CN106519723A - An anti-ageing plastic-wood material and a preparing method thereof - Google Patents
An anti-ageing plastic-wood material and a preparing method thereof Download PDFInfo
- Publication number
- CN106519723A CN106519723A CN201610980886.XA CN201610980886A CN106519723A CN 106519723 A CN106519723 A CN 106519723A CN 201610980886 A CN201610980886 A CN 201610980886A CN 106519723 A CN106519723 A CN 106519723A
- Authority
- CN
- China
- Prior art keywords
- wood material
- ageing
- resistant plastic
- plastic
- wood
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Embodiments of the invention disclose an anti-ageing plastic-wood material and a preparing method thereof. The material includes, by mass, 110-120 parts of phenolic resin, 135-145 parts of polyethylene, 150-165 parts of plant ash, 2-5 parts of a solubilizer, 1-2 parts of an antimicrobial agent, 2-4 parts of an antiager, 2-3 parts of an ultraviolet ray stabilizing agent and 4-5 parts of a coupling agent. According to the anti-ageing plastic-wood material and the preparing method thereof, the problem that plastic-wood materials are poor in ageing resistance and short in service lifetime can be effectively improved.
Description
Technical field
The present invention relates to Material Field, more particularly to a kind of ageing-resistant plastic-wood material and preparation method thereof.
Background technology
With the development of society, composite is widely used in industry-by-industry field.Wherein, plastic-wood material is compound
One kind of material.As modeling wood has two kinds of characteristics of texture of plastics and timber concurrently so that it becomes a kind of function admirable very
Durable outdoor building materials；Also replace the Wood member that harbour, harbour etc. are used, it may also be used for substitute timber and make various packagings
Thing, pallet, warehouse pallet etc. are too numerous to enumerate, and purposes is extremely wide.Plastic wood sheet, combines Plant fiber and plastics macromolecule material
The plurality of advantages of material, can substitute timber in a large number, can effectively alleviate that China's Forest Resources are poor, the contradiction that wood supply is in short supply, be
A kind of low-carbon (LC) of great development prospect, green, renewable ecological plastic-wood material capable of circulation.
But, as plastic-wood material is much used for outdoor, through exposing to wind and rain, it is easy to aging, where important, such as
It is really aging too fast, go back entail dangers to personal safety.
The content of the invention
In view of this, the invention provides a kind of ageing-resistant plastic-wood material and preparation method thereof, can be effectively improved modeling wood
Material aging resistance is poor, the problem of short life.
A kind of ageing-resistant plastic-wood material and preparation method thereof, the plastic-wood material is included by mass component：
Preferably, the plastic-wood material is included by mass component：
Preferably, the plastic-wood material is included by mass component：
Preferably, the solubilizing agent is Polyglycerol ester of fatty acids.
Preferably, the ultra-violet stabilizer is sodium salicylate.
Preferably, the anti-microbial inoculum be bromo- 2 nitropropane -1 of 2-, 3- glycol.
Preferably, the coupling agent is silane coupler.
Preferably, the age resister is polypropylene.
A kind of preparation method of ageing-resistant plastic-wood material, the method include：
It is prepared by premix material：Wood powder is added in high mixer, with 2100-2400 rev/min of high-speed stirred 8 minutes, wood powder
Humid control is then respectively adding remaining above-mentioned each component below 0.6%, carries out batch mixing, and batch mixing is by above-mentioned batch mixing by mixing
The hot mixing system discharging of material machine is cooled to 62 DEG C, obtains premix material to cold mixing system；
It is prepared by pelletize pellet：Premix material Jing parallel double-screw extruder extruding pelletizations, technological temperature are set in into 180-185
DEG C, it is to be used as semi-finished product pelletize pellet etc.；
It is prepared by extrusion molding：Particle after extruding pelletization is added to into extrusion molding in conical double-screw, technological temperature sets
170-180 DEG C is scheduled on, is extruded by mould, that is, is obtained the product obtained by ageing-resistant plastic-wood material.
A kind of ageing-resistant plastic-wood material and preparation method thereof of the present invention, it is poor to be effectively improved plastic-wood material aging resistance,
The problem of short life.
Specific embodiment
Below in conjunction with the embodiment of the present invention, the technical scheme in the embodiment of the present invention is clearly and completely described,
Obviously, described embodiment is a part of embodiment of the invention, rather than the embodiment of whole.Based on the enforcement in the present invention
Example, the every other embodiment obtained under the premise of creative work is not made by those of ordinary skill in the art are belonged to
The scope of protection of the invention.
It should be appreciated that when using in this specification and in the appended claims, term " including " and "comprising" are indicated
The presence of described feature, entirety, step, operation, element and/or component, but it is not precluded from one or more of the other feature, whole
The presence or addition of body, step, operation, element, component and/or its set.
It will be further appreciated that, the term "and/or" used in description of the invention and appended claims is
Refer to any combinations of one or more and be possible to combination being associated in the item listed, and including these combinations.
Embodiment 1
By weight, the composition component of a kind of ageing-resistant plastic-wood material of the present embodiment and preparation method thereof is as follows：
Embodiment 2
By weight, the composition component of a kind of ageing-resistant plastic-wood material of the present embodiment and preparation method thereof is as follows：
Embodiment 3
By weight, the composition component of a kind of ageing-resistant plastic-wood material of the present embodiment and preparation method thereof is as follows：
Embodiment 4
By weight, the composition component of a kind of ageing-resistant plastic-wood material of the present embodiment and preparation method thereof is as follows：
Embodiment 5
By weight, the composition component of a kind of ageing-resistant plastic-wood material of the present embodiment and preparation method thereof is as follows：
A kind of preparation method of ageing-resistant plastic-wood material, method include：1. it is prepared by premix material：Wood powder is added to into high mixer
In, with 2100-2400 rev/min of high-speed stirred 8 minutes, wood powder humid control is then respectively adding above-mentioned below 0.6%
Remaining each component, carries out batch mixing, batch mixing by above-mentioned batch mixing by the hot mixing system discharging of batch mixer to cold mixing system, be cooled to 62 DEG C,
Obtain premix material；2. prepared by pelletize pellet：Premix material Jing parallel double-screw extruder extruding pelletizations, technological temperature are set in
It is 180-185 DEG C, to be used as semi-finished product pelletize pellet etc.；3. it is prepared by extrusion molding：Particle after extruding pelletization is added to
Extrusion molding in conical double-screw, technological temperature are set in 170-180 DEG C, are extruded by mould, that is, obtain ageing-resistant modeling timber
The obtained product of material.
Step in present invention method can carry out order adjustment according to actual needs, merge and delete.
It is more than that to provided by the present invention, beneficial effects of the present invention are：Plastic-wood material aging resistance can be effectively improved
Difference, the problem of short life.
It is described in detail herein, applies specific case and the principle and embodiment of the present invention are explained
State, above example is only intended to help and understands the method for the present invention and its core concept；Simultaneously for the general skill of this area
Art personnel, according to the thought of the present invention, will change in specific embodiments and applications, in sum, this
Description should not be construed as limiting the invention.
Those skilled in the art can be understood that, for convenience and simplicity of description, the system of foregoing description
With the specific work process of unit, the corresponding process in preceding method embodiment is may be referred to, be will not be described here.
Claims (9)
1. a kind of ageing-resistant plastic-wood material, it is characterised in that the plastic-wood material is included by mass component：
2. ageing-resistant plastic-wood material as claimed in claim 1, it is characterised in that the plastic-wood material is included by mass component：
3. ageing-resistant plastic-wood material as claimed in claim 1, it is characterised in that the plastic-wood material is included by mass component：
4. ageing-resistant plastic-wood material as claimed in claim 1, it is characterised in that：The solubilizing agent is Polyglycerol ester of fatty acids.
5. ageing-resistant plastic-wood material as claimed in claim 1, it is characterised in that：The ultra-violet stabilizer is sodium salicylate.
6. ageing-resistant plastic-wood material as claimed in claim 1, it is characterised in that：The anti-microbial inoculum be bromo- 2 nitropropanes of 2--
1,3- glycol.
7. ageing-resistant plastic-wood material as claimed in claim 1, it is characterised in that：The coupling agent is silane coupler.
8. ageing-resistant plastic-wood material as claimed in claim 1, it is characterised in that：The age resister is polypropylene.
9. the preparation method of the ageing-resistant plastic-wood material as described in claim 1-8 is arbitrary, it is characterised in that the method includes：
It is prepared by premix material：Wood powder is added in high mixer, with 2100-2400 rev/min of high-speed stirred 8 minutes, wood powder humidity
Control below 0.6% is then respectively adding remaining above-mentioned each component, carries out batch mixing, and batch mixing is by above-mentioned batch mixing by batch mixer
Hot mixing system discharging is cooled to 62 DEG C, obtains premix material to cold mixing system；
It is prepared by pelletize pellet：Premix material Jing parallel double-screw extruder extruding pelletizations, technological temperature are set in into 180-185 DEG C,
It is to be used as semi-finished product pelletize pellet etc.；
It is prepared by extrusion molding：Particle after extruding pelletization is added to into extrusion molding in conical double-screw, technological temperature is set in
170-180 DEG C, extruded by mould, that is, obtain the product obtained by ageing-resistant plastic-wood material.