is nanometer diamagnetism metal, and the nanometer is inverse
Magnetic metal is prepared by the method for arc discharge.
By mass percentage, diamagnetism tenor is 8%.Diamagnetism metal is selected from gold, silver, copper, bismuth, titanium dioxide
The mixture of silicon, chlorination aluminum and zinc.The film forming matter includes resin, and the resin is selected from epoxy resin.Auxiliary agent is organic
Silicon defoaming agent.Solvent is organic solvent of ketone.Ink can be constructed by the way of showering.The curing mode of ink adopts photocuring
Mode carry out.
The anti-counterfeiting mark manufacture method being identified by presentation space pattern of suitable industrialized production simple to operate, bag
Include following steps：
1) above-mentioned magnetic ink by weight is coated in into the surface of printing mark sheet material 1 by spray painting or silk-screen；2)
It is coated with the mark sheet material of magnetic ink coating 4 and places sizing in magnetic orientation printing plate 2, forms the figure with dynamic three-dimensional decorative pattern
Case；3) the mark sheet material that surface has been formed dynamic three-dimensional decorative pattern is obtained through the transformation high-temperature baking dry solidification of device 3
Finished product
Embodiment 5
The anti-counterfeiting mark being identified by presentation space pattern of this test, the anti-counterfeiting mark is tied using magnetic ink
Close magnetic orientation printing plate to align, form space pattern：The magnetic ink includes diamagnetism ink：The diamagnetism ink is
Pigment containing diamagnetic material；
35 parts of film forming matters, in magnetic field can counter field arrangement 11 parts of the pigment containing diamagnetic material and 7 parts of auxiliary agents and
78 parts of solvent；
Wherein, with reflectorized material class pigment as base material, the base material overlying inverse magnetic to the pigment of the diamagnetic material
Property material.The diamagnetic material is diamagnetism metal, and the diamagnetism metal is nanometer diamagnetism metal, and the nanometer is against magnetic
Property metal is prepared by the method for arc discharge.
By mass percentage, in nanometer diamagnetism metal, diamagnetism tenor is 11%.
Diamagnetism metal is the mixture selected from gold, silver, copper, bismuth, silicon dioxide, aluminum chloride and/or zinc.The film forming matter
Matter includes inorganic macromolecule material.Auxiliary agent is the mixture selected from fluorine class levelling agent, organic silicon defoamer and adhesive agent.Solvent is
Selected from the mixture of esters, alcohols and ether organic solvent.Ink can be constructed by the way of showering.The curing mode of ink is adopted
Carried out with the mode of photocuring.
The anti-counterfeiting mark manufacture method being identified by presentation space pattern of suitable industrialized production simple to operate, bag
Include following steps：
1) above-mentioned magnetic ink by weight is coated in into the surface of printing mark sheet material 1 by spray painting or silk-screen；2)
It is coated with the mark sheet material of magnetic ink coating 4 and places sizing in magnetic orientation printing plate 2, forms the figure with dynamic three-dimensional decorative pattern
Case；3) the mark sheet material that surface has been formed dynamic three-dimensional decorative pattern is obtained through the transformation high-temperature baking dry solidification of device 3
Finished product
Embodiment 6
The anti-counterfeiting mark being identified by presentation space pattern of this test, the anti-counterfeiting mark is tied using magnetic ink
Close magnetic orientation printing plate to align, form space pattern：The magnetic ink includes diamagnetism ink：The diamagnetism ink is
Pigment containing diamagnetic material；
65 parts of film forming matters, in magnetic field can counter field arrangement 5 parts of the pigment containing diamagnetic material and 3 parts of auxiliary agents and molten
58 parts of agent；
Wherein, with reflectorized material class pigment as base material, the base material overlying inverse magnetic to the pigment of the diamagnetic material
Property material.The diamagnetic material is diamagnetism metal, and the diamagnetism metal is nanometer diamagnetism metal, and the nanometer is against magnetic
Property metal is prepared by the method for arc discharge.
By mass percentage, in the nanometer diamagnetism metal, diamagnetism tenor is 11%.Diamagnetism metal is
Selected from gold, silver, copper, bismuth, silicon dioxide, chlorination aluminum and zinc mixture.The film forming matter includes resin, and the resin is choosing
From epoxy resin and the mixture of celluosic resin.Auxiliary agent is selected from the mixed of fluorine class levelling agent, organic silicon defoamer and adhesive agent
Compound.Solvent is the mixture selected from esters, ketone and ether organic solvent.Ink can be constructed by the way of silk-screen.Ink
Curing mode carried out by the way of photocuring.
The anti-counterfeiting mark manufacture method being identified by presentation space pattern of suitable industrialized production simple to operate, bag
Include following steps：
1) above-mentioned magnetic ink by weight is coated in into the surface of printing mark sheet material 1 by spray painting or silk-screen；2)
It is coated with the mark sheet material of magnetic ink coating 4 and places sizing in magnetic orientation printing plate 2, forms the figure with dynamic three-dimensional decorative pattern
Case；3) the mark sheet material that surface has been formed dynamic three-dimensional decorative pattern is obtained through the transformation high-temperature baking dry solidification of device 3
Finished product
Embodiment 7
The anti-counterfeiting mark being identified by presentation space pattern of this test, the anti-counterfeiting mark is tied using magnetic ink
Close magnetic orientation printing plate to align, form space pattern：The magnetic ink includes diamagnetism ink：The diamagnetism ink is
Pigment containing diamagnetic material；
75 parts of film forming matters, in magnetic field can counter field arrangement 13 parts of the pigment containing diamagnetic material and 3 parts of auxiliary agents and
55 parts of solvent；
Wherein, with reflectorized material class pigment as base material, the base material overlying inverse magnetic to the pigment of the diamagnetic material
Property material.The diamagnetic material is diamagnetism metal, and the diamagnetism metal is nanometer diamagnetism metal, and the nanometer is against magnetic
Property metal is prepared by the method for arc discharge.
By mass percentage, in nanometer diamagnetism metal, diamagnetism tenor is 15%.
Diamagnetism metal is the mixture selected from bismuth, silicon dioxide and zinc.The film forming matter includes resin, the resin
It is the mixture selected from epoxy resin, polyurethane and celluosic resin.Auxiliary agent be selected from fluorine class levelling agent, organic silicon defoamer and
The mixture of adhesive agent.Solvent is the mixture selected from alcohols and ether organic solvent.Ink can be constructed by the way of silk-screen.
The curing mode of ink is carried out by the way of photocuring.
The anti-counterfeiting mark manufacture method being identified by presentation space pattern of suitable industrialized production simple to operate, bag
Include following steps：
1) above-mentioned magnetic ink by weight is coated in into the surface of printing mark sheet material 1 by spray painting or silk-screen；2)
It is coated with the mark sheet material of magnetic ink coating 4 and places sizing in magnetic orientation printing plate 2, forms the figure with dynamic three-dimensional decorative pattern
Case；3) the mark sheet material that surface has been formed dynamic three-dimensional decorative pattern is obtained through the transformation high-temperature baking dry solidification of device 3
Finished product
The more intuitive method for anti-counterfeit of vision realized by ink that above-described embodiment 1-7 is prepared is used for into anti-counterfeit stamping
Brush, observes pattern and is shown in Table 1 with the presence or absence of three-dimensional imaging effect after printing：
The magnetic ink that embodiment 1-7 of table 1 is prepared is used for pattern three-dimensional imaging effect after anti-counterfeit printing
Presently preferred embodiments of the present invention is the foregoing is only, not to limit the present invention, all essences in the present invention
Any modification, equivalent and improvement made within god and principle etc., should be included within the scope of the present invention.
Claims (10)
1. a kind of by the way that the anti-counterfeiting mark that space pattern is identified is presented, the anti-counterfeiting mark is fixed with reference to magnetic using magnetic ink
Align to printing plate, form space pattern, it is characterised in that：The magnetic ink includes paramagnetism ink or diamagnetism oil
Ink：The paramagnetism ink is the pigment containing ferromagnetic material；The diamagnetism ink is the pigment containing diamagnetic material；It is described
Paramagnetism or diamagnetism ink include following components by weight：
10-95 parts of film forming matters, the pigment 1-25 containing ferromagnetic material or diamagnetic material that can be aligned in magnetic field
Part and auxiliary agent 1-10 parts and solvent 0-88 parts；
The pigment containing ferromagnetic material or diamagnetic material with reflectorized material class pigment as base material, by the base material overlying
Ferromagnetic material or diamagnetic material.
2. according to claim 1 by the way that the anti-counterfeiting mark that space pattern is identified is presented, it is characterised in that：The ferrum
Magnetisable material is brown iron oxide；The diamagnetic material is diamagnetism metal, and the diamagnetism metal is nanometer diamagnetism metal,
The nanometer diamagnetism metal is prepared by the method for arc discharge.
3. according to claim 2 by the way that the anti-counterfeiting mark that space pattern is identified is presented, it is characterised in that：By quality
Percentages, in the nanometer diamagnetism metal, the diamagnetism tenor is 2-17%.
4. according to claim 3 by the way that the anti-counterfeiting mark that space pattern is identified is presented, it is characterised in that：It is described to press
Mass percent meter, the diamagnetism tenor is 6.5%.
5., according to the arbitrary described anti-counterfeiting mark being identified by presentation space pattern of claim 1-4, its feature exists
In：The diamagnetism metal is the mixing of one or more in gold, silver, copper, bismuth, silicon dioxide, aluminum chloride and/or zinc
Thing.
6. according to claim 1 by the way that the anti-counterfeiting mark that space pattern is identified is presented, it is characterised in that：It is described into
Membrane substance includes resin, oils and fatss, rubber, inorganic macromolecule material, and the resin is selected from epoxy resin, polyurethane, acrylic acid
With the mixture of one or more in celluosic resin.
7. according to claim 1 by the way that the anti-counterfeiting mark that space pattern is identified is presented, it is characterised in that：It is described to help
Agent is selected from silicone levelling agent, fluorine class levelling agent, organic silicon defoamer and adhesive agent.
8. according to claim 1 by the way that the anti-counterfeiting mark that space pattern is identified is presented, it is characterised in that：It is described molten
Agent is the mixture of one or more in esters, ketone, alcohols and ether organic solvent.
9. according to claim 1-8 by the way that the anti-counterfeiting mark manufacture method that is identified of space pattern, its feature is presented
It is to comprise the following steps：
1) above-mentioned magnetic ink by weight is coated in into printing mark sheet surface by spray painting or silk-screen；
2) it is coated with the mark sheet material of magnetic ink and places sizing in magnetic orientation printing plate, forms the figure with dynamic three-dimensional decorative pattern
Case；
3) the mark sheet material that surface has been formed dynamic three-dimensional decorative pattern is obtained finished product through high-temperature baking dry solidification.
10. according to claim 9 by the way that the anti-counterfeiting mark manufacture method that space pattern is identified is presented, its feature exists
In：The step 3) in drying mode be to be dried using UV photocurings.