CN106541679A - The production method of the microsphere foaming frost flower ornament materials of building interior trim - Google Patents
The production method of the microsphere foaming frost flower ornament materials of building interior trim Download PDFInfo
- Publication number
- CN106541679A CN106541679A CN201610914288.2A CN201610914288A CN106541679A CN 106541679 A CN106541679 A CN 106541679A CN 201610914288 A CN201610914288 A CN 201610914288A CN 106541679 A CN106541679 A CN 106541679A
- Authority
- CN
- China
- Prior art keywords
- microsphere
- frost flower
- ornament materials
- interior trim
- building interior
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The production method of frost flower ornament materials the invention discloses a kind of microsphere for commercial location building interior trim foams, which has body paper production, Silk Procossing, bonding, application and microsphere foaming, press polish, noctilucence masking liquid is prepared and sprayed, frost flower is embossed step, final that the microsphere foaming frost flower ornament materials for commercial location building interior trim being made up of original paper layer, silk layer, foamed material layer and noctilucence frost flower layer is obtained.
Description
Technical field
The present invention relates to building interior trim decoration material field, and in particular to the microsphere for commercial location building interior trim foams
The production method of frost flower ornament materials.
Background technology
At present, further abundant with material life, people are to shelter and consumption place such as club, KTV boxes, meeting
The environmental requirement in the Room etc. is also significantly improved, and is embodied in emphatically environmental-protecting performance, anti-microbial property, intensity and endurance quality, the dress of interior trim
The decorations aspect such as class and light illumination, it is not enough yet with existing interior material one side antibacterial and mouldproof performance, on the one hand fill
Decorations class is difficult to satisfactory to both parties, generally existing performance defect with Costco Wholesale.In addition, existing consumption place for example club, KTV boxes,
There is the powerful luminaire of needs to improve the phenomenon of indoor light illumination in conference hall etc., which greatly enhances electric energy into
This, thus the use of high-power illumination equipment is reduced, energy saving is a great problem urgently to be resolved hurrily.
The content of the invention
The invention aims to providing, a kind of cost is relatively low, simple process, client's performance requirement and section are disclosure satisfy that
About the energy for commercial location building interior trim microsphere foam frost flower ornament materials production method.
The purpose of the present invention is achieved through the following technical solutions（In description, all numbers for referring to, percentage composition are equal
For calculated by mass）：A kind of production method of the microsphere foaming frost flower ornament materials for commercial location building interior trim, processing step
It is rapid as follows：
（1）Body paper is produced：With true qualities silver-containing antibacterial needle-leaved wood fibre material as raw material, on drainage cartridge type paper machine, wet method is manufactured paper with pulp
Without vertically and horizontally poor body paper, the wherein quantification of 100-110g/m of body paper2；
（2）Silk Procossing：With antibacterial filamentary silver and waxy luster staple as raw material, the silk face of plover grid pattern is formed using Suzhou embroidery maneuver
Material, wherein the weight accounting of antibacterial filamentary silver are 4-10wt%；
（3）Bonding：Using environment-friendly adhesive by step（2）In silk fabrics be bonded in step（1）In body paper surface, formed
Quantification of 120-130g/m2Substrate layer；
（4）Apply and microsphere foaming：Microsphere expanded material is applied to into step（3）In base material layer surface, and adopt infrared ray
Drying system carries out coated and dried foaming, forms microsphere foamed material layer, the microsphere expanded material sending out for island type structure
Foam material, wherein island are that the modeling spherical particle that organic alkane is formed and silica gel particle are mixed, and sea is Lauxite and trimerization
The thermo-plastic mixture that melamine resin is formed；
（5）Press polish：Soft calendaring is carried out to foamed material layer using paper calender roll so as to surface uniform ground, be easy to following process；
（6）Noctilucence masking liquid is prepared：In stirred tank, add epoxy resin and acrylate to be stirred mixing, continuously add
Glass microballoon and waxiness, are stirred 60-80min with magnetic rotor after being warming up to 80-90 DEG C, further add noctilucent powder,
It is sufficiently mixed, after adding solvent, is formed noctilucence masking liquid of the solid content for 25-30%；
（7）Spraying：By step（6）In noctilucence masking liquid dilution thicken after applied to step using high-pressure atomization paint finishing（5）
Sheet surface after press polish, forms the microsphere foaming Noctilucent decoration material that liquid layer is applied containing noctilucence after being dried；
（8）Frost flower is embossed：By step（7）In containing noctilucence apply liquid layer Noctilucent decoration material surface soften after, using frost flower figure
The embossing roller of case forms frost flower texture on its surface, according to required specification after solidification, its tailoring is sheared to be formed as business
The microsphere foaming frost flower ornament materials of place building interior trim.
The step（1）In true qualities silver-containing antibacterial needle-leaved wood fibre material in silver content be 4wt%.
The step（1）In the quantification of 105g/m of body paper2。
The step（2）In antibacterial filamentary silver weight accounting be 7wt%.
The step（3）In the natural gum that boils for Sargassum of environment-friendly adhesive.
The step（3）The quantification of 125g/m of substrate layer of middle formation2。
The step（4）In microsphere expanded material average particulate diameter be 20-30 μm, meso-position radius be 25 μm, foaming
Temperature is 160-180 DEG C, and foamed time is 2-4h.
The step（6）In noctilucence masking liquid consist of：30 parts of epoxy resin, 40 parts of acrylic resin, glass microballoon 20
Part, 10 parts of waxiness, 15 parts of noctilucent powder, solvent is enough.
The step（6）In warming temperature be 85 DEG C, magnetic rotor mixing time be 70min, noctilucence apply fluid solid content
For 28%.
The quantification of 140-150g/m of obtained microsphere foaming frost flower ornament materials2, flexible anti-tensile degree is 20.5-
22.5kN/m, bursting strength are 720-780kPa, and environmental protection grade is E0Level, antibacterial and mouldproof grade are excellent, and life cycle reaches 8-10
Year, full moon noctilucence illumination is 5.5-7.5 luxs.
The present invention is had the following advantages that compared with prior art：Cost is relatively low, simple process, and first by silk fabrics
Combine to improve interior trim class, physical strength and usage cycles with antibacterial body paper, by applying and the frost flower of noctilucence masking liquid
Embossing, substantially increases reflection and the refraction action of light, improves the light illumination of building interior trim, also with energy-conserving and environment-protective
Advantage, and compared with commercially available interior material, its flexible anti-tensile degree, bursting strength, environmental protection grade, antibacterial and mouldproof grade, life cycle
And full moon noctilucence illumination is respectively provided with significant advantage.
Specific embodiment：
In order to deepen the understanding of the present invention, below in conjunction with embodiment, the invention will be further described, and the embodiment is only used
In the present invention is explained, limiting the scope of the present invention is not constituted.
A kind of production method of the microsphere foaming frost flower ornament materials for commercial location building interior trim, procedure of processing is such as
Under：
（1）Body paper is produced：With true qualities silver-containing antibacterial needle-leaved wood fibre material as raw material, on drainage cartridge type paper machine, wet method is manufactured paper with pulp
Without vertically and horizontally poor body paper, the wherein quantification of 100-110g/m of body paper2；
（2）Silk Procossing：With antibacterial filamentary silver and waxy luster staple as raw material, the silk face of plover grid pattern is formed using Suzhou embroidery maneuver
Material, wherein the weight accounting of antibacterial filamentary silver are 4-10wt%；
（3）Bonding：Using environment-friendly adhesive by step（2）In silk fabrics be bonded in step（1）In body paper surface, formed
Quantification of 120-130g/m2Substrate layer；
（4）Apply and microsphere foaming：Microsphere expanded material is applied to into step（3）In base material layer surface, and adopt infrared ray
Drying system carries out coated and dried foaming, forms microsphere foamed material layer, the microsphere expanded material sending out for island type structure
Foam material, wherein island are that the modeling spherical particle that organic alkane is formed and silica gel particle are mixed, and sea is Lauxite and trimerization
The thermo-plastic mixture that melamine resin is formed；
（5）Press polish：Soft calendaring is carried out to foamed material layer using paper calender roll so as to surface uniform ground, be easy to following process；
（6）Noctilucence masking liquid is prepared：In stirred tank, add epoxy resin and acrylate to be stirred mixing, continuously add
Glass microballoon and waxiness, are stirred 60-80min with magnetic rotor after being warming up to 80-90 DEG C, further add noctilucent powder,
It is sufficiently mixed, after adding solvent, is formed noctilucence masking liquid of the solid content for 25-30%；
（7）Spraying：By step（6）In noctilucence masking liquid dilution thicken after applied to step using high-pressure atomization paint finishing（5）
Sheet surface after press polish, forms the microsphere foaming Noctilucent decoration material that liquid layer is applied containing noctilucence after being dried；
（8）Frost flower is embossed：By step（7）In containing noctilucence apply liquid layer Noctilucent decoration material surface soften after, using frost flower figure
The embossing roller of case forms frost flower texture on its surface, according to required specification after solidification, its tailoring is sheared to be formed as business
The microsphere foaming frost flower ornament materials of place building interior trim.
The step（1）In true qualities silver-containing antibacterial needle-leaved wood fibre material in silver content be 4wt%.
The step（1）In the quantification of 105g/m of body paper2。
The step（2）In antibacterial filamentary silver weight accounting be 7wt%.
The step（3）In the natural gum that boils for Sargassum of environment-friendly adhesive.
The step（3）The quantification of 125g/m of substrate layer of middle formation2。
The step（4）In microsphere expanded material average particulate diameter be 20-30 μm, meso-position radius be 25 μm, foaming
Temperature is 160-180 DEG C, and foamed time is 2-4h.
The step（6）In noctilucence masking liquid consist of：30 parts of epoxy resin, 40 parts of acrylic resin, glass microballoon 20
Part, 10 parts of waxiness, 15 parts of noctilucent powder, solvent is enough.
The step（6）In warming temperature be 85 DEG C, magnetic rotor mixing time be 70min, noctilucence apply fluid solid content
For 28%.
The quantification of 140-150g/m of obtained microsphere foaming frost flower ornament materials2, flexible anti-tensile degree is 20.5-
22.5kN/m, bursting strength are 720-780kPa, and environmental protection grade is E0Level, antibacterial and mouldproof grade are excellent, and life cycle reaches 8-10
Year, full moon noctilucence illumination is 5.5-7.5 luxs.
Embodiment 1
A kind of production method of the microsphere foaming frost flower ornament materials for commercial location building interior trim, procedure of processing are as follows：
（1）Body paper is produced：With true qualities argentiferous 4wt% antibacterial needle-leaved wood fibre materials as raw material, the wet method on drainage cartridge type paper machine
Manufacture paper with pulp without vertically and horizontally poor body paper, the wherein quantification of 100g/m of body paper2；
（2）Silk Procossing：With antibacterial filamentary silver and waxy luster staple as raw material, the silk face of plover grid pattern is formed using Suzhou embroidery maneuver
Material, wherein the weight accounting of antibacterial filamentary silver are 4wt%；
（3）Bonding：The natural gum boiled using Sargassum is by step（2）In silk fabrics be bonded in step（1）In base paper sheet
Face, forms quantification of 120g/m2Substrate layer；
（4）Apply and microsphere foaming：Microsphere expanded material is applied to into step（3）In base material layer surface, and adopt infrared ray
Drying system carries out coated and dried foaming, forms microsphere foamed material layer, the microsphere expanded material sending out for island type structure
Foam material, wherein island are that the modeling spherical particle that organic alkane is formed and silica gel particle are mixed, and sea is Lauxite and trimerization
The thermo-plastic mixture that melamine resin is formed；
（5）Press polish：Soft calendaring is carried out to foamed material layer using paper calender roll so as to surface uniform ground, be easy to following process；
（6）Noctilucence masking liquid is prepared：In stirred tank, add 40 parts of 30 parts of epoxy resin and acrylate to be stirred mixing,
10 parts of 20 parts of glass microballoon and waxiness are continuously added, 60min is stirred with magnetic rotor after being warming up to 80 DEG C, is further added
15 parts of noctilucent powder, is sufficiently mixed, and the noctilucence masking liquid that solid content is 25% is formed after adding sufficient solvent；
（7）Spraying：By step（6）In noctilucence masking liquid dilution thicken after applied to step using high-pressure atomization paint finishing（5）
Sheet surface after press polish, forms the Noctilucent decoration material that liquid layer is applied containing noctilucence after being dried；
（8）Frost flower is embossed：By step（7）In containing noctilucence apply liquid layer Noctilucent decoration material surface soften after, using frost flower figure
The embossing roller of case forms frost flower texture on its surface, according to required specification after solidification, its tailoring is sheared to be formed as business
The microsphere foaming frost flower ornament materials of place building interior trim.
The quantification of 140g/m of obtained microsphere foaming frost flower ornament materials2, flexible anti-tensile degree is 20.5kN/m, resistance to broken
Spend for 720kPa, environmental protection grade is E0Level, antibacterial and mouldproof grade are excellent, and up to 8 years, full moon noctilucence illumination was 5.5 to life cycle
Lux.
Embodiment 2
A kind of production method of the microsphere foaming frost flower ornament materials for commercial location building interior trim, procedure of processing are as follows：
（1）Body paper is produced：With true qualities argentiferous 4wt% antibacterial needle-leaved wood fibre materials as raw material, the wet method on drainage cartridge type paper machine
Manufacture paper with pulp without vertically and horizontally poor body paper, the wherein quantification of 105g/m of body paper2；
（2）Silk Procossing：With antibacterial filamentary silver and waxy luster staple as raw material, the silk face of plover grid pattern is formed using Suzhou embroidery maneuver
Material, wherein the weight accounting of antibacterial filamentary silver are 7wt%；
（3）Bonding：The natural gum boiled using Sargassum is by step（2）In silk fabrics be bonded in step（1）In base paper sheet
Face, forms quantification of 125g/m2Substrate layer；
（4）Apply and microsphere foaming：Microsphere expanded material is applied to into step（3）In base material layer surface, and adopt infrared ray
Drying system carries out coated and dried foaming, forms microsphere foamed material layer, the microsphere expanded material sending out for island type structure
Foam material, wherein island are that the modeling spherical particle that organic alkane is formed and silica gel particle are mixed, and sea is Lauxite and trimerization
The thermo-plastic mixture that melamine resin is formed；
（5）Press polish：Soft calendaring is carried out to foamed material layer using paper calender roll so as to surface uniform ground, be easy to following process；
（6）Noctilucence masking liquid is prepared：In stirred tank, add 40 parts of 30 parts of epoxy resin and acrylate to be stirred mixing,
10 parts of 20 parts of glass microballoon and waxiness are continuously added, 70min is stirred with magnetic rotor after being warming up to 85 DEG C, is further added
15 parts of noctilucent powder, is sufficiently mixed, and the noctilucence masking liquid that solid content is 28% is formed after adding sufficient solvent；
（7）Spraying：By step（6）In noctilucence masking liquid dilution thicken after applied to step using high-pressure atomization paint finishing（5）
Sheet surface after press polish, forms the Noctilucent decoration material that liquid layer is applied containing noctilucence after being dried；
（8）Frost flower is embossed：By step（7）In containing noctilucence apply liquid layer Noctilucent decoration material surface soften after, using frost flower figure
The embossing roller of case forms frost flower texture on its surface, according to required specification after solidification, its tailoring is sheared to be formed as business
The microsphere foaming frost flower ornament materials of place building interior trim.
The quantification of 145g/m of obtained microsphere foaming frost flower ornament materials2, flexible anti-tensile degree is 21.5kN/m, resistance to broken
Spend for 750kPa, environmental protection grade is E0Level, antibacterial and mouldproof grade are excellent, and up to 9 years, full moon noctilucence illumination was 6.5 to life cycle
Lux.
Embodiment 3
A kind of production method of the microsphere foaming frost flower ornament materials for commercial location building interior trim, procedure of processing are as follows：
（1）Body paper is produced：With true qualities argentiferous 4wt% antibacterial needle-leaved wood fibre materials as raw material, the wet method on drainage cartridge type paper machine
Manufacture paper with pulp without vertically and horizontally poor body paper, the wherein quantification of 110g/m of body paper2；
（2）Silk Procossing：With antibacterial filamentary silver and waxy luster staple as raw material, the silk face of plover grid pattern is formed using Suzhou embroidery maneuver
Material, wherein the weight accounting of antibacterial filamentary silver are 10wt%；
（3）Bonding：The natural gum boiled using Sargassum is by step（2）In silk fabrics be bonded in step（1）In base paper sheet
Face, forms quantification of 130g/m2Substrate layer；
（4）Apply and microsphere foaming：Microsphere expanded material is applied to into step（3）In base material layer surface, and adopt infrared ray
Drying system carries out coated and dried foaming, forms microsphere foamed material layer, the microsphere expanded material sending out for island type structure
Foam material, wherein island are that the modeling spherical particle that organic alkane is formed and silica gel particle are mixed, and sea is Lauxite and trimerization
The thermo-plastic mixture that melamine resin is formed；
（5）Press polish：Soft calendaring is carried out to foamed material layer using paper calender roll so as to surface uniform ground, be easy to following process；
（6）Noctilucence masking liquid is prepared：In stirred tank, add 40 parts of 30 parts of epoxy resin and acrylate to be stirred mixing,
10 parts of 20 parts of glass microballoon and waxiness are continuously added, 80min is stirred with magnetic rotor after being warming up to 90 DEG C, is further added
15 parts of noctilucent powder, is sufficiently mixed, and the noctilucence masking liquid that solid content is 30% is formed after adding sufficient solvent；
（7）Spraying：By step（6）In noctilucence masking liquid dilution thicken after applied to step using high-pressure atomization paint finishing（5）
Sheet surface after press polish, forms the Noctilucent decoration material that liquid layer is applied containing noctilucence after being dried；
（8）Frost flower is embossed：By step（7）In containing noctilucence apply liquid layer Noctilucent decoration material surface soften after, using frost flower figure
The embossing roller of case forms frost flower texture on its surface, according to required specification after solidification, its tailoring is sheared to be formed as business
The microsphere foaming frost flower ornament materials of place building interior trim.
The quantification of 150g/m of obtained microsphere foaming frost flower ornament materials2, flexible anti-tensile degree is 22.5kN/m, resistance to broken
Spend for 780kPa, environmental protection grade is E0Level, antibacterial and mouldproof grade are excellent, and up to 10 years, full moon noctilucence illumination was 7.5 to life cycle
Lux.
The microsphere foaming frost flower ornament materials of the present invention and commercially available interior material performance comparison such as following table：：
Note：Above table fullness in the epigastrium and abdomen moonlit night illuminance refers to the light illumination after full moon environment next month light irradiation interior material.
As shown above, its superior performance compared with commercially available interior material of the invention.It is mainly reflected in that cost is relatively low, technique
Simplicity, and silk fabrics is combined to improve interior trim class, physical strength and usage cycles with antibacterial body paper first, by night
The applying of light masking liquid and frost flower embossing, substantially increase reflection and the refraction action of light, improve the light of building interior trim
Illumination, the also advantage with energy-conserving and environment-protective, and compared with commercially available interior material, its flexible anti-tensile degree, bursting strength, environmental protection grade,
Antibacterial and mouldproof grade, life cycle and full moon noctilucence illumination are respectively provided with significant advantage.
Above-mentioned embodiment is only the present invention preferably technical scheme, other any spirit without departing from the present invention
With the change, modification, replacement made under action principle, combine, simplify, should be equivalent substitute mode, be included in this
Within bright protection domain.
Claims (10)
1. a kind of microsphere for building interior trim foams the production method of frost flower ornament materials, it is characterised in that procedure of processing is such as
Under：
（1）Body paper is produced：With true qualities silver-containing antibacterial needle-leaved wood fibre material as raw material, on drainage cartridge type paper machine, wet method is manufactured paper with pulp
Without vertically and horizontally poor body paper, the wherein quantification of 100-110g/m of body paper2；
（2）Silk Procossing：With antibacterial filamentary silver and waxy luster staple as raw material, the silk face of plover grid pattern is formed using Suzhou embroidery maneuver
Material, wherein the weight accounting of antibacterial filamentary silver are 4-10wt% or so；
（3）Bonding：Using environment-friendly adhesive by step（2）In silk fabrics be bonded in step（1）In body paper surface, formed
Quantification of 120-130g/m2Substrate layer；
（4）Apply and microsphere foaming：Microsphere expanded material is applied to into step（3）In base material layer surface, and adopt infrared ray
Drying system carries out coated and dried foaming, forms microsphere foamed material layer, the microsphere expanded material sending out for island type structure
Foam material, wherein island are that the modeling spherical particle that organic alkane is formed and silica gel particle are mixed, and sea is Lauxite and trimerization
The thermo-plastic mixture that melamine resin is formed；
（5）Press polish：Soft calendaring is carried out to foamed material layer using paper calender roll so as to surface uniform ground, be easy to following process；
（6）Noctilucence masking liquid is prepared：In stirred tank, add epoxy resin and acrylate to be stirred mixing, continuously add
Glass microballoon and waxiness, are stirred 60-80min or so with magnetic rotor after being warming up to 80-90 DEG C, further add luminescent powder
End, is sufficiently mixed, and noctilucence masking liquid of the solid content for 25-30% is formed after adding solvent；
（7）Spraying：By step（6）In noctilucence masking liquid dilution thicken after applied to step using high-pressure atomization paint finishing（5）
Sheet surface after press polish, forms the microsphere foaming Noctilucent decoration material that liquid layer is applied containing noctilucence after being dried；
（8）Frost flower is embossed：By step（7）In containing noctilucence apply liquid layer Noctilucent decoration material surface soften after, using frost flower figure
The embossing roller of case forms frost flower texture on its surface, according to required specification after solidification, its tailoring is sheared to be formed as business
The microsphere foaming frost flower ornament materials of place building interior trim.
2. a kind of microsphere for building interior trim according to claim 1 foams the production method of frost flower ornament materials, its
It is characterised by, step（1）In true qualities silver-containing antibacterial needle-leaved wood fibre material in silver content be for about 4wt%.
3. a kind of microsphere for building interior trim according to claim 1 foams the production method of frost flower ornament materials, its
It is characterised by, step（1）In the quantification of 105g/m of body paper2。
4. a kind of microsphere for building interior trim according to claim 1 foams the production method of frost flower ornament materials, its
It is characterised by, step（2）In antibacterial filamentary silver weight accounting be 7wt%.
5. a kind of microsphere for building interior trim according to claim 1 foams the production method of frost flower ornament materials, its
It is characterised by, step（3）In the natural gum that boils for Sargassum of environment-friendly adhesive.
6. a kind of microsphere for building interior trim according to claim 1 foams the production method of frost flower ornament materials, its
It is characterised by, step（3）The quantification of 125g/m of substrate layer of middle formation2。
7. a kind of microsphere for building interior trim according to claim 1 foams the production method of frost flower ornament materials, its
It is characterised by, step（4）In microsphere expanded material average particulate diameter be 20-30 μm, meso-position radius be 25 μm, blowing temperature
For 160-180 DEG C, foamed time is 2-4h.
8. a kind of microsphere for building interior trim according to claim 1 foams the production method of frost flower ornament materials, its
It is characterised by, step（6）In noctilucence masking liquid consist of：30 parts of epoxy resin, 40 parts of acrylic resin, 20 parts of glass microballoon,
10 parts of waxiness, 15 parts of noctilucent powder, solvent is enough.
9. a kind of microsphere for building interior trim according to claim 1 foams the production method of frost flower ornament materials, its
It is characterised by, step（6）In warming temperature be 85 DEG C, magnetic rotor mixing time be 70min, noctilucence apply fluid solid content be
28%。
10. a kind of microsphere foaming frost flower ornament materials for building interior trim according to any one of claim 1-9
Production method, it is characterised in that the quantification of 140-150g/m of obtained microsphere foaming frost flower ornament materials2, flexible anti-tensile degree
For 20.5-22.5kN/m, bursting strength is 720-780kPa, and environmental protection grade is E0Level, antibacterial and mouldproof grade are excellent, life cycle
Up to 8-10, full moon noctilucence illumination is 5.5-7.5 luxs.